CN115484926A - 包含可生物降解聚合物的化妆品组合物 - Google Patents
包含可生物降解聚合物的化妆品组合物 Download PDFInfo
- Publication number
- CN115484926A CN115484926A CN202180029736.XA CN202180029736A CN115484926A CN 115484926 A CN115484926 A CN 115484926A CN 202180029736 A CN202180029736 A CN 202180029736A CN 115484926 A CN115484926 A CN 115484926A
- Authority
- CN
- China
- Prior art keywords
- composition
- pha
- poly
- cosmetic composition
- hydroxybutyrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
公开了一种化妆品组合物,其包含至少一种平均直径(d50)为0.1nm至50pm的颗粒形式的聚羟基链烷酸酯(PHA)。所述PHA可以包含0.1%w/w至30%w/w的总化妆品组合物,并且一些实施例可以使用1%w/w至8%w/w。所述组合物可以包括硅氧烷外相或者可以呈松散或压实粉末的形式。可以使用各种PHA,尽管有利的是,所述PHA可以具有1个至8个碳的链长。在一些实施例中,可以选择PHA以使每100克PHA具有60克至150克所期望油的吸油量,其中所期望油可以是,例如,皮脂。进一步,所述组合物可以可选地包括一种或多种颜料。在使用中,所述组合物可以应用于使用者的皮肤或头发。
Description
相关专利申请的交叉引用
本申请要求于2020年6月26日提交的美国专利申请号16/913,379以及于2020年8月20日提交的法国专利申请号FR2008581的优先权,其通过援引以其全文并入本文。
技术领域
本发明涉及化妆品组合物,并且具体地涉及使用聚羟基链烷酸酯并且具有硅氧烷外相或呈松散或压制粉末形式的化妆品组合物。
背景技术
化妆品组合物通常被开发为允许使用者在身体、面部或头发上放置特定的所期望的成分,例如有色颜料、抗氧化剂、皮肤保护剂和保湿剂、质地粉末,而产品的美观性不会使其成为不愉快的体验。
这些组合物中的一些利用各种填料为组合物提供所期望的特性。然而,化妆品填料通常不溶于油相或水相,因此配方设计师通常需要制造乳液以确保产品的货架稳定性。在一些情况下,硅氧烷用作外相或连续相。进一步,一些化妆品组合物含有粉末并可用作遮光剂、填充剂、吸油剂、消光剂。取决于所用粉末的类型以及它如何与制剂的其余部分相互作用,化妆品组合物的性质可能会有所不同,甚至可能对皮肤有害,使其感觉暗淡、干燥和/或粗糙。
进一步,许多消费者希望产品所含成分可以被视为环保且不会对环境造成负面影响。考虑到生产、使用和降解对环境的影响,消费者会寻找不会对大气产生新碳的成品。然而,许多化妆品粉末是不可生物降解的。例如,聚(甲基丙烯酸甲酯)(PMMA)和尼龙-12是化妆品中常用的填充剂或遮光剂的标准成分,可在皮肤上营造饱满光滑的外观,减少光泽/光亮,并赋予制剂所期望的感觉。然而,PMMA和尼龙-12都不是非常可生物降解的,而且制造这些材料的典型制造工艺也不环保。
因此,需要一种可用于化妆品组合物的可生物降解、环保型粉末材料,特别是用于具有硅氧烷作为外相或具有松散或压制粉末形式的化妆品组合物中。
发明内容
公开了一种化妆品组合物,其包含0.1%w/w至30%w/w的至少一种平均直径(d50)为0.1nm至50μm的颗粒形式的聚羟基链烷酸酯(PHA)。PHA可以以1%w/w至8%w/w的量存在于组合物中。该组合物可以包括硅氧烷外相或者可以呈松散或压实粉末的形式。有利地,PHA具有1个至8个碳,更特别地2个至6个碳,诸如2个至5个碳,诸如2个至4个碳,诸如4个碳的链长。在某些实施例中,PHA选自由以下各项组成的组:聚-3-羟基丁酸酯(PHB)、聚-3-羟基戊酸酯(PHV)、聚-3-羟基己酸酯(PHH)、聚-3-羟基辛酸酯(PHO)、聚(3-羟基丁酸酯-共-3-羟基戊酸酯)(PHBV)、聚(3-羟基丁酸酯-共-3-羟基己酸酯)(PHBH)、聚(3-羟基丁酸酯-共-4-羟基丁酸酯)、聚(3-羟基辛酸酯-共-3-羟基-10-十一烯酸酯)(PHOU)和聚(3-羟基丁酸酯-共-3-羟基戊酸酯-共-4-羟基戊酸酯)(PHBW)。
可以选择PHA以使每100克PHA具有60克至150克所期望油的吸油量。
该组合物可以可选地包括一种或多种颜料。在使用中,该组合物可以应用于使用者的皮肤或头发。
具体实施方式
如本文所用,冠词诸如“一”和“一种”在权利要求中使用时,应理解为意指要求保护或描述的对象中的一种或多种。
如本文所用,表述“至少一种”是指一种或多种,因此包括单个组分以及混合物/组合。
除非另有说明,否则所有列出的百分比均按重量计。
如本文所用,术语“约[数字]”旨在包括修约至适当的有效数位的值。因此,“约1”将包括在0.5与1.5之间的值,而“约1.0”将包括在0.95与1.05之间的值。
如本文所用,术语“包括”、“包含”和“含”为非限制性的。
如本文所用,“取代的”意指包含至少一个取代基。用于取代的取代基的非限制性实例包括原子(诸如氧原子和氮原子)以及官能团(诸如羟基基团、醚基团、烷氧基基团、酰氧基烷基基团、氧化烯基基团、聚氧化烯基基团、羧酸基团、胺基团、酰氨基基团、酰胺基团、含卤素基团、酯基团、硫醇基团、磺酸基团、硫代硫酸基团、硅氧烷基团和聚硅氧烷基团)。取代基可以被进一步取代。
本发明涉及一种化妆品组合物,特别是涉及使用聚羟基链烷酸酯并具有硅氧烷外相的化妆品组合物。该化妆品组合物可以是硅氧烷包水乳液。在某些实施例中,该组合物中硅氧烷的总量可以大于10%w/w。在某些实施例中,该组合物中硅氧烷的总量可以大于15%w/w。在某些实施例中,该组合物中硅氧烷的量可以在10%w/w和40%w/w之间。该化妆品组合物可以包含一种或多种硅氧烷,其可以包括但不限于聚二甲基硅氧烷、苯基聚三甲基硅氧烷或挥发性硅油。
在某些实施例中,该化妆品组合物是护肤、护发或化妆组合物。
该化妆品组合物通常包含至少一种聚羟基链烷酸酯(PHA)。已知PHA是可生物降解的并且可以通过例如环保的发酵过程来生产。
令人惊讶的是,PHA可以在各种基质中替代更传统的粉末(诸如PMMA或尼龙),以提供等效的粘度调节、消光效果和皮脂转移阻力。
在某些实施例中,PHA可以具有1个至8个碳,更特别地2个至6个碳,诸如2个至5个碳,诸如2个至4个碳,诸如4个碳的链长。所有范围都包括端点。在某些实施例中,PHA可以包括但不限于:聚-3-羟基丁酸酯(PHB)、聚-3-羟基戊酸酯(PHV)、聚-3-羟基己酸酯(PHH)、聚-3-羟基辛酸酯(PHO)、聚(3-羟基丁酸酯-共-3-羟基戊酸酯)(PHBV)、聚(3-羟基丁酸酯-共-3-羟基己酸酯)(PHBH)、聚(3-羟基丁酸酯-共-4-羟基丁酸酯)、聚(3-羟基辛酸酯-共-3-羟基-10-十一烯酸酯)(PHOU)、聚(3-羟基丁酸酯-共-3-羟基戊酸酯-共-4-羟基戊酸酯)(PHBW)或其组合。PHA可以是共聚物的一部分,或者共聚物可以衍生自两种或更多种PHA。
优选地,PHA是PHB,诸如可以从TianAn Biopolymer以ENMATTM品牌获得的PHB。
在某些实施例中,存在于组合物中的PHA总量大于约0.01%w/w。在某些实施例中,存在于组合物中的PHA总量大于约0.1%w/w。在某些实施例中,存在于组合物中的PHA总量大于约0.5%w/w。在某些实施例中,存在于组合物中的PHA总量大于约1%w/w。在某些实施例中,存在于组合物中的PHA总量大于约2%w/w。
在某些实施例中,存在于组合物中的PHA总量小于约50%w/w。在某些实施例中,存在于组合物中的PHA总量小于约30%w/w。在某些实施例中,存在于组合物中的PHA总量小于约15%w/w。在某些实施例中,存在于组合物中的PHA总量小于约8%w/w。
在优选的实施例中,存在于组合物中的PHA的总量在约0.1%w/w和约30%w/w之间。在更优选的实施例中,存在于组合物中的PHA的总量在约1%w/w和约8%w/w之间。
在本发明和所附权利要求的上下文中,除非另有说明,否则“平均粒径”特别是指直径d50(中值),即发现50重量%的颗粒群的直径值小于其的直径值(参见“A Guidebookto Particle Size Analysis”,Horiba Instruments Inc.2016年出版,可在www.horiba.corn/fileadmin/uploads/Scientific/eMag/PSA/Guidebook/pdf/PSA_Guidebook.pdf获得)。它可以根据ISO 13320:2008标准通过激光衍射技术确定,或者可以通过TEM透射电子显微镜确定。
在某些实施例中,PHA呈平均直径(d50)小于100μm的颗粒形式。在某些实施例中,d50小于50μm。在某些实施例中,d50小于30μm。在某些实施例中,d50小于20μm。在某些实施例中,d50大于0.1nm。在某些实施例中,d50大于1nm。在某些实施例中,d50大于100nm。在某些实施例中,d50大于1μm。在优选的实施例中,d50介于0.1nm和50μm之间,更优选地介于1μm和20μm之间。
在某些实施例中,选择PHA以使每100克PHA具有60克至150克的一种或多种所期望油的吸油量。在某些实施例中,所期望的一种或多种油是天然或合成皮脂。在某些实施例中,所期望的一种或多种油是组合物中存在的化妆品油,诸如硅氧烷、酯、香料或抗氧化剂。
化妆品组合物可具有多种形式,包括松散或压实的粉末、具有例如硅氧烷外相和/或为水相的内相的乳液或凝胶。该组合物可以是乳液或乳膏。
挥发性溶剂
所公开的组合物的实施例可以可选地包含至少一种挥发性溶剂(在室温和大气压下,在与皮肤或嘴唇接触时能够在少于一小时内蒸发的任何非水性介质)。
合适的挥发性溶剂的实例包括挥发性烃基油,诸如例如具有8个至16个碳原子的挥发性烃油及其混合物,特别是支链的C8至C16烷烃,诸如C8至C16异烷烃(也称为异链烷烃)、异十二烷、异癸烷、异十六烷和例如以商品名Isopar或Permerhyl销售的油、C8至C16支链酯,诸如新戊酸异己酯或异癸酯、醇和它们的混合物。优选地,挥发性烃基油具有至少40℃的闪点。
挥发性烃基油的实例包括但不限于异十二烷、异十六烷、新戊酸异癸酯、丙二醇正丁醚、3-乙氧基丙酸乙酯、丙二醇甲醚乙酸酯和异链烷烃(诸如异链烷烃C11-C13或异链烷烃C11-C12)。
挥发性溶剂也可以选自挥发性硅油。可选地,这些挥发性硅油可以是线性的或环状的,并且在室温下可以具有小于或等于6cSt的粘度。这些挥发性硅油可以选自具有2个至7个硅原子的硅油。这些可以是取代的或未取代的链。一个可选的实施例使用具有2个至7个硅原子并被1个至10个碳原子的烷基或烷氧基取代的硅油。
合适的挥发性硅油的实例包括但不限于辛基聚三甲基硅氧烷、己基聚三甲基硅氧烷、十甲基环五硅氧烷(环五硅氧烷或D5)、八甲基环四硅氧烷(环四二甲基硅氧烷或D4)十二甲基环六硅氧烷(D6)、十甲基四硅氧烷(L4)、来自Shin Etsu的KF-96A、PDMS(聚二甲基硅氧烷)来自Dow Coming的DC 200(1.5cSt)、来自Dow Coming的PDMS DC 200(2cSt)、来自DowComing的PDMS DC 200(5cSt)和来自Dow Coming的PDMS DC200(3St)。
在某些实施例中,至少一种挥发性溶剂通常以约5重量%至约70重量%的量存在于化妆品组合物中。在某些实施例中,它以约25重量%至约50重量%存在。在某些实施例中,它以约30重量%至约40重量%存在。
佐剂
化妆品组合物可以可选地包含佐剂,诸如防腐剂、抗氧化剂、香料、螯合剂(诸如EDTA)或染料。这些各种佐剂的量是所考虑的领域中常规使用的量,例如相对于化妆品的总重量,0.01重量%至10重量%,优选地0.01重量%至5重量%。
化妆品组合物可以包含至少一种化妆品可接受的着色剂,诸如颜料或染料。合适颜料的实例包括但不限于无机颜料、有机颜料、色淀、珠光颜料、虹彩或光学可变颜料及其混合物。颜料应理解为是指无机或有机、白色或有色颗粒。在本发明的范围内,所述颜料可以可选地进行表面处理,但不限于诸如硅氧烷、全氟化合物、卵磷脂和氨基酸的处理。
可用于本发明的无机颜料的代表性实例包括选自以下各项组成的组的那些:金红石或锐钛矿二氧化钛,在颜色索引中以参考Cl 77,891编码;黑色、黄色、红色和棕色氧化铁,以参考Cl 77,499、77、492和77,491编码;锰紫(Cl 77,742);群青(Cl 77,007);氧化铬(Cl 77,288);水合铬(Cl 77,289);和铁蓝(Cl 77,510)及其混合物。
可用于本发明的有机颜料和色淀的代表性实例包括但不限于D&C红色19号(Cl45,170)、D&C红色9号(Cl 15,585)、D&C红色21号(Cl 45,380)、D&C橙色4号(Cl 15,510)、D&C橙色号(Cl 45,370)、D&C红色27号(Cl 45,410)、D&C红色13号(Cl 15,630)、D&C红色7号(Cl 15,850)、D&C红色6号(Cl 15,850)、D&C黄色5号(Cl 19,140)、D&C红色36号(Cl 12,085)、D&C橙色10号(Cl 45,425)、D&C黄色6号(Cl 15,985)、D&C红色30号(Cl 73,360)、D&C红色3号(Cl 45,430)和基于胭脂虫红(Cl 75,570)及其混合物的染料或色淀。
可用于本发明的珠光颜料的代表性实例包括选自以下各项组成的组的那些:白色珠光颜料诸如涂有氧化钛的云母、涂有二氧化钛的云母、氯氧化铋、氯氧化钛、有色珠光颜料诸如具有氧化铁的钛云母、具有铁蓝、氧化铬等的钛云母、具有上述类型的有机颜料的钛云母以及基于氯氧化铋的那些及其混合物。
在所公开的组合物的实施例中使用的着色剂的精确量和类型将取决于化妆品组合物的颜色、强度和用途,因此将由化妆品制剂领域的技术人员确定。然而,用于本发明的着色剂的一种优选的量为约0.5%至约7.5%,基于组合物的重量计。
然后可以使用各种已知的应用技术将这些组合物应用到使用者的皮肤或头发上。
实例1(硅氧烷包水)
给定一个基础的硅氧烷包水配方,使用1%w/w、2%w/w和3%w/w的尼龙-12、PMMA或PHB生成了九个测试配方。还测试了基础配方。
实例
相 | 化学品 | 百分比(%) |
A | 聚二甲基硅氧烷 | 1%-20% |
异十二烷 | 1%-20% | |
表面活性剂 | 0.1%-10% | |
填料 | 0.1%-30% | |
硅氧烷MQ树脂 | 0.1%-15% | |
稳定剂 | 0.01%-2% | |
颜料 | 0.1%-41% | |
B | 水 | 5%-45% |
硫酸镁 | 0.1%-2% | |
防腐剂 | 0.01%-2% |
为了生产,请在室温下在高剪切下混合A相的成分。在室温下在低剪切下混合B相的成分直至均匀。将B相缓慢加入A相,同时混合以产生乳液。
在测试中,每种配方都施用在皮肤上。在10分钟、20分钟、30分钟、60分钟和24小时时测量光泽度。在纸基基材上制备3密耳湿膜,并在室温下干燥过夜。将薄膜放置并锁定在含有合成皮脂的装置中,通过倒置装置将其暴露于薄膜的背面。由BYK提供的光泽度计(micro-TRI-gloss)用于光泽度测量。
在60分钟时,对照的光泽度约为8个光泽度单位,而其他制剂的光泽度在1个和4个光泽度单位之间。在九种测试配方中,尼龙通常是光泽度最低的制剂,光泽度通常在1左右,而PMMA的光泽度最高,从10分钟时的1左右上升到60分钟时的4左右。PHB配方介于两者之间,一般在10分钟时的约1上升到约2(1%,2%使用)至3(3%使用)。
在24小时时,对照的光泽度为约28个光泽度单位,而测试配方的光泽度测量值为约3个至约8个光泽度单位。
在多重挑战磨损测试中,使用1mL下拉条将薄膜沉积在黑色byko-chart BlackScrub Panels P121-10N#5015等表面上。在37℃下干燥24小时后,沉积物可以被人造皮脂或汗水覆盖。然后使用配备有粘在最低条上的Velcro(3/4″白色010 PSA 0172)片的自动拉伸机(Gardco Automatic Drawdown Machine)研磨样品。将Velcro粘合条与薄膜界面接触,然后将条自动拖过样品一次。然后可以使用吸收性材料(例如,来自Kimberly-Clark的bioskin和/或KIMWIPESTM品牌精细工作擦拭器)用手轻轻擦拭薄膜。然后,可以确定有多少样品保持在擦洗板上没有被破坏,以及有多少样品已经转移到吸收材料上,使用诸如如上所述的一种等级量表来评估样品从基材去除的程度或样品转移到吸收材料的程度,其中1是完全破坏和极端转移到吸收材料,2是大部分破坏,大部分转移到吸收材料,3是一半破坏,部分转移到吸收材料,4是最少破坏,最少转移到吸收材料,以及5是基本上没有去除和转移。结果列于下表1
表1:
实例2(散粉制剂)
根据表2制备具有以下组成的散粉。
表2:
粉末很容易在脸上涂抹,并具有良好的柔软性。
实例3(压实的粉末制剂)
根据表3制备具有以下组成的粉饼。
表3:
将粉末过筛,倒入金属盘中,然后压实。粉末很容易在脸上涂抹,并具有良好的柔软性。
仅使用常规实验,本领域技术人员将认识到或能够确定本文所述的本发明的具体实施例的许多等同方案。这样的等同方案旨在由所附权利要求涵盖。
Claims (8)
1.一种化妆品组合物,其包含:
0.1%w/w至30%w/w的至少一种平均直径(d50)为0.1nm至50μm的颗粒形式的聚羟基链烷酸酯(PHA),
其中所述组合物具有硅氧烷外相或者呈松散或压实粉末的形式。
2.根据权利要求1所述的化妆品组合物,其中所述PHA具有1个至8个碳的链长。
3.根据权利要求1所述的化妆品组合物,其中所述PHA为聚-3-羟基丁酸酯(PHB)、聚-3-羟基戊酸酯(PHV)、聚-3-羟基己酸酯(PHH)、聚-3-羟基辛酸酯(PHO)、聚(3-羟基丁酸酯-共-3-羟基戊酸酯)(PHBV)、聚(3-羟基丁酸酯-共-3-羟基己酸酯)(PHBH)、聚(3-羟基丁酸酯-共-4-羟基丁酸酯)、聚(3-羟基辛酸酯-共-3-羟基-10-十一烯酸酯)(PHOU)、聚(3-羟基丁酸酯-共-3-羟基戊酸酯-共-4-羟基戊酸酯)(PHBW)或其组合。
4.根据权利要求1所述的化妆品组合物,其中所述组合物进一步包含至少一种颜料。
5.根据权利要求1所述的化妆品组合物,其中选择所述PHA以使每100克PHA具有60克至150克所期望油的吸油量。
6.根据权利要求1所述的化妆品组合物,其中所述PHA以1%w/w至8%w/w的量存在于所述组合物中。
7.根据权利要求1所述的化妆品组合物,其中所述PHA为PHB,并且其中所述组合物具有硅氧烷外相。
8.一种使用化妆品组合物的方法,其包括:
提供根据权利要求1所述的组合物;以及
将所述组合物应用于使用者的皮肤或头发。