CN1151937A - 一种金库用复合材料 - Google Patents
一种金库用复合材料 Download PDFInfo
- Publication number
- CN1151937A CN1151937A CN 95114262 CN95114262A CN1151937A CN 1151937 A CN1151937 A CN 1151937A CN 95114262 CN95114262 CN 95114262 CN 95114262 A CN95114262 A CN 95114262A CN 1151937 A CN1151937 A CN 1151937A
- Authority
- CN
- China
- Prior art keywords
- grid
- aluminium alloy
- composite
- composite material
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金库用复合材料及其制造方法，本发明由于用铸造方法将铝合金与一定尺寸的陶瓷球复合一体，一方面降低了成本，另一方面铝合金散热快可防切割，表层金刚砂及内部陶瓷颗粒可防钻，综合性能优良。
Description
本发明涉及一种复合材料，更具体地说涉及一种一种金库用复合材料及其制造方法。
以往的金库门及组合金库墙板的设计，为达到防钻、防火焰切割及其它防破坏的目的，通常是在门体及墙板内衬以淬硬的厚钢板。这样虽然可提高上述产品的防钻、防破坏的功能，但因材料消耗费用巨大，成本提高，且门体及墙板重量大大增加，制造、运输甚为不便。此外，其防切割效果也不理想。
本发明的目的在于提供一种金库用复合材料，具有较高防钻、防火焰切割及其它防破坏的能力，且成本较低。
为实现本发明的上述目的，具体技术方案为：一种金库用复合材料，为多层复合材料，由铝合金作基体合金，铸造成形，中间为一层或一层以上的增强材料陶瓷球，球直径为2～10mm，球料置于支持网格中。
本发明由于用铸造方法将铝合金与一定尺寸的陶瓷球复合一体，一方面降低了成本，另一方面铝合金散热快可防切割，表层金刚砂及内部陶瓷颗粒可防钻，综合性能优良。
以下结合附图举出本发明的最佳实施例。
图1为本发明的结构图。
由图1可见，本发明为多层复合材料，由铝合金作基体合金(2)，中间为一层或一层以上的增强材料陶瓷球(4)，球直径为2～10mm，球料置于支持网格(3)中。其制造方法为，将铁丝作成支持网格，并置于料盖(5)中，可为一层或一层以上；将直径为2～10mm的陶瓷球(4)放在支持网格的各网格中；注入铝合金熔体；在表面敷上一层金刚砂(1)。为防止基体合金与料盖脱离，可预先在料盖的底部焊上一些金属丝，以加强连接。经试验，140mm厚的钢板只需5分钟即可钻穿，同样的材料4分钟即被氧气-乙炔火焰割断。本发明材料在防钻、防火焰切割及其它防破坏能力均达到美国保险业工会UL标准的最高等级，耐火6小时，防破坏2小时。
Claims (2)
1.一种金库用复合材料，为多层复合材料，由铝合金作基体合金，中间为一层或一层以上的增强材料陶瓷球，球直径为2～10mm，球料置于支持网格中。
2.一种金库用复合材料，其制造方法为，将铁丝作成支持网格，并置于料盖中，可为一层或一层以上；将直径为2～10mm的陶瓷球放在支持网格的各网格中；注入铝合金熔体；在表面敷上一层金刚砂。