CN115534488A - Waterproof manufacturing process of sun-proof double-layer composite fabric - Google Patents
Waterproof manufacturing process of sun-proof double-layer composite fabric Download PDFInfo
- Publication number
- CN115534488A CN115534488A CN202210558997.7A CN202210558997A CN115534488A CN 115534488 A CN115534488 A CN 115534488A CN 202210558997 A CN202210558997 A CN 202210558997A CN 115534488 A CN115534488 A CN 115534488A
- Authority
- CN
- China
- Prior art keywords
- cloth
- waterproof
- drying
- pressing
- sun
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof manufacturing process of a sun-proof double-layer composite fabric, which comprises the following steps: step a: the cloth is finished, the cloth is placed in a washing machine for washing, and a proper amount of washing solvent and bleaching powder are added; step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan; step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling; step d: and uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue. The invention realizes the purpose of improving the application range of the sun-proof double-layer composite fabric, improves the waterproof performance of the sun-proof double-layer composite fabric, and solves the problems that the existing sun-proof double-layer composite fabric has single functionality and poor fabric waterproof performance, so that the sun-proof double-layer composite fabric has functional deviation and the application range of the fabric is reduced.
Description
Technical Field
The invention relates to the technical field of sun-proof double-layer composite fabrics, in particular to a waterproof manufacturing process of a sun-proof double-layer composite fabric.
Background
The composite fabric is a novel material formed by bonding and jointing one or more layers of textile materials, non-woven materials and other functional materials, is suitable for being used as textiles such as sofas, clothes and the like, is one of the indispensable fabrics for people's home life, has single function of the existing sun-resistant double-layer composite fabric, has poor performance in the aspect of fabric water resistance, causes the functional deviation of the sun-resistant double-layer composite fabric, and reduces the application range of the fabric.
Disclosure of Invention
The invention aims to provide a waterproof manufacturing process of a sun-proof double-layer composite fabric, which has the advantage of application range and solves the problems that the existing sun-proof double-layer composite fabric is single in functionality and poor in fabric waterproof performance, so that the sun-proof double-layer composite fabric is deviated in functionality and the application range of the fabric is reduced.
In order to achieve the purpose, the invention provides the following technical scheme: a waterproof manufacturing process of a sun-resistant double-layer composite fabric comprises the following steps:
a, step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting adhesive;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Preferably, the time for cleaning the cloth in the step a is 30-50 minutes.
Preferably, the time for drying the cloth in the step b is 5-10 minutes.
Preferably, the waterproof inner layer in the step e is PVC plastic coated cloth.
Preferably, when the pressing roller is used for pressing the cloth in the step f, the whole cloth needs to be repeatedly pressed twice, the pressing is performed by matching with the drying fan for the first time, and the pressing roller is used for pressing the cloth for the second time.
Compared with the prior art, the invention has the following beneficial effects:
the invention realizes the purpose of improving the application range of the sun-proof double-layer composite fabric, improves the waterproof performance of the sun-proof double-layer composite fabric, and solves the problems that the existing sun-proof double-layer composite fabric has single functionality and poor fabric waterproof performance, so that the sun-proof double-layer composite fabric has functional deviation and the application range of the fabric is reduced.
Detailed Description
The technical solutions in the embodiments of the present invention will be described clearly and completely below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
A waterproof manufacturing process of a sun-proof double-layer composite fabric comprises the following steps:
step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Example 1
A waterproof manufacturing process of a sun-resistant double-layer composite fabric comprises the following steps:
step a: the cloth is finished, the cloth is placed in a washing machine for washing, and a proper amount of washing solvent and bleaching powder are added;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Example 2
In example 1, the following additional steps were added:
the time for cleaning the cloth in the step a is 30-50 minutes.
A waterproof manufacturing process of a sun-proof double-layer composite fabric comprises the following steps:
step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying fan to use, drying fan is pressing gyro wheel the place ahead, and drying fan carries out effectual softening to connecting glue, is pressing through pressing the gyro wheel for connect glue and waterproof inlayer and carry out the abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Example 3
In example 2, the following steps were added:
and c, drying the cloth in the step b for 5-10 minutes.
A waterproof manufacturing process of a sun-proof double-layer composite fabric comprises the following steps:
a, step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting adhesive;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying fan to use, drying fan is pressing gyro wheel the place ahead, and drying fan carries out effectual softening to connecting glue, is pressing through pressing the gyro wheel for connect glue and waterproof inlayer and carry out the abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Example 4
In example 3, the following additional steps were added:
and e, the waterproof inner layer in the step e is PVC plastic-coated cloth.
A waterproof manufacturing process of a sun-proof double-layer composite fabric comprises the following steps:
step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Example 5
In example 4, the following steps were added:
and f, when the pressing roller is used for pressing the cloth in the step f, the whole cloth needs to be repeatedly pressed twice, the first time of pressing is matched with the drying fan, and the second time of pressing is carried out by independently using the pressing roller.
A waterproof manufacturing process of a sun-proof double-layer composite fabric comprises the following steps:
step a: the cloth is finished, the cloth is placed in a washing machine for washing, and a proper amount of washing solvent and bleaching powder are added;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and similarly cleaning, drying, leveling and coating the connecting glue on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (5)
1. A waterproof manufacturing process of a sun-proof double-layer composite fabric is characterized by comprising the following steps of: the method comprises the following steps:
step a: arranging the cloth, putting the cloth in a washing machine for washing, and adding a proper amount of washing solvent and bleaching powder;
step b: after cleaning, taking out the cloth, spreading the cloth, and drying the cloth by using a drying fan;
step c: after drying, leveling the cloth by using a cloth iron to prevent the surface of the cloth from wrinkling;
step d: uniformly coating the top of the cloth with a connecting primer, and then uniformly coating the top of the connecting primer with a connecting glue;
step e: placing the waterproof inner layer on the top of the cloth, then laying the other cloth on the top of the waterproof inner layer, and carrying out cleaning, drying, leveling and connecting glue coating treatment on the other cloth;
step f: the cloth is uniformly rolled by using the pressing roller, so that the pressing roller presses the waterproof inner layer, and the cloth and the waterproof inner layer are stably connected together;
step g: when rolling and pressing cloth and waterproof inlayer, need cooperate drying blower to use, drying blower is pressing gyro wheel the place ahead, and drying blower carries out effectual softening to connecting gluey, is pressing through pressing the gyro wheel for connect gluey and waterproof inlayer carry out abundant contact, and then can improve the connectivity between cloth and the waterproof inlayer.
2. The waterproof manufacturing process of the sun-proof double-layer composite fabric according to claim 1, characterized in that: the time for cleaning the cloth in the step a is 30-50 minutes.
3. The waterproof manufacturing process of the sun-proof double-layer composite fabric according to claim 1, characterized in that: and the time for drying the cloth in the step b is 5-10 minutes.
4. The waterproof manufacturing process of the sun-proof double-layer composite fabric according to claim 1, characterized in that: and e, the waterproof inner layer in the step e is PVC plastic-coated cloth.
5. The waterproof manufacturing process of the sun-proof double-layer composite fabric according to claim 1, characterized in that: and f, when the pressing roller is used for pressing the cloth in the step f, the whole cloth needs to be repeatedly pressed twice, the pressing is matched with the drying fan for the first time, and the pressing roller is independently used for pressing the cloth for the second time.