CN1150283C - 一种抗裂外墙腻子 - Google Patents
一种抗裂外墙腻子 Download PDFInfo
- Publication number
- CN1150283C CN1150283C CNB011275049A CN01127504A CN1150283C CN 1150283 C CN1150283 C CN 1150283C CN B011275049 A CNB011275049 A CN B011275049A CN 01127504 A CN01127504 A CN 01127504A CN 1150283 C CN1150283 C CN 1150283C
- Authority
- CN
- China
- Prior art keywords
- powder
- putty
- fiber
- cracking
- frostproofer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种抗裂外墙腻子,含有带橡胶弹性的聚丙烯酸酯乳液20%~35%、氧化锌或白碳黑2%~5%、纤维3%~5%以及适量的增稠剂、分散稳定剂。还含有金红石型钛白粉5%~10%、石英粉20%~30%、双飞粉10%~15%、滑石粉10%~15%、水15%~20%。本发明具有弹性高,抗拉强度大,附着力强,具有较高的延伸率,能抵抗基层所产生的龟裂和细裂纹,在较潮湿环境下水汽易透出,不易起鼓和剥落。使用本发明抗裂外墙腻子所批刮的墙面,整体美观,无龟裂和泛碱现象。
Description
技术领域
本发明涉及一种涂料及其制备方法,特别是涉及一种外墙腻子及其制备方法。
背景技术
现有的外墙腻子多采用水泥腻子,其主要成分为107建筑胶和白水泥。这种水泥腻子在施工后经过半年甚至更短时间就会产生龟裂,从而使外墙表面布满裂纹,不仅影响了外墙的美观,而且大大降低了外墙漆的保护作用,这是由于水泥本身的性质即抗压强度高但抗拉强度低决定的。另外使用水泥腻子,外墙表面易泛碱发花。现在也有用聚醋酸乙烯酯乳液或107建筑胶、老粉、双飞粉等做成的外墙腻子,但用这种腻子批刮的墙面见水易粉化、起鼓、剥落。
发明内容
本发明的目的是提供一种弹性好、附着力强的抗裂外墙腻子,使它在施工后不粉化、不起鼓、不剥落。
本发明的另一目的是提供一种制备上述外墙腻子的方法。
为达到上述目的,本发明采用如下技术方案:一种抗裂外墙腻子,含有下列组分,其配比为重量百分比: 带橡胶弹性的聚丙烯酸酯乳液20%~35%、氧化锌或白碳黑2%~5%、选自丙纶纤维、芳纶纤维或玻璃纤维的纤维3%~5%以及适量的选自碱溶丙烯酸乳液、羟乙基纤维素或羧甲基纤维素的增稠剂、选自六偏磷酸钠或聚甲基丙烯酸钠的分散稳定剂。
还含有金红石型钛白粉5%~10%、石英粉10%~20%、双飞粉10%~15%、滑石粉10%~15%、水15%~20%。
还含有适量的防霉剂和防冻剂。
增稠剂含量为0.2%~0.5%,分散稳定剂含量为0.2%~0.3%,防霉剂含量为0.1%~0.2%,防冻剂含量为1.5%~2%。
防霉剂采用五氯酚钠或百菌清或异噻唑酮类化合物,防冻剂采用乙二醇或丙二醇。
制备上述腻子的方法为:将上述重量配比的增稠剂、分散稳定剂、防霉剂、防冻剂和水加入搅拌机在高速搅拌下混合均匀后加入聚丙烯酸酯乳液,将其混合物加入捏合机,同时加入钛白粉、双飞粉、滑石粉、石英粉、氧化锌或白碳黑和纤维,经捏合机搅拌均匀,之后将上述混合物经三辊研磨机研磨、低速搅拌机搅拌成为纤维均匀分布的膏状体即可。
本发明采用了带橡胶弹性的聚丙烯酸酯乳液,由于该乳液干燥成膜后的延伸率可达500%~600%,从而使本发明具有弹性高,抗拉强度大,附着力强,具有较高的延伸率,能抵抗基层所产生的龟裂和细裂纹。由于加入了纤维,本发明外墙腻子干燥成膜后为纤维纵横交错均匀分布的细网格状,这样的结构不仅能显著提高本发明的抗拉强度和刚度,而且能减少收缩,提高热变形温度和低温冲击强度。同时纤维和石英粉的加入也增加了抗裂外墙腻子的透气性,使其在较潮湿环境下,水汽较易透出,不易起鼓和剥落。经测试,本发明外墙腻子抗老化性能优良,人工老化七周无裂纹,不变色,粘结性、弹性良好,同时水浸泡4~5天不粉化,不起鼓、不剥落。测试结果见表一。使用本发明抗裂外墙腻子所批刮的墙面,整体美观,无龟裂和泛碱现象,并且由于抗裂外墙腻子的保护作用,外墙面能显著抵抗雨水、紫外线的侵蚀,大大延长了使用寿命。
表一
1 | 在容器中的状态 | 经搅拌后呈均匀状态,无结块 |
2 | 施工性 | 刮涂无障碍 |
3 | 干燥时间 | ≤3小时 |
4 | 耐水性 | 48小时试验后,涂层无裂纹、起泡、剥落,无软化物析出 |
5 | 耐碱性 | 24小时试验后,涂层无裂纹、起泡、剥落,无软化物析出 |
6 | 粘结强度 | ≥0.60MPa |
7 | 初期干燥抗裂性 | 不出现裂纹 |
8 | 耐冻融性 | 10次冻融循环试验后,涂层无裂纹、起泡、剥落 |
9 | 柔韧性 | 直径50mm弯曲腻子表面无裂纹 |
具体实施方式
实施例1:按如下重量配料:
带橡胶弹性的聚丙烯酸酯乳液250kg、金红石型钛白粉80kg、双飞粉150kg、滑石粉100kg、石英粉200kg、白碳黑20kg、丙纶纤维30kg、水150kg、羟乙基纤维素2kg、六偏磷酸钠2kg、五氯酚钠1kg、乙二醇15kg。
将上述重量的羟乙基纤维素、六偏磷酸钠、五氯酚钠、乙二醇和水加入搅拌机在高速搅拌下混合均匀后加入带橡胶弹性的聚丙烯酸酯乳液,将其混合物加入捏合机,同时加入钛白粉、双飞粉、滑石粉、石英粉、白碳黑和丙纶纤维,经捏合机搅拌均匀,之后将上述混合物经三辊研磨机研磨、经低速搅拌机搅拌成为均匀膏状体即可。
实施例2:按如下重量配料:
带橡胶弹性的聚丙烯酸酯乳液350kg、金红石型钛白粉50kg、双飞粉100kg、滑石粉100kg、石英粉100kg、氧化锌50kg、芳纶纤维50kg、水170kg、羧甲基纤维素5kg、聚甲基丙烯酸钠3kg、百菌清2kg、丙二醇20kg。
将上述重量的羧甲基纤维素、聚甲基丙烯酸钠、百菌清、丙二醇和水加入搅拌机在高速搅拌下混合均匀后加入带橡胶弹性的聚丙烯酸酯乳液,将其混合物加入捏合机,同时加入钛白粉、双飞粉、滑石粉、石英粉、氧化锌和芳纶纤维,经捏合机搅拌均匀,之后将上述混合物经三辊研磨机研磨、经低速搅拌机搅拌成为均匀膏状体即可。
实施例3:按如下重量配料:
带橡胶弹性的聚丙烯酸酯乳液200kg、金红石型钛白粉100kg、双飞粉120kg、滑石粉150kg、石英粉130kg、氧化锌40kg、玻璃纤维40kg、水200kg、碱溶丙烯酸乳液(氨水中和后)2kg、聚甲基丙烯酸钠2kg、异噻唑酮类化合物1kg、乙二醇15kg。
将上述重量的碱溶丙烯酸乳液(氨水中和后)、聚甲基丙烯酸钠、异噻唑酮类化合物、乙二醇和水加入搅拌机在高速搅拌下混合均匀后加入带橡胶弹性的聚丙烯酸酯乳液,将其混合物加入捏合机,同时加入钛白粉、双飞粉、滑石粉、石英粉、氧化锌和玻璃纤维,经捏合机搅拌均匀,之后将上述混合物经三辊研磨机研磨、低速搅拌机搅拌成为均匀膏状体即可。
上述实施例中的石英粉的细度最好在80目~120目之间,纤维长度为1~2cm。带橡胶弹性的聚丙烯酸酯乳液可采用市售的BA163纯丙乳液或BA154纯丙乳液。
Claims (6)
1、一种抗裂外墙腻子,其特征在于,含有下列组分,其配比为重量百分比:带橡胶弹性的聚丙烯酸酯乳液20%~35%、氧化锌或白碳黑2%~5%、选自丙纶纤维、芳纶纤维或玻璃纤维的纤维3%~5%以及适量的选自碱溶丙烯酸乳液、羟乙基纤维素或羧甲基纤维素的增稠剂、选自六偏磷酸钠或聚甲基丙烯酸钠的分散稳定剂。
2、如权利要求1所述的外墙腻子,其特征在于,还含有金红石型钛白粉5%~10%、石英粉10%~20%、双飞粉10%~15%、滑石粉10%~15%、水15%~20%。
3、如权利要求1或2所述的外墙腻子,其特征在于,还含有适量的防霉剂和防冻剂。
4、如权利要求3所述的外墙腻子,其特征在于,增稠剂含量为0.2%~0.5%,分散稳定剂含量为0.2%~0.3%,防霉剂含量为0.1%~0.2%,防冻剂含量为1.5%~2%。
5、如权利要求4所述的外墙腻子,其特征在于,防霉剂采用五氯酚钠或百菌清或异噻唑酮类化合物,防冻剂采用乙二醇或丙二醇。
6、一种制备权利要求3,4或5所述抗裂外墙腻子的方法,其特征在于,将上述重量配比的增稠剂、分散稳定剂、防霉剂、防冻剂和水加入搅拌机在高速搅拌下混合均匀后加入带橡胶弹性的聚丙烯酸酯乳液,将其混合物加入捏合机,同时加入钛白粉、双飞粉、滑石粉、石英粉、氧化锌或白碳黑和纤维,经捏合机搅拌均匀,之后将上述混合物经三辊研磨机研磨、低速搅拌机搅拌成为纤维均匀分布的膏状体即可。