CN115447231A - Reflective fabric and production process thereof - Google Patents
Reflective fabric and production process thereof Download PDFInfo
- Publication number
- CN115447231A CN115447231A CN202211066866.3A CN202211066866A CN115447231A CN 115447231 A CN115447231 A CN 115447231A CN 202211066866 A CN202211066866 A CN 202211066866A CN 115447231 A CN115447231 A CN 115447231A
- Authority
- CN
- China
- Prior art keywords
- fabric
- reflective
- resin
- adhesive
- retroreflective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a reflective fabric, relates to the technical field of reflective fabrics, and particularly relates to a reflective fabric and a production process thereof. The reflective fabric is composed of a base fabric, a reflective material and an adhesive. The prepared reflective fabric has high fastness and can be washed for more than 50 times without falling off; the processing method is widely applied to various different woven fabrics and low-elasticity knitted fabrics; the product has higher light reflection degree than other light-reflecting fabrics, and can play a role in safety warning at night; the prepared fabric has a relatively thin reflective layer, is light and thin and has good hand feeling.
Description
Technical Field
The invention relates to the technical field of reflective fabrics, in particular to a reflective fabric and a production process thereof.
Background
With the increase of activities at night or in a low-light environment and the rise of safety consciousness of people for enhancing safety and avoiding accidents, the application of the reflective material on the clothes is developed dramatically. Reflecting material above the existing market mainly adopts reflection of light yarn directly to weave into the surface fabric or uses reflection of light strip concatenation, the mode of reflection of light stamp, and because the mode that uses reflection of light yarn to weave into has received the restraint of unable high temperature dyeing, make the mode that reflection of light yarn directly weaves into use not much, mainly be with the mode of reflection of light strip concatenation with reflection of light stamp, and reflection of light strip concatenation and traditional reflecting material screen printing, the reflecting material layer of modes such as thermoprint is than thicker, it is harder to feel, this can influence the travelling comfort demand of dress, reflection of light effect also remains to promote simultaneously.
Patent CN114132019A discloses a production process of breathable fancy type reflective fabric and noctilucent reflective fabric, which comprises the steps of printing oil agent patterns on a PET film to form an oil agent pattern layer, coating glue, compounding with the fabric, peeling off the PET release film to obtain the fabric with the patterns, compounding a bead planting film with the fabric with the patterns, and peeling off a bead planting protective film after curing to obtain the breathable fancy type reflective fabric.
Therefore, it is necessary to adopt a new production process to obtain a thinner reflective layer, a higher reflective effect and a reflective print with better hand feeling to solve the above problems.
Disclosure of Invention
In order to solve the technical problems, the invention provides a reflective fabric and a production process thereof, so as to obtain a thinner reflective layer, a higher reflective effect and a reflective printing with better hand feeling.
The application provides a reflective fabric, which consists of a base fabric, a reflective material and an adhesive.
Preferably, the base fabric is one of a woven fabric and a knitted fabric.
Preferably, the base fabric is a knitted fabric;
preferably, the knitted fabric is one of low elasticity, medium elasticity, high elasticity and ultrahigh elasticity.
Preferably, the knitted fabric is a low-elasticity knitted fabric.
Preferably, the reflective material is one of reflective film, reflective cloth, reflective leather and reflective woven tape.
Preferably, the reflective material is a reflective film;
preferably, the reflective film comprises one of blue, red, yellow, purple, orange and green;
preferably, the Reflective film is a CFC Reflective film, which is Reflective Blue and purchased from CFC company.
As a preferred technical scheme, the adhesive comprises the following components in parts by weight: 2.5-5.5 parts of resin, 1.5-4.5 parts of curing agent and 1.5-4.5 parts of solvent.
Preferably, the components of the adhesive comprise, by weight: 3-5 parts of resin, 2-4 parts of curing agent and 2-4 parts of solvent.
Preferably, the resin is one of polyurethane resin, epoxy resin, silicone resin and polyimide resin;
preferably, the resin is a polyurethane resin, model No. KD-6300, available from KYUNGIL HI-CHEM for fibers.
Preferably, the curing agent is one of isocyanates, melamines and epoxy;
preferably, the curing agent is an isocyanate curing agent, model AK-75, available from Seiki chemical Co.
Preferably, the solvent is one of butanone, acetone and cyclohexanone;
preferably, the solvent is methyl ethyl ketone MEK.
Preferably, the weight ratio of the resin, the curing agent and the solvent in the adhesive is 4: 3.
preferably, the weight ratio of the resin, the curing agent and the solvent in the adhesive is 4.
In the invention, the weight ratio of the three components is preferably 4.5-3.5: 3, especially when the weight ratio of the three components is 4.
The application also provides a production process of the reflective fabric, which comprises the following steps: 1) Adding the adhesive to the base fabric through a printing plate, and then drying in an oven; 2) And (3) adopting gold stamping silver stamping equipment, transferring the reflective material to the surface of the base fabric with the adhesive by a hot-pressing transfer printing technology, curing after transfer printing, and cooling to obtain the reflective fabric.
Preferably, the addition amount of the binder is 6 to 8g/m 2 ;
Preferably, the addition amount of the binder is 7g/m 2 ;
Preferably, the drying treatment is carried out for 10 to 15 seconds under the condition that the temperature of an oven is 120 to 140 ℃.
Preferably, the drying treatment is carried out for 11-13s under the condition that the temperature of the oven is 130 ℃.
More preferably, the drying treatment is drying treatment for 12s under the condition that the temperature of the oven is 130 ℃.
In the application of the invention, the applicant reasonably controls the drying temperature and the drying time under the constant-temperature and constant-humidity working environment by controlling the addition amount of the adhesive, so that the adhesive is in a semi-dry state and can reach the optimal viscosity under the drying treatment condition in the range, the subsequent finished products are ensured not to be degummed, and the hand feeling is not influenced; the thickness of the adhesive is limited on the premise of ensuring the viscosity, and the adhesive is thinner after being combined with the reflective layer, so that the adhesive is suitable for processing thinner fabrics without influencing the hand feeling of the fabrics.
The printing plate type is not specially limited, and the plate making is carried out according to the patterns provided by customers when in use; preferably, the width range of the lines in the flower type is 1-15mm. For example, the width of the lines in the pattern is 1mm,2mm,3mm,4mm,5mm,6mm,7mm,8mm,9mm,10mm, 111mm, 12mm,13mm,14mm, and 15mm.
Preferably, the hot-pressing temperature of the hot-pressing transfer printing is 160-180 ℃, and the transfer printing speed is 4-6 yards per minute;
preferably, the hot-pressing temperature of the hot-pressing transfer printing is 170 ℃, and the transfer printing speed is 5 yards per minute.
Preferably, the curing temperature is 60-70 ℃, the curing time is 44-52h, the cooling temperature is 25 +/-2 ℃, and the cooling time is 20-28h.
Preferably, the curing temperature is 65 ℃, the curing time is 48 hours, the cooling temperature is 25 ℃, and the cooling time is 24 hours.
The invention obtains the following beneficial effects: 1) The invention has little gas pollution and no water pollution, uses high-strength adhesive, has high fastness, can be washed by water for more than 50 times and does not fall off; 2) The processing technology of the invention has little limitation on the base fabric, can process on the water-splashing fabric, and can be widely applied to various different woven fabrics and low-elasticity knitted fabrics; 3) The processed fabric has higher light reflection degree than other light-reflecting fabrics, and can play a role in safety warning at night; 4) The invention adopts the optimized reflective material and the processing technology to obtain a thinner reflective layer, the fabric has good hand feeling, and is suitable for light and thin fabrics; 5) The invention has short flow, easy pattern change and low cost and can realize continuous large-scale production.
Drawings
FIG. 1 shows an example of the printing plate type in this example 1.
Fig. 2 shows an example of the printing plate type in this embodiment 3.
Detailed Description
Example 1
The embodiment 1 of the invention provides a reflective fabric, which consists of a base fabric, a reflective material and an adhesive. Fig. 1 shows an example of the printing plate type in the present embodiment.
The base fabric is a low-elasticity knitted fabric, and the specifications of the fabric are as follows: 100% polyester, count 50D 40Guage, grammage 116g/m 2 And a width 62inch.
The reflecting material is a CFC reflecting film with the model of Reflective Blue, and is purchased from Korean CFC company.
The adhesive comprises the following components in parts by weight: 4 parts of resin, 3 parts of curing agent and 3 parts of solvent.
The resin is polyurethane resin, the type is fiber resin KD-6300, and the resin is purchased from KYUNGIL HI-CHEM.
The curing agent is isocyanate curing agent with the model of AK-75, and is purchased from the Kingji chemical Co.
The solvent is methyl ethyl ketone MEK.
In another aspect, embodiment 1 of the present invention provides a production process of a reflective fabric, including the following steps: 1) Adding the adhesive to the base fabric through a printing plate, and then drying in an oven; 2) And (3) adopting gold stamping silver stamping equipment, transferring the reflective material to the surface of the base fabric with the adhesive by a hot-pressing transfer printing technology, curing after transfer printing, and cooling to obtain the reflective fabric.
The addition amount of the adhesive is 7g/m 2 ;
The drying treatment is carried out for 12s under the condition that the temperature of an oven is 130 ℃.
The width of lines in the printing plate type is 7mm.
The hot-pressing temperature of the hot-pressing transfer printing is 170 ℃, and the transfer printing speed is 5 yards per minute.
The curing temperature is 65 ℃, the curing time is 48 hours, the cooling temperature is 25 ℃, and the cooling time is 24 hours.
Example 2
The embodiment 2 of the invention provides a reflective fabric, which consists of a base fabric, a reflective material and an adhesive.
The base fabric is woven fabric, and the fabric specification is as follows: 100% polyester, count 50D, gram weight 75g/m 2 And a width 59inch.
The reflecting material is a CFC reflecting film with the model of Reflective Blue, and is purchased from Korean CFC company.
The adhesive comprises the following components in parts by weight: 4 parts of resin, 2.5 parts of curing agent and 3 parts of solvent.
The resin is polyurethane resin, the model is fiber resin KD-6300, and the resin is purchased from KYUNGIL HI-CHEM.
The curing agent was an isocyanate-based curing agent, model AK-75, purchased from Touris chemical Co.
The solvent is methyl ethyl ketone MEK.
In another aspect, embodiment 2 of the present invention provides a production process of a reflective fabric, including the following steps: 1) Adding the adhesive to the base fabric through a printing plate, and then drying in an oven; 2) And (3) adopting gold stamping and silver stamping equipment, transferring the reflective material to the surface of the base fabric with the adhesive by a hot-pressing transfer printing technology, solidifying after transfer printing, and cooling to obtain the reflective fabric.
The addition amount of the adhesive is 6g/m 2 ;
The drying treatment is carried out for 13s under the condition that the temperature of an oven is 125 ℃.
The width of lines in the printing plate type is 5mm.
The hot-pressing temperature of the hot-pressing transfer printing is 160 ℃, and the transfer printing speed is 4 yards per minute.
The curing temperature is 60 ℃, the curing time is 52h, the cooling temperature is 25 ℃, and the cooling time is 28h.
Example 3
The embodiment 3 of the invention provides a reflective fabric, which consists of a base fabric, a reflective material and an adhesive. Fig. 2 shows an example of the printing plate type in the present embodiment.
The base fabric is a low-elasticity knitted fabric, and the specifications of the fabric are as follows: 100% polyester, count 50D × 40Guage, grammage 116g/m2, breadth 62inch.
The reflecting material is a CFC reflecting film with the model of Reflective Blue, and is purchased from Korean CFC company.
The adhesive comprises the following components in parts by weight: 4 parts of resin, 3.5 parts of curing agent and 3 parts of solvent.
The resin is polyurethane resin, the model is fiber resin KD-6300, and the resin is purchased from KYUNGIL HI-CHEM.
The curing agent was an isocyanate-based curing agent, model AK-75, purchased from Touris chemical Co.
The solvent is methyl ethyl ketone MEK.
In another aspect, embodiment 3 of the present invention provides a production process of a reflective fabric, including the following steps: 1) Adding the adhesive to the base fabric through a printing plate, and then drying in an oven; 2) And (3) adopting gold stamping silver stamping equipment, transferring the reflective material to the surface of the base fabric with the adhesive by a hot-pressing transfer printing technology, curing after transfer printing, and cooling to obtain the reflective fabric.
The addition amount of the adhesive is 8g/m 2 ;
The drying treatment is carried out for 11s under the condition that the temperature of an oven is 135 ℃.
The width of lines in the printing plate type is 1mm.
The hot-pressing temperature of the hot-pressing transfer printing is 180 ℃, and the transfer printing speed is 6 yards per minute.
The curing temperature is 70 ℃, the curing time is 44 hours, the cooling temperature is 25 ℃, and the cooling time is 20 hours.
Comparative example 1
The invention comparative example 1 provides a reflective fabric, which is the same as the embodiment 1 in the specific implementation manner, and is characterized in that the adhesive comprises the following components in parts by weight: 4 parts of resin, 1 part of curing agent and 1 part of solvent.
Comparative example 2
Comparative example 2 of the present invention provides a reflective fabric, which is similar to example 1, except that the amount of the binder is 5g/m 2 ;
Comparative example 3
Comparative example 3 of the present invention provides a reflective fabric, which is the same as example 1 except that the amount of the binder added is 10g/m 2 ;
Comparative example 4
The invention provides a comparative example 4 which is a reflective fabric, and the specific implementation mode of the reflective fabric is the same as that of example 1, except that the drying treatment is carried out for 9s under the condition that the temperature of an oven is 150 ℃.
Comparative example 5
Comparative example 5 of the present invention provides a reflective fabric, which is the same as example 1 in the specific embodiment, except that the reflective material is a PE reflective film, model number KBD-B-001, purchased from ningbo kobaoda new materials ltd.
Performance test
Washing resistance: the fabric is washed according to the regulation of the fabric washing mode in the reference standard GB/T8629, and after drying, whether the reflective film falls off after washing for 50 times is judged, wherein the judgment is divided into 3 grades, A grade: the coating is perfect and does not fall off; b stage: the film is broken and does not fall off completely; c level: completely fall off.
The test results are shown in Table 1.
TABLE 1
Washing resistance | |
Example 1 | A |
Example 2 | A |
Example 3 | A |
Comparative example 1 | C |
Comparative example 2 | B |
Comparative example 3 | B |
Comparative example 4 | B |
Comparative example 5 | B |
Claims (10)
1. The reflective fabric is characterized by comprising a base fabric, a reflective material and an adhesive.
2. The retroreflective fabric of claim 1, wherein the base fabric is one of a woven fabric and a knitted fabric.
3. The reflective fabric of claim 1, wherein the reflective material is one of reflective film, reflective cloth, reflective leather, and reflective woven tape.
4. The retroreflective fabric of claim 1, wherein the binder comprises, in parts by weight: 2.5-5.5 parts of resin, 1.5-4.5 parts of curing agent and 1.5-4.5 parts of solvent.
5. The retroreflective fabric of claim 4, wherein the resin is one of a polyurethane resin, an epoxy resin, a silicone resin, and a polyimide resin.
6. The retroreflective fabric of claim 4, wherein the weight ratio of resin, curing agent, and solvent in the binder is 4: 3.
7. a process for producing a retroreflective fabric according to any one of claims 1 to 6, comprising the steps of: 1) Adding the adhesive to the base fabric through a printing plate, and then drying in an oven; 2) And (3) adopting gold stamping and silver stamping equipment, transferring the reflective material to the surface of the base fabric with the adhesive by a hot-pressing transfer printing technology, solidifying after transfer printing, and cooling to obtain the reflective fabric.
8. The process for producing retroreflective sheeting of claim 7 wherein the binder is added in an amount of 6 to 8g/m 2 。
9. The process for producing the retroreflective sheeting of claim 7 wherein the drying is carried out at an oven temperature of 120-140 ℃ for 10-15 seconds.
10. The process for producing a retroreflective sheeting of claim 7 wherein the hot press temperature of the hot press transfer is 160-180 ℃ and the transfer rate is 4-6 yards per minute.