CN115148096A - 显示装置 - Google Patents
显示装置 Download PDFInfo
- Publication number
- CN115148096A CN115148096A CN202210311411.7A CN202210311411A CN115148096A CN 115148096 A CN115148096 A CN 115148096A CN 202210311411 A CN202210311411 A CN 202210311411A CN 115148096 A CN115148096 A CN 115148096A
- Authority
- CN
- China
- Prior art keywords
- adhesive layer
- adhesive
- display device
- protective film
- window
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及显示装置。显示装置包括能够绕着折叠轴线折叠的显示面板、在显示面板上的窗、在窗上的保护膜、以及在窗和保护膜之间的多个粘合剂层。粘合剂层包括在窗上的第一粘合剂层和在第一粘合剂层上的第二粘合剂层。第一粘合剂层包括侧链结晶聚合物,并且第二粘合剂层的模量小于第一粘合剂层的模量。
Description
相关申请的交叉引用
本申请要求于2021年3月29日提交的第10-2021-0040688号韩国专利申请的优先权、以及由其产生的所有权益,该韩国专利申请的内容通过引用以其整体并入本文。
技术领域
本公开涉及显示装置。更具体地,本公开涉及可折叠显示装置。
背景技术
显示装置通过显示屏幕显示各种图像以向用户提供信息。正在开发包括可折叠的柔性显示面板的柔性显示装置。由于柔性显示装置的形状以各种方式改变,因此改善了柔性显示装置的运输的方便性,无论原始屏幕尺寸如何。
发明内容
将保护膜施加到显示装置以保护显示装置的显示表面。然而,保护膜根据显示装置的操作容易从显示装置的显示表面剥离,或者在保护膜更换过程期间会对显示装置的显示表面造成损坏。
本公开提供了一种包括保护膜的显示装置,即使显示装置重复折叠和展开保护膜也不会被剥离,并且在更换保护膜时不会对显示装置的部件造成损坏。
实施方式提供一种显示装置,其包括能够绕着在第一方向上延伸的折叠轴线折叠的显示面板、在显示面板上的窗、在窗上的保护膜、以及在窗和保护膜之间的多个粘合剂层。粘合剂层包括在窗上的第一粘合剂层和在第一粘合剂层上的第二粘合剂层。第一粘合剂层包括侧链结晶聚合物,并且第二粘合剂层的模量小于第一粘合剂层的模量。
第一粘合剂层可以在室温下具有第一粘合力,并且在等于或大于约70摄氏度的温度下具有第二粘合力,并且第二粘合力等于或小于第一粘合力的约50%。
在等于或大于约70摄氏度的温度下,第二粘合剂层的粘合力可以大于第二粘合力。
侧链结晶聚合物可以包括(甲基)丙烯酸十六烷基酯共聚物、(甲基)丙烯酸十八烷基酯共聚物、(甲基)丙烯酸二十烷基酯共聚物和(甲基)丙烯酸二十二烷基酯共聚物中的至少一种。
第一粘合剂层的厚度可以小于第二粘合剂层的厚度。
第一粘合剂层可以具有等于或大于约5μm且等于或小于约25μm的厚度。
第二粘合剂层可以具有等于或大于约10μm且等于或小于约100μm的厚度。
第二粘合剂层的模量在负20摄氏度下可以是约0.2兆帕(MPa)。
第一粘合剂层和第二粘合剂层中的至少一个还可以包括发泡剂。
第一粘合剂层中的发泡剂的含量可以等于或小于约3%。
第二粘合剂层中的发泡剂的含量可以等于或小于约3%。
显示装置还可以包括在显示面板下方的支承模块,并且显示面板可以包括在与第一方向交叉的第二方向上布置的第一非折叠区域、折叠区域和第二非折叠区域。支承模块可以包括在显示面板下方的缓冲层和在缓冲层下方的支承板。
支承板可以包括与第一非折叠区域重叠的第一支承件和在第二方向上与第一支承件间隔开并与第二非折叠区域重叠的第二支承件。
支承板可以设置有限定在其中的多个开口,以与折叠区域重叠。
实施方式提供一种显示装置,其包括可折叠的显示面板、在显示面板上的窗、在窗上的保护膜、以及在窗和保护膜之间的多个粘合剂层。粘合剂层包括在窗上的第一粘合剂层、以及在第一粘合剂层上并与第一粘合剂层接触的第二粘合剂层。第一粘合剂层在室温下具有第一粘合力,并且在等于或大于约70摄氏度的温度下具有第二粘合力,第二粘合剂层在等于或大于约70摄氏度的温度下具有第三粘合力,并且第二粘合力小于第三粘合力,并且等于或小于第一粘合力的约50%。
第一粘合剂层可以具有等于或大于约5μm并且等于或小于约25μm的厚度,并且第二粘合剂层可以具有等于或大于约10μm并且等于或小于约100μm的厚度。
第一粘合剂层可以包括侧链结晶聚合物。
侧链结晶聚合物可以包括(甲基)丙烯酸十六烷基酯共聚物、(甲基)丙烯酸十八烷基酯共聚物、(甲基)丙烯酸二十烷基酯共聚物和(甲基)丙烯酸二十二烷基酯共聚物中的至少一种。
第二粘合剂层的模量可以小于第一粘合剂层的模量。
第一粘合剂层和第二粘合剂层中的至少一个还可以包括发泡剂。
根据以上描述的一个或多个实施方式,显示装置设置有保护膜,即使显示装置重复折叠和展开,保护膜也不会被容易地剥离。
此外,当更换保护膜时,保护膜在不会对显示装置的部件造成损坏的情况下被容易地更换。
附图说明
当结合附图考虑时,通过参考以下详细描述,本公开的以上和其它优点将变得显而易见,在附图中:
图1是示出显示装置的实施方式的立体图;
图2A至图2C是示出显示装置的实施方式的立体图;
图3是示出显示装置的实施方式的分解立体图;
图4是示出显示面板的实施方式的剖视图;
图5是示出显示装置的实施方式的剖视图;
图6A是示出第一粘合剂层的实施方式和比较性粘合剂层的温度和粘合力之间的关系的曲线图;
图6B是示出第一粘合剂层的分子结构的实施方式的示意图;
图7A至图7C是示出显示装置的实施方式的剖视图;
图8A和图8B是示出显示装置的实施方式的剖视图;以及
图9A至图9D是示出保护膜的更换过程的实施方式的立体图。
具体实施方式
本公开可以被不同地修改并且实现成许多不同的形式,并且因此实施方式将被例示在附图中并且在下文中详细描述。然而,本公开不应受限于所公开的形式,并且应被解释为包括包含在本公开的精神和范围内的所有修改、等同或替代。
在本公开中,将理解的是,当元件或层被称为与另一元件或层相关时,诸如“在”另一元件或层“上”、“连接到”或“联接到”另一元件或层时,其可以直接在另一元件或层上、直接连接到或直接联接到另一元件或层,或者可以存在居间的元件或层。相反,当元件或层被称为与另一元件或层相关时,诸如“直接在”另一元件或层“上”、“直接连接到”或“直接联接到”另一元件或层时,不存在其它元件或层、或居间的元件或层。
相同的附图标记通篇表示相同的元件。附图标记可以指示单个元件或多个元件。例如,在附图中标记单数形式的元件的附图标记可以在说明书的文本内用于表示多个单数元件。
在附图中,为了有效地描述技术内容,夸大了部件的厚度、比例和尺寸。
将理解的是,尽管术语第一、第二等可以在本文中用于描述各种元件,但是这些元件不应被这些术语限制。这些术语仅用于将一个元件与另一元件区分开。因此,在不背离本公开的教导的情况下,下面讨论的第一元件可以被称为第二元件。
本文中所使用的术语仅出于描述特定实施方式的目的,而不旨在进行限制。如本文中所使用的,单数形式“一”、“一个”和“该”旨在也包括复数形式,除非上下文另外清楚地指示。例如,“元件”具有与“至少一个元件”相同的含义,除非上下文另外清楚地指示。“至少一个”将不被解释为限制“一”或“一个”。“或”意指“和/或”。如本文中所使用的,术语“和/或”包括相关所列项中的一个或多个的任何和所有组合。
为了便于描述,在本文中可以使用诸如“下面”、“下方”、“下”、“上方”、“上”等的空间相对术语来描述如图中所示的一个元件或特征与另一元件或特征的关系。
还将理解的是,当在本说明书中使用时,术语“包括”和/或“包括有”指定所陈述的特征、整体、步骤、操作、元件和/或部件的存在,但不排除一个或多个其它特征、整体、步骤、操作、元件、部件和/或其组的存在或添加。
如在本文中使用的“约”或“近似”包括所述值以及如本领域普通技术人员考虑所讨论的测量以及与特定量的测量相关的误差(即,测量系统的限制)所确定的特定值的可接受偏差范围内的平均值。例如,“约”可以意指在一个或多个标准偏差内,或在所述值的±30%、±20%、±10%或±5%内。
除非另有限定,否则本文中使用的所有术语(包括技术术语和科学术语)具有与本公开所属领域的普通技术人员通常理解的含义相同的含义。还将理解的是,术语,诸如在常用词典中限定的那些术语,应被解释为具有与它们在相关技术的上下文中的含义一致的含义,并且将不以理想化的或过分正式的含义来解释,除非在本文中明确地如此限定。
本文中参考作为理想化实施方式的示意性图示的剖视图来描述实施方式。由此,将预期到由于例如制造技术和/或公差而导致的与图示的形状的偏差。因此,本文中描述的实施方式不应被解释为限于如本文中所示的区域的特定形状,而将包括例如由制造而导致的形状偏差。例如,示出或描述为平坦的区域通常可以具有粗糙和/或非线性特征。此外,所示的尖角可以是圆润的。因此,图中所示的区域在本质上是示意性的,并且它们的形状不旨在表示区域的精确形状,并且不旨在限制本权利要求的范围。
在下文中,将参考附图详细说明显示装置1000的实施方式。
图1以及图2A至图2C是示出显示装置1000的实施方式的立体图。图1示出了展开的显示装置1000,并且图2A至图2C示出了折叠的显示装置1000。
显示装置1000可以是响应于电信号而被激活的装置。显示装置1000可以应用于各种电子装置。在实施方式中,例如,显示装置1000可以应用于诸如移动电话、智能手表、平板计算机、笔记本计算机、计算机、智能电视等的电子装置。显示装置1000可以应用于其它电子装置,只要不背离本发明的范围即可。图1示出了应用于移动电话的显示装置1000。
显示装置1000可以向显示装置1000外部显示图像。显示装置1000的前表面可以包括显示区域DA和非显示区域NDA。显示装置1000的前表面可以基本上平行于由彼此交叉的第一方向DR1和第二方向DR2限定的平面。显示装置1000的前表面可以对应于通过其显示图像的显示表面。
显示装置1000可以在显示区域DA处显示图像。显示装置1000的显示区域DA可以基本上平行于由第一方向DR1和第二方向DR2限定的平面。展开的显示装置1000可以在第三方向DR3上显示图像。显示装置1000的各种部件或层可以包括与针对显示装置1000描述的显示区域DA和非显示区域NDA对应的显示区域DA和非显示区域NDA。
与第一方向DR1和第二方向DR2交叉的第三方向DR3可以指示显示装置1000及其各种部件或层的厚度方向。显示装置1000的每个部件的前表面(或上表面)和后表面(或下表面)可以在第三方向DR3上或沿着第三方向DR3彼此相对,并且前表面和后表面中的每个的法线方向可以基本上平行于第三方向DR3。由第一方向DR1、第二方向DR2和第三方向DR3指示的方向可以彼此相对,并且可以改变成其它方向。
非显示区域NDA可以是在其中不显示图像的区域(例如,平面区域)。非显示区域NDA可以限定成与显示区域DA相邻。如图1中所示,非显示区域NDA可以围绕显示区域DA,然而,不应限于此或不应由此限制。根据实施方式,非显示区域NDA可以限定成仅与显示区域DA的一侧相邻,或者可以被省略。
显示装置1000可以是可折叠和/或可弯曲的柔性显示装置。在本公开中,在本文中针对构件使用的术语“柔性的”可以意指构件具有可弯曲的特性,并且柔性显示装置可以具有可弯曲成被完全折叠的结构,然而,不应限于此或不应由此限制。柔性显示装置可以具有其一部分可弯曲的结构。
显示装置1000可以包括折叠区域FA和一个或多个非折叠区域,诸如非折叠区域NFA1和NFA2。显示装置1000可以在折叠区域FA处是可折叠的。展开的显示装置1000可以将折叠区域FA设置成平坦的,并且折叠或弯曲的显示装置1000可以根据显示装置1000的折叠操作将折叠区域FA设置成曲形。即使显示装置1000被折叠,非折叠区域NFA1和NFA2也可以是平坦的。折叠区域FA和非折叠区域NFA1和NFA2中的每个可以设置成多个,并且不应被特别限制。图1示出了在第一方向DR1上或沿着第一方向DR1顺序布置的第一非折叠区域NFA1、折叠区域FA和第二非折叠区域NFA2。
参考图2A至图2C,显示装置1000可以绕着在一个方向上延伸的假想折叠轴线(下文中,折叠轴线FX)折叠。图2A至图2C示出了绕着在第二方向DR2上延伸的折叠轴线FX折叠的显示装置1000,然而,折叠轴线FX沿其延伸的方向不应限于此或不应由此限制。根据实施方式,折叠轴线FX可以在第一方向DR1上延伸。在这种情况下,非折叠区域NFA1和NFA2可以在第二方向DR2上布置,且折叠区域FA插置在它们之间。
显示装置1000可以绕着折叠轴线FX以一角度折叠。图2A和图2B示出了部分折叠的显示装置1000,并且图2C示出了以约180度的角度完全折叠的显示装置1000。
参考图2A,在实施方式中,折叠轴线FX可以限定在显示装置1000的与显示表面相对的后表面下方,并且显示装置1000的折叠区域FA可以根据折叠操作形成对于折叠轴线FX凸出的曲形表面。这可以被称为向外折叠的显示装置1000的向外折叠状态。向外折叠的显示装置1000将显示装置1000的显示区域DA的部分暴露于显示装置1000的外部(例如,面向外)。尽管在图中未示出,但是以约180度的角度完全向外折叠的显示装置1000将第一非折叠区域NFA1和第二非折叠区域NFA2设置成面向彼此相反的方向,以在相反的方向上显示图像。
参考图2B,在实施方式中,折叠轴线FX可以限定在显示装置1000的前表面上方,并且显示装置1000的折叠区域FA可以形成对于折叠轴线FX凹入的曲形表面。这可以被称为向内折叠的显示装置1000的向内折叠状态。向内折叠的显示装置1000将显示区域DA的多个部分设置成相对于一方向彼此面对。在向内折叠的显示装置1000中,第一非折叠区域NFA1可以面对第二非折叠区域NFA2。如图2C中所示,以约180度的角度完全向内折叠的显示装置1000可以将显示区域DA设置成不暴露于显示装置1000的外部(例如,面向内)。
显示装置1000的折叠操作不应限于以上描述的实施方式,并且可以以各种方式设计。
图3是示出显示装置1000的实施方式的分解立体图。图3是示出图1中所示的显示装置1000的实施方式的分解立体图。显示装置1000可以包括在第三方向DR3上顺序地堆叠的支承模块300、显示模块100和保护模块200。支承模块300、显示模块100和保护模块200中的每个可以绕着折叠轴线FX是可折叠的。即,支承模块300、显示模块100和保护模块200以及其中的各种部件或层可以在折叠显示装置1000时可与彼此一起折叠。
显示模块100可以是响应于电信号生成图像的模块。显示模块100可以包括显示面板DP和窗WP。
显示面板DP可以生成和/或显示图像。然而,显示面板DP可以是液晶显示面板或发光型显示面板,然而,不应被特别限制。在实施方式中,例如,发光型显示面板可以是有机发光显示面板或量子点发光显示面板。有机发光显示面板的发光层可以包括有机发光材料。量子点发光显示面板的发光层可以包括量子点或量子棒。在下文中,将对有机发光显示面板进行描述作为显示面板DP的代表性示例。
窗WP可以设置在显示面板DP上以保护显示面板DP。窗WP可以面向显示面板DP。窗WP可以减少或有效地防止显示面板DP由于对显示装置1000的外部冲击而损坏或故障。窗WP可以包括光学透明绝缘材料。因此,由显示面板DP生成的图像可以通过窗WP传输,以便从显示装置1000外部可见。
窗WP可以包括柔性材料。窗WP可以绕着折叠轴线FX重复折叠或展开。因此,根据显示装置1000的操作,窗WP的形状可以改变成与显示面板DP的形状对应。
窗WP可以包括薄玻璃或合成树脂膜。包括在窗WP中的薄玻璃可以具有等于或小于约100微米、例如约30微米的厚度,然而,包括在窗WP中的薄玻璃的厚度不应限于此或不应由此限制。包括在窗WP中的合成树脂膜可以包括聚酰亚胺(PI)膜或聚对苯二甲酸乙二醇酯(PET)膜。
窗WP可以具有单层或多层结构。在实施方式中,例如,窗WP可以包括通过粘合剂彼此联接的多个合成树脂膜、有机衬底和通过粘合剂联接到有机衬底的合成树脂膜、或者薄玻璃和通过粘合剂联接到薄玻璃的合成树脂膜,然而,不应被特别限制。
尽管在图中未示出,但是显示模块100可以包括设置在显示面板DP和窗WP之间的至少一个功能层。作为示例,功能层可以是抗反射层,以减少或有效防止外部光被反射。抗反射层可以减少或有效地防止显示面板DP的元件由于通过显示装置1000的前表面入射到显示装置1000的外部光而从其外部可见。抗反射层可以包括延迟器、偏振器和滤色器中的至少一种。
保护模块200可以设置在显示模块100上(例如,面对显示模块100),以减少或有效地防止显示模块100受到外部冲击。保护模块200可以与显示模块100接触。作为示例,保护模块200可以附接到显示模块100的窗WP。保护模块200可以包括多个粘合剂层和保护膜PF(参见图5)。稍后将对其进行详细描述。
保护模块200可以包括光学透明材料。因此,由显示面板DP生成并从窗WP出射的图像可以通过保护模块200传输,以便从显示装置1000外部可见。
保护模块200可以包括柔性材料。保护模块200可以绕着折叠轴线FX重复展开或折叠。因此,保护模块200的形状可以改变成与显示模块100的形状对应,其中显示模块100的形状根据显示装置1000的操作而改变。
支承模块300可以设置在显示模块100的后表面上,并且可以支承显示模块100。支承模块300可以包括缓冲层310和支承板320。
缓冲层310可以设置在显示模块100的后表面上。缓冲层310可以吸收施加到显示模块100的外部冲击。作为示例,缓冲层310可以包括海绵、泡沫或聚氨酯树脂。然而,用于缓冲层310的材料不应限于此或不应由此限制,并且缓冲层310可以包括各种材料,只要缓冲层310可以保护显示模块100并且可以吸收外部冲击即可。
支承板320可以设置在缓冲层310的后表面上以支承显示模块100,并且可以减少或有效地防止显示模块100变形。支承板320可以面对显示模块100,且缓冲层310在它们之间。支承板320可以具有与显示面板DP的形状对应的整板形状。支承板320可以具有在与折叠区域FA重叠或对应的区域中具有增加的柔性的结构,然而,不应限于此或不应由此限制。根据实施方式,支承板320可以包括两个或更多个彼此间隔开的板,且折叠区域FA插置在其间,并且这将参考图8A和图8B进行详细描述。
支承板320可以包括具有相对高模量的材料。作为示例,支承板320可以包括金属材料。详细地,支承板320可以包括不锈钢、铝或其合金。然而,用于支承板320的材料不应限于此或不应由此限制,并且支承板320可以包括各种材料,只要它们可以支承显示面板DP即可。
尽管在图中未示出,但是显示装置1000还可以包括设置在显示面板DP上的输入感测单元。显示装置1000可以感测以各种形式施加到其的外部输入。在实施方式中,例如,外部输入可以包括压力、温度或光。外部输入可以包括以一距离靠近或接近显示装置1000的外部输入(例如,悬停输入)、以及通过输入工具(诸如,身体部分(例如,用户的手)、笔等)的触摸输入(例如,接触)。
图4是示出显示面板DP的实施方式的剖视图。显示面板DP可以包括基础衬底SUB、电路层DP-CL、显示元件层DP-OL和封装层TFE。
基础衬底SUB可以是柔性的。基础衬底SUB可以具有单层或多层结构。基础衬底SUB可以包括塑料衬底、玻璃衬底、金属衬底或有机/无机复合衬底。基础衬底SUB可以包括合成树脂膜。在实施方式中,例如,合成树脂膜可以包括基于聚酰亚胺的树脂、基于丙烯酸的树脂、基于乙烯的树脂、基于环氧的树脂、基于氨基甲酸酯的树脂、基于纤维素的树脂和基于二萘嵌苯的树脂。然而,合成树脂膜不应限于此或不应由此限制。
电路层DP-CL可以设置在基础衬底SUB上。电路层DP-CL可以包括绝缘层、半导体图案、导电图案和信号线。可以通过涂覆或沉积工艺在基础衬底SUB上形成绝缘层、半导体层和导电层。然后,可以通过光刻工艺对绝缘层、半导体层和导电层进行选择性地图案化,并且因此可以形成或设置包括在电路层DP-CL中的绝缘层、半导体图案、导电图案和信号线。
显示元件层DP-OL可以设置在电路层DP-CL上。显示元件层DP-OL可以包括设置成与显示装置1000的显示区域DA对应的发光元件。在实施方式中,例如,显示元件层DP-OL可以包括有机发光元件、量子点、量子棒、微米LED或纳米LED作为发光元件。
显示面板DP可以包括响应于电信号生成图像的多个像素。像素中的每个可以包括包含在显示元件层DP-OL中的发光元件和包含在电路层DP-CL中并电连接到发光元件的薄膜晶体管。像素可以布置在显示区域DA中,然而,不应限于此或不应由此限制。像素中的一些可以布置在非显示区域NDA中。
封装层TFE可以在电路层DP-CL上设置成覆盖显示元件层DP-OL。封装层TFE可以包括多个无机层和设置在无机层之间的有机层,然而,包括在封装层TFE中的层不应限于此或不应由此限制。
包括在封装层TFE中的无机层可以保护像素免受水分和氧气的影响。作为示例,无机层可以包括氮化硅层、氧化硅层、氮氧化硅层、氧化钛层或氧化铝层。包括在封装层TFE中的有机层可以保护像素免受诸如灰尘颗粒的异物的影响。作为示例,有机层可以包括基于丙烯酸的有机层,然而,用于无机层和有机层的材料不应限于此或不应由此限制。
图5是示出显示装置1000的实施方式的剖视图。图5是沿着图3中所示的线I-I'截取的显示装置1000的剖视图。图5示意性地示出了显示装置1000的显示模块100和保护模块200。
保护膜PF可以包括聚合物膜。作为示例,聚合物膜可以包括聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚碳酸酯(PC)、聚萘二甲酸乙二醇酯(PEN)、聚苯乙烯(PS)、聚甲基丙烯酸甲酯(PMMA)、聚氯乙烯(PVC)、聚醚砜(PES)、聚丙烯(PP)、聚酰胺(PA)、改性聚苯醚(m-PPO)、聚甲醛(POM)、聚砜(PSU)、聚苯硫醚(PPS)、聚酰亚胺(PI)、聚乙烯亚胺(PEI)、聚醚醚酮(PEEK)、聚酰胺酰亚胺(PAI)、聚芳酯(PAR)和热塑性聚氨酯(TPU)中的至少一种聚合物树脂。
显示装置1000可以具有折叠特性和抗冲击性,其根据保护膜PF的厚度而改变。当保护膜PF的厚度太薄时,显示装置1000可能由于外部冲击而损坏,并且当保护膜PF的厚度太厚时,显示装置1000的折叠特性可能降低。作为示例,保护膜PF的厚度可以等于或大于约25微米(μm)并且等于或小于约200μm。详细地,保护膜PF的厚度可以等于或大于约50μm并且等于或小于约100μm。然而,保护膜PF的厚度不应限于此或不应由此限制。
第一粘合剂层AD1和第二粘合剂层AD2可以设置在显示模块100和保护膜PF之间,并且可以将显示模块100附接到保护膜PF。第一粘合剂层AD1可以与窗WP的上表面WP-U接触。多个元件可以在接触时在其间形成界面或边界。第一粘合剂层AD1可以比第二粘合剂层AD2更靠近显示模块100。第二粘合剂层AD2可以与第一粘合剂层AD1的上表面和保护膜PF的后表面接触。
第一粘合剂层AD1和第二粘合剂层AD2中的每个可以包括压敏粘合剂的基础树脂。作为示例,第一粘合剂层AD1和第二粘合剂层AD2中的每个可以包括基于丙烯酸的树脂、基于硅酮的树脂、基于氨基甲酸酯的树脂、基于环氧的树脂、基于橡胶的树脂和基于聚酯的树脂中的至少一种,并且可以包括相同树脂系列中的一种或两种或更多种树脂。第一粘合剂层AD1和第二粘合剂层AD2可以具有根据基础树脂的刚性和表面能而变化的粘合力。
保护膜PF、第一粘合剂层AD1和第二粘合剂层AD2中的每个可以包括光学透明材料。因此,在保护膜PF被附接到显示模块100且其间插置有第一粘合剂层AD1和第二粘合剂层AD2的结构中,由显示模块100生成的图像可以通过第一粘合剂层AD1和第二粘合剂层AD2以及保护膜PF被传输到显示装置1000外部。
保护模块200在室温下可以是光学透明的。作为示例,保护模块200在室温下可以具有等于或小于约4%的雾度值。然而,保护模块200的雾度值不应限于此或不应由此限制。
第一粘合剂层AD1的粘合力可以随着温度从室温升高到高温度(例如,高于室温的温度)而降低。第一粘合剂层AD1的粘合力可以在大于参考温度时显著变化。作为示例,第一粘合剂层AD1可以在室温下具有第一粘合力,并且可以在高温度下具有第二粘合力,并且与第一粘合力相比,第二粘合力可以降低到约50%或降低得更多。详细地,第一粘合剂层AD1可以在约25摄氏度的温度下具有第一粘合力,并且可以在约70摄氏度的温度下具有第二粘合力,并且第二粘合力可以小于第一粘合力的一半。
当与第一粘合剂层AD1的粘合力相比时,第二粘合剂层AD2的粘合力可以随着温度从室温升高到高温度而逐渐降低。第一粘合剂层AD1和窗WP之间在室温下的粘合力可以基本上等于或类似于第二粘合剂层AD2和窗WP之间在室温下的粘合力。作为示例,在室温下,第一粘合剂层AD1和窗WP之间的粘合力以及第二粘合剂层AD2和窗WP之间的粘合力可以等于或大于约400克力/英寸(gf/inch)。
然而,第一粘合剂层AD1和窗WP之间在高温度下的粘合力可以小于第二粘合剂层AD2和窗WP之间在高温度下的粘合力。例如,在等于或大于70摄氏度的温度下,第二粘合剂层AD2可以具有大于第一粘合剂层AD1的第二粘合力的粘合力。作为示例,第二粘合剂层AD2和窗WP之间在约80摄氏度的温度下的粘合力可以是约400gf/inch,并且第一粘合剂层AD1和窗WP之间的粘合力在约80摄氏度的温度下可以等于或小于约50gf/inch。
由于与窗WP接触的第一粘合剂层AD1的粘合力在参考温度下显著降低,因此在高温度下可以将保护膜PF从窗WP的上表面WP-U容易地剥离。作为示例,当需要更换保护膜PF时,通过对保护膜PF施加热量,可以将保护膜PF从显示模块100容易地剥离,并且在更换过程中可以减少或有效地防止对显示面板DP的损坏。即,对保护膜PF的加热降低了第一粘合剂层AD1在保护模块200和显示模块100之间的界面处的粘合力。
第一粘合剂层AD1可以包括侧链结晶聚合物。侧链结晶聚合物可以包括通过一种或多种单体的聚合形成的共聚物。在实施方式中,例如,第一粘合剂层AD1可以包括(甲基)丙烯酸十六烷基酯共聚物、(甲基)丙烯酸十八烷基酯共聚物、(甲基)丙烯酸二十烷基酯共聚物和(甲基)丙烯酸二十二烷基酯共聚物中的至少一种。由于第一粘合剂层AD1包括侧链结晶聚合物,因此第一粘合剂层AD1的粘合力的变化程度可以在高温度下增加。
第二粘合剂层AD2可以具有相对小的模量。第二粘合剂层AD2的模量可以小于第一粘合剂层AD1的模量。作为示例,第二粘合剂层AD2的模量在负20摄氏度下可以等于或小于约0.2兆帕(MPa)。由于第二粘合剂层AD2具有相对小的模量,因此即使显示装置1000重复折叠和展开,也可以不损坏粘合剂层或使其变形。
第一粘合剂层AD1和第二粘合剂层AD2中的每个的厚度可以影响折叠可靠性。可以通过调节第一粘合剂层AD1和第二粘合剂层AD2的厚度来改善折叠可靠性。作为示例,第一粘合剂层AD1的第一厚度D1可以等于或大于约5μm并且等于或小于约25μm。第二粘合剂层AD2的第二厚度D2可以等于或大于约10μm并且等于或小于约100μm。第一粘合剂层AD1的第一厚度D1可以在以上描述的范围内小于第二粘合剂层AD2的第二厚度D2,然而,不应限于此或不应由此限制。
图6A是示出第一粘合剂层AD1-a的实施方式和比较性粘合剂层AD'的温度和粘合力之间的关系的曲线图。图6B是示出第一粘合剂层的分子结构的实施方式的示意图。
图6A是示意性地示出与以上描述的第一粘合剂层AD1对应的第一粘合剂层AD1-a的、根据温度变化的粘合力的曲线图。第一粘合剂层AD1-a可以包括侧链结晶聚合物。图6A还示出了不包括侧链结晶聚合物的比较性粘合剂层AD'的根据温度变化的粘合力,以与第一粘合剂层AD1-a的粘合力进行比较。
第一粘合剂层AD1-a可以在第一温度T1下具有第一粘合力F1。第一温度T1可以是室温。在第一温度T1附近的温度范围内,第一粘合剂层AD1-a的粘合力可以与第一粘合力F1基本上相同,或者第一粘合剂层AD1-a的粘合力与第一粘合力F1之间的差可以很小。另一方面,在第一温度T1附近的温度范围内,比较性粘合剂层AD'的粘合力可以随着温度的升高而逐渐降低。在实施方式中,例如,在第一温度T1附近的温度范围内,比较性粘合剂层AD'的粘合力的降低程度可以大于第一粘合剂层AD1-a的粘合力的降低程度。当第一粘合剂层AD1-a在室温下保持第一粘合力F1时,保护膜PF可以附接到窗WP的上表面WP-U(参考图5),而即使在重复的折叠和展开操作的情况下也不会被剥离。
即使温度升高,第一粘合剂层AD1-a的粘合力也可以保持在一值处,并且然后可以在高于参考温度时显著降低。第一粘合剂层AD1-a可以在高于第一温度T1的第二温度T2下具有第二粘合力F2。第二温度T2可以高于第一粘合剂层AD1-a熔化时的温度。第二粘合力F2可以等于或小于第一粘合力F1的一半。由于第一粘合剂层AD1-a的粘合力在高温度下显著降低,因此通过与窗WP接触的第一粘合剂层AD1-a附接到窗WP的保护膜PF(参考图5)可以从窗WP的上表面WP-U(参考图5)容易地剥离。
因此,通过向保护膜PF施加热量,保护膜PF可以从窗WP的上表面WP-U容易地去除,并且可以在显示装置1000内更换保护膜PF的过程中,减少或有效地防止对显示面板DP的损坏。
另一方面,比较性粘合剂层AD'在第二温度T2下的比较性粘合力F2'可以大于第二粘合力F2。当温度从第一温度T1升高到第二温度T2时,第一粘合剂层AD1-a的粘合力的降低程度可以大于比较性粘合剂层AD'的粘合力的降低程度。
第一粘合剂层AD1-a可以在高于第二温度T2的第三温度T3下具有第三粘合力F3。当温度从第二温度T2升高到第三温度T3时,第一粘合剂层AD1-a的粘合力的降低程度可以大于比较性粘合剂层AD'的粘合力的降低程度。在第三温度T3下,第一粘合剂层AD1-a的粘合力可以小于比较性粘合剂层AD'的粘合力。第三粘合力F3可以小于第一粘合力F1和第二粘合力F2。作为示例,第三温度T3可以等于或大于约90摄氏度,并且第三粘合力F3可以等于或小于第一粘合力F1的约10%。
图6B示意性地示出了第一粘合剂层AD1-a在第一温度T1下的分子结构(图形AA)和第一粘合剂层AD1-a在第二温度T2下的分子结构(图形BB)。
参考图6B,第一粘合剂层AD1-a的分子结构在室温下可以具有侧链SC竖直键合在彼此平行排列的多个主链MC之间的结晶结构。当温度由于热量(“热能量”)而升高时,第一粘合剂层AD1-a的分子可以具有增加的自由度并且可以容易彼此缠结。因此,如图6B的图形BB中所示,键合在主链MC之间的侧链SC可以彼此缠结,并且因此,第一粘合剂层AD1-a的粘合力可以降低。
下面的表1示出了通过根据实施例和比较例的第一粘合剂层AD1和第二粘合剂层AD2中的每个的厚度来评估保护模块200的可靠性而获得的结果。通过在约25摄氏度的温度下测量保护模块200和窗WP之间的第一粘合力以及在约80摄氏度的温度下测量保护模块200和窗WP之间的第二粘合力来执行保护模块200的可靠性评估。此外,评估在将实施方式保护模块和比较性保护模块中的每个应用到显示装置1000之后保护模块200在重复折叠和展开显示装置1000时是否被剥离、显示面板DP在更换每个相应的保护膜PF时是否被损坏、以及粘合剂层在使用显示装置1000期间是否被改变。
表1
在表1中,“E1至E6”分别对应于实施例1至实施例6,并且“C1至C5”对应于比较例1至比较例5。实施例和比较例可以包括与图5中所示的显示装置1000的元件对应的元件,实施例和比较例中的每个的第一粘合剂层AD1包括(甲基)丙烯酸十六烷基酯共聚物,并且实施例和比较例中的每个的第二粘合剂层AD2包括基于丙烯酸的树脂。然而,比较例4不包括与第二粘合剂层AD2对应的元件,并且比较例5不包括与第一粘合剂层AD1对应的元件。
在表1中,“D1”表示第一粘合剂层AD1的第一厚度,并且“D2”表示第二粘合剂层AD2的第二厚度。“A1”表示第一粘合力,并且“A2”表示第二粘合力。“FR”表示在折叠测试期间保护膜PF是否被剥离。在FR为1的情况下,这意指当显示装置1000重复折叠和展开1000次时,保护膜PF未被剥离。在FR小于1(FR<1)的情况下,这意指当显示装置1000重复折叠和展开少于1000次时,保护膜PF被剥离。
通过180度(°)剥离测试来测量第一粘合力和第二粘合力,并且通过在重复折叠和展开显示装置1000(保护膜PF在其中利用粘合剂层进行附接)时目视观察保护膜PF的剥离来评估保护膜PF在折叠测试中是否被剥离。通过目视观察显示面板DP在保护膜PF与显示模块100分离时是否被损坏来评估显示面板DP在更换保护模块200时是否被损坏。通过在附接保护模块200之后在使用显示装置1000时目视观察粘合剂层是否变色或变形来评估粘合剂层在使用显示装置1000期间是否被改变。
在实施例1至6中,第一粘合剂层AD1的每个厚度等于或大于约5μm并且等于或小于约25μm,并且第二粘合剂层AD2的每个厚度等于或大于约10μm并且等于或小于约100μm。在实施例1至6中,每个第一粘合力为约500gf/inch,并且每个第二粘合力等于或小于约50gf/inch。具体地,在实施例3中,第一粘合剂层的厚度为约25μm,第二粘合力为约20gf/inch,并且粘合力在高温度下显著降低。
在实施例1、5和6中,即使显示装置1000重复折叠和展开200,000次,保护膜PF也不会被剥离并且不会被损坏,并且在实施例2至4中,即使显示装置1000重复折叠和展开100,000次,保护膜PF也不会被剥离并且不会被损坏。
比较例1至3和实施例的第一粘合剂层和第二粘合剂层中的每个的厚度存在一些差异。在比较例1中,第一粘合剂层AD1的厚度超过约25μm、为约30μm,并且保护膜PF在折叠和展开操作重复少于10,000次时被剥离。在比较例2中,第二粘合剂层AD2的厚度小于约10μm、为约8μm,并且保护膜PF在折叠和展开操作重复少于10,000次时被剥离。在比较例3中,第二粘合剂层AD2的厚度超过约100μm、为约120μm,并且保护膜PF在折叠和展开操作重复少于1000次时被剥离。因此,在第一粘合剂层AD1和第二粘合剂层AD2中的每个的厚度不在一范围内的情况下,可能降低显示装置1000的折叠可靠性。
在不包括第二粘合剂层AD2的比较例4中,保护膜PF在折叠和展开操作重复少于1000次时被剥离。在不包括第二粘合剂层AD2的情况下,粘合剂层的模量可以大于实施例的粘合剂层的模量。因此,当包括具有相对高模量的粘合剂层的保护模块200被施加到显示装置1000时,可能降低折叠可靠性。
不包括第一粘合剂层AD1的比较例5的第二粘合力为约400gf/inch。在不包括第一粘合剂层AD1的情况下,粘合剂层可以在高温度下具有相对大的粘合力。因此,尽管折叠和展开操作重复200,000次,但在比较例5中仍保持了折叠可靠性,但显示面板DP在分离保护膜PF时被损坏。这是因为保护膜PF很难被分离,因为用于将保护膜PF附接到显示模块100的粘合剂层的粘合力很大。
在实施例中,即使保护膜PF与显示模块100分离,也不会损坏显示面板DP,并且粘合剂层不会变色或变形。此外,与比较例中的折叠可靠性相比,在实施例中折叠可靠性得到了改善。
当粘合剂层和显示模块100之间的粘合力低时,具有这样的优势:当更换保护膜PF时,保护膜PF可以从显示模块100容易地去除,然而,具有这样的缺点:保护膜PF可能由于重复的折叠和展开操作而容易被剥离。当粘合剂层和显示模块100之间的粘合力高时,具有这样的优势:即使显示装置1000重复折叠和展开,保护膜PF也不会容易剥离,然而,具有这样的缺点:当更换保护膜PF时会损坏显示模块100。因此,有必要控制粘合剂层的粘合力,并且本公开的粘合剂层可以在室温下不会从显示模块100被容易地剥离,可以具有改善的折叠可靠性,并且可以在高温度下从显示模块100容易地去除。
图7A至图7C是示出显示装置1000的实施方式的剖视图。除了一些元件之外,图7A至图7C中所示的显示装置1000包括与以上描述的实施方式中的元件基本上相同的元件。在下文中,将主要描述与以上描述的实施方式的特征不同的特征。
粘合剂层AD1和AD2中的至少一个还可以包括发泡剂,诸如第一发泡剂FF1和/或第二发泡剂FF2。图7A中所示的保护模块200-1可以包括包含第一发泡剂FF1的第一粘合剂层AD1。图7B中所示的保护模块200-2可以包括包含第二发泡剂FF2的第二粘合剂层AD2。图7C中所示的保护模块200-3可以包括分别包括第一发泡剂FF1和第二发泡剂FF2的第一粘合剂层AD1和第二粘合剂层AD2。
发泡剂FF1和FF2可以是当其温度升高或当紫外线(UV)照射到其时体积增加的材料。作为示例,发泡剂FF1和FF2可以包括包含粘合力控制剂的芯部分、以及围绕该芯部分的外部分。粘合力控制剂可以在提供热量或紫外线的条件下蒸发,并且因此,发泡剂FF1和FF2的体积可以增加。随着发泡剂FF1和FF2的体积增加,包括发泡剂FF1和FF2的粘合剂层的粘合力可以降低。
发泡剂FF1和FF2可以分散在包括在第一粘合剂层AD1和第二粘合剂层AD2中的聚合物树脂中。包括在同一个粘合剂层中的发泡剂可以具有基本上彼此相同的尺寸,然而,不应限于此或不应由此限制。根据实施方式,发泡剂FF1和FF2可以具有彼此不同的尺寸。然而,发泡剂FF1和FF2可以具有球形形状,不应限于此或不应由此限制。
根据实施方式,发泡剂FF1和FF2可以具有椭圆形形状。
在热量或UV照射条件下,由于包括发泡剂FF1和FF2的粘合剂层AD1和AD2,保护膜PF可以与显示模块100容易地分离,并且可以在不对显示面板DP造成损坏的情况下更换保护膜PF。然而,当包括在粘合剂层AD1和AD2中的发泡剂FF1和FF2的含量大时,相应的粘合剂层的厚度可能增加,并且相应的粘合剂层的模量可能增加。因此,当发泡剂FF1和FF2的含量太高时,显示装置1000的折叠可靠性可能降低。
作为示例,发泡剂FF1和FF2中的每个在相应的粘合剂层中的含量可以等于或小于约3%。详细地,基于包括在第一粘合剂层AD1中的材料的总含量(100%),包括在第一粘合剂层AD1中的第一发泡剂FF1的含量可以等于或小于约3%。基于包括在第二粘合剂层AD2中的材料的总含量,包括在第二粘合剂层AD2中的第二发泡剂FF2的含量可以等于或小于约3%。
图8A和图8B是示出显示装置1000a的实施方式的剖视图。图8A和图8B是示出完全折叠(完全向内折叠)的显示装置1000a的剖视图。以上描述可以应用于显示装置1000a的元件。除了支承模块300的一些元件之外,分别在图8A和图8B中示出的显示装置1000a可以包括基本上相同的元件,并且在下文中,将主要描述显示装置1000a的不同特征。
参考图8A,显示装置1000a可以包括支承板320,并且支承板320可以包括多个支承件321a和322a。支承件321a和322a可以包括与第一非折叠区域NFA1重叠的第一支承件321a和与第二非折叠区域NFA2重叠的第二支承件322a。
展开的显示装置1000a可以将第一支承件321a和第二支承件322a设置成在折叠区域FA处在第一方向DR1上彼此间隔开。即,支承板320可以在折叠区域FA处断开。第一支承件321a和第二支承件322a可以在与折叠区域FA重叠的区域中彼此间隔开。第一支承件321a可以支承显示模块100的与第一非折叠区域NFA1重叠的后表面,并且第二支承件322a可以支承显示模块100的与第二非折叠区域NFA2重叠的后表面。
在完全向内折叠的显示装置1000a中,第一支承件321a的后表面和第二支承件322a的后表面可以彼此面向相反的方向。支承板320可以包括彼此间隔开的支承件321a和322a,并且因此,当显示装置1000a被折叠时,支承板320可以不被折叠成在折叠区域FA中具有曲率。即,在被折叠的显示装置1000a中,支承件321a和322a中的每个可以在保持平坦状态的同时支承显示模块100,并且可以不在折叠区域FA中曲化或变形。
参考图8B,显示装置1000a可以包括具有整板形状的支承板320。支承板320可以包括与第一非折叠区域NFA1重叠的第一部分321b、与第二非折叠区域NFA2重叠的第二部分322b、以及与折叠区域FA重叠的第三部分323b。
支承板320可以设置有限定在与折叠区域FA重叠的第三部分323b中的多个开口OP。开口OP可以限定成穿过支承板320。开口OP可以在一个方向上布置成彼此间隔开。作为示例,开口OP可以在第三部分323b内布置成矩阵形状或锯齿形形状,并且开口OP的布置不应被特别限制。支承板320的实心部分可以与开口OP交替以限定第三部分323b,但不限于此。
尽管在图中未示出,但是开口OP可以设置为从支承板320的上表面凹入但不穿透支承板320的凹槽。支承板320的上表面可以最靠近显示模块100,但不限于此。因此,支承板320在支承板320的第三部分323b的一部分处的厚度可以小于支承板320在第一部分321b处和在第二部分322b处的厚度。
展开的显示装置1000a可以限定开口OP的原始尺寸。由于被折叠的显示装置1000a中的拉伸力,被折叠的显示装置1000a可以限定开口OP的大于原始尺寸的尺寸。支承板320可以设置有限定成与折叠区域FA重叠的开口OP,并且由此可以改善支承板320的柔性。
图9A至图9D是示出显示装置1000'或1000的实施方式的立体图。图9A至图9D是示出保护模块200的受损保护膜PF'的更换过程的实施方式的立体图。
图9A示出了包括受损保护模块200'(其包括受损保护膜PF')的显示装置1000'。显示装置1000'的受损保护膜PF'可能由于外部冲击或重复的折叠和展开操作而损坏。可能需要更换受损保护膜PF'。
参考图9B,热量供应装置10可以设置在显示装置1000'上方以更换受损保护膜PF'。热量供应装置10可以将热量HT提供到显示装置1000'。由于热量HT,可以改变第一粘合剂层AD1的结晶相。作为示例,如图6B中所示,第一粘合剂层AD1的分子结构可以由于热量HT而改变。因此,如上所述,在与第一粘合剂层AD1在室温下的粘合力相比时,第一粘合剂层AD1在高温度下的粘合力可以显著降低。
图9C示出了在提供热量HT之后从窗WP的上表面WP-U分离将被更换的受损保护膜PF'的过程。用于将受损保护膜PF'附接到窗WP的上表面WP-U的第一粘合剂层AD1的粘合力可以通过热量HT降低,并且因此,受损保护膜PF'可以与窗WP容易地分离。因此,当更换受损保护膜PF'时,可以减少或有效地防止对显示面板DP的损坏。
详细地,第一粘合力可以在室温下作用在第一粘合剂层AD1的后表面AD1-B和窗WP的上表面WP-U之间,并且第二粘合力可以在高温度下作用在第一粘合剂层AD1的后表面AD1-B和窗WP的上表面WP-U之间。通过施加热量HT,与第一粘合力相比,第二粘合力可以降低到约50%或降低得更多。在实施方式中,例如,第一粘合力在约25摄氏度的温度下可以是约500gf/inch,并且第二粘合力在约80摄氏度的温度下可以是约50gf/inch。
图9D示出了包括未受损保护模块200-N的被修复的显示装置1000。未受损保护模块200-N可以包括未被损坏的未受损保护膜PF-N、设置在未受损保护膜PF-N的后表面上的第二粘合剂层AD2-N、以及设置在第二粘合剂层AD2-N的后表面上的第一粘合剂层AD1-N。未受损保护模块200-N可以附接到显示模块100使得第一粘合剂层AD1-N与窗WP的上表面WP-U(参见图9C)接触。
第一粘合剂层AD1-N在室温下的粘合力可以大于第一粘合剂层AD1-N在高温度下的粘合力,并且未受损保护膜PF-N不容易从窗WP剥离。即,即使显示装置1000重复折叠和展开,未受损保护膜PF-N也不容易剥离。此外,尽管显示装置1000被重复折叠和展开,但是可以通过具有相对小的模量的第二粘合剂层AD2-N来保持折叠可靠性。
显示装置1000可以包括保护膜PF和设置在保护膜PF下方的粘合剂层。粘合剂层可以包括具有相对小模量的粘合剂层和具有在高温度下具有高可变程度的粘合力的粘合剂层。即使显示装置1000重复折叠和展开,通过粘合剂层,显示装置1000的折叠可靠性也不会降低,并且保护膜PF可以不会从显示模块100被容易地剥离。此外,保护膜PF可以在高温度下通过粘合剂层容易地从显示模块100去除,并且保护膜PF可以在不对显示模块100造成损坏的情况下被更换。
尽管已经描述了本公开的实施方式,但是应理解的是,本公开不应限于这些实施方式,而是如在本文中要求保护的本公开的精神和范围内,本领域普通技术人员可以进行各种改变和修改。
因此,所公开的主题不应限于本文中所描述的任何单个实施方式,并且本发明的范围应根据所附权利要求来确定。
Claims (10)
1.显示装置,包括:
显示面板,能够绕着在第一方向上延伸的折叠轴线折叠;
窗,面对所述显示面板;
保护膜,面对所述显示面板,且所述窗在所述保护膜和所述显示面板之间;以及
多个粘合剂层,在所述窗和所述保护膜之间并且将所述窗联接到所述保护膜,所述多个粘合剂层从所述窗到所述保护膜依序包括:
第一粘合剂层,包括侧链结晶聚合物和模量;以及
第二粘合剂层,面对所述第一粘合剂层并且包括小于所述第一粘合剂层的所述模量的模量。
2.根据权利要求1所述的显示装置,其中,在从所述窗到所述保护膜依序设置的所述第一粘合剂层和所述第二粘合剂层中:
所述第一粘合剂层在室温下具有第一粘合力并且在等于或大于70摄氏度的温度下具有第二粘合力,以及
所述第二粘合力等于或小于所述第一粘合力的50%。
3.根据权利要求2所述的显示装置,其中,在等于或大于70摄氏度的所述温度下,所述第二粘合剂层具有大于所述第一粘合剂层的所述第二粘合力的粘合力。
4.根据权利要求1所述的显示装置,其中,所述侧链结晶聚合物包括(甲基)丙烯酸十六烷基酯共聚物、(甲基)丙烯酸十八烷基酯共聚物、(甲基)丙烯酸二十烷基酯共聚物和(甲基)丙烯酸二十二烷基酯共聚物中的至少一种。
5.根据权利要求1所述的显示装置,其中,在从所述窗到所述保护膜依序设置的所述第一粘合剂层和所述第二粘合剂层中:
所述第一粘合剂层和所述第二粘合剂层中的每个具有厚度,以及
所述第一粘合剂层的所述厚度小于所述第二粘合剂层的所述厚度。
6.根据权利要求1所述的显示装置,其中,所述第一粘合剂层和所述第二粘合剂层中的至少一个还包括发泡剂。
7.根据权利要求6所述的显示装置,其中,在从所述窗到所述保护膜依序设置的所述第一粘合剂层和所述第二粘合剂层中:
所述第一粘合剂层中包括的所述发泡剂基于总含量具有等于或小于3%的含量。
8.显示装置,包括:
显示面板,能够绕着折叠轴线折叠;
窗,面对所述显示面板;
保护膜,面对所述显示面板,且所述窗在所述保护膜和所述显示面板之间;以及
多个粘合剂层,在所述窗和所述保护膜之间并且将所述窗联接到所述保护膜,所述多个粘合剂层在所述窗和所述保护膜之间依序包括:
第一粘合剂层,在室温下具有第一粘合力并且在等于或大于70摄氏度的温度下具有第二粘合力;以及
第二粘合剂层,与所述第一粘合剂层接触并且在等于或大于70摄氏度的所述温度下具有第三粘合力,
其中,
所述第一粘合剂层的所述第二粘合力小于所述第二粘合剂层的所述第三粘合力,以及
所述第一粘合剂层的所述第二粘合力等于或小于所述第一粘合剂层的所述第一粘合力的50%。
9.根据权利要求8所述的显示装置,其中,在从所述窗到所述保护膜依序设置的所述第一粘合剂层和所述第二粘合剂层中:
所述第一粘合剂层和所述第二粘合剂层中的每个具有厚度,
所述第一粘合剂层的所述厚度等于或大于5微米并且等于或小于25微米,以及
所述第二粘合剂层的所述厚度等于或大于10微米并且等于或小于100微米。
10.根据权利要求8所述的显示装置,其中,在从所述窗到所述保护膜依序设置的所述第一粘合剂层和所述第二粘合剂层中,所述第一粘合剂层包括侧链结晶聚合物。