CN116251437A - Cloth bag dust collector for collecting nano-scale spherical silicon dioxide powder - Google Patents
Cloth bag dust collector for collecting nano-scale spherical silicon dioxide powder Download PDFInfo
- Publication number
- CN116251437A CN116251437A CN202310102233.1A CN202310102233A CN116251437A CN 116251437 A CN116251437 A CN 116251437A CN 202310102233 A CN202310102233 A CN 202310102233A CN 116251437 A CN116251437 A CN 116251437A
- Authority
- CN
- China
- Prior art keywords
- water
- water storage
- bag
- cavity
- dust collector
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a bag-type dust remover for collecting nano-scale spherical silicon dioxide powder, which comprises: the shell comprises a box body and a flow guide baffle; the flow guide baffle is arranged in the box body and divides the box body into an upper cavity and a lower cavity; the cloth bag capturing component is fixed in the box body through a flow guide baffle; the water curtain capturing component is arranged inside the cloth bag capturing component and forms a water film inside the cloth bag capturing component and is used for collecting silicon dioxide powder. According to the invention, the structure for capturing the silica particles is improved, and the water curtain capturing assembly and the water storage cavity are arranged, so that the water flow of the water curtain capturing assembly under the action of self gravity and the water in the water storage cavity can be used for cooling the gas just entering the lower cavity simultaneously when the water curtain capturing assembly captures the nano-scale spherical silica particles, the gas temperature in the box body can be effectively reduced, the working environment of the cloth bag capturing assembly is ensured, and the service life of the cloth bag dust collector is prolonged.
Description
Technical Field
The invention relates to the technical field of silicon dioxide powder collection, in particular to a bag-type dust collector for collecting nanoscale spherical silicon dioxide powder.
Background
The nano spherical silicon dioxide mainly refers to silicon dioxide powder with D50 smaller than 1 μm, and single particles of the nano spherical silicon dioxide are spherical. The particle size is small, the sphericity is high, and the particle has low expansion coefficient, high chemical and physical stability, low water absorption, high filling quantity, low forming stress, low friction and good dielectric property, thus having irreplaceable functions in various industries and fields. The nano spherical silicon dioxide can be used as an additive, a catalyst carrier, a plastic filler, an ink thickener, a metal soft polishing agent and an insulating and heat-insulating filler, and can be widely used in various fields of integrated circuit packaging, copper-clad plates, high-grade daily cosmetic fillers, spraying materials, medicines, environmental protection and the like.
The nanometer spherical silica used in the market at present is prepared by adopting a chemical method or a physical heating method, when the preparation is carried out by adopting the physical heating method, because the preparation of the nanometer spherical silica is carried out by melting quartz powder at high temperature, the temperature of the gas to be collected containing the silica is generally overhigh during final collection, the high temperature resistance of the conventional bag-type dust collector is generally 240 ℃ at most, the high temperature resistance is easy to damage when the bag-type dust collector is operated in a high temperature environment for a long time, the service life is short, the collection life is influenced, and a large amount of nanometer spherical silica is not easy to collect.
Disclosure of Invention
In order to solve the defects in the prior art, the invention aims to provide a cloth bag dust collector for collecting nano-scale spherical silicon dioxide powder.
In order to achieve the above purpose, the present invention adopts the following technical scheme:
a bag-type dust collector for collecting nano-sized spherical silica powder, the bag-type dust collector comprising:
the shell comprises a box body and a flow guide baffle; the flow guide baffle is arranged in the box body and divides the box body into an upper cavity and a lower cavity;
the cloth bag capturing component is fixed in the box body through the flow guide baffle plate;
the water curtain capturing component is arranged inside the cloth bag capturing component and forms a water film inside the cloth bag capturing component and is used for collecting silicon dioxide powder.
Further, the box body is provided with an airflow inlet and an airflow outlet;
the air flow inlet is arranged at the lower part of the box body and is communicated with the lower cavity; the air flow outlet is arranged at the upper part of the box body and is communicated with the upper cavity;
the upper cavity is communicated with the lower cavity through the cloth bag capturing component.
Further, a water storage cavity is formed in the bottom of the box body, and the water storage cavity is connected with a water supply pipe;
the upper end of the water supply pipe is connected with the water curtain capturing component, and the lower end of the water supply pipe is connected with the water storage cavity;
the water supply pipe is provided with a circulating water pump;
the water in the water storage cavity is supplied with energy through the circulating water pump and flows to the water curtain capturing component through the water supply pipe.
Further, a water filter screen is arranged in the water storage cavity, and the water filter screen divides the water storage cavity into a dust-containing water cavity and a filtering water cavity which are arranged up and down;
the filtering water cavity is communicated with the lower end of the water supply pipe;
the bottom of the shell is provided with a discharge outlet for discharging all water in the water storage cavity;
the lower end of the water supply pipe is provided with a flow regulating valve;
the water supply pipe is connected with a water inlet pipe, and the water inlet pipe is used for providing water source for the water supply pipe;
the water inlet pipe is provided with a water valve which is used for opening and closing the water inlet pipe;
the water supply pipe can be opened and closed or the water supply speed of the water supply pipe to the water curtain capturing component can be regulated through the flow regulating valve.
Further, the cloth bag capturing component comprises a supporting frame and a dust removing cloth bag sleeved outside the supporting frame; the water curtain capturing component is arranged in the supporting frame;
the support frame comprises a cylindrical support main body frame, a fixed seat arranged at one end of the support main body frame and a round sealing plate arranged at the other end of the support main body frame and used for sealing one end of the support frame; a plurality of vent holes are formed in the support main body frame;
the support frame is fixedly arranged on the flow guide baffle through the fixing seat, and a flow hole is formed in the end part of the flow guide baffle, which corresponds to the support frame.
Further, the water curtain capturing component comprises a central tube connected with the sealing plate, a water storage disc vertically connected with one end of the central tube, a water curtain tube body with the upper end connected with the water storage disc, a collecting block arranged at the lower end of the water curtain tube body and a limiting ring fixedly arranged on the inner wall of the supporting frame corresponding to the water storage disc;
the water curtain pipe body is a cylindrical tubular piece;
an annular overflow port is formed between the limiting ring and the water storage disc, and water flow of the water storage disc flows to the outer surface of the water curtain pipe body through the overflow port to form a water film.
Further, the central tube, the water storage disc, the limiting ring, the water curtain tube body, the collecting block and the supporting frame are coaxially arranged, and the maximum diameters of the cross sections of the water storage disc, the water curtain tube body and the collecting block are consistent.
Further, the central tube is axially arranged in the center of the sealing plate, and the central tube is arranged on the sealing plate in a penetrating manner;
the water storage disc is characterized in that a plurality of outflow holes are radially formed in the end portion, connected with the water storage disc, of the central tube, the upper end of the central tube is arranged corresponding to the water outlet of the water supply tube, and water in the water supply tube enters the central tube through the water outlet and flows onto the water storage disc through the outflow holes.
Further, the water storage disc is arranged in a disc shape, a circular limiting block is arranged on the upper surface of the water storage disc, the limiting block and the water storage disc are coaxially arranged, and a water storage space is formed on the upper surface of the water storage disc through limiting of the limiting block;
the cross section of stopper is triangle-shaped, just the base of limiting plate cross section with the upper surface laminating of water storage disc is fixed, makes the inner wall and the outer wall of stopper all set up to the inclined plane.
Further, the limiting ring is in a horn shape, the diameter of the upper end of the limiting ring is larger than that of the lower end of the limiting ring, the upper end of the limiting ring is fixedly connected with the inner wall of the supporting frame, and the lower end of the limiting ring is arranged corresponding to the outer wall of the limiting block;
a gap is arranged between the lower end of the limiting ring and the outer wall of the limiting block, and the gap is the overflow port.
Compared with the prior art, the invention has the advantages that:
according to the invention, the structure for capturing the silica particles is improved, and the water curtain capturing assembly and the water storage cavity are arranged, so that the water flow of the water curtain capturing assembly under the action of self gravity and the water in the water storage cavity can be used for cooling the gas just entering the lower cavity simultaneously when the water curtain capturing assembly captures the nano-scale spherical silica particles, the gas temperature in the box body can be effectively reduced, the working environment of the cloth bag capturing assembly is ensured, and the service life of the cloth bag dust collector is prolonged.
Drawings
FIG. 1 is a schematic view of a bag-type dust collector of the present invention;
FIG. 2 is a schematic diagram of the connection structure of the water curtain capturing component and the cloth bag capturing component in the invention;
FIG. 3 is a schematic view of the connection structure of the central tube of the present invention;
FIG. 4 is a schematic structural view of a device for preparing nano spherical silica powder;
FIG. 5 is a schematic view of the structure of the gasification furnace;
FIG. 6 is a cross-sectional view of a combustor;
FIG. 7 is a top view of a combustor;
FIG. 8 is a view in the A-A direction of FIG. 5;
FIG. 9 is an SEM image of spherical silica collected by a bag-type dust collector in accordance with example one;
FIG. 10 is an SEM image of spherical silica collected by a bag house in example two.
Wherein:
1-a gasification furnace; a 2-condenser; 3-cyclone collector; 4-a bag-type dust remover; 5-induced draft fan; 11-an inner layer body; 12-middle layer body; 13-an outer layer body; 14-a protection part; 15-a burner; 16-exhaust port; 41-a housing; 42-a water curtain capture assembly; 43-a cloth bag capturing component; 44-an air flow outlet; 45-box body; 46, a flow guide baffle; 47-air inlet; 48-water storage cavity; 49-water screen; 50-a water supply pipe; 111-bottom guide blocks; 112-top guide block; 141-protecting the guide groove; 142-a first connection tube; 143-a second connection tube; 144-communicating pipe; 151-communicating portions; 152-flame spreading part; 153-combustion tank; 154-a feed line; 155-a combustible gas conduit; 156-a fuel gas assisting pipeline; 157-a shielding gas conduit; 421-central tube; 422-a water storage disc; 423-limiting rings; 424-water curtain pipe body; 425-collection blocks; 426—overflow port; 427-limiting block; 428-outflow hole; 431-a dust removing cloth bag; 432-a support body frame; 433-fixing seat; 434-closing plates; 1411-guide groove walls; 1421-guide section; 1422-connecting section; 4211-a fixed segment; 4212-a clamping section; 4213-fixed block.
Detailed Description
The invention is further described below with reference to the accompanying drawings:
a bag-type dust collector 4 for collecting nano-sized spherical silica powder as shown in fig. 1, the bag-type dust collector 4 comprising a housing 41, a water curtain catching assembly 42 and a bag catching assembly 43. The housing 41 includes an airflow outlet 44, a box 45, a baffle 46, and an airflow inlet 47. The flow guide baffle 46 is disposed inside the box 45, and the flow guide baffle 46 divides the inside of the housing 41 into an upper cavity and a lower cavity, and the upper cavity is communicated with the lower cavity through the cloth bag capturing component 43. The air flow outlet 44 is provided at an upper portion of the case 45 and communicates with the upper chamber, and the air flow inlet 47 is provided at a lower portion of the case 45 and communicates with the lower chamber. The cloth bag capturing component 43 is fixed inside the box 45 through the flow guiding baffle 46. The water curtain capturing component 42 is fixedly arranged inside the cloth bag capturing component 43. The gas containing nano-sized spherical silica enters the inside of the tank 45 through the gas flow inlet 47 and is discharged from the gas flow outlet 44 by the filtering action of the water curtain catching member 42 and the cloth bag catching member 43.
The bottom of the box 45 is provided with a water storage cavity 48, the lower end of a water supply pipe 50 is communicated with the water storage cavity 48, and the upper end of the water supply pipe 50 is communicated with the water curtain capturing component 42. The water supply pipe 50 is provided with a circulating water pump, and water in the water storage cavity 48 flows to the water curtain catching assembly 42 through the water supply pipe 50 by the energy of the circulating water pump so as to form a water curtain for catching particles of the silicon dioxide-containing gas.
A water filter screen 49 is arranged in the water storage cavity 48, and the water filter screen 49 divides the water storage cavity 48 into a dust-containing water cavity and a filtering water cavity which are arranged up and down. The dust-containing water cavity is arranged above the filtering water cavity. The lower end of the water supply pipe 50 is communicated with the filtering water cavity, and the arrangement of the water filter screen 49 reduces the silicon dioxide particles from entering the water circulation.
Generally, the bottom of the housing 41 is provided with a discharge port, and the lower end of the water supply pipe 50 is provided with a flow rate adjusting valve. The water supply pipe 50 is connected with a water inlet pipe, and a water valve is arranged on the water inlet pipe. The water supply pipe 50 can be opened and closed by the flow regulating valve or the water supply speed of the water supply pipe 50 to the water curtain catching assembly 42 can be regulated, the discharge outlet is used for discharging all water in the water storage cavity 48, the water inlet pipe is used for providing a new water source for the water supply pipe 50, and the water valve is used for opening and closing the water inlet pipe.
The water filter 49 is detachable or rotatable, when silica is collected, the water in the water storage cavity 48 is drained, the flow regulating valve and the water valve are closed, the water filter 49 is detached or rotated, and silica particles of the water filter 49 are accumulated in the drain port to be collected and drained in a concentrated mode.
The invention adopts the physical flame combustion method to prepare spherical silicon dioxide, even if the condenser 2 is arranged in the middle for cooling and spheroidizing solidification, the discharged gas with silicon dioxide particles still has higher temperature, the conventional cyclone collector 3 adopts a wind power sedimentation mode to separate solid particles, so the temperature requirement of the cyclone collector 3 on the gas is not high, but for the conventional bag-type dust collector, the general working temperature of a high-temperature dust collection bag is 160-260 ℃, the corresponding structure of the captured particles is improved, and the water curtain capturing assembly 42 is arranged to capture nano-scale spherical silicon dioxide particles, meanwhile, the water flow of the water curtain capturing assembly 42 under the action of self gravity and the water in the water storage cavity 48 can be used for cooling the gas just entering the lower cavity, so the gas temperature in the box 45 can be effectively reduced, the working environment of the bag capturing assembly 43 is ensured, and the working life of dust collection is prolonged.
The connection structure of the water curtain capturing component and the cloth bag capturing component is shown in fig. 2. The cloth bag capturing assembly 43 includes a support frame and a dust removing cloth bag 431. The dust removing cloth bag 431 is fixedly sleeved outside the supporting frame, and the water curtain capturing component 42 is arranged in the supporting frame. The support frame comprises a cylindrical support main body frame 432, and a plurality of ventilation holes are formed in the support main body frame 432, so that gas can pass through the dust removing cloth bag 431 from the inside of the support frame to the outside. One end of the supporting main body frame 432 is provided with a fixing seat 433, the other end is provided with a circular sealing plate 434, and the sealing plate 434 seals one end of the supporting frame. The support frame is fixedly arranged on the flow guide baffle 46 through the fixing seat 433, and a flow hole is formed in the end part of the flow guide baffle 46 corresponding to the support frame, so that the gas in the lower cavity can conveniently enter the support frame through the flow hole. Generally, the fixing seat 433 is provided in a ring shape, and the fixing seat 433 is fixedly sleeved at the end of the supporting frame.
The water curtain catching assembly 42 comprises a central tube 421, a water storage disc 422, a limiting ring 423, a water curtain tube 424 and a collecting block 425. The water curtain pipe body 424 is a cylindrical pipe-shaped member, and the water storage disc 422 is fixedly arranged at the upper end of the water curtain pipe body 424. The lower end of the water curtain pipe 424 is fixedly provided with the collecting block 425. The limiting ring 423 is fixedly arranged on the inner wall of the supporting frame corresponding to the water storage disc 422. The central tube 421 is fixedly disposed on the sealing plate 434, and one end of the central tube 421 is vertically fixed on the water storage disc 422. An annular overflow port 426 is formed between the limiting ring 423 and the water storage disc 422. The water flow of the water storage disc 422 flows to the outer surface of the water curtain pipe body 424 through the overflow port 426 to form a continuous and uniformly distributed water film.
Preferably, the central pipe 421, the water storage disc 422, the limiting ring 423, the water curtain pipe body 424, the collecting block 425 and the supporting frame are all coaxially arranged, and the maximum diameters of the cross sections of the water storage disc 422, the water curtain pipe body 424 and the collecting block 425 are consistent, so that a water film which is uniformly distributed is formed outside the water curtain capturing assembly 42.
When the gas enters the inside of the supporting frame, the gas circulates in the annular space between the water curtain pipe body 424 and the supporting frame and passes through the dust removing cloth bag 431, and in the circulation process of the annular space, the gas contacts with the surface of the water film, so that the water film can catch silica particles in the gas, the caught silica moves downwards along the water film, finally is collected in the water storage cavity 48, and the water is filtered and remained on the water filter 49 through the water filter 49.
According to the invention, through the dry and wet dual particle capturing of the cloth bag capturing component 43 and the water curtain capturing component 42, the collection efficiency of nano-scale silicon dioxide particles in gas is greatly improved, and meanwhile, the particles are collected in a concentrated manner in a water flow mode, so that the dust emission phenomenon of nano-scale silicon dioxide during recycling is avoided, and the final nano-scale silicon dioxide particles can be obtained by carrying out water vapor evaporation on the silicon dioxide liquid with the particles.
Preferably, the central tube 421 is disposed in a central axial direction of the sealing plate 434, the central tube 421 penetrates through and is fixedly disposed on the sealing plate 434, a plurality of outflow holes 428 are radially disposed at an end portion of the central tube 421 connected with the water storage disc 422, an upper end of the central tube 421 is disposed corresponding to a water outlet of the water supply tube 50, and water in the water supply tube 50 enters the central tube 421 through the water outlet and flows onto the water storage disc 422 through the outflow holes 428.
Generally, the water storage disc 422 is disc-shaped, and the upper surface of the water storage disc 422 is provided with a circular limiting block 427, the limiting block 427 and the water storage disc 422 are coaxial, a water storage space is formed on the upper surface of the water storage Shui Yuanpan by limiting the limiting block 427, water flowing out of the central tube 421 is converged in the water storage space, and after converging to a certain volume, the liquid level in the water storage space is higher than the upper edge of the limiting block 427, so that a water film is formed along the outer wall of the limiting block 427 from the overflow port 426 to the water curtain tube 424.
Preferably, the cross section of the limiting block 427 is set to be triangular, and the bottom edge of the cross section of the limiting block 427 is attached to the upper surface of the water storage disc 422, so that the inner wall and the outer wall of the limiting block 427 are both inclined surfaces, and water flows overflow conveniently.
The limiting ring 423 is in a horn shape, the diameter of the upper end of the limiting ring 423 is larger than that of the lower end of the limiting ring 423, the upper end of the limiting ring 423 is fixedly connected with the inner wall of the supporting frame, the lower end of the limiting ring 423 corresponds to the outer wall of the limiting block 427, a gap is arranged between the lower end of the limiting ring 423 and the outer wall of the limiting block 427, and the gap is the overflow port 426.
Through the spacing ring 423 with the structure setting of water storage disc 422 forms overflow mouth 426, and in the course of the work, overflow mouth 426 is submerged by water, forms watertight structure to avoid dust-laden gas from getting into from the upper end of sack capture assembly 43.
Preferably, the collecting block 425 is provided as a cone, and the circular bottom of the collecting block 425 is fixedly provided at the bottom end of the water curtain pipe 424, so that water of the water film is convenient to flow down at the tip of the collecting block.
As shown in the connection structure schematic diagram of the central tube in fig. 3, a connection hole is provided at the center of the sealing plate 434, and the connection hole is provided as a threaded hole, corresponding to the threaded hole, and an external thread is provided on the outer circular surface of the central tube 421, and the central tube 421 is in threaded connection with the connection hole, so that the rapid disassembly between the water curtain capturing component 42 and the cloth bag capturing component 43 can be realized.
For realizing to spacing ring 423 with the accurate counterpoint of stopper 427, control the size of overflow mouth 426, center tube 421 includes fixed section 4211 and joint section 4212, the cross section diameter of fixed section 4211 is less than the cross section diameter of joint section 4212, be provided with the external screw thread on the fixed section 4211, fixed section 4211 with shrouding 434 is connected, joint section 4212 upper end with shrouding 434 joint location to guarantee to dismantle at every turn after, spacing ring 423 with stopper 427 homoenergetic is accurate counterpoint.
Similarly, the fixing section 4211 is further screwed with a fixing block 4213, the fixing block 4213 is disposed above the sealing plate 434, and the fixing block 4213 is attached to the sealing plate 434, so as to enhance the connection stability between the central tube 421 and the sealing plate 434, and simultaneously, the central tube 421 can be adjusted by adjusting the position of the central tube 421 and fixing the central tube 421 by the fixing block 4213, so that real-time adjustment of the size of the overflow port 426 is achieved.
The cloth bag dust collector, the gasification furnace, the condenser, the cyclone collector and the induced draft fan form a silicon dioxide powder preparation device. Fig. 4 is a schematic structural view of a silica powder preparation apparatus, which includes a vaporization furnace 1, a condenser 2, a cyclone collector 3, a bag-type dust collector 4 and an induced draft fan 5, which are sequentially connected. The bottom in the gasification furnace 1 is provided with a burner, the upper end of the gasification furnace 1 is connected with the condenser 2 through a conveying pipeline, and a temperature monitor is arranged in the gasification furnace 1. The condenser 2, the cyclone collector 3, the bag-type dust collector 4 and the induced draft fan 5 are sequentially connected, and the combustion control system is connected with the burner and the temperature monitor to control the combustion temperature of the burner so as to control the temperature in the gasification furnace 1.
As shown in fig. 5, the gasification furnace 1 includes a furnace body. The inside cylinder-shaped inner chamber that is provided with of furnace body, the bottom of inner chamber is provided with combustor 15. The top of the inner cavity is provided with an exhaust port 16, the exhaust port 16 is connected with the condenser 2 through a conveying pipeline, and the burner 15 generates high-temperature flame with the temperature of more than 3000 ℃. The furnace body comprises an inner layer body 11, a middle layer body 12 and an outer layer body 13, wherein the inner layer body 11 is made of corundum-alumina material, and the thickness of the corundum-alumina material is 250-400 mm. The middle layer body 12 adopts heat-insulating rock wool, and the thickness of the heat-insulating rock wool is 200 mm-300 mm. The outer layer 13 is a carbon steel protective layer. The furnace body is provided with a protection part 14 corresponding to the arc surface of the inner cavity, and the protection part is used for reducing contact between silicon dioxide steam and the inner wall of the furnace body.
The vaporization furnace 1 is different from the existing high-temperature melting furnace with flame balling, the burner 15 for heating the material is arranged at the bottom of the furnace body, and the vaporized silicon dioxide rises through bottom feeding, is discharged from the upper part of the furnace body to the condenser 2 for rapid cooling, so that nano-scale silicon dioxide particles are easier to form. Compared with the existing high-temperature melting furnace, the invention has less solid particles of silicon dioxide discharged from the vaporizing furnace 1, and the silicon dioxide is more easy to sink under the action of self gravity in the rising process of the silicon dioxide and is vaporized again by the heating of the burner 15, so that the purity of the silicon dioxide vapor cooled in the condenser 2 is improved, and the final nano-scale spherical silicon dioxide generation amount is improved. And the flame temperature of the burner 15 is far higher than the boiling point of quartz 2230 ℃, so that the overall temperature in the inner cavity is higher than 2230 ℃ and the silicon dioxide in the inner cavity is ensured to be in a better vaporization state.
As shown in fig. 6 and 7, the burner 15 includes a communication portion 151 and a flame spreading portion 152. The flame spreading part 152 is fixedly arranged on the furnace body, the communication part 151 is fixedly arranged at the bottom of the flame spreading part 152, and the communication part 151 and the flame spreading part 152 are coaxially arranged. The flame expansion portion 152 is internally provided with a combustion groove 153, the cross section of the combustion groove 153 is circular, and the cross section diameter of the combustion groove 153 gradually increases in the axial direction away from the communication portion 151, so as to form a combustion flame with a better shape. The center of the communicating part 151 is axially provided with a feeding pipeline 154, and the communicating part 151 is provided with a combustible gas pipeline 155, a combustion-supporting gas pipeline 156 and a protective gas pipeline 157 from inside to outside in sequence by taking the feeding pipeline 154 as the center. The combustible gas pipeline 155, the combustion-supporting gas pipeline 156 and the protection gas pipeline 157 are all arranged in a circular ring groove shape, and the combustible gas pipeline 155, the combustion-supporting gas pipeline 156, the protection gas pipeline 157 and the feeding pipeline 154 are all coaxially arranged. The feeding pipe 154 is used for conveying oxygen and quartz powder, the combustible gas pipe 155 is used for conveying combustible gas, the combustion-supporting gas pipe 156 is used for conveying combustion-supporting gas, and the protecting gas pipe 157 is used for conveying oxygen.
Through the above structure, the burner 15 can ensure that the combustion-supporting gas and oxygen in the protective gas pipe 157 and the combustion-supporting gas pipe 156 enter the combustion groove 153 more uniformly, and the quartz powder needs to be moved outwards from the center of the combustion flame, so that the quartz powder can be fully combusted, and the oxygen in the protective gas pipe forms a barrier in the combustion groove 153, so as to avoid the adhesion of melted particles on the wall of the combustion groove 153. Meanwhile, due to the centralized arrangement of the feeding pipeline 154, the combustible gas pipeline 155, the combustion-supporting gas pipeline 156 and the protecting gas pipeline 157, in the moving process of quartz powder, the quartz powder is atomized under the impact action of the gas exhausted by the combustible gas pipeline 155, the combustion-supporting gas pipeline 156 and the protecting gas pipeline 157, so that mutual adhesion among particles can be effectively avoided, each quartz glass liquid drop can be independently balled, and the generation of large particles and the granularity drift are reduced.
For the connection of each pipeline and outside of being convenient for, the intercommunication portion 151 includes a plurality of cylinder type connecting blocks of fixed connection in proper order, the connecting block is coaxial to be set up, and follows to keep away from the direction of flame expansion portion 152, each the diameter of connecting block reduces in proper order, thereby form a plurality of bosss on the intercommunication portion 151, each be provided with the connection interface on the outer disc of connecting block respectively to correspond different pipelines, in order to realize the connection between different pipelines and each air feed subassembly, when reducing combustor 15 weight, guarantee innermost the distance of combustible gas pipeline 155 and corresponding connection interface also can reach minimumly.
The burner 15 in the invention can adjust the length of the combustion flame through adjusting the flow of the combustible gas and the flow of the combustion-supporting gas, so that powder particles are completely melted into gas, and can also adjust the residence time of quartz powder particles in the flame through adjusting the flow rate of quartz powder, so that the oxygen is used for conveying raw materials to keep a full-oxygen atmosphere, and the combustion efficiency is improved.
The inner layer 11 is provided with a bottom guide block 111 corresponding to the burner 15, the bottom guide block 111 is provided with a ring-shaped member with a trapezoid cross section, the burner 15 is arranged at the center of the bottom guide block 111, the upper end of the bottom guide block 111 is provided with a cylindrical bottom guide groove, the diameter of the cross section of the upper end of the bottom guide groove is larger than that of the cross section of the lower end, so that the upper end of the bottom guide block 111 is obliquely arranged towards the center, the accumulation of solid quartz powder in the furnace body is avoided, and the solid quartz powder is gathered towards the burner 15 under the action of self gravity due to the inclined end of the bottom guide block 111, so that full combustion and vaporization are realized.
The inner layer 11 is provided with a top guide block 112 at the top of the furnace body, the top guide block 112 is provided with a ring-shaped member with a triangular cross section, the exhaust port 16 is arranged at the center of the top guide block 112, the center of the top guide block 112 is provided with a cylindrical top guide groove, the cross section diameter of the lower end of the top guide groove is larger than that of the upper end, so that the inner wall of the top guide block 112 is inclined towards the center, and the silicon dioxide steam in the inner cavity is conveniently discharged from the exhaust port 16 smoothly.
The protection part 14 comprises a plurality of protection air passage components, at least three protection air passage components are arranged at the same height of the furnace body, annular protection groups are uniformly distributed on the protection air passage components arranged at the same height in an annular mode, and a plurality of annular protection groups are vertically arranged on the furnace body. The gas introduced through the protective gas passage assembly can form a gas circulation on the inner wall of the furnace so as to reduce the contact between the silica vapor and the inner layer 11.
As shown in fig. 8, the protection airway assembly includes a protection guide groove 141, a first connection pipe 142, a second connection pipe 143, and a connection pipe 144. The protection guide groove 141 is provided on the inner wall of the inner layer 11. The first connecting pipe 142 is fixedly arranged on the inner layer 11, and the second connecting pipe 143 is fixedly arranged on the outer layer 13. The communicating pipe 144 is fixedly disposed in the middle layer 12, one end of the communicating pipe 144 is communicated with the protection guide groove 141 through the first connecting pipe 142, and the other end of the communicating pipe 144 is communicated with an external air supply device through the second connecting pipe 143. The protection guide groove 141, the first connection pipe 142 and the communication pipe 144 are integrally spirally extended outside the inner cavity, and the protection guide groove 141, the first connection pipe 142 and the communication pipe 144 are sequentially arranged from high to low.
The structure of the protection air flue assembly is arranged when the inner wall of the inner layer body 11 forms a protection air layer, the protection air layer flows in a spiral mode, so that a certain supporting effect is achieved on the silicon dioxide steam in the furnace body, the silicon dioxide steam is conveniently discharged from the exhaust port 16, and the moving speed of the silicon dioxide steam to the condenser 2 is accelerated.
The first connecting pipe 142 penetrates through the inner layer 11, and the port axis of the first connecting pipe 142 connected with the protection guide groove 141 is tangential to the circular cross section of the inner cavity, so that the disturbance of the exhaust gas of the first connecting pipe 142 to the silica vapor in the inner cavity is reduced, and meanwhile, the arrangement of the protection guide groove 141 is more beneficial to forming a protection air layer on the inner wall of the inner layer 11.
Preferably, the first connecting pipe 142 includes a guiding section 1421 and a connecting section 1422 that are connected to each other, the guiding section 1421 is connected to the protecting guiding groove 141, and the axis of the guiding section 1421 is tangential to the circular cross section of the inner cavity, and the connecting section 1422 is connected to the communicating pipe 144, so as to ensure that the communicating pipe 144 slowly excessively passes toward the guiding section 1421.
The communicating pipe 144 is buried in the middle layer 12, and the whole length of the communicating pipe 144 is longer due to the spiral extension, so that the temperature of the gas in the communicating pipe 144 is conveniently increased in the furnace body, and the influence of the temperature of the protective gas layer on the silica vapor is avoided.
Preferably, the second connection pipe 143 is communicated with an external air supply device through a heat exchange pipe, and the heat exchange pipe is wound on the conveying pipeline between the air outlet 16 and the condenser 2, and exchanges heat with the silica vapor of the conveying pipeline, so as to further ensure the temperature of the protective air layer conveyed into the inner cavity. It is worth noting that it is also possible to operate directly by heat exchange with the silica vapor in the condenser 2.
The protection guide groove 141 extends spirally along the inner layer 11, and a guide groove wall 1411 is further provided at the edge of the protection guide groove 141, in addition to the position corresponding to the first connecting pipe 142, and the guide groove wall 1411 extends obliquely from the bottom of the protection guide groove 141 to the inner wall of the inner layer 11, so as to form a protection air layer attached to the inner wall of the inner layer 11.
The preparation method for preparing the nano spherical silicon dioxide powder by adopting the preparation device comprises the following steps:
s1, mixing and burning combustible gas and combustion-supporting gas through a burner, wherein the burner is arranged in the gasification furnace 1, and the mixed combustion generates high-temperature flame with the temperature of more than 3000 ℃ in the gasification furnace 1, and the temperature of the outer flame of the high-temperature flame is more than 2500 ℃.
S2, feeding quartz powder into high-temperature flame from a feeding pipeline, and performing solid-liquid-gas conversion on the quartz powder to obtain silicon dioxide steam.
S3, starting the induced draft fan 5, generating negative pressure in the gasification furnace 1, enabling silicon dioxide steam to enter the condenser 2 along the conveying pipeline under the action of the negative pressure, rapidly cooling in the condenser 2, and converting the gas state into the solid state to form spherical silicon dioxide particles.
S4, spherical nano silicon dioxide particles in the condenser 2 move into the collecting part under the traction of the induced draft fan 5, and the collecting part collects the spherical silicon dioxide particles.
Preferably, in the step S1, the heat value of the combustible gas is higher than 12500Kcal/Nm3, and the combustion-supporting gas adopts oxygen with purity higher than 99%.
The gas flow rate of the combustible gas in the burner is 50m 3/h-250 m3/h, and the gas flow rate of the combustion-supporting gas is 100m 3/h-500 m3/h.
Preferably, the median particle diameter of the quartz powder is set to be 5-30 mu m, the maximum particle is not more than 100 mu m, and the feeding speed of the quartz powder is 50-200 kg/h.
In the step S2, the quartz powder is fed into the gasification furnace 1 from the burner center by using oxygen as a conveying gas, and the pressure of the conveying gas is set to be 0.3Mpa to 0.6Mpa. Because the inert gas does not participate in combustion, the invention adopts oxygen to transport raw materials, can avoid the disturbance of inert gas to the normal distribution of flame temperature, improve the balling rate, reduce the influence of transport medium to flame form and flame temperature, and simultaneously reduce the pollution of impurities to silicon dioxide particles.
Generally, the refrigerating capacity of the condenser 2 is not lower than 200kw; the induced draft fan 5 is a variable frequency fan, and the power is 110 kw-160 kw.
Preferably, the granularity of the final nano particles is controlled by controlling the cooling rate of the condenser 2, and when the cooling rate of the condenser 2 is set to be 100 ℃/s to 200 ℃/s, the granularity of the nano-scale spherical silica particles is 50 nanometers to 1500 nanometers; when the cooling rate of the condenser 2 is set to be 200 ℃/s-400 ℃/s, the granularity of the nanoscale spherical silica particles is 20-1000 nanometers.
The collecting part comprises a cyclone collector 3 and a cloth bag dust collector 4, wherein the cyclone collector 3 is connected with the condenser 2, the cloth bag dust collector 4 is arranged between the cyclone collector 3 and the induced draft fan 5, the cyclone collector 3 is used for collecting spherical silica particles with the micron level, and the cloth bag dust collector 4 is used for collecting spherical silica particles with the nanometer level.
In the step S1, the gasification furnace 1 includes an inner layer body, a middle layer body and an outer layer body, the inner layer body is made of corundum alumina, the thickness is 250 mm-400 mm, the middle layer body is made of thermal insulation rock wool, the thickness is 200 mm-300 mm, and the outer layer body is made of carbon steel protective layer.
It should be noted that, during the process of transporting the silicon dioxide from the gasification furnace 1 to the condenser 2, an auxiliary heating device can be added to heat and preserve heat of the silicon dioxide, so as to ensure that the silicon dioxide is always in a gas state during the process of transporting the gasification furnace 1 to the condenser 2. The auxiliary heating device can be an existing conventional heating means such as a heating patch or an auxiliary heating furnace arranged in the conveying pipeline.
The invention can control the growth of silicon dioxide crystal grains by adjusting the factors of flame temperature, feeding granularity, cooling speed and the like to control the granularity of the final spherical nano silicon dioxide, and the high-temperature flame with the temperature of more than 3000 ℃ is used for vaporizing quartz powder and cooling to obtain the nano-scale spherical silicon dioxide with large proportion. According to the invention, the solid quartz powder raw material is directly heated to form gaseous silicon dioxide gas, and the gaseous silicon dioxide is directly condensed in the condenser to form spherical silicon dioxide solid particles, so that the generation amount of the nano-scale silicon dioxide solid particles can be greatly increased, and a large amount of nano-spherical silicon dioxide powder is prepared.
In the embodiment, the height of the gasification furnace 1 is 6 meters, the effective diameter is 1200mm, 4 infrared thermometers are uniformly distributed on the gasification furnace 1 to measure the temperature of flame outer flame, and the combustion control system adjusts the flow of fuel gas and oxygen through temperature feedback.
The inner layer body of the gasification furnace is an alumina brick with the thickness of 300mm, the middle layer body is heat-insulating rock wool with the thickness of 200mm, and the outer layer body is a carbon steel protective layer. The burner is positioned at the bottom of the gasification furnace 1, and the material outlet is positioned at the top of the gasification furnace 1.
The power of the induced draft fan 5 is 132kw, the induced draft fan 5 is started, the frequency of the frequency converter is 45Hz, negative pressure is generated in the whole process pipeline system, and the pressure is controlled to be-1.5 kpa. Starting the condenser 2, wherein the refrigerating capacity of the condenser 2 is 200kw; the cooling rate of the condenser 2 is set to 200 ℃/s.
The burner is started, acetylene is used as fuel, oxygen (the purity is more than 99%) is used as combustion-supporting gas, the combustion-supporting gas is mixed by the oxy-fuel burner, high-temperature flame is generated in the gasification furnace 1 in a combustion mode, the flame outer flame temperature is 2500 ℃, and the inner flame temperature is 3100 ℃.
Crystalline quartz powder is used as a raw material, D50=5μm, the maximum particle size is smaller than 30 μm, the SiO2 content is 99.81%, and the specific surface area is 3.1m < 2 >/g. Oxygen with purity not lower than 99% is used as conveying gas, crystalline quartz powder is added into the gasification furnace 1 through the feeding pipeline, and the quartz powder absorbs heat in flame due to the fact that flame temperature is far higher than quartz boiling point 2230 ℃, so that solid-liquid-gas conversion is instantly completed, and silicon dioxide steam is formed.
Under the action of negative pressure, the silicon dioxide steam enters the condenser 2 along a conveying pipeline, is rapidly cooled in the condenser 2, and is converted from a gaseous state to a solid state to form spherical nano silicon dioxide particles.
The cyclone collector 3 collects the mu m-grade spherical silica d50=3 mu m, the bag-type dust collector 4 collects the nano-grade spherical silica d50=0.4 mu m, the maximum particle is 0.9 mu m, the SiO2 content is 99.72 percent, and the specific surface area is 23.1m < 2 >/g.
Fig. 9 is an SEM image of spherical silica collected by the bag-type dust collector 4 of the present embodiment. As is evident from FIG. 9, most of the spherical silica particles have a nano-scale particle size, except that a very small fraction of the spherical silica particles can reach a particle size of approximately 1. Mu.m.
Example two
In the embodiment, the height of the gasification furnace 1 is 6 meters, the effective diameter is 1200mm, 4 infrared thermometers are uniformly distributed on the gasification furnace 1 to measure the temperature of flame outer flame, and the combustion control system adjusts the flow of fuel gas and oxygen through temperature feedback.
The inner layer body of the gasification furnace is an alumina brick with the thickness of 300mm, the middle layer body is heat-insulating rock wool with the thickness of 200mm, and the outer layer body is a carbon steel protective layer. The burner is positioned at the bottom of the gasification furnace 1, and the material outlet is positioned at the top of the gasification furnace 1.
The power of the induced draft fan 5 is 132kw, the induced draft fan 5 is started, the frequency of the frequency converter is 30Hz, negative pressure is generated in the whole process pipeline system, and the pressure is controlled to be-0.9 kpa. Starting the condenser 2, wherein the refrigerating capacity of the condenser 2 is 300kw; the cooling rate of the condenser 2 was set at 320 deg.c/s.
The burner is started, acetylene is used as fuel, oxygen (the purity is more than 99%) is used as combustion-supporting gas, the combustion-supporting gas is mixed by the oxy-fuel burner, high-temperature flame is generated in the gasification furnace 1 in a combustion mode, the flame outer flame temperature is 2700 ℃, and the inner flame temperature is 3300 ℃.
Crystalline quartz powder is used as a raw material, D50=15 mu m, the maximum particle size is smaller than 60 mu m, the SiO2 content is 99.83%, and the specific surface area is 1.2m2/g. Oxygen with purity not lower than 99% is used as conveying gas, crystalline quartz powder is added into the gasification furnace 1 through the feeding pipeline, and the quartz powder absorbs heat in flame due to the fact that flame temperature is far higher than quartz boiling point 2230 ℃, so that solid-liquid-gas conversion is instantly completed, and silicon dioxide steam is formed.
Under the action of negative pressure, the silicon dioxide steam enters the condenser 2 along a conveying pipeline, is rapidly cooled in the condenser 2, and is converted from a gaseous state to a solid state to form spherical nano silicon dioxide particles.
The cyclone collector 3 collects the mu m-grade spherical silica d50=2 mu m, the bag-type dust collector 4 collects the nano-grade spherical silica d50=0.2 mu m, the maximum particle size is 0.8 mu m, the SiO2 content is 99.65%, and the specific surface area is 32.6m2/g.
Other embodiments are the same as the first embodiment.
Fig. 10 is an SEM image of spherical silica collected by the bag-type dust collector 4 of the present embodiment. It is apparent from fig. 10 that the particle sizes of all the spherical silica particles are nano-sized.
The above examples are only illustrative of the preferred embodiments of the present invention and are not intended to limit the scope of the present invention, and various modifications and improvements made by those skilled in the art to the technical solutions of the present invention should fall within the scope of protection defined by the claims of the present invention without departing from the spirit of the present invention.
Claims (10)
1. A bag-type dust collector for collecting nano-scale spherical silica powder, characterized in that the bag-type dust collector comprises:
the shell comprises a box body and a flow guide baffle; the flow guide baffle is arranged in the box body and divides the box body into an upper cavity and a lower cavity;
the cloth bag capturing component is fixed in the box body through the flow guide baffle plate;
the water curtain capturing component is arranged inside the cloth bag capturing component and forms a water film inside the cloth bag capturing component and is used for collecting silicon dioxide powder.
2. The bag-type dust collector according to claim 1, wherein an air inlet and an air outlet are formed in the box body;
the air flow inlet is arranged at the lower part of the box body and is communicated with the lower cavity; the air flow outlet is arranged at the upper part of the box body and is communicated with the upper cavity;
the upper cavity is communicated with the lower cavity through the cloth bag capturing component.
3. The bag-type dust collector according to claim 1, wherein a water storage cavity is formed in the bottom of the box body, and a water supply pipe is connected to the water storage cavity;
the upper end of the water supply pipe is connected with the water curtain capturing component, and the lower end of the water supply pipe is connected with the water storage cavity;
the water supply pipe is provided with a circulating water pump;
the water in the water storage cavity is supplied with energy through the circulating water pump and flows to the water curtain capturing component through the water supply pipe.
4. A bag-type dust collector according to claim 3, wherein a water filter screen is arranged in the water storage cavity, and the water filter screen divides the water storage cavity into a dust-containing water cavity and a filtering water cavity which are arranged up and down;
the filtering water cavity is communicated with the lower end of the water supply pipe;
the bottom of the shell is provided with a discharge outlet for discharging all water in the water storage cavity;
the lower end of the water supply pipe is provided with a flow regulating valve;
the water supply pipe is connected with a water inlet pipe, and the water inlet pipe is used for providing water source for the water supply pipe;
the water inlet pipe is provided with a water valve which is used for opening and closing the water inlet pipe;
the water supply pipe can be opened and closed or the water supply speed of the water supply pipe to the water curtain capturing component can be regulated through the flow regulating valve.
5. The bag-type dust collector of claim 1, wherein the bag-type capturing assembly comprises a support frame and a dust collection bag sleeved outside the support frame; the water curtain capturing component is arranged in the supporting frame;
the support frame comprises a cylindrical support main body frame, a fixed seat arranged at one end of the support main body frame and a round sealing plate arranged at the other end of the support main body frame and used for sealing one end of the support frame; a plurality of vent holes are formed in the support main body frame;
the support frame is fixedly arranged on the flow guide baffle through the fixing seat, and a flow hole is formed in the end part of the flow guide baffle, which corresponds to the support frame.
6. The bag-type dust collector according to claim 5, wherein the water curtain capturing component comprises a central tube connected with the sealing plate, a water storage disc vertically connected with one end of the central tube, a water curtain tube body with the upper end connected with the water storage disc, a collecting block arranged at the lower end of the water curtain tube body and a limiting ring fixedly arranged on the inner wall of the supporting frame corresponding to the water storage disc;
the water curtain pipe body is a cylindrical tubular piece;
an annular overflow port is formed between the limiting ring and the water storage disc, and water flow of the water storage disc flows to the outer surface of the water curtain pipe body through the overflow port to form a water film.
7. The bag-type dust collector of claim 6, wherein the central tube, the water storage disc, the limiting ring, the water curtain tube body, the collecting block and the supporting frame are all coaxially arranged, and the maximum diameters of cross sections of the water storage disc, the water curtain tube body and the collecting block are consistent.
8. The bag-type dust collector of claim 6 wherein the center tube is disposed axially in the center of the closure plate, the center tube being disposed through the closure plate;
the water storage disc is characterized in that a plurality of outflow holes are radially formed in the end portion, connected with the water storage disc, of the central tube, the upper end of the central tube is arranged corresponding to the water outlet of the water supply tube, and water in the water supply tube enters the central tube through the water outlet and flows onto the water storage disc through the outflow holes.
9. The bag-type dust collector according to claim 6, wherein the water storage disc is arranged in a disc shape, a circular limiting block is arranged on the upper surface of the water storage disc, the limiting block and the water storage disc are coaxially arranged, and a water storage space is formed on the upper surface of the water storage disc through limiting of the limiting block;
the cross section of stopper is triangle-shaped, just the base of limiting plate cross section with the upper surface laminating of water storage disc is fixed, makes the inner wall and the outer wall of stopper all set up to the inclined plane.
10. The bag-type dust collector according to claim 1, wherein the limiting ring is horn-shaped, the diameter of the upper end of the limiting ring is larger than that of the lower end of the limiting ring, the upper end of the limiting ring is fixedly connected with the inner wall of the supporting frame, and the lower end of the limiting ring is arranged corresponding to the outer wall of the limiting block;
a gap is arranged between the lower end of the limiting ring and the outer wall of the limiting block, and the gap is the overflow port.