CN115521643A - 一种除醛涂料及其制备方法 - Google Patents
一种除醛涂料及其制备方法 Download PDFInfo
- Publication number
- CN115521643A CN115521643A CN202211253018.3A CN202211253018A CN115521643A CN 115521643 A CN115521643 A CN 115521643A CN 202211253018 A CN202211253018 A CN 202211253018A CN 115521643 A CN115521643 A CN 115521643A
- Authority
- CN
- China
- Prior art keywords
- parts
- aldehyde
- mixing
- formaldehyde
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种除醛涂料及其制备方法，涉及除醛涂料技术领域，包括如下质量比成分：纤维素3‑4份、淀粉7‑9份、奶油触变剂0.3份、负离子粉0.5‑1份、香精2份、硅藻土10‑15份、甲醛捕捉剂3份、钙粉1000份；本发明以纤维素、淀粉、奶油触变剂、负离子粉、香精、硅藻土、甲醛捕捉剂、钙粉制备而成，经过验证：使用本涂料涂覆后，空气中负氧离子含量高，可有效快速去除空气中甲醛，甲醛净化率达96.2％，且本发明作为涂料可以涂覆到室内墙壁或者一些板材上，便于长效持续分解整个室内释放的叠加甲醛，更稳定更持久，同时，使用硅藻土和钙粉作为基料，成本低，性能高，可以添加到任何装修建材里实现净醛和无醛的效果。
Description
技术领域
本发明涉及除醛涂料技术领域，尤其涉及一种除醛涂料及其制备方法。
背景技术
在经济高速发展的国家，世界卫生组织统计表明，室内空气污染每年导致430 万人左右死亡，特别是在室内装修中，每年因为装修的甲醛污染，造成的健康问题数不胜数；
甲醛被称为“室内污染第一杀手”，甲醛是导致新生儿畸形、儿童白血病、青少年记忆力和智力下降的主要原因，被WHO确定为致癌和致畸性物质，长期接触低剂量甲醛，能引起慢性中毒，引发呼吸系统、神经系统、生殖系统等疾病，装修材料如果单项超标必然会引起空气质量的不达标，另外值得注意的是，即使每项产品都在标准范围之内，如果房间中这些含有甲醛的建材太多，累加起来也容易引起空气质量不合格，大部分有害气体是有味的，哪怕装修几年后污染依然存在，现有技术中，除甲醛的方式有很多中，一般通过一些喷剂除甲醛，这种喷剂除甲醛效果低，极易挥发，而且只能去除表面的部分实时甲醛，无法应对后续从墙壁等内里发散出来的甲醛，室内甲醛量难以达到不超过0.10mg/m3的国家标准，因此，本发明提出一种除醛涂料及其制备方法以解决现有技术中存在的问题。
发明内容
针对上述问题，本发明提出一种除醛涂料及其制备方法，该除醛涂料使用后，空气中负氧离子含量高，可有效快速去除空气中甲醛，甲醛净化率达96.2％。
为实现本发明的目的，本发明通过以下技术方案实现：一种除醛涂料，包括如下质量比成分：纤维素3-4份、淀粉7-9份、奶油触变剂0.3份、负离子粉0.5-1 份、香精2份、硅藻土10-15份、甲醛捕捉剂3份、钙粉1000份。
进一步改进在于：包括如下质量比成分：纤维素3.5份、淀粉8份、奶油触变剂0.3份、负离子粉0.8份、香精2份、硅藻土12份、甲醛捕捉剂3份、钙粉1000份。
进一步改进在于：所述淀粉为木薯淀粉或糯米淀粉。
进一步改进在于：所述硅藻土选择二氧化硅含量≥80％、氧化铁含量1-1.5％、氧化铝含量为3-6％、有机物含量大于等于30％的硅藻土，并经100℃-300℃烘干获得。
进一步改进在于：所述负离子粉选择粒度3000-5000目，负离子发生量 40000ions的粉末。
进一步改进在于：所述甲醛捕捉剂由环状低聚糖5-40份、尿素15-50份、水25-90份、聚丙烯酸2-3份和柠檬酸3-6份混合组成。
一种除醛涂料的制备方法，包括以下步骤：
步骤一：将纤维素、淀粉、香精、硅藻土和钙粉放入混合机中进行预混合，获得预混合物；
步骤二：将低聚糖、尿素、水、聚丙烯酸和柠檬酸混合并超声波均质，制成甲醛捕捉剂；
步骤三：将甲醛捕捉剂输入至预混合物中，同步加入奶油触变剂，混合搅拌，获得混合物：
步骤四：将混合物输入至混炼机中，通过混炼将混合物在熔融状态下达到均匀分散的效果；
步骤五：将熔融物输入至挤出机，挤出成条状物料；
步骤六：将条状物料挤压成薄片并进行冷却，冷却后，送入粉碎研磨机，研磨成粉末颗粒并筛分，获得产品。
进一步改进在于：所述步骤一中，预混合时，控制混合机的转速为 1000-1300r/min，预混合20-40min，混合温度为常温。
进一步改进在于：所述步骤三中，混合搅拌时，控制混合机的转速为 1500-1800r/min，预混合20-60min，混合温度为常温，并通入氮气进行保护。
进一步改进在于：所述步骤六中，在粉碎研磨机将物料粉碎成粉末颗粒的过程中，控制机内气流温度≤40℃，且获得产品的细度控制为≤50μm。
本发明的有益效果为：
1、本发明以纤维素、淀粉、奶油触变剂、负离子粉、香精、硅藻土、甲醛捕捉剂、钙粉制备而成，经过验证：使用本涂料涂覆后，空气中负氧离子含量高，可有效快速去除空气中甲醛，甲醛净化率达96.2％。
2、本发明作为涂料可以涂覆到室内墙壁或者一些板材上，便于长效持续分解整个室内释放的叠加甲醛，更稳定更持久，同时，使用硅藻土和钙粉作为基料，成本低，性能高，可以添加到任何装修建材里实现净醛和无醛的效果。
附图说明
图1为本发明的制备流程图。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明做进一步详述，本实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实施例一
本实施例提出了一种除醛涂料，包括如下质量比成分：纤维素3份、淀粉7 份、奶油触变剂0.3份、负离子粉0.5份、香精2份、硅藻土10份、甲醛捕捉剂3份、钙粉1000份。
所述淀粉为木薯淀粉或糯米淀粉。所述硅藻土选择二氧化硅含量≥80％、氧化铁含量1％、氧化铝含量为3％、有机物含量大于等于30％的硅藻土，并经200℃烘干获得。所述负离子粉选择粒度3000目，负离子发生量40000ions的粉末。所述甲醛捕捉剂由环状低聚糖5份、尿素15份、水25份、聚丙烯酸2份和柠檬酸3份混合组成。
根据图1所示，本实施例提出了一种除醛涂料的制备方法，包括以下步骤：
将纤维素、淀粉、香精、硅藻土和钙粉放入混合机中进行预混合，控制混合机的转速为1200r/min，预混合30min，混合温度为常温，获得预混合物；
将低聚糖、尿素、水、聚丙烯酸和柠檬酸混合并超声波均质，制成甲醛捕捉剂；
将甲醛捕捉剂输入至预混合物中，同步加入奶油触变剂，混合搅拌，控制混合机的转速为1700r/min，预混合50min，混合温度为常温，并通入氮气进行保护，获得混合物：
将混合物输入至混炼机中，通过混炼将混合物在熔融状态下达到均匀分散的效果；
将熔融物输入至挤出机，挤出成条状物料；
将条状物料挤压成薄片并进行冷却，冷却后，送入粉碎研磨机，研磨成粉末颗粒并筛分，在研磨的过程中，控制机内气流温度≤40℃，获得产品，产品的细度控制为≤50μm。
实施例二
本实施例提出了一种除醛涂料，包括如下质量比成分：纤维素3.5份、淀粉 8份、奶油触变剂0.3份、负离子粉0.8份、香精2份、硅藻土12份、甲醛捕捉剂3份、钙粉1000份。
所述淀粉为木薯淀粉或糯米淀粉。所述硅藻土选择二氧化硅含量≥80％、氧化铁含量1.2％、氧化铝含量为5％、有机物含量大于等于30％的硅藻土，并经200℃烘干获得。所述负离子粉选择粒度4000目，负离子发生量40000ions的粉末。所述甲醛捕捉剂由环状低聚糖25份、尿素35份、水75份、聚丙烯酸2份和柠檬酸4份混合组成。
根据图1所示，本实施例提出了一种除醛涂料的制备方法，包括以下步骤：
将纤维素、淀粉、香精、硅藻土和钙粉放入混合机中进行预混合，控制混合机的转速为1200r/min，预混合30min，混合温度为常温，获得预混合物；
将低聚糖、尿素、水、聚丙烯酸和柠檬酸混合并超声波均质，制成甲醛捕捉剂；
将甲醛捕捉剂输入至预混合物中，同步加入奶油触变剂，混合搅拌，控制混合机的转速为1700r/min，预混合50min，混合温度为常温，并通入氮气进行保护，获得混合物：
将混合物输入至混炼机中，通过混炼将混合物在熔融状态下达到均匀分散的效果；
将熔融物输入至挤出机，挤出成条状物料；
将条状物料挤压成薄片并进行冷却，冷却后，送入粉碎研磨机，研磨成粉末颗粒并筛分，在研磨的过程中，控制机内气流温度≤40℃，获得产品，产品的细度控制为≤50μm。
实施例三
本实施例提出了一种除醛涂料，包括如下质量比成分：纤维素4份、淀粉9 份、奶油触变剂0.3份、负离子粉1份、香精2份、硅藻土15份、甲醛捕捉剂3 份、钙粉1000份。
所述淀粉为木薯淀粉或糯米淀粉。所述硅藻土选择二氧化硅含量≥80％、氧化铁含量1.5％、氧化铝含量为6％、有机物含量大于等于30％的硅藻土，并经200℃烘干获得。所述负离子粉选择粒度5000目，负离子发生量40000ions的粉末。所述甲醛捕捉剂由环状低聚糖40份、尿素50份、水90份、聚丙烯酸3份和柠檬酸6份混合组成。
根据图1所示，本实施例提出了一种除醛涂料的制备方法，包括以下步骤：
将纤维素、淀粉、香精、硅藻土和钙粉放入混合机中进行预混合，控制混合机的转速为1200r/min，预混合30min，混合温度为常温，获得预混合物；
将低聚糖、尿素、水、聚丙烯酸和柠檬酸混合并超声波均质，制成甲醛捕捉剂；
将甲醛捕捉剂输入至预混合物中，同步加入奶油触变剂，混合搅拌，控制混合机的转速为1700r/min，预混合50min，混合温度为常温，并通入氮气进行保护，获得混合物：
将混合物输入至混炼机中，通过混炼将混合物在熔融状态下达到均匀分散的效果；
将熔融物输入至挤出机，挤出成条状物料；
将条状物料挤压成薄片并进行冷却，冷却后，送入粉碎研磨机，研磨成粉末颗粒并筛分，在研磨的过程中，控制机内气流温度≤40℃，获得产品，产品的细度控制为≤50μm。
根据实施例一、实施例二和实施例三可以得出，本发明通过如下质量比成份：纤维素3-4份、淀粉7-9份、奶油触变剂0.3份、负离子粉0.5-1份、香精2份、硅藻土10-15份、甲醛捕捉剂3份、钙粉1000份，制备出的除醛涂料，可有效且快速去除空气中甲醛，甲醛净化率达96.2％。
其中，负离子是一种带负电荷的空气微粒，它像食物中的维生素一样，对人的生命活动有着很重要的影响，所以有人称其为“空气维生素”有的甚至认为空气负氧离子与长寿有关，称它为“长寿素”。同样，负离子浓度的高低与人们的健康息息相关，人们时刻需要负离子，尤其在污染日益严重的今天。据环境学家研究，负氧离子治疗疾病：(1)消烟、除尘：负离子能迅速中和空气中属于正离子的焦烟、“二手烟”、油烟及飘尘。(2)改善空气结构：人每天需要130 亿个负离子，而我们居室，办公室，娱乐场所等环境仅能提供约2-20亿个负离子，往往容易导致肺炎、气管炎等呼吸道疾病。(3)改善肺功能：吸入负离子 30分钟后，肺能增加氧气吸收量20％，而多排出14.5％二氧化碳。(4)改善心肌功能:有明显降压作用，可使人精神振奋。提高工作效率。(5)促进新陈代谢：负离子能少许活肌体多种酶，促进新陈代谢，改善睡眠。(6)增强肌体抗病能力：负离子可改善肌体的反应性，增强肌体抗病能力。
检测报告：
结论：本涂覆材料具有持久净化室内甲醛性能，经国家建筑材料测试中心检验，符合标准JC/T1074-2008I类技术要求
对比例：
时间14:00，注入相同浓度的甲醛，1分钟后，本产品涂覆后的样品仓与传统样品仓甲醛数值同时达到2.50mg/m3。
时间14:10，10分钟后，本产品样品仓甲醛数值开始快速下降，达到2.01mg/m3，而传统样品仓，数值未变。
时间14:30，30分钟后，本产品样品仓甲醛数值下降至0.93mg/m3，传统样品仓数值未变。
时间15:30，1小时30分钟后，本产品样品仓甲醛数值下降至0.25mg/m3,而传统样品仓数值未变。
时间16:00，2小时后，本产品样品仓甲醛数值下降至0.17mg/m3，而传统样品仓数值未变。
时间17:00，3小时后，本产品样品仓甲醛数值下降至0.03mg/m3,已达到国家规定家庭甲醛释放安全标准，而传统样品仓数值仍未变。
本发明以纤维素、淀粉、奶油触变剂、负离子粉、香精、硅藻土、甲醛捕捉剂、钙粉制备而成，经过验证：使用本涂料涂覆后，空气中负氧离子含量可达到 1000-3000个/cm3、可净化空气中的pm2.5，有效去除空气中甲醛(甲醛超标10 倍且不再增加，约3小时甲醛降低到环保范围)甲醛净化率达96.2％，配合香精的香味，有利于构建24小时全天氧吧。且本发明作为涂料可以涂覆到室内墙壁或者一些板材上，便于长效持续分解整个室内释放的叠加甲醛，更稳定更持久，同时，使用硅藻土和钙粉作为基料，成本低，性能高，可以添加到任何装修建材里实现净醛和无醛的效果。
以上显示和描述了本发明的基本原理、主要特征和优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (10)
1.一种除醛涂料，其特征在于，包括如下质量比成分：纤维素3-4份、淀粉7-9份、奶油触变剂0.3份、负离子粉0.5-1份、香精2份、硅藻土10-15份、甲醛捕捉剂3份、钙粉1000份。
2.根据权利要求1所述的一种除醛涂料，其特征在于：包括如下质量比成分：纤维素3.5份、淀粉8份、奶油触变剂0.3份、负离子粉0.8份、香精2份、硅藻土12份、甲醛捕捉剂3份、钙粉1000份。
3.根据权利要求1所述的一种除醛涂料，其特征在于：所述淀粉为木薯淀粉或糯米淀粉。
4.根据权利要求1所述的一种除醛涂料，其特征在于：所述硅藻土选择二氧化硅含量≥80％、氧化铁含量1-1.5％、氧化铝含量为3-6％、有机物含量大于等于30％的硅藻土，并经100℃-300℃烘干获得。
5.根据权利要求1所述的一种除醛涂料，其特征在于：所述负离子粉选择粒度3000-5000目，负离子发生量40000ions的粉末。
6.根据权利要求1所述的一种除醛涂料，其特征在于：所述甲醛捕捉剂由环状低聚糖5-40份、尿素15-50份、水25-90份、聚丙烯酸2-3份和柠檬酸3-6份混合组成。
7.一种除醛涂料的制备方法，其特征在于：包括以下步骤：
步骤一：将纤维素、淀粉、香精、硅藻土和钙粉放入混合机中进行预混合，获得预混合物；
步骤二：将低聚糖、尿素、水、聚丙烯酸和柠檬酸混合并超声波均质，制成甲醛捕捉剂；
步骤三：将甲醛捕捉剂输入至预混合物中，同步加入奶油触变剂，混合搅拌，获得混合物：
步骤四：将混合物输入至混炼机中，通过混炼将混合物在熔融状态下达到均匀分散的效果；
步骤五：将熔融物输入至挤出机，挤出成条状物料；
步骤六：将条状物料挤压成薄片并进行冷却，冷却后，送入粉碎研磨机，研磨成粉末颗粒并筛分，获得产品。
8.根据权利要求7所述的一种除醛涂料的制备方法，其特征在于：所述步骤一中，预混合时，控制混合机的转速为1000-1300r/min，预混合20-40min，混合温度为常温。
9.根据权利要求8所述的一种除醛涂料的制备方法，其特征在于：所述步骤三中，混合搅拌时，控制混合机的转速为1500-1800r/min，预混合20-60min，混合温度为常温，并通入氮气进行保护。
10.根据权利要求9所述的一种除醛涂料的制备方法，其特征在于：所述步骤六中，在粉碎研磨机将物料粉碎成粉末颗粒的过程中，控制机内气流温度≤40℃，且获得产品的细度控制为≤50μm。