CN1157348C - 锆尖晶石质上水口 - Google Patents
锆尖晶石质上水口 Download PDFInfo
- Publication number
- CN1157348C CN1157348C CNB011151919A CN01115191A CN1157348C CN 1157348 C CN1157348 C CN 1157348C CN B011151919 A CNB011151919 A CN B011151919A CN 01115191 A CN01115191 A CN 01115191A CN 1157348 C CN1157348 C CN 1157348C
- Authority
- CN
- China
- Prior art keywords
- spinelle
- zircon
- upper sprue
- steel
- sprue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种锆尖晶石质上水口，属一种钢水连铸中间包的钢流控制定形耐火材料。本发明要解决的技术问题是使用时不会影响钢水质量、使用过程中不易堵塞、耐温耐蚀、使用寿命长。本发明是一组以镁铝尖晶石为主体的耐火制品，其组份按重量百分比计为：镁铝尖晶石85～95%，铝酸钙水泥1～4%，硅微粉1～5%，氧化锆2～8%，减水0.1～0.4%。本发明适用于各种普通钢及品种钢的连铸，特别是铝镇静钢的连铸。
Description
技术领域：本发明涉及一种铸造熔融物的功能材料，特别是用于钢水连铸中间包的钢流控制定形耐火材料。
背景技术：目前常用的中间包水口为熔融石英质或铝碳质，采用熔融石英质虽可不经烘烤直接使用，但石英质水口抗蚀性差，不利于多炉连浇，而且又易使钢水渗入非金属夹杂，浇注高锰钢时影响钢水质量。而铝碳质或铝锆碳质水口使用过程中易堵塞，影响正常生产。
发明内容：本发明要解决的技术问题是克服上述现有技术的不足，提供一种使用时不会影响钢水质量、使用过程中不易堵塞、耐温耐蚀、使用寿命长的锆尖晶石质上水口。
本发明是一组以镁铝尖晶石为主体的耐火制品，其组份按重量百分比计为：
镁铝尖晶石 85～95％ 铝酸钙水泥 1～4％
硅微粉 1～5％ 氧化锆 2～8％
减水剂 0.1～0.4％
各组份重量之和为100％。
在上述组方中，镁铝尖晶石是主体原料，它耐高温钢侵蚀，不污染钢水，其质量指标是：MgO≥23％，SiO2≤1.0％，颗粒体积密度≥3.3g/cm3，灼减量≤0.3％。镁铝尖晶石可以是烧结尖晶石或电熔尖晶石。铝酸钙水泥起粘结剂作用，使制品在低温时具有强度，其质量指标为Al2O3≥70％，CaO≤24％。硅微粉起结合作用及填充作用，其质量指标是SiO2≥95％。氧化锆起增加材料热震稳定性作用，其质量指标为ZrO2≥99％。减水剂主要使材料浇注时加水量减少，易于浇注减少气孔率，该减水剂可以是磷酸盐或磺酸缩聚物。
本发明的一个更具体的组份按重量百分比计是：镁铝尖晶石：90～95％，铝酸钙水泥：1～3％，硅微粉：1～3％，氧化锆：2～5％，减水剂：0.2～0.3％。各组份重量之和为100％。
本发明的生产工艺是：将各原料按比例混合，在混合机中干混3分钟，然后加入水进行混合后出料，在振动台上振动成型，养护24小时后脱模，经烘烤后于1600℃烧成。
本发明适用于各种普通钢及品种钢的连铸，特别是铝镇静钢的连铸。
本发明与铝碳质水口相较，无碳，因此不存在由于铝碳质水口中的碳氧化后，水口表面变粗糙，造成氧化铝易附着的问题。本发明产品表面光滑，镁铝尖晶石与氧化铝反应性低，氧化铝不易附着。
具体实施方式：本发明采用镁铝尖晶石8-5mm、18％，5-3mm、25％，3-1mm、15％，＜1mm、12％，＜0.074mm、20％；铝酸钙水泥3％，硅微粉3％，氧化锆4％，三聚磷酸钠0.2％。先将各合格原料比例称量，然后加入行量式混合机中干混3分钟，再加入水7％进行混合出料，在振动台上振动成型，养护24小时后脱模，经烘烤后于1600℃进行烧成。所生产的锆尖晶石质上水口的质量指标为：MgO 21.3％，Al2O3 64.5％，体积密度2.95g/cm3，耐压强度64MPa。
本发明产品在18吨连铸中间包上使用，抗侵蚀性优良，氧化铝不易附着，水口无堵塞结瘤现象。
Claims (5)
1、一种锆尖晶石质上水口，其特征是一组以镁铝尖晶石为主体的耐火制品，其组份按重量百分比计为：
镁铝尖晶石 85～95％ 铝酸钙水泥 1～4％
硅微粉 1～5％ 氧化锆 2～8％
减水剂 0.1～0.4％
各组份重量之和为100％；
上述的镁铝尖晶石的质量指标是：MgO≥23％，SiO2≤1.0％，颗粒体积密度≥3.3g/cm3，灼减量≤0.3％；铝酸钙水泥的质量指标为Al2O3≥70％，CaO≤24％；硅微粉的质量指标是SiO2≥95％；氧化锆的质量指标是ZrO2≥99％。
2.如权利要求1所述的锆尖晶石质上水口，其特征是镁铝尖晶石是电熔尖晶石。
3.如权利要求1所述的锆尖晶石质上水口，其特征是镁铝尖晶石是烧结尖晶石。
4.如权利要求1或2所述的锆尖晶石质上水口，其特征是减水剂是磷酸盐。
5.如权利要求1或2所述的锆尖晶石质上水口，其特征是减水剂是磺酸缩聚物。