CN115214205A - 一种玻璃组件 - Google Patents

一种玻璃组件 Download PDF

Info

Publication number
CN115214205A
CN115214205A CN202210984601.5A CN202210984601A CN115214205A CN 115214205 A CN115214205 A CN 115214205A CN 202210984601 A CN202210984601 A CN 202210984601A CN 115214205 A CN115214205 A CN 115214205A
Authority
CN
China
Prior art keywords
layer
glass
selenium
glass assembly
film layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210984601.5A
Other languages
English (en)
Inventor
胡兴微
蒋玉东
余强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Mammoth Semiconductor Technology Co ltd
Original Assignee
Sichuan Mammoth Semiconductor Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Mammoth Semiconductor Technology Co ltd filed Critical Sichuan Mammoth Semiconductor Technology Co ltd
Priority to CN202210984601.5A priority Critical patent/CN115214205A/zh
Publication of CN115214205A publication Critical patent/CN115214205A/zh
Pending legal-status Critical Current

Abstract

本发明涉及玻璃技术领域，特别地涉及一种玻璃组件。本发明公开了一种玻璃组件，包括透明的第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板；第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板依次层叠设置。本发明具有隔热保温、全部区域透明和发电功能。

Description

一种玻璃组件
技术领域
本发明属于玻璃技术领域，具体地涉及一种可作为汽车玻璃的玻璃组件。
背景技术
随着汽车上的玻璃的使用量越来越大，汽车玻璃的功能越来越受到关注。目前在汽车制造领域中，使用汽车天窗或天幕作为通风及观景的方式十分常见，传统的汽车玻璃不具备隔热保温功能，在夏天由于阳光较大且现在高温天气频繁，在阳光的持续照射下，车内温度极易升高，进而导致在准备进入驾驶前由于车辆内部温度较高导致驾驶体验不好，而且目前只能通过驾驶员在驾驶前开窗及开启空调进行解决，但是这样需要时间，并且空调在工作时需要电能供给，而且只有驾驶员上车后才能开启，若提前开启容易导致蓄电池没有电量，导致车辆无法发动。在冬天，特别是北方冬天，车子内部的热量很容易通过汽车玻璃使热量损失，使车内很冰冷，汽车玻璃外表面很容易结冰、积雪，这就使得人们从车内看车外的视线受阻。
为了解决汽车玻璃在夏天、冬天使用时存在的上述问题，人们进行了很多努力，但都不够理想。如现有的可发电汽车玻璃都是在两片玻璃之间夹进不透明的太阳能电池，这些太阳能电池有硅片电池、非晶硅薄膜电池、铜铟镓硒基薄膜电池、钙钛矿薄膜电池、有机太阳能电池等，这些汽车玻璃只具有发电的功能而不能同时具备整面透明的性能，因此就失去了汽车玻璃观察外部环境的本质。
也有部分可发电汽车玻璃为了达到部分区域透明的目的，采用激光刻蚀将部分薄膜电池刻蚀掉(如公开专利CN201410013602所公开的薄膜太阳能光伏汽车玻璃组件)，或将硅片间隔排列，于是在硅片与硅片的间隔处就有光透过而达到部分区域透明的目的(如公开专利CN201220731431.1所公开的汽车用太阳能天窗)，这种汽车玻璃虽具有可发电和部分透明功能但其隔热保温性能大大降低，而且这种部分透明是形成了类似百叶窗的形状，使人们从车内往车外看风景的视觉上非常难受，且不能用于汽车的侧窗和后挡风玻璃上。
还有一种汽车玻璃是在两片汽车玻璃中夹进具有低辐射率功能的膜层同时采用深色PVB胶片将两片玻璃夹层在一起，这种汽车玻璃可以达到整面透明性能，但是这种汽车玻璃不能发电，且只具有一定的隔热保温效果，但是其隔热保温效果不够理想，其太阳能总透射比还比较高。
综上所述，截止目前为止，并没有一种能够兼具整面透明、隔热保温和发电的多功能汽车玻璃。随着汽车设计的玻璃用量越来越大及新能源汽车越来越普及，对汽车玻璃的功能提出了更多的要求。因此急需一种同时具有上述多功能的汽车玻璃。
发明内容
本发明的目的在于提供一种具有隔热保温、全部区域透明和发电功能的玻璃组件用以解决上述存在的技术问题。
为实现上述目的，本发明采用的技术方案为：一种玻璃组件，包括透明的第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板；第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板依次层叠设置。
进一步的，所述柔性碲化镉硒基太阳能组件层的可见光透过率为1％-45％。
进一步的，所述柔性碲化镉硒基太阳能组件层的厚度小于0.8mm。
进一步的，所述第一胶片层和第二胶片层为PVB胶片层、EVA胶片层或POE胶片层。
进一步的，所述第二玻璃基板的背向第二胶片层的外表面沉积有透明导电层。
更进一步的，所述透明导电层为氧化锡层、氧化锡掺氟层、氧化铟掺锡层、氧化锌掺铝层、氧化铟掺钛层、氧化钛掺铌层或氧化铟掺铈层。
进一步的，该玻璃组件的太阳能总透射比小于25％。
进一步的，该玻璃组件的太阳能总透射比小于10％。
进一步的，所述柔性碲化镉硒基太阳能组件层具有多个电池单元，电池单元与电池单元之间具有刻划线。
进一步的，该玻璃组件为汽车玻璃，包括天窗或天幕玻璃、后挡风玻璃和侧窗玻璃。
本发明的有益技术效果：
本发明具有：1.隔热保温性能，且隔热保温性能良好；2.全部区域透明，不影响玻璃组件的观察外部环境的本质；3.发电的功能，可进行双面发电，且在弱光条件下也可发电，发电效率高，实现了节能和清洁发电，为有效减碳提供了一种保障。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简要介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域的普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明的的玻璃组件的一种结构示意图；
图2为本发明的的玻璃组件的另一种结构示意图；
图3为现有的隔热汽车天窗玻璃的结构示意图。
具体实施方式
为进一步说明各实施例，本发明提供有附图。这些附图为本发明揭露内容的一部分，其主要用以说明实施例，并可配合说明书的相关描述来解释实施例的运作原理。配合参考这些内容，本领域普通技术人员应能理解其他可能的实施方式以及本发明的优点。图中的组件并未按比例绘制，而类似的组件符号通常用来表示类似的组件。
现结合附图和具体实施方式对本发明进一步说明，以下实施例以玻璃组件作为汽车玻璃为例来进行说明，但并不限于此，本发明的玻璃组件也可以用于其它领域，如其它交通工具的玻璃等。
如图1所示，一种玻璃组件，包括透明(这里所述的透明也包括半透明)的第一玻璃基板1、第一胶片层2、柔性碲化镉硒基太阳能组件层3、第二胶片层4和第二玻璃基板5；第一玻璃基板1、第一胶片层2、柔性碲化镉硒基太阳能组件层3、第二胶片层4和第二玻璃基板5依次层叠设置，第一玻璃基板1用于朝向汽车外部，第二玻璃基板5用于朝向汽车内部，柔性碲化镉硒基太阳能组件层3具有双面发电及弱光发电的功能，柔性碲化镉硒基太阳能组件层3与车内的电路系统连接，可为汽车的蓄电池充电，实现节能和清洁发电，为汽车行业的有效减碳提供了一种保障。且在冬季汽车玻璃的外侧被冰雪覆盖的情况下，可通过车内侧面使该汽车玻璃发电，在发电过程会使汽车玻璃的外侧表面的冰雪融化同时起到保温的效果。
优选的，柔性碲化镉硒基太阳能组件层3的可见光透过率为1％-45％，可见光透过率小于1％时太暗，不适合用于汽车玻璃；可见光透过率大于45％时，柔性碲化镉硒基太阳能组件层3基本不发电。
优选的，柔性碲化镉硒基太阳能组件层3的厚度小于0.8mm，厚度若大于0.8mm则不够柔性，不能用于汽车玻璃。
进一步的，第二玻璃基板5的朝向汽车内部的外表面还沉积有透明导电层6，如图2所示。
具体的，透明导电层6为氧化锡层、氧化锡掺氟层、氧化铟掺锡层、氧化锌掺铝层、氧化铟掺钛层、氧化钛掺铌层或氧化铟掺铈层；第一胶片层2和第二胶片层4为PVB胶片层、EVA胶片层或POE胶片层等胶片层。
进一步的，该玻璃组件的太阳能总透射比小于25％，优选该玻璃组件的太阳能总透射比小于15％，更优选该玻璃组件的太阳能总透射比小于10％，进一步提升隔热性能，同时提高发电效率。
具体的，该玻璃组件可作为汽车的天窗或天幕玻璃、后挡风玻璃和侧窗玻璃等。
具体的，柔性碲化镉硒基太阳能组件层3具有多个电池单元，电池单元与电池单元之间具有刻划线。该玻璃组件用于汽车的侧窗玻璃时，刻划线横向设置，即与汽车底盘平行或大致平行的方向。
进一步的，还可在第一玻璃基板1的外表面沉积减反射膜层、亲水膜层、疏水膜层或自清洁膜层。
下面结合具体实施例对本发明进行详细说明。
实施例1
在第一玻璃基板1上铺设第一PVB胶片层作为第一胶片层2；接着将柔性碲化镉硒基太阳能组件层3铺设在第一PVB胶片层上；接着在柔性碲化镉硒基太阳能组件层3上铺设第二PVB胶片层作为第二胶片层4；接着在第二PVB胶片层上放上第二玻璃基板5；接着采用汽车玻璃的夹层工艺进行层压处理，由此获得本发明的玻璃组件，结构如图1所示。第一玻璃基板1和第二玻璃基板5为玻璃原片，其表面都没有任何的镀膜层；第一PVB胶片和第二PVB胶片都为无色透明的PVB胶片；经此工艺制作完成后，对其进行测试，测试结果：可见光透射比为6.4％、太阳能总透射比9.6％、遮阳系数为0.11。
实施例2
在第一玻璃基板1上铺设第一PVB胶片层作为第一胶片层2；接着将柔性碲化镉硒基太阳能组件层3铺设在第一PVB胶片层上；接着在柔性碲化镉硒基太阳能组件层3上铺设第二PVB胶片层作为第二胶片层4；接着在第二PVB胶片层上放上第二玻璃基板5，第二玻璃基板5的背对第二PVB胶片层的外表面上沉积透明导电层6；接着采用汽车玻璃的夹层工艺进行层压处理，由此获得本发明的玻璃组件，结构如图2所示。第一玻璃基板1为玻璃原片，其表面都没有任何的镀膜层；第一PVB胶片和第二PVB胶片都为无色透明的PVB胶片；经此工艺制作完成后，对其进行测试，测试结果：可见光透射比为6.2％、太阳能总透射比9.1％、遮阳系数为0.10。
对比例
在第一玻璃基板1的内表面沉积三银膜系的低辐射膜层7；接着在低辐射膜层7上放上深色PVB胶片层8(如灰色PVB胶片)；接着在深色PVB胶片层8上放上第二玻璃基板5，第二玻璃基板5的外表面上沉积透明导电层6；接着采用汽车玻璃的夹层工艺进行层压处理，由此获得的具有全区域透明、隔热保温的汽车玻璃，结构如图3所示。经此工艺制作完成后，对其进行测试，测试结果：可见光透射比为6.3％、太阳能总透射比15％、遮阳系数为0.20。这是目前市面上汽车天窗隔热性能最好的产品。
通过对比例与实施例的比较可得出：在可见光透射比基本相同的情况下，本发明具有比目前市面上隔热性能最好的汽车玻璃的隔热性能还要好得多，而且本发明的玻璃组件可进行双面发电，尤其在弱光条件下就可发电。
尽管结合优选实施方案具体展示和介绍了本发明，但所属领域的技术人员应该明白，在不脱离所附权利要求书所限定的本发明的精神和范围内，在形式上和细节上可以对本发明做出各种变化，均为本发明的保护范围。

Claims (10)

1.一种玻璃组件，其特征在于：包括透明的第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板；第一玻璃基板、第一胶片层、柔性碲化镉硒基太阳能组件层、第二胶片层和第二玻璃基板依次层叠设置。
2.根据权利要求1所述的玻璃组件，其特征在于：所述柔性碲化镉硒基太阳能组件层的可见光透过率为1％-45％。
3.根据权利要求1所述的玻璃组件，其特征在于：所述柔性碲化镉硒基太阳能组件层的厚度小于0.8mm。
4.根据权利要求1所述的玻璃组件，其特征在于：所述第一胶片层和第二胶片层为PVB胶片层、EVA胶片层或POE胶片层。
5.根据权利要求1所述的玻璃组件，其特征在于：所述第二玻璃基板的背向第二胶片层的外表面沉积有透明导电层。
6.根据权利要求5所述的玻璃组件，其特征在于：所述透明导电层为氧化锡层、氧化锡掺氟层、氧化铟掺锡层、氧化锌掺铝层、氧化铟掺钛层、氧化钛掺铌层或氧化铟掺铈层。
7.根据权利要求1所述的玻璃组件，其特征在于：该玻璃组件的太阳能总透射比小于25％。
8.根据权利要求1所述的玻璃组件，其特征在于：该玻璃组件的太阳能总透射比小于10％。
9.根据权利要求1所述的玻璃组件，其特征在于：所述柔性碲化镉硒基太阳能组件层具有多个电池单元，电池单元与电池单元之间具有刻划线。
10.根据权利要求1所述的玻璃组件，其特征在于：该玻璃组件为汽车玻璃，包括天窗或天幕玻璃、后挡风玻璃和侧窗玻璃。
CN202210984601.5A 2022-08-17 2022-08-17 一种玻璃组件 Pending CN115214205A (zh)