CN115126175A - Method for manufacturing external wall decoration heat insulation waterproof integrated plate - Google Patents
Method for manufacturing external wall decoration heat insulation waterproof integrated plate Download PDFInfo
- Publication number
- CN115126175A CN115126175A CN202210054117.2A CN202210054117A CN115126175A CN 115126175 A CN115126175 A CN 115126175A CN 202210054117 A CN202210054117 A CN 202210054117A CN 115126175 A CN115126175 A CN 115126175A
- Authority
- CN
- China
- Prior art keywords
- heat
- flame
- heat insulation
- retardant
- shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an external wall decoration heat insulation waterproof integrated plate, which comprises the following steps: firstly, manufacturing a shell; secondly, arranging a decorative layer on the top surface of the shell; thirdly, preparing flame-retardant heat-preservation composite slurry; fourthly, pouring the flame-retardant heat-preservation composite slurry into the shell, standing and curing to obtain a heat-preservation layer, and carrying out wet maintenance for at least 72 hours at the temperature of 15-35 ℃. The fireproof flame-retardant composite slurry is integrated with the shell in the curing process, and the manufactured outer wall decoration heat-insulation waterproof integrated plate is good in integration, strong in anti-interference capability, high in reliability and long in service life compared with an adhesive plate.
Description
Technical Field
The invention relates to a method for manufacturing a plate, in particular to a method for manufacturing an outer wall decoration heat insulation waterproof integrated plate.
Background
The outer wall insulation board is an important component of a passive building, the outer wall insulation board is coated on the outermost layer of the passive building, the effects of heat insulation and sealing are achieved, indoor heat energy is retained to the maximum extent, and therefore a comfortable indoor thermal environment can be maintained without active heating or extremely low energy consumption.
The quality of the external wall insulation board directly affects the energy-saving effect of a passive building, and the existing external wall insulation board has certain defects, for example, the invention patent with the name of 'a tooth-jointed external wall insulation integrated board' disclosed by the publication number CN105544915A, an external wall decoration board and an insulation layer are fixedly connected together through a silicone weather-resistant adhesive to form a square external wall insulation integrated board. The heat-insulating layer and the outer wall decorative plate are adhered by the silicone weather-resistant adhesive, so that the integrity is poor, the adhesive is easily influenced by the environment and is easily failed at higher temperature, and therefore, the plate is short in service life and poor in reliability.
Disclosure of Invention
The invention aims to provide a method for manufacturing an outer wall decoration heat insulation waterproof integrated plate.
The technical scheme of the invention is as follows:
a manufacturing method of an external wall decoration heat insulation waterproof integrated plate comprises the following steps:
firstly, manufacturing a shell;
secondly, arranging a decorative layer on the top surface of the shell;
thirdly, preparing flame-retardant heat-preservation composite slurry;
fourthly, pouring the flame-retardant heat-preservation composite slurry into the shell, standing and curing to obtain a heat-preservation layer, and carrying out wet maintenance for at least 72 hours at the temperature of 15-35 ℃.
According to the manufacturing method of the outer wall decoration heat insulation waterproof integrated plate, the flame-retardant heat insulation composite slurry is poured into the formed shell, the heat insulation layer is formed after static curing, the heat insulation layer and the shell are integrated, and the heat insulation layer is maintained for at least 72 hours in a humid environment at 15-35 ℃, so that the structural strength and uniformity of the heat insulation layer are ensured.
According to the manufacturing method of the outer wall decoration heat insulation waterproof integrated plate, the flame-retardant heat insulation composite slurry is integrated with the shell in the curing process, and compared with an adhesive plate, the manufactured outer wall decoration heat insulation waterproof integrated plate is good in integration, strong in anti-interference capability, high in reliability and long in service life.
Preferably, the preparation method of the flame-retardant heat-preservation composite slurry comprises the following steps:
a. mixing a flame retardant (HBCD) hexabromocyclododecane, graphene and polystyrene foaming particles according to a mass ratio of 0.5-1.0: 0.8-1.2: 98-100 to prepare B1-grade flame-retardant polystyrene foaming particles, and transferring the B1-grade flame-retardant polystyrene foaming particles into a storage container for later use;
mixing PO42.5 cement, fine sand, closed-cell vitrified micro bubbles, polypropylene fibers and ZK-1 rubber powder in a mass ratio of 25-30: 35-40: 25-30: 0.15-0.18: 0.2-0.25 in a multifunctional dry powder mixing stirrer, fully stirring for about 30 minutes, and transferring into a storage container for later use;
c. respectively weighing a cement foaming agent, a foaming cement reinforcing water reducing agent and water according to 0.2%, 0.3% and 45-50% of the used mass of the cement for later use;
d. and (3) mixing the mixture obtained in the step a and the mixture obtained in the step b according to the mass ratio of 1: 1, putting the mixture into a drum type concrete mixer, stirring for 12-15 minutes, determining that the mixture is basically uniformly stirred, adding the water prepared in the step c and the foamed cement reinforced water reducing agent, and continuously stirring for 12-15 minutes;
e. and (d) adding the cement foaming agent prepared in the step (c) into the mixture obtained in the step (d) before pouring the mixture into a shell, and continuously stirring for 5-10 minutes.
After the flame-retardant heat-preservation composite slurry produced in the way is cured, a porous structure is formed in the heat-preservation layer, and the heat-preservation effect is good; the ZK-1 rubber powder seals gaps on the surface of the heat-insulating layer after the flame-retardant heat-insulating composite slurry is cured, so that the waterproof effect is good; the flame-retardant heat-preservation composite slurry is non-flammable in raw materials, and good in flame-retardant effect due to the assistance of the flame retardant.
Preferably, the flame-retardant heat-preservation composite slurry is filled into the shell within 30 minutes after the preparation is finished. So guarantee fire-retardant heat preservation composite slurry and have good mobility when watering to the casing in, can fully be covered with the casing, reduce the defect of heat preservation.
Preferably, the relative humidity of the environment during the wet maintenance in the third step is 70-85%. The relative humidity of the environment during the wet maintenance is properly higher, so that the internal defects of the heat-insulating layer are reduced, and the cracking of the heat-insulating layer is avoided.
Preferably, the decorative layer is formed by UV printing. The UV printing operation is convenient, the color of the printing generated decorative layer is rich, the wear resistance is good, and the production efficiency of the UV printing is high.
Preferably, the shell is provided with an insulation zone, and flame-retardant insulation composite slurry is not poured in the insulation zone. The heat insulation area can contain air, the heat conductivity of the air is poor, and the heat insulation performance of the outer wall decoration heat insulation waterproof integrated plate can be further improved. The heat insulation area is not poured with the flame-retardant heat-preservation composite slurry, so that space is reserved for installing the outer wall decoration heat-preservation waterproof integrated plate, and the heat insulation layer is prevented from being damaged during installation to influence the heat insulation effect.
Preferably, the temperature insulation region is provided with a mounting hole. The pressing plate can be installed in the mounting hole, and the fixing assembly can be conveniently pressed to fix the outer wall decoration heat insulation waterproof integrated plate.
The invention has the beneficial effects that: the flame-retardant heat-preservation composite slurry is integrated with the shell in the curing process, and the manufactured external wall decoration heat-insulation waterproof integrated board has good integration, strong anti-interference capability, high reliability and long service life compared with an adhesive board.
Drawings
FIG. 1 is a top view of an integrated heat-insulating and water-proof plate for exterior wall decoration.
Fig. 2 is a cross-sectional view of the housing.
Fig. 3 is a sectional view of the heat insulation waterproof integrated plate for exterior wall decoration.
Fig. 4 is a partially enlarged view of a portion a in fig. 3.
In the figure:
the heat insulation structure comprises a shell 1, a heat insulation area 1.1 and a mounting hole 1.2;
a heat-insulating layer 2;
and a decorative layer 3.
Detailed Description
In order to make the objects, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions of the embodiments of the present invention are clearly explained and illustrated below with reference to the accompanying drawings, but the following embodiments are only preferred embodiments of the present invention, and not all embodiments. Based on the embodiments in the implementation, other embodiments obtained by those skilled in the art without any creative effort belong to the protection scope of the present invention.
Reference will now be made in detail to embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the same or similar elements or elements having the same or similar functions throughout. The embodiments described below by referring to the drawings are exemplary only for explaining the present scheme and are not construed as limiting the scheme of the present invention.
These and other aspects of embodiments of the invention will be apparent with reference to the following description and attached drawings. In the description and drawings, particular embodiments of the invention have been disclosed in detail as being indicative of some of the ways in which the principles of the embodiments of the invention may be practiced, but it is understood that the scope of the embodiments of the invention is not limited thereby. On the contrary, the embodiments of the invention include all changes, modifications and equivalents coming within the spirit and terms of the claims appended hereto.
In the description of the present invention, it is to be understood that the terms "thickness", "upper", "lower", "horizontal", "top", "bottom", "inner", "outer", "circumferential", and the like, indicate orientations and positional relationships based on those shown in the drawings, and are used merely for convenience in describing the present invention and for simplicity in description, and do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and thus, should not be construed as limiting the present invention. In the description of the present invention, "a plurality" means at least two, e.g., two, three, etc., and "a plurality" means one or more unless specifically limited otherwise.
In the present invention, unless otherwise expressly stated or limited, the terms "mounted," "connected," "fixed," and the like are to be construed broadly and can include, for example, fixed connections, removable connections, or integral connections, either mechanical or electrical, or communicating with each other; they may be directly connected or indirectly connected through intervening media, or they may be connected internally or in any other suitable relationship, unless expressly stated otherwise. The specific meanings of the above terms in the present invention can be understood by those skilled in the art according to specific situations.
The first embodiment is as follows: as shown in fig. 1 to 4, a method for manufacturing an exterior wall decoration heat insulation waterproof integrated plate includes the following steps:
firstly, manufacturing a shell 1;
secondly, arranging a decorative layer 3 on the top surface of the shell 1;
thirdly, preparing flame-retardant heat-preservation composite slurry;
fourthly, pouring the flame-retardant heat-preservation composite slurry into the shell 1, standing and curing to obtain the heat-preservation layer 2, and carrying out wet maintenance for at least 72 hours at the temperature of 15-35 ℃.
In this embodiment, the housing 1 is an aluminum housing and is made by a sheet metal process, which is well known in the art and will not be described again.
According to the manufacturing method of the outer wall decoration heat insulation waterproof integrated plate, the flame-retardant heat insulation composite slurry is poured into the formed shell 1, the heat insulation layer 2 is formed after static curing, the heat insulation layer 2 and the shell 1 are integrated, and the outer wall decoration heat insulation waterproof integrated plate is maintained in a wet state for at least 72 hours at 25 ℃ so as to ensure the structural strength and uniformity of the heat insulation layer 2.
According to the manufacturing method of the outer wall decoration heat insulation waterproof integrated plate, the flame-retardant heat insulation composite slurry is integrated with the shell 1 in the curing process, and compared with an adhesive plate, the manufactured outer wall decoration heat insulation waterproof integrated plate is good in integration, strong in anti-interference capability, high in reliability and long in service life.
Further, the preparation method of the flame-retardant heat-preservation composite slurry comprises the following steps:
a. mixing a flame retardant (HBCD) hexabromocyclododecane, graphene and polystyrene foaming particles according to a mass ratio of 0.5-1.0: 0.8-1.2: 98-100 to prepare B1-grade flame-retardant polystyrene foaming particles, and transferring the B1-grade flame-retardant polystyrene foaming particles into a storage container for later use;
mixing PO42.5 cement, fine sand, closed-cell vitrified micro bubbles, polypropylene fibers and ZK-1 rubber powder in a mass ratio of 25-30: 35-40: 25-30: 0.15-0.18: 0.2-0.25 in a multifunctional dry powder mixing stirrer, fully stirring for about 30 minutes, and transferring into a storage container for later use;
c. respectively weighing 0.2%, 0.3% and 45-50% of cement by mass of a cement foaming agent, a foaming cement reinforcing water reducing agent and water for later use;
d. and (3) mixing the mixture obtained in the step a and the mixture obtained in the step b according to the mass ratio of 1: 1, putting the mixture into a drum type concrete mixer, stirring for 12-15 minutes, determining that the mixture is basically uniformly stirred, adding the water prepared in the step c and the foamed cement reinforced water reducing agent, and continuously stirring for 12-15 minutes;
e. and (d) adding the cement foaming agent prepared in the step (c) into the mixture obtained in the step (d) before pouring the mixture into the shell 1, and continuously stirring for 5-10 minutes.
After the flame-retardant heat-preservation composite slurry produced in the way is cured, a porous structure is formed in the heat-preservation layer 2, and the heat-preservation effect is good; the ZK-1 rubber powder seals the gaps on the surface of the insulating layer 2 after the flame-retardant insulating composite slurry is cured, so that the waterproof effect is good; the flame-retardant heat-preservation composite slurry is non-flammable in raw materials, and good in flame-retardant effect due to the assistance of the flame retardant.
Further, the flame-retardant heat-preservation composite slurry is filled into the shell 1 within 30 minutes after the preparation is finished. So guarantee fire-retardant heat preservation composite paste occasionally good mobility when watering to casing 1 in, can fully be covered with casing 1, reduce the defect of heat preservation 2.
Further, the relative humidity of the environment during the wet curing in the third step is more than 70%. The relative humidity of the environment during the wet maintenance is properly higher, so that the internal defects of the heat-insulating layer 2 are reduced, and the heat-insulating layer 2 is prevented from cracking.
Further, the decorative layer 3 is formed by UV printing. The UV printing operation is convenient, 3 colors of the decorative layer generated by printing are rich, the wear resistance is good, and the production efficiency of the UV printing is high. In other embodiments, the decorative layer 3 may also be formed by spraying, but the decorative layer formed by spraying has poor wear resistance, and should be sprayed on the top surface of the casing 1 after the heat-insulating layer 2 is obtained, so as to prevent the top surface of the casing 1 from being scratched with the ground during the pouring and fixing processes of the flame-retardant heat-insulating composite slurry to damage the decorative layer 3.
Further, the shell 1 is provided with an insulation area 1.1, and flame-retardant insulation composite slurry is not poured in the insulation area 1.1. The heat insulation area 1.1 can contain air, the heat conductivity of the air is poor, and the heat insulation performance of the outer wall decoration heat insulation waterproof integrated plate can be further improved. The heat insulation area 1.1 is not watered with the flame-retardant heat insulation composite slurry, so that a space is reserved for installing the outer wall decoration heat insulation waterproof integrated plate, and the heat insulation layer 2 is prevented from being damaged during installation to influence the heat insulation effect.
Furthermore, the temperature insulation area 1.1 is provided with a mounting hole 1.2. The mountable clamp plate in mounting hole 1.2 is convenient for fixed subassembly and is compressed tightly fixed outer wall and decorates thermal-insulated waterproof integrated board, and the clamp plate inserts in the mounting hole 1.2 of two adjacent outer wall decoration thermal-insulated waterproof integrated boards, fixes on the wall body by threaded component, and the clamp plate setting can not destroy the heat preservation in separating temperature district 1.1.
The above description is only a preferred embodiment of the present invention, and is not intended to limit the present invention, and all simple modifications, alterations and equivalents of the above embodiments according to the technical spirit of the present invention are still within the protection scope of the technical solution of the present invention.
Claims (7)
1. A manufacturing method of an outer wall decoration heat insulation waterproof integrated plate is characterized by comprising the following steps:
firstly, manufacturing a shell (1);
secondly, arranging a decorative layer (3) on the top surface of the shell (1);
thirdly, preparing flame-retardant heat-preservation composite slurry;
fourthly, pouring the flame-retardant heat-preservation composite slurry into the shell (1), standing and curing to obtain the heat-preservation layer (2), and carrying out wet maintenance for at least 72 hours at the temperature of 15-35 ℃.
2. The method for manufacturing the heat-insulating waterproof integrated board for the exterior wall decoration according to claim 1, wherein the preparation method of the flame-retardant heat-insulating composite slurry comprises the following steps:
a. mixing a flame retardant (HBCD) hexabromocyclododecane, graphene and polystyrene foaming particles according to a mass ratio of 0.5-1.0: 0.8-1.2: 98-100 to prepare B1-grade flame-retardant polystyrene foaming particles, and transferring the B1-grade flame-retardant polystyrene foaming particles into a storage container for later use;
mixing PO42.5 cement, fine sand, closed-cell vitrified micro bubbles, polypropylene fibers and ZK-1 rubber powder in a mass ratio of 25-30: 35-40: 25-30: 0.15-0.18: 0.2-0.25 in a multifunctional dry powder mixing stirrer, fully stirring for about 30 minutes, and transferring into a storage container for later use;
c. respectively weighing a cement foaming agent, a foaming cement reinforcing water reducing agent and water according to 0.2%, 0.3% and 45-50% of the used mass of the cement for later use;
d. mixing the mixture obtained in the step a and the step b according to the mass ratio of 1: 1, putting the mixture into a drum-type concrete mixer, stirring for 12-15 minutes, determining that the mixture is basically uniformly stirred, adding the water prepared in the step c and the foamed cement reinforced water reducing agent, and continuously stirring for 12-15 minutes;
e. and c, adding the cement foaming agent prepared in the step c into the mixture obtained in the step d before pouring the mixture into the shell (1), and continuously stirring for 5-10 minutes.
3. The method for manufacturing the heat-insulating waterproof integrated board for exterior wall decoration according to claim 2, wherein the flame-retardant heat-insulating composite slurry is poured into the shell (1) within 30 minutes after the preparation is completed.
4. The method for manufacturing the exterior wall decorating, heat insulating and waterproof integrated plate as claimed in any one of claims 1 to 3, wherein the relative humidity of the environment during the wet curing in the third step is 70% to 85%.
5. The method for manufacturing the heat insulation and waterproof integrated board for exterior wall decoration according to claim 1, wherein the decoration layer (3) is formed by UV printing.
6. The method for manufacturing the heat insulation and waterproof integrated board for the exterior wall decoration according to claim 1, wherein the shell (1) is provided with a heat insulation area (1.1), and flame retardant and heat insulation composite slurry is not poured in the heat insulation area (1.1).
7. The method for manufacturing the heat insulation and waterproof integrated board for the exterior wall decoration according to claim 6, wherein the heat insulation area (1.1) is provided with mounting holes (1.2).