CN115073977A - 一种儿童房可洗刷高档水性内墙涂料的制备方法 - Google Patents
一种儿童房可洗刷高档水性内墙涂料的制备方法 Download PDFInfo
- Publication number
- CN115073977A CN115073977A CN202210783610.8A CN202210783610A CN115073977A CN 115073977 A CN115073977 A CN 115073977A CN 202210783610 A CN202210783610 A CN 202210783610A CN 115073977 A CN115073977 A CN 115073977A
- Authority
- CN
- China
- Prior art keywords
- agent
- stirrer
- interior wall
- filler
- children
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明专利公开了一种儿童房可洗刷高档水性内墙涂料的制备方法，分散剂0.5‑0.6％，润湿剂0.1‑0.2％，杀菌剂0.1‑0.15％，消泡剂0.2‑0.3％，钛白粉21‑25％，填料16‑18％，低气味苯丙乳液20‑23％，功能性丙烯酸乳液6‑9％，遮盖聚合物2‑8％，增稠剂0.3‑0.4％，余量为水，本发明专利采用特殊的壳核结构低气味苯丙乳液，利用水为外增塑剂，不需要添加任何成膜助剂即能较好成膜，采用特殊的保护胶体，具有优异的抗冻融性，不需要添加防冻剂和成膜助剂，制备了VOC含量很低(几乎为零)、涂膜抗污性能佳的环保型内墙乳胶漆，并且在该涂料中添加了功能性填料以及遮盖聚合物，能够极大限度的提升涂料整体的抗污和防涂鸦性能，因此该涂料十分适合在儿童房的内墙上进行使用，非常值得推广。
Description
技术领域
本发明专利涉及涂料技术领域，具体为一种儿童房可洗刷高档水性内墙涂料的制备方法。
背景技术
涂料，在中国传统名称为油漆，所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。
环保型乳胶漆，由于其施工简单、无毒害、清洗方便、色彩丰富、对环境造成污染小等优点，越来越受到人们的青睐和认可。近年来，随着市场的细化，越来越多的用户对儿童房用的墙面漆有了特殊的要求:一般要求环保性能好，因儿童的免疫力较成人差，又是生长发育期，这样涂料的安全要求较普通内墙涂料严格许多，不含(或不添加有机可挥发性物质)(VOC)、重金属、APEO、甲醛等，另一方面要求儿童房用内墙涂料耐污渍性能佳，由于小孩喜欢在墙面涂鸦，这就要求在儿童玩闹使墙面受污染后，只需用清水或洗洁精轻轻擦拭，就能够还原白净如昔的墙面，基于此我们发明一种儿童房可洗刷高档水性内墙涂料来满足市场需求。
发明专利内容
本发明专利的目的在于提供一种儿童房可洗刷高档水性内墙涂料的制备方法，为实现上述目的，本发明专利提供如下技术方案：一种儿童房可洗刷高档水性内墙涂料，所述儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水。
优选的，所述儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水。
一种儿童房可洗刷高档水性内墙涂料的制备方法，其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备。
优选的，所述填料包括超细硅酸铝、硅藻土和滑石粉。
优选的，所述步骤(1)中，助剂混合时搅拌器的转速为1000r/min，且持续时间为15min。
优选的，所述步骤(2)中，填料以及钛白粉研磨后的平均粒径为50μm。
优选的，所述步骤(3)中，填料混合时搅拌器的转速为2500r/min，且持续时间为1h。
优选的，所述步骤(4)中，基料投放到搅拌器中混合时，搅拌器的转速为1500r/min，且持续时间为30min。
优选的，所述步骤(5)中，剩余消泡剂在添加的时候，搅拌器的转速以300r/min的速度逐级降低，并且降低到300r/min时保持匀速，此时再向搅拌器中添加增稠剂，所述该涂料的PVC设计在35％-40％。
与现有技术相比，本发明专利的有益效果如下：
本发明专利采用特殊的壳核结构低气味苯丙乳液，利用水为外增塑剂，不需要添加任何成膜助剂即能较好成膜，采用特殊的保护胶体，具有优异的抗冻融性，不需要添加防冻剂和成膜助剂，制备了VOC含量很低(几乎为零)、涂膜抗污性能佳的环保型内墙乳胶漆，并且在该涂料中添加了功能性填料以及遮盖聚合物，能够极大限度的提升涂料整体的抗污和防涂鸦性能，因此该涂料十分适合在儿童房的内墙上进行使用，非常值得推广。
具体实施方式
下面将结合本发明专利中的实施例，对本发明专利实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明专利一部分实施例，而不是全部的实施例。基于本发明专利中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明专利保护的范围。
一种儿童房可洗刷高档水性内墙涂料的制备方法，儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水；儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水，其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备。
实施例一：
一种儿童房可洗刷高档水性内墙涂料的制备方法，儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水；儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水，核壳结构乳液聚合物属于异种分子复合乳液，是由于不同性质的两种或多种单体在一定条件下按阶段聚合(即种子聚合或多阶段聚合)，使乳液颗粒内部的内侧和外侧分别富集不同种成分，通过核壳的不同组合，得到一系列不同形态的非均相粒子，从而赋予核壳乳液不同的功能，得到一般无规共聚物、机械共混物难以得到的优异性能，并且单独选择用低气味苯丙的抗污效果并不明显，选用低气味苯丙与功能性丙烯酸乳液配合，抗污效果好，而且气味也非常小，同时不含APEO，其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备。
实施例二：
一种儿童房可洗刷高档水性内墙涂料的制备方法，儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水；儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水，核壳结构乳液聚合物属于异种分子复合乳液，是由于不同性质的两种或多种单体在一定条件下按阶段聚合(即种子聚合或多阶段聚合)，使乳液颗粒内部的内侧和外侧分别富集不同种成分，通过核壳的不同组合，得到一系列不同形态的非均相粒子，从而赋予核壳乳液不同的功能，得到一般无规共聚物、机械共混物难以得到的优异性能，并且单独选择用低气味苯丙的抗污效果并不明显，选用低气味苯丙与功能性丙烯酸乳液配合，抗污效果好，而且气味也非常小，同时不含APEO，填料包括超细硅酸铝、硅藻土和滑石粉，超细硅酸铝代替部分钛白粉，其干膜遮盖力不会改变，并能提高其白度，若钛白粉的用量不变，其干膜遮盖力明显提高，白度大幅度提高，超细硅酸铝pH值范围为9.7-10.8，其具有pH值的缓冲作用，尤其是在醋酸乙烯乳胶漆贮存过程中可以防止因醋酸乙烯水解而使pH值下降的现象，增加了乳胶漆的贮存稳定性，同时避免了金属容器内壁遭受腐蚀，硅酸铝的超细、网络结构使乳胶漆体系稍增稠，具有很好的悬浮性，并防止固体分的沉底及表面分水现象的出现，超细硅酸铝使乳胶涂膜有很好的耐擦洗性、耐候性，另外能缩短表干时间，硅藻土作为填料，具有孔隙度大、吸收性强、化学性质稳定、耐磨、耐热等特点、能为涂料提供优异的表面性能，并能增容、增稠以及提高附着力，由于它具有较大的孔体积，能使涂膜缩短干燥时间，还可以减少乳液的用量，降低成本，还能均衡地控制涂膜表面光泽，增加涂膜的耐磨性和抗划痕性、去湿、除臭，而且具有能净化空气、隔音、防水和隔热、通透性好的特点，由于滑石粉具有润滑性、抗黏、助流、耐火性、抗酸性、绝缘性、熔点高、化学性不活泼、手感良好、柔软、光泽好、吸附力强等优良的物理化学性能，在涂料中的使用可起到骨架作用，降低制造成本同时提高涂料的涂膜硬度，滑石粉的片状结构使涂膜具有较高程度的耐水性及污渍的不渗性，其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备。
实施例三：
一种儿童房可洗刷高档水性内墙涂料的制备方法，儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水；儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水，核壳结构乳液聚合物属于异种分子复合乳液，是由于不同性质的两种或多种单体在一定条件下按阶段聚合(即种子聚合或多阶段聚合)，使乳液颗粒内部的内侧和外侧分别富集不同种成分，通过核壳的不同组合，得到一系列不同形态的非均相粒子，从而赋予核壳乳液不同的功能，得到一般无规共聚物、机械共混物难以得到的优异性能，并且单独选择用低气味苯丙的抗污效果并不明显，选用低气味苯丙与功能性丙烯酸乳液配合，抗污效果好，而且气味也非常小，同时不含APEO，填料包括超细硅酸铝、硅藻土和滑石粉，超细硅酸铝代替部分钛白粉，其干膜遮盖力不会改变，并能提高其白度，若钛白粉的用量不变，其干膜遮盖力明显提高，白度大幅度提高，超细硅酸铝pH值范围为9.7-10.8，其具有pH值的缓冲作用，尤其是在醋酸乙烯乳胶漆贮存过程中可以防止因醋酸乙烯水解而使pH值下降的现象，增加了乳胶漆的贮存稳定性，同时避免了金属容器内壁遭受腐蚀，硅酸铝的超细、网络结构使乳胶漆体系稍增稠，具有很好的悬浮性，并防止固体分的沉底及表面分水现象的出现，超细硅酸铝使乳胶涂膜有很好的耐擦洗性、耐候性，另外能缩短表干时间，硅藻土作为填料，具有孔隙度大、吸收性强、化学性质稳定、耐磨、耐热等特点、能为涂料提供优异的表面性能，并能增容、增稠以及提高附着力，由于它具有较大的孔体积，能使涂膜缩短干燥时间，还可以减少乳液的用量，降低成本，还能均衡地控制涂膜表面光泽，增加涂膜的耐磨性和抗划痕性、去湿、除臭，而且具有能净化空气、隔音、防水和隔热、通透性好的特点，由于滑石粉具有润滑性、抗黏、助流、耐火性、抗酸性、绝缘性、熔点高、化学性不活泼、手感良好、柔软、光泽好、吸附力强等优良的物理化学性能，在涂料中的使用可起到骨架作用，降低制造成本同时提高涂料的涂膜硬度，滑石粉的片状结构使涂膜具有较高程度的耐水性及污渍的不渗性，其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌，步骤(1)中，助剂混合时搅拌器的转速为1000r/min，且持续时间为15min；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨，步骤(2)中，填料以及钛白粉研磨后的平均粒径为50μm；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌，步骤(3)中，填料混合时搅拌器的转速为2500r/min，且持续时间为1h；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合，步骤(4)中，基料投放到搅拌器中混合时，搅拌器的转速为1500r/min，且持续时间为30min，遮盖聚合物具有普通无机填料优异的3个性能特点：一，中空玻璃珠球形结构，耐污渍效果好，二，粒径微细且均匀，可以提高钛白粉的效率，从而取代部分钛白粉，减少配方成本，三，与聚合物粘结剂亲和力强，粘结剂需求量低，随着遮盖聚合物的添加量的增加，耐污渍效果越来越好，遮盖聚合物帮助涂膜更加致密，当添加量超过6％时，耐污渍效果上升的趋势并不明显，遮盖聚合物添加量过多，使涂膜掉粉的可能性增加，所以遮盖聚合物添加量选择在6％比较好；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备，步骤(5)中，剩余消泡剂在添加的时候，搅拌器的转速以300r/min的速度逐级降低，并且降低到300r/min时保持匀速，此时再向搅拌器中添加增稠剂，该涂料的PVC设计在35％-40％，基料刚好填满颜填料无规则堆积所形成的空隙时，这时的PVC值被称为临界颜料体积浓度CPVC，高PVC时污渍易清洁是因为涂膜被擦掉了，因此综合成本考虑，当配方的PVC达到35％-40％时，涂膜物化性能好、耐污渍效果达到最佳。
尽管已经示出和描述了本发明专利的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明专利的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明专利的范围由所附权利要求及其等同物限定。
Claims (9)
1.一种儿童房可洗刷高档水性内墙涂料，其特征在于：所述儿童房可洗刷高档水性内墙涂料的组成部分按照质量百分比计为：分散剂0.5-0.6％，润湿剂0.1-0.2％，杀菌剂0.1-0.15％，消泡剂0.2-0.3％，钛白粉21-25％，填料16-18％，低气味苯丙乳液20-23％，功能性丙烯酸乳液6-9％，遮盖聚合物2-8％，增稠剂0.3-0.4％，余量为水。
2.根据权利要求1所述的一种儿童房可洗刷高档水性内墙涂料，其特征在于：所述儿童房可洗刷高档水性内墙涂料按重量份数包括如下组成部分：分散剂0.5份，润湿剂0.2份，杀菌剂0.15份，消泡剂0.25份，钛白粉23份，填料17份，低气味苯丙乳液22份，功能性丙烯酸乳液8份，遮盖聚合物7份，增稠剂0.4份，余量为水。
3.根据权利要求1-2中任意一项所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：其制备方法包括如下步骤：
(1)助剂混合：将水、分散剂、润湿剂、杀菌剂和部分消泡剂添加到多功能搅拌器中，并且启动搅拌器对混合物进行充分混合搅拌；
(2)填料研磨：将钛白粉和填料投放到球形磨粉机中进行研磨；
(3)填料混合：将研磨后的钛白粉以及填料投放到搅拌器中，使钛白粉以及填料与搅拌器中的混合液充分搅拌；
(4)基料混合：将低气味丙苯乳液和功能性丙烯酸乳液以及遮盖聚合物投放到搅拌器中进行充分搅拌混合；
(5)消泡以及粘稠度调整：将剩余的消泡剂添加到搅拌器中充分消泡，然后添加适量的增稠剂调整混合液的粘稠度即可完成涂料的制备。
4.根据权利要求1所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述填料包括超细硅酸铝、硅藻土和滑石粉。
5.根据权利要求3所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述步骤(1)中，助剂混合时搅拌器的转速为1000r/min，且持续时间为15min。
6.根据权利要求3所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述步骤(2)中，填料以及钛白粉研磨后的平均粒径为50μm。
7.根据权利要求3所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述步骤(3)中，填料混合时搅拌器的转速为2500r/min，且持续时间为1h。
8.根据权利要求3所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述步骤(4)中，基料投放到搅拌器中混合时，搅拌器的转速为1500r/min，且持续时间为30min。
9.根据权利要求3所述的一种儿童房可洗刷高档水性内墙涂料的制备方法，其特征在于：所述步骤(5)中，剩余消泡剂在添加的时候，搅拌器的转速以300r/min的速度逐级降低，并且降低到300r/min时保持匀速，此时再向搅拌器中添加增稠剂，所述该涂料的PVC设计在35％-40％。