CN110438625A - A kind of production method of cool feeling foldover Fashion - Google Patents
A kind of production method of cool feeling foldover Fashion Download PDFInfo
- Publication number
- CN110438625A CN110438625A CN201910764881.7A CN201910764881A CN110438625A CN 110438625 A CN110438625 A CN 110438625A CN 201910764881 A CN201910764881 A CN 201910764881A CN 110438625 A CN110438625 A CN 110438625A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cool feeling
- foldover
- follows
- paper matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of cool feeling foldover Fashion, include the following steps: that fabric → fabric desizing → washing, sour neutralization → stoving process → coating digit printing → foldover → decatize is formed → tear rod open and play cloth → cool feeling test.The present invention produces plain weave fabric using ultra-high molecular weight polyethylene long filament and cool feeling polyester filament on loom, wherein warp thread uses 50D ultra-high molecular weight polyethylene long filament, weft yarn uses 50D cool feeling terylene silk face fabric, after desizing drying, coating digit printing, fabric is bonded using corrugated board, it is converted into irregular fold, by fabric clamping in paper mold heat-shaping, fabric is set irregular fold occur, fabric is 3-5 DEG C lower than normal temperature simultaneously, and cool feeling Q-max value is up to 0.58 after tested, nice and cool as summer clothes fabric not only fashion.
Description
Technical field
The invention belongs to textile industry fabric fields, and in particular to a kind of production method of cool feeling foldover Fashion.
Background technique
Fold imparts the unique vision of fabric and haptic effect, is widely used in clothes and decorative fabric.It is existing double
The production method of layer crinkle fabric is predominantly weaved using double-beam or is sewed to fabric, crimped or chemical paste stamp etc.
Final finishing is made, and double-beam weaves the concave-convex fold for being differently formed web surface through tension using two beams of a loom, and this method is raw
It is production. art complexity, the high requirements on the equipment, more difficult to control;Fabric is sewed, the post-processings system such as crimped or chemical paste stamp
At the double-deck crinkle fabric, fold is easily stretched in fabric use process and deforms and influence beautiful and sense of touch, and this side
It is method low efficiency, at high cost.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the present invention provides a kind of lifes of cool feeling foldover Fashion
Production method.
Technical solution: a kind of production method of cool feeling foldover Fashion, include the following steps: fabric → fabric desizing →
Washing, sour neutralization → stoving process → coating digit printing → foldover → decatize is formed → tear rod open and play cloth → cool feeling test;Wherein:
The fabric desizing:
Technology preparation and condition:
The washing, acid neutralize:
Process flow is as follows: high temperature washing → cold water washes → acid neutralization;
The washing of a high temperature: temperature is 80-90 DEG C;Time is 2-3min;
B cold water is washed: temperature is 30-40 DEG C;Time is 2-3min;
It is as follows that c acid neutralizes formula: glacial acetic acid 1-2g/L;PH value is 6-8;
The coating digit printing:
Process flow is as follows: fabric pre-processes -- printing of coating direct-injection -- drying;
The formula of fabric pretreatment fluid is as follows:
Penetrating agent JFC 4-6g/L;
Hydrophilic softener 2-3g/L;
The printing of coating direct-injection: by ink printed to fabric, wide format printer is controlled by computer, printing ink is ejected into
On fabric;
Drying: drying temperature is 140-150 DEG C, time 2-3min;
The foldover:
A. do paper matrix: paper matrix is made of Double layer corrugated paper, and upper and lower level can be bonded to form alphabetical layer, paper matrix according to fabric most
Whole effect die sinking;
B. patch is engaged: upper layer paper matrix being opened, fabric is attached on lower layer's paper matrix, then by upper layer paper matrix together with fabric
It is snapped on lower layer's paper matrix;
C. it pricks rod: paper matrix interval 30-40cm is tightened with plastic knitting band, paper matrix is in long stick shape.
As further optimization: the fabric specification is as follows: warp thread uses 50D ultra-high molecular weight polyethylene long filament,
Weft yarn uses 50D cool feeling terylene silk face fabric, breadth 240-245cm, grammes per square metre 140-150g/m2。
As further optimization: the stoving process: forming machine drying temperature is 100 DEG C -105 DEG C, and the time is
3min-5min, door width are 240-245cm.
As further optimization: corrugated paper rod the decatize sizing: being carried out decatize sizing, process conditions: temperature
Are as follows: 102 DEG C -105 DEG C;Time are as follows: 8min-10min.
As further optimization: the rod of tearing open plays cloth: corrugated paper being separated with fabric, fabric presents and corrugated paper mould
The same fold.
As further optimization: the cool feeling test: fabric cool feeling index Q-max value is up to 0.58.
The utility model has the advantages that specific advantage of the invention is as follows:
1, fabric of the invention is interweaved using 50D ultra-high molecular weight polyethylene and 50D cool feeling dacron thread, is had good thermally conductive
Property, thermal resistance is small, and surface is soft and smooth nice and cool, is mainly used as summer clothes fabric.
2, due to ultra-high molecular weight polyethylene non-refractory, it is unable to high temperature pre-setting, dyeing print can not be carried out using dyestuff
Flower, therefore use coating digit printing.
3, the fold finishing in summer clothes fabric, is the fabric favored by fashion designer, and irregular fold makes fabric
More personalized.
4, the present invention is combined using high-performance and high functional fabric, using coating digit printing green environmental protection technique, knot
Close that garment material is personalized, fashion-orientation is the theme, it is multi-field multidisciplinary transboundary to merge.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can better understand advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, those of ordinary skill in the art's every other implementation obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment
The present invention produces plain weave fabric using ultra-high molecular weight polyethylene long filament and cool feeling polyester filament on loom,
Wherein warp thread uses 50D ultra-high molecular weight polyethylene long filament, and weft yarn uses 50D cool feeling terylene silk face fabric, breadth 240-
245cm, grammes per square metre 140-150g/m2, after desizing drying, coating digit printing is bonded fabric using corrugated board, is converted into and does not advise
Fold then, by fabric clamping in paper mold heat-shaping, so that fabric irregular fold is occurred, while fabric is lower than normal temperature
3-5 DEG C, cool feeling Q-max value is up to 0.58 after tested, nice and cool as summer clothes fabric not only fashion.
Specific embodiment 1
Process flow of the invention is as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → coating are digital
Stamp → foldover → decatize is formed → tears rod open and plays cloth → cool feeling test.
1, fabric specification:
Warp thread uses 50D ultra-high molecular weight polyethylene long filament, and weft yarn uses 50D cool feeling terylene silk face fabric, and breadth is
240cm, grammes per square metre 140g/m2。
2, fabric desizing:
Technology preparation and condition:
3, washing, acid neutralize:
Process flow is as follows: high temperature washing → cold water washes → acid neutralization;
The washing of a high temperature: temperature is 80 DEG C;Time is 2min;
B cold water is washed: temperature is 30 DEG C;Time is 2min;
It is as follows that c acid neutralizes formula: glacial acetic acid 1g/L;PH value is 6.
4, stoving process:
Forming machine drying temperature is 100 DEG C, time 3min, and door width is 240cm.
5, coating digit printing:
Process flow is as follows: fabric pre-processes -- printing of coating direct-injection -- drying;
The formula of fabric pretreatment fluid is as follows:
Penetrating agent JFC 4g/L;
Hydrophilic softener 2g/L;
The printing of coating direct-injection: by ink printed to fabric, wide format printer is controlled by computer, printing ink is ejected into
On paper material.
Drying: drying temperature is 140 DEG C, time 2min.
6, foldover:
A. do paper matrix: paper matrix is made of Double layer corrugated paper, and upper and lower level can be bonded to form alphabetical layer, paper matrix according to fabric most
Whole effect die sinking;
B. patch is engaged: upper layer paper matrix being opened, fabric is attached on lower layer's paper matrix, then by upper layer paper matrix together with fabric
It is snapped on lower layer's paper matrix;
C. it pricks rod: paper matrix interval 30cm is tightened with plastic knitting band, paper matrix is in long stick shape.
7, decatize is formed: corrugated paper rod is carried out decatize sizing.Process conditions: temperature are as follows: 102 DEG C;Time are as follows: 8min.
8, it tears rod open and plays cloth: corrugated paper is separated with fabric, the fold as corrugated paper mould is presented in fabric.
9, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.58.
Specific embodiment 2
Process flow of the invention is as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → coating are digital
Stamp → foldover → decatize is formed → tears rod open and plays cloth → cool feeling test.
1, fabric specification:
Warp thread uses 50D ultra-high molecular weight polyethylene long filament, and weft yarn uses 50D cool feeling terylene silk face fabric, breadth 240-
245cm, grammes per square metre 140-150g/m2。
2, fabric desizing:
Technology preparation and condition:
3, washing, acid neutralize:
Process flow is as follows: high temperature washing → cold water washes → acid neutralization;
The washing of a high temperature: temperature is 90 DEG C;Time is 3min;
B cold water is washed: temperature is 40 DEG C;Time is 3min;
It is as follows that c acid neutralizes formula: glacial acetic acid 2g/L;PH value is 8.
4, stoving process:
Forming machine drying temperature is 105 DEG C, time 5min, and door width is 245cm.
5, coating digit printing:
Process flow is as follows: fabric pre-processes -- printing of coating direct-injection -- drying;
The formula of fabric pretreatment fluid is as follows:
Penetrating agent JFC 6g/L;
Hydrophilic softener 3g/L;
The printing of coating direct-injection: by ink printed to fabric, wide format printer is controlled by computer, printing ink is ejected into
On paper material.
Drying: drying temperature is 150 DEG C, time 3min.
6, foldover:
A. do paper matrix: paper matrix is made of Double layer corrugated paper, and upper and lower level can be bonded to form alphabetical layer, paper matrix according to fabric most
Whole effect die sinking;
B. patch is engaged: upper layer paper matrix being opened, fabric is attached on lower layer's paper matrix, then by upper layer paper matrix together with fabric
It is snapped on lower layer's paper matrix;
C. it pricks rod: paper matrix interval 40cm is tightened with plastic knitting band, paper matrix is in long stick shape.
7, decatize is formed: corrugated paper rod is carried out decatize sizing.Process conditions: temperature are as follows: 105 DEG C;Time are as follows: 8-
10min。
8, it tears rod open and plays cloth: corrugated paper is separated with fabric, the fold as corrugated paper mould is presented in fabric.
9, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.58.
Specific embodiment 3
Process flow of the invention is as follows: fabric → fabric desizing → washing, sour neutralization → stoving process → coating are digital
Stamp → foldover → decatize is formed → tears rod open and plays cloth → cool feeling test.
1, fabric specification:
Warp thread uses 50D ultra-high molecular weight polyethylene long filament, and weft yarn uses 50D cool feeling terylene silk face fabric, and breadth is
242cm, grammes per square metre 143g/m2。
2, fabric desizing:
Technology preparation and condition:
3, washing, acid neutralize:
Process flow is as follows: high temperature washing → cold water washes → acid neutralization;
The washing of a high temperature: temperature is 87 DEG C;Time is 2.5min;
B cold water is washed: temperature is 34 DEG C;Time is 2.5min;
It is as follows that c acid neutralizes formula: glacial acetic acid 1.5g/L;PH value is 7.
4, stoving process:
Forming machine drying temperature is 103 DEG C, time 4min, and door width is 243cm.
5, coating digit printing:
Process flow is as follows: fabric pre-processes -- printing of coating direct-injection -- drying;
The formula of fabric pretreatment fluid is as follows:
Penetrating agent JFC 5g/L;
Hydrophilic softener 2.6g/L;
The printing of coating direct-injection: by ink printed to fabric, wide format printer is controlled by computer, printing ink is ejected into
On paper material.
Drying: drying temperature is 143 DEG C, time 2.4min.
6, foldover:
A. do paper matrix: paper matrix is made of Double layer corrugated paper, and upper and lower level can be bonded to form alphabetical layer, paper matrix according to fabric most
Whole effect die sinking;
B. patch is engaged: upper layer paper matrix being opened, fabric is attached on lower layer's paper matrix, then by upper layer paper matrix together with fabric
It is snapped on lower layer's paper matrix;
C. it pricks rod: paper matrix interval 33cm is tightened with plastic knitting band, paper matrix is in long stick shape.
7, decatize is formed: corrugated paper rod is carried out decatize sizing.Process conditions: temperature are as follows: 104 DEG C;Time are as follows: 9min.
8, it tears rod open and plays cloth: corrugated paper is separated with fabric, the fold as corrugated paper mould is presented in fabric.
9, cool feeling is tested: fabric cool feeling index Q-max value is up to 0.58.
Fabric of the invention is interweaved using 50D ultra-high molecular weight polyethylene and 50D cool feeling dacron thread, is had good thermally conductive
Property, thermal resistance is small, and surface is soft and smooth nice and cool, is mainly used as summer clothes fabric.It, cannot due to ultra-high molecular weight polyethylene non-refractory
High temperature pre-setting can not be carried out dyeing and printing using dyestuff, therefore use coating digit printing.Fold in summer clothes fabric
It arranges, is the fabric favored by fashion designer, irregular fold makes fabric more personalized.The present invention using high-performance and
High functional fabric combines, using coating digit printing green environmental protection technique, personalized, the fashion-orientation bamboo master in conjunction with garment material
Topic, it is multi-field multidisciplinary transboundary to merge.
Claims (6)
1. a kind of production method of cool feeling foldover Fashion, characterized by the following steps: fabric → fabric desizing →
Washing, sour neutralization → stoving process → coating digit printing → foldover → decatize is formed → tear rod open and play cloth → cool feeling test;Wherein:
The fabric desizing:
Technology preparation and condition:
The washing, acid neutralize:
Process flow is as follows: high temperature washing → cold water washes → acid neutralization;
The washing of a high temperature: temperature is 80-90 DEG C;Time is 2-3min;
B cold water is washed: temperature is 30-40 DEG C;Time is 2-3min;
It is as follows that c acid neutralizes formula: glacial acetic acid 1-2g/L;PH value is 6-8;
The coating digit printing:
Process flow is as follows: fabric pre-processes -- printing of coating direct-injection -- drying;
The formula of fabric pretreatment fluid is as follows:
Penetrating agent JFC 4-6g/L;
Hydrophilic softener 2-3g/L;
The printing of coating direct-injection: by ink printed to fabric, wide format printer is controlled by computer, printing ink is ejected into fabric
On;
Drying: drying temperature is 140-150 DEG C, time 2-3min;
The foldover:
A. do paper matrix: paper matrix is made of Double layer corrugated paper, and upper and lower level can be bonded to form primary and secondary layer, and paper matrix is finally imitated according to fabric
Fruit die sinking;
B. patch is engaged: upper layer paper matrix being opened, fabric is attached on lower layer's paper matrix, then upper layer paper matrix is engaged together with fabric
Onto lower layer's paper matrix;
C. it pricks rod: paper matrix interval 30-40cm is tightened with plastic knitting band, paper matrix is in long stick shape.
2. the production method of cool feeling foldover Fashion according to claim 1, it is characterised in that: the fabric specification
As follows: warp thread uses 50D ultra-high molecular weight polyethylene long filament, and weft yarn uses 50D cool feeling terylene silk face fabric, breadth 240-
245cm, grammes per square metre 140-150g/m2。
3. the production method of cool feeling foldover Fashion according to claim 1, it is characterised in that: the drying work
Skill: forming machine drying temperature is 100 DEG C -105 DEG C, time 3min-5min, and door width is 240-245cm.
4. the production method of cool feeling foldover Fashion according to claim 1, it is characterised in that: the decatize is fixed
Type: corrugated paper rod is subjected to decatize sizing, process conditions: temperature are as follows: 102 DEG C -105 DEG C;Time are as follows: 8min-10min.
5. the production method of cool feeling foldover Fashion according to claim 1, it is characterised in that: the rod of tearing open rises
Cloth: corrugated paper is separated with fabric, and the fold as corrugated paper mould is presented in fabric.
6. the production method of cool feeling foldover Fashion according to claim 1, it is characterised in that: the cool feeling is surveyed
Examination: fabric cool feeling index Q-max value is up to 0.58.