CN1147426C - Process for preparation of self-spread high-temp. synthesizing ferro-silicon nitride powder - Google Patents
Process for preparation of self-spread high-temp. synthesizing ferro-silicon nitride powderInfo
- Publication number
- CN1147426C CN1147426C CNB001168037A CN00116803A CN1147426C CN 1147426 C CN1147426 C CN 1147426C CN B001168037 A CNB001168037 A CN B001168037A CN 00116803 A CN00116803 A CN 00116803A CN 1147426 C CN1147426 C CN 1147426C
- Authority
- CN
- China
- Prior art keywords
- powder
- silicon nitride
- ferro
- ferrosilicon
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a preparing method of synthesizing silicon iron nitride powder by self spread and at a high temperature, which belongs to the preparing field of non-oxide superfine powder. In the present invention, metallic silicon iron powder and silicon iron nitride powder are mixed according the proportion of 1 to 10:1 to 6, or silicon iron powder, metallic silicon powder and the silicon iron nitride powder are mixed according to the proportion of 1 to 10:1 to 6:1 to 6, an additive agent is added, and 3 to 15MPas nitrogen gas is led. The solid additive agent is an aminium salt (NH4Cl, or NH4F, or the mixture of the NH4Cl and the NH4F), and the adding amount is from 1 to 10 wt%. The present invention is characterized in that prebriquetting operation is not needed; reaction is carried out in an upstanding circular cylinder made of carbon felt and a disk-shaped container; the added additive agent is favorable for reducing reaction speed, can reduce the impurity content of the whole reaction system, and prompts the structure of a combustion product to be loose.
Description
The present invention relates to the preparation method of ferro-silicon nitride powder, particularly with self propagating high temperature synthetic (SHS) preparation ferro-silicon nitride powder.Belong to non-oxidized substance ultrafine powder preparation field.
Essential substance in the ferro-silicon nitride is a silicon nitride, and principal crystalline phase is the β phase, accounts for 72~80wt%, silicone content 49~53wt% wherein, and nitrogen content 29~32wt%, iron level 11~14wt%, color is a canescence.
The ferro-silicon nitride material has good resistance to fouling to fusion Al, Pb, Sn, Zn, Bi, and fusion Mg, Cu, Ni are also had resistance to fouling preferably.To Cl
2, H
2S, HCl, H
2SO
4, HNO
3, H
2P
2O
7Good erosion resistance is arranged, but easily corroded by HF and NaOH.
Ferro-silicon nitride can improve the hot strength and the oxidation-resistance of silicon carbide refractory material as structured material and oxidation-resistant material.Simultaneously, mix with other refractory materials, be equipped with suitable tackiness agent, can make the refractory materials of anti-molten metal excellent property when it.
During as coating and mold material use, the castings surface is good, improves mould life.
Owing to high nitrogenous rate is arranged, thereby it is the good additives of various nitrogenous corrosion resistant alloy materials again.In addition, ferro-silicon nitride also is applied in high-temperature structural material, high temperature electric material, humidifying appliance material etc.So far, the preparation method of ferro-silicon nitride powder is mainly ferrosilicon powder and the long-time nitrogenize of silica flour high temperature in nitrogen." manufacture method of ferro-silicon nitride " (the clear 58-151311) that steps on etc. people's invention as Japanese mountain bank is in perpendicular type nitriding furnace, metallic silicon power and ferrosilicon are placed on the top of stove, give in the stove and supply with nitrogen, heat to it from the body of heater bottom then, obtain ferro-silicon nitride in the body of heater bottom at last.Furnace temperature remains on more than 800 ℃ and keeps.Raw material is a kind of in powdery, granular or their mixture.
Japan adds " ferro-silicon nitride and preparation method thereof " (flat 8-59216) of people such as He Tiefu invention, be to be raw material with metallic silicon power, ferrosilicon powder, under nitrogen atmosphere, temperature is between 1000~1400 ℃, temperature rise rate is higher than 10 ℃/hour, descends nitrogenize to generate ferro-silicon nitride for a long time.
Preceding two kinds of technologies and improved method thereof can obtain the silicon nitride iron powder, need consume the more energy but common drawback is a production process.The preparation of ferro-silicon nitride at present mainly obtain by ferrosilicon long-time nitrogenize in nitrogen, so these production method energy consumptions is higher, and to obtain the silicon nitride of high β phase in the product, nitrogenize for a long time, and nitriding temperature is very high, so energy consumption is very big.
Synthetic (SHS) method of self propagating high temperature is the mid-1960s a kind of new preparation process newly developed, advantages such as technology is simple, energy consumption is low, product purity is high, less investment that it has.So far not useful as yet SHS method prepares the report of ferro-silicon nitride powder.
The objective of the invention is to utilize the self propagating high temperature synthetic method, change its processing parameter, provide a kind of easy, quick, energy-conservation, prepare the method for ferro-silicon nitride powder efficiently.
At first, use 75 ferrosilicon to come synthesizing silicon nitride iron, maximum difficulty is how to control the content of iron in the product in suitable scope, 75 ferrosilicon nitrogenizing reactions do not resemble strong exothermal reactions such as titanium, aluminium nitrogenize, it belongs to the thermopositive reaction of medium tenacity, therefore temperature of combustion is lower, and the iron contamination volatilization is less during combustion reactions.Must in raw material, add silica flour for this reason.And ammonium salt, NH
4Cl and NH
4F, or the interpolation of both mixtures make iron when building-up reactions, and the halogenide that generates iron vapors away, and can reduce the addition of silica flour so effectively or not add silica flour, thereby can reduce production costs effectively.
Secondly, ammonium salt (NH
4Cl and NH
4F) or the interpolation of both mixtures, also can reduce the addition of ferro-silicon nitride thinner and crystal seed effectively, when not adding the ammonium salt additive, the ratio of ferrosilicon and ferro-silicon nitride is 10: 4, and after having added the ammonium salt additive, the ratio of ferrosilicon and ferro-silicon nitride dropped to 10: 3, can increase the output of the finished product like this, raised the efficiency.
The 3rd, the main raw material that the present invention adopts is ferrosilicon powder, metallic silicon power and silicon nitride iron powder, and granularity is respectively 0.5~40 μ m, 0.3~30 μ m and 0.3~40 μ m, and the size range of broad can effectively reduce cost;
The 4th, with 3~15MPa high pressure nitrogen as nitridation source, for nitrogenize furnishes ample material;
The 5th, can be with ammonium salt (NH
4Cl and NH
4F) or both mixtures be additive, also reduce other impurity in the reactant and impel the products of combustion short texture.
Concrete preparation method be with ferrosilicon powder, silicon nitride iron powder by a certain percentage (both ratios are 1~10: 1~6) or ferrosilicon powder, silica flour and silicon nitride iron powder (three's ratio is 1~10: 1~6: after 1~6) mixing, with ammonium salt NH by a certain percentage
4Cl, NH
4F or their mixture NH
4Cl: NH
4F=1: 1 (weight ratio) additive mixes, and the add-on of additive is 1~10wt% of ferrosilicon powder and ferro-silicon nitride powder weight, or is the 1~10wt% (can also without additive) of ferrosilicon powder, silica flour and ferro-silicon nitride powder weight.Pine is loaded in the upright ring-type tube or disc shaped container of carbon felt, and is synthetic through the igniting self propagating high temperature in high pressure vessel then, can generate required silicon nitride iron powder after the cooling.
What provide in high pressure vessel provided by the invention and the general SHS method is similar, need not particular requirement, only is that reactant and additive are behind the uniform mixing or behind the uniform mixing of reactant own, with 2.3~3.0kg/cm
3Loose density is placed in the upright ring-type tube and disc shaped container of carbon felt, and their shape figure is respectively shown in Fig. 1-1,1-2.1 is the tungsten filament heating element among the figure, and 2 is priming mixture, and 3 is that reactant 4 is carbon felt container, and Fig. 1-1 is upright ring-type, and Fig. 1-2 is a disc shaped container.Naturally cooling is adopted in the synthetic back of self propagating high temperature.
Obviously, the present invention has overcome the shortcoming that above-mentioned two patents exist, and has had following advantage by process modification:
(1) energy consumption is low, does not need any energy except that starting combustion synthesis reaction;
(2) do not need specific installation;
(3) output is big, the efficient height;
(4) additive that adds had both helped slowed down reaction speed and can reduce the usage quantity of silica flour and ferro-silicon nitride effectively, and iron level is kept within the specific limits, also can reduce the content of other impurity in the whole reaction system simultaneously.
Further illustrate progress of invention essence and innovative point of the present invention below by embodiment.
Performance by the ferro-silicon nitride powder of present embodiment preparation is listed in table 1.
The salient features of the silicon nitride iron powder of table 1 the present invention preparation
Claims (10)
1. the synthetic method for preparing the ferro-silicon nitride powder of self propagating high temperature comprises batching, mixing, nitrogenize, it is characterized in that:
(1) in ferrosilicon powder: silicon nitride iron powder=1~10: 1~6 ratio batching or ferrosilicon powder: silica flour: silicon nitride iron powder=1~10: 1~6: 1~6 ratio batching, be loaded on the powder type pine in the upright ring-type tube or disc shaped container of carbon felt, carry out self propagating high temperature in the high pressure vessel of packing into then and synthesize;
(2) Fan Ying high pressure nitrogen is 3~15MPa;
(3) naturally cooling is adopted in the synthetic back of self propagating high temperature.
2. by the described ferro-silicon nitride powder preparation method of claim 1, it is characterized in that described ferrosilicon powder granularity particle size range is 0.5~40 μ m, the particle size range of ferro-silicon nitride is 0.3~40 μ m, and the particle size range of silica flour is 0.3~30 μ m.
3. by the described ferro-silicon nitride powder preparation method of claim 1, it is characterized in that the mixture pine of silica flour and silicon nitride iron powder is loaded in the upright ring-type tube or disc shaped container of carbon felt, loose density is 2.3~3.0g/cm
3
4. by the described ferro-silicon nitride powder preparation method of claim 1, it is characterized in that:
(1) ferrosilicon powder: silicon nitride iron powder=10: 4 (weight ratio);
(2) the powder pine is loaded in the upright ring-type tube of carbon felt after mixing, and loose density is 2.70g/cm
3
(3) Fan Ying high pressure nitrogen pressure is 3~15MPa;
(4) the synthetic back of self propagating high temperature naturally cooling.
5. by the described ferro-silicon nitride powder preparation method of claim 1, it is characterized in that:
(1) ferrosilicon powder: silica flour: silicon nitride iron powder=10: 3: 3 (weight ratio);
(2) the powder pine is loaded in the upright ring-type tube of carbon felt after mixing, and loose density is 2.52g/cm
3
(3) Fan Ying high pressure nitrogen pressure is 3~15MPa;
(4) the synthetic back of self propagating high temperature naturally cooling.
6. the synthetic method for preparing the ferro-silicon nitride powder of self propagating high temperature comprises additive use, batching, mixing, nitrogenize, it is characterized in that:
(1) in ferrosilicon powder: silica flour=1~10: 1~6 ratio batching or ferrosilicon powder: silica flour: silicon nitride iron powder=1~10: 1~6: 1~6 ratio batching, then with the solid additive uniform mixing after, be loaded on the powder type pine in the upright ring-type tube or disc shaped container of carbon felt, carry out the self propagating high temperature building-up reactions in the high pressure vessel of packing into then;
(2) solid additive is NH
4F, NH
4Cl or their mixture, NH
4F: NH
4Cl=1: 1 (weight ratio), add-on are 1~10wt% of silica flour, ferrosilicon and ferro-silicon nitride weight, or are 1~10wt% of ferrosilicon and ferro-silicon nitride weight;
(3) Fan Ying high pressure nitrogen is 3~15MPa;
(4) naturally cooling is adopted in the synthetic back of self propagating high temperature.
7. by the described ferro-silicon nitride powder preparation method of claim 6, it is characterized in that described ferrosilicon powder granularity particle size range is 0.5~40 μ m, the particle size range of ferro-silicon nitride is 0.3~40 μ m, and the particle size range of silica flour is 0.3~30 μ m.
8. by the described ferro-silicon nitride powder preparation method of claim 6, it is characterized in that the mixture pine of silica flour and silicon nitride iron powder and solid additive is loaded in the upright ring-type tube or disc shaped container of carbon felt, loose density is 2.3~3.0g/cm
3
9. by the described ferro-silicon nitride powder preparation method of claim 6, it is characterized in that:
(1) ferrosilicon powder: silica flour=10: 3 (weight ratio);
(2) solid additive is ammonium salt NH
4Cl, add-on is 2wt%;
(3) the powder pine is loaded in the disc shaped container of carbon felt after mixing, and loose density is 2.67g/cm
3
(4) Fan Ying high pressure nitrogen pressure is 3~15MPa;
(5) the synthetic back of self propagating high temperature naturally cooling.
10. by the described ferro-silicon nitride powder preparation method of claim 6, it is characterized in that
(1) ferrosilicon powder: silicon nitride iron powder=10: 3 (weight ratio);
(2) solid additive is ammonium salt NH
4Cl and NH
4F, add-on is 2wt%, wherein NH
4F: NH
4Cl=1: 1 (weight ratio);
(3) the powder pine is loaded in the upright ring-type tube and disc shaped container of carbon felt after mixing, and loose density is 2.61g/cm
3
(4) Fan Ying high pressure nitrogen pressure is 3~15MPa;
(5) the synthetic back of self propagating high temperature naturally cooling.