CN115433496A - 一种抗污外墙乳胶漆的制备方法 - Google Patents
一种抗污外墙乳胶漆的制备方法 Download PDFInfo
- Publication number
- CN115433496A CN115433496A CN202211307179.6A CN202211307179A CN115433496A CN 115433496 A CN115433496 A CN 115433496A CN 202211307179 A CN202211307179 A CN 202211307179A CN 115433496 A CN115433496 A CN 115433496A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- latex paint
- fouling
- wall latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗污外墙乳胶漆的制备方法，包括：S1:将填料和颜料做研磨处理，其中填料过80‑120目筛，颜料过60‑80目筛；S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌5‑10min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌30‑40min，并进行过滤处理得抗污外墙乳胶漆。其离水剂使污水、灰尘、不易粘结在涂膜表面，产生自洁功能；空心玻璃粉因其自身的空心结构特性，在乳胶漆中形成保护结构，具有隔热、防紫外线的功能。
Description
本申请是名为《一种抗污外墙乳胶漆及其制备方法》的专利申请的分案申请，原申请的申请日为2021年12月23日，申请号为202111594585.0。
技术领域
本发明涉及乳胶漆技术领域，特别是涉及一种抗污外墙乳胶漆的制备方法。
背景技术
乳胶漆是一类以水为分散介质，聚合物乳液为成膜物质，通过加入颜填料和助剂，经一定工艺过程合成的水性涂料。由于乳胶漆具有低成本、污染少、施工方便和美观等特点，而在建筑涂料中得到广泛地应用。乳胶漆主要有内墙乳胶漆和外墙乳胶漆两大类。外墙乳胶漆的主要功能是装饰和保护建筑物面，使建筑物外貌整洁美观，从而达到美化城市环境的目的，同时能起到保护建筑物外墙的作用，延长其使用寿命。
外墙乳胶漆产品在使用时，要求其具有较强的耐污性和较好的保温性，以保证在一定的涂覆周期内墙体具有较好的外观和较强的使用性能，而现有的外墙乳胶漆性能参次不齐，耐污性能和保温效果均较差，无法满足使用需求。
发明内容
为了克服现有技术的不足，本发明的目的是提供一种抗污外墙乳胶漆的制备方法。
为实现上述目的，本发明提供了如下方案：
一种抗污外墙乳胶漆的制备方法，包括如下步骤：
S1:将填料和颜料做研磨处理，其中填料过80-120目筛，颜料过60-80目筛；
S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌5-10min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌30-40min，并进行过滤处理得抗污外墙乳胶漆；
其中，所述空心玻璃粉的制备方法为：
A1:准备重量份数如下的各组分：石英砂50份、纯碱12份、碳酸钙3份、长石3份、芒硝2份、碳酸钾2份、碳酸锂2份、氧化铁2份、工业盐4份、氧化锆1份、氧化钛2份；
A2:将配好的原料破碎混合后在600-700℃烘干0.5h，经球磨机粉磨成0.7-0.8mm的颗粒，膨化之后投入到电熔坩埚中熔制，熔制温度为1300℃，使用天然气烧制2h，然后将熔制好的玻璃液冷却，经过收集器收集后，通过漂浮在水面上收集空心玻璃微珠。
优选地，所述离水剂为纳米抗污助剂。
优选地，所述颜料为钛白粉、硫化锌、氧化锑、氧化锌和立德粉中的至少一种。
优选地，所述填料为轻钙粉、重钙粉和氧化铝的混合物，所述轻钙粉、重钙粉和所述氧化铝的重量比为2：2：1。
优选地，所述抗污外墙乳胶漆的重量分数的各组份为：纯净水370-420份、丙烯酸乳液300-350份、填料150-200份、颜料180-200份、空心玻璃粉250-280份、纤维素1.5-3份、防腐剂1.5-2份、防霉剂0.5-1.5份、分撒剂3-7份、润湿剂1-3份、悬浮剂3-8份、流平剂2-5份、成膜助剂20-25份、防腐剂1.5-3份、防霉剂1-3份、PH值调节剂2-5份、离水剂5-8份。
优选地，所述抗污外墙乳胶漆的重量分数的各组份为：纯净水400份、丙烯酸乳液350份、填料215份、钛白粉200份、空心玻璃粉250份、纤维素1.5份、防腐剂1.5份、防霉剂1.5份、分撒剂5份、润湿剂3份、悬浮剂5份、流平剂3份、成膜助剂25份、防腐剂1.5份、防霉剂1.5份、PH值调节剂3份、离水剂4份。
本发明技术方案的有益效果是：
1.通过添加防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂等助剂，其中润湿剂能够降低液体和固体表面的界面张力，而分散剂能够促进颜填料分散，保证乳胶漆的细度；增稠剂能够调节涂料的粘度和防止涂料流挂；成膜助剂主要用于提高乳液的成膜性能，使得乳胶颗粒表面软化，达到降低乳液最低成膜温度的目的；离水剂使污水、灰尘、不易粘结在涂膜表面，产生自洁功能。
2.空心玻璃粉因其自身的空心结构特性，在乳胶漆中形成保护结构，具有隔热、防紫外线的功能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
在本文中提及“实施例”意味着，结合实施例描述的特定特征、结构或特性可以包含在本申请的至少一个实施例中。在说明书中的各个位置出现该短语并不一定均是指相同的实施例，也不是与其它实施例互斥的独立的或备选的实施例。本领域技术人员显式地和隐式地理解的是，本文所描述的实施例可以与其它实施例相结合。
本申请的说明书和权利要求书中的术语“第一”、“第二”、“第三”和“第四”等是用于区别不同对象，而不是用于描述特定顺序。此外，术语“包括”和“具有”以及它们任何变形，意图在于覆盖不排他的包含。例如包含了一系列步骤、过程、方法等没有限定于已列出的步骤，而是可选地还包括没有列出的步骤，或可选地还包括对于这些过程、方法、产品或设备固有的其它步骤元。
为使本发明的上述目的、特征和优点能够更加明显易懂，下面结合具体实施方式对本发明作进一步详细的说明。
实施例1
本发明技术方案提供一种抗污外墙乳胶漆，包括如下重量分数的各组份：纯净水400份、丙烯酸乳液350份、填料215份、钛白粉200份、空心玻璃粉250份、纤维素1.5份、防腐剂1.5份、防霉剂1.5份、分撒剂5份、润湿剂3份、悬浮剂5份、流平剂3份、成膜助剂25份、防腐剂1.5份、防霉剂1.5份、PH值调节剂3份、离水剂4份。
所述填料为轻钙粉、重钙粉和氧化铝的混合物，所述轻钙粉、重钙粉和所述氧化铝的重量比为2：2：1。所述颜料为钛白粉、硫化锌、氧化锑、氧化锌和立德粉中的至少一种。所述离水剂为纳米抗污助剂。
所述空心玻璃粉的制备过程为：
A1:准备重量份数如下的各组分：石英砂50份、纯碱12份、碳酸钙3份、长石3份、芒硝2份、碳酸钾2份、碳酸锂2份、氧化铁2份、工业盐4份、氧化锆1份、氧化钛2份；
A2:将配好的原料破碎混合后在650℃烘干0.5h，经球磨机粉磨成0.7mm的颗粒，膨化之后投入到电熔坩埚中熔制，熔制温度为1300℃，使用天然气烧制2h，然后将熔制好的玻璃液冷却，经过收集器收集后，通过漂浮在水面上收集空心玻璃微珠。
一种抗污外墙乳胶漆的制备方法，包括如下步骤：
S1:将填料和颜料做研磨处理，其中填料过100目筛，颜料过70目筛；
S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌8min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌37min得抗污外墙乳胶漆。
实施例2
本发明技术方案提供一种抗污外墙乳胶漆，包括如下重量分数的各组份：纯净水370份、丙烯酸乳液300份、填料150份、颜料180份、空心玻璃粉250份、纤维素1.5份、防腐剂1.5份、防霉剂0.5份、分撒剂7份、润湿剂3份、悬浮剂8份、流平剂5份、成膜助剂25份、防腐剂3份、防霉剂3份、PH值调节剂5份、离水剂份。
所述填料为轻钙粉、重钙粉和氧化铝的混合物，所述轻钙粉、重钙粉和所述氧化铝的重量比为2：2：1。所述颜料为钛白粉、硫化锌、氧化锑、氧化锌和立德粉中的至少一种。所述离水剂为纳米抗污助剂。
所述空心玻璃粉的制备过程为：
A1:准备重量份数如下的各组分：石英砂50份、纯碱12份、碳酸钙3份、长石3份、芒硝2份、碳酸钾2份、碳酸锂2份、氧化铁2份、工业盐4份、氧化锆1份、氧化钛2份；
A2:将配好的原料破碎混合后在600℃烘干0.5h，经球磨机粉磨成0.7mm的颗粒，膨化之后投入到电熔坩埚中熔制，熔制温度为1300℃，使用天然气烧制2h，然后将熔制好的玻璃液冷却，经过收集器收集后，通过漂浮在水面上收集空心玻璃微珠。
一种抗污外墙乳胶漆的制备方法，包括如下步骤：
S1:将填料和颜料做研磨处理，其中填料过80目筛，颜料过60目筛；
S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌5min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌30min得抗污外墙乳胶漆。
实施例3
本发明技术方案提供一种抗污外墙乳胶漆，包括如下重量分数的各组份：纯净水420份、丙烯酸乳液350份、填料200份、颜料200份、空心玻璃粉280份、纤维素3份、防腐剂2份、防霉剂1.5份、分撒剂3份、润湿剂1份、悬浮剂3份、流平剂2份、成膜助剂20份、防腐剂1.5份、防霉剂1份、PH值调节剂2份、离水剂5份。
所述填料为轻钙粉、重钙粉和氧化铝的混合物，所述轻钙粉、重钙粉和所述氧化铝的重量比为2：2：1。所述颜料为钛白粉、硫化锌、氧化锑、氧化锌和立德粉中的至少一种。所述离水剂为纳米抗污助剂。
所述空心玻璃粉的制备过程为：
A1:准备重量份数如下的各组分：石英砂50份、纯碱12份、碳酸钙3份、长石3份、芒硝2份、碳酸钾2份、碳酸锂2份、氧化铁2份、工业盐4份、氧化锆1份、氧化钛2份；
A2:将配好的原料破碎混合后在700℃烘干0.5h，经球磨机粉磨成0.8mm的颗粒，膨化之后投入到电熔坩埚中熔制，熔制温度为1300℃，使用天然气烧制2h，然后将熔制好的玻璃液冷却，经过收集器收集后，通过漂浮在水面上收集空心玻璃微珠。
一种抗污外墙乳胶漆的制备方法，包括如下步骤：
S1:将填料和颜料做研磨处理，其中填料过120目筛，颜料过80目筛；
S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌10min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌40min得抗污外墙乳胶漆。
对实施例1-实施例3制备的抗污外墙乳胶漆进行性能测试，测试结果如下表1所示：
表1
| 测试项目 | 实施例1 | 实施例2 | 实施例3 |
| 干燥时间(h) | 1.2 | 1.3 | 1.2 |
| 耐水性 | 150h无异常 | 150h无异常 | 150h无异常 |
| 耐碱性(ph＝11) | 48h无异常 | 48h无异常 | 48h无异常 |
| 耐洗刷性/次 | ≥2000次 | ≥2000次 | ≥2000次 |
| 低温稳定性(-15℃) | 不变质 | 不变质 | 不变质 |
由表1可知，本发明制备的抗污外墙乳胶漆具有较强的耐水、耐碱性能，较好的低温稳定性，已经较为稳定的外形结构。
本说明书中各个实施例采用递进的方式描述，每个实施例重点说明的都是与其他实施例的不同之处，各个实施例之间相同相似部分互相参见即可。
本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处。综上所述，本说明书内容不应理解为对本发明的限制。
Claims (6)
1.一种抗污外墙乳胶漆的制备方法，其特征在于，包括如下步骤：
S1:将填料和颜料做研磨处理，其中填料过80-120目筛，颜料过60-80目筛；
S2:将空心玻璃粉和过筛处理的填料、颜料加入分散罐中，然后加入水、丙烯酸乳液搅拌5-10min；然后加入纤维素、防腐剂、防霉剂、分撒剂、润湿剂、悬浮剂、流平剂、成膜助剂、防腐剂、防霉剂、PH值调节剂、离水剂，搅拌30-40min，并进行过滤处理得抗污外墙乳胶漆；
其中，所述空心玻璃粉的制备方法为：
A1:准备重量份数如下的各组分：石英砂50份、纯碱12份、碳酸钙3份、长石3份、芒硝2份、碳酸钾2份、碳酸锂2份、氧化铁2份、工业盐4份、氧化锆1份、氧化钛2份；
A2:将配好的原料破碎混合后在600-700℃烘干0.5h，经球磨机粉磨成0.7-0.8mm的颗粒，膨化之后投入到电熔坩埚中熔制，熔制温度为1300℃，使用天然气烧制2h，然后将熔制好的玻璃液冷却，经过收集器收集后，通过漂浮在水面上收集空心玻璃微珠。
2.根据权利要求1所述的一种抗污外墙乳胶漆的制备方法，其特征在于，所述离水剂为纳米抗污助剂。
3.根据权利要求1所述的一种抗污外墙乳胶漆的制备方法，其特征在于，所述颜料为钛白粉、硫化锌、氧化锑、氧化锌和立德粉中的至少一种。
4.根据权利要求1所述的一种抗污外墙乳胶漆的制备方法，其特征在于，所述填料为轻钙粉、重钙粉和氧化铝的混合物，所述轻钙粉、重钙粉和所述氧化铝的重量比为2：2：1。
5.根据权利要求1所述的一种抗污外墙乳胶漆的制备方法，其特征在于，所述抗污外墙乳胶漆的重量分数的各组份为：纯净水370-420份、丙烯酸乳液300-350份、填料150-200份、颜料180-200份、空心玻璃粉250-280份、纤维素1.5-3份、防腐剂1.5-2份、防霉剂0.5-1.5份、分撒剂3-7份、润湿剂1-3份、悬浮剂3-8份、流平剂2-5份、成膜助剂20-25份、防腐剂1.5-3份、防霉剂1-3份、PH值调节剂2-5份、离水剂5-8份。
6.根据权利要求1所述的一种抗污外墙乳胶漆的制备方法，其特征在于，所述抗污外墙乳胶漆的重量分数的各组份为：纯净水400份、丙烯酸乳液350份、填料215份、钛白粉200份、空心玻璃粉250份、纤维素1.5份、防腐剂1.5份、防霉剂1.5份、分撒剂5份、润湿剂3份、悬浮剂5份、流平剂3份、成膜助剂25份、防腐剂1.5份、防霉剂1.5份、PH值调节剂3份、离水剂4份。