CN114712262A - 一种含有可迁移型透明质酸盐的纸巾与整理液组合物 - Google Patents
一种含有可迁移型透明质酸盐的纸巾与整理液组合物 Download PDFInfo
- Publication number
- CN114712262A CN114712262A CN202210270157.0A CN202210270157A CN114712262A CN 114712262 A CN114712262 A CN 114712262A CN 202210270157 A CN202210270157 A CN 202210270157A CN 114712262 A CN114712262 A CN 114712262A
- Authority
- CN
- China
- Prior art keywords
- hyaluronic acid
- hydrocarbon
- salt
- composition
- paper towel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有透明质酸或其盐的纸巾,所述纸巾包含透明质酸或其盐和疏水性物质的组合物,通过将疏水性物质与透明质酸或其盐相组合,可以显著提高透明质酸在纸巾摩擦过程中的迁移性。
Description
技术领域
本发明涉及纸品制备技术领域,尤其涉及一种含有可迁移型透明质酸盐的纸巾与整理液组合物。
背景技术
透明质酸钠(HA,又称玻尿酸,或透明质酸)是一种天然保湿成分,已被广泛应用于药品和个人健康消费品中。近年来,消费品市场又出现了玻尿酸纸巾,意在添加HA,提升纸巾的护肤性。
然而,由于HA分子存在大量的羟基和羧基,HA可与纸巾的纤维素形成强烈的氢键。因此,在纸巾与皮肤摩擦过程中,HA难以从纸巾表面迁移到皮肤表面,从而也就很难实现HA的护肤效果。
发明内容
为了解决上述问题,本发明提供了一种整理液组合物以及含有透明质酸或其盐的纸巾,所述整理液组合物通过将疏水性物质与HA组合,添加在纸巾表面,能够显著提升HA在纸巾摩擦过程中的迁移性。
本发明具体技术方案如下:
1.一种整理液组合物,其包含透明质酸或其盐和疏水性物质。
2.根据项1所述的组合物,其中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。
3.根据项2所述的组合物,其中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。
4.根据项2或3所述的组合物,其中,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
5.根据权利要求1-4中任一项所述的组合物,其中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
6.根据项1-4中任一项所述的组合物,其中,所述透明质酸或其盐为交联的透明质酸或其盐。
7.根据项1-6中任一项所述的组合物,其中,所述整理液组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自硬脂酰谷氨酸钠、月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
8.根据项1-7中任一项所述的组合物,其中,以在组合物中所占的质量百分比计,所述透明质酸或其盐为0.01-0.5%,优选为0.1-0.2%;
优选的,所述疏水性物质为0.5-25%,进一步优选为5-20%。
9.根据项1-8中任一项所述的组合物,其中,所述组合物还包含甘油和水溶性活性成分,优选的,所述水溶性活性成分选自依克多因、麦角硫因、γ-氨基丁酸、氨基酸和蛋白质中的一种或两种以上。
10.项1-9中任一项所述的组合物在纸品中的用途。
11.一种纸巾,其包含透明质酸或其盐和疏水性物质的组合物。
12.根据项11所述的纸巾,其中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。
13.根据项12所述的纸巾,其中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。
14.根据项12或13所述的纸巾,其中,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
15.根据项11-14中任一项所述的纸巾,其中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
16.根据项11-14中任一项所述的纸巾,其中,所述透明质酸或其盐为交联的透明质酸或其盐。
17.根据项11-16中任一项所述的纸巾,其中,所述组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自硬脂酰谷氨酸钠、月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
18.根据项11-17中任一项所述的纸巾,其中,所述透明质酸或其盐在纸巾中的含量为5-5000ppm,优选为300-900ppm,进一步优选为300-500ppm。
19.根据项11-18中任一项所述的纸巾,其中,所述疏水性物质在纸巾中的含量为0.1-6%,优选为2-5%。
20.根据项11-19中任一项所述的纸巾,其中,所述组合物还包含甘油和水溶性活性成分,优选的,所述水溶性活性成分选自依克多因、麦角硫因、γ-氨基丁酸、氨基酸和蛋白质中的一种或两种以上。
21.根据项11-20中任一项所述的纸巾,其中,所述透明质酸或其盐的迁移率≥1%,优选≥5%。
22.根据项11-21中任一项所述的纸巾,其中,所述纸巾中含有纤维素纤维,优选的,所述纤维素纤维的含量≥50%。
发明的效果
本发明所述的整理液组合物,通过将疏水性物质与HA组合,将其涂布在纸巾上,可以显著提升HA在纸巾摩擦过程中的迁移性。
附图说明
图1是进行涂布的流程图。
图2是测定仿皮中HA的流程图,其中,图2A是将纸巾固定于正方体重块上的示意图,图2B是摩擦迁移测试方法的示意图。
其中,1-纸巾基材,2-第一导辊,3-第二导辊,4-第三导辊,5-第四导辊,6-挤压辊,7-转移辊,8-浸渍辊,9-料槽,10-第五导辊,11-涂布后纸巾
具体实施方式
下面结合附图所描述的实施方式对本发明做以详细说明,其中所有附图中相同的数字表示相同的特征。虽然附图中显示了本发明的具体实施例,然而应当理解,可以以各种形式实现本发明而不应被这里阐述的实施例所限制。相反,提供这些实施例是为了能够更透彻地理解本发明,并且能够将本发明的范围完整的传达给本领域的技术人员。
需要说明的是,在说明书及权利要求当中使用了某些词汇来指称特定组件。本领域技术人员应可以理解,技术人员可能会用不同名词来称呼同一个组件。本说明书及权利要求并不以名词的差异作为区分组件的方式,而是以组件在功能上的差异作为区分的准则。如在通篇说明书及权利要求当中所提及的“包含”或“包括”为开放式用语,故应解释成“包含但不限定于”。说明书后续描述为实施本发明的较佳实施方式,然而所述描述乃以说明书的一般原则为目的,并非用以限定本发明的范围。本发明的保护范围当视所附权利要求所界定者为准。
本发明提供了一种纸巾,其包含透明质酸或其盐和疏水性物质的组合物。
现有纸巾中加入透明质酸意在提升纸巾的护肤性,但是,由于透明质酸分子中存在大量的羟基和羧基,透明质酸可与纸巾的纤维素形成强烈的氢键。因此,在纸巾与皮肤摩擦过程中,透明质酸难以从纸巾表面迁移到皮肤表面,从而也就很难实现透明质酸的护肤效果,本发明通过在纸巾中加入含有透明质酸和疏水性物质的组合物,疏水性物质通过降低透明质酸和纸巾纤维间的氢键,从而显著提升透明质酸在纸巾摩擦过程中的迁移性,透明质酸在纸巾的迁移率在1%以上,优选在5%以上。
在一些实施方式中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物,优选的,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂;优选的,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
所述酯蜡指的是由长链的高级脂肪酸和高级脂肪醇所形成的酯,可包括天然形成的以及人工合成的,比如,霍霍巴油、霍霍巴酯的主要成分是天然形成的酯蜡。
所述烃类物质指的仅含有碳和氢元素所组成的化学物质,在常温呈现液体或半固体的蜡状;所述非烃类物质在常温下同样呈现液体或半固体的蜡状,并且分子结构中包含碳和氢以外的元素,比如氧、硅、硫等,例如,甘油三脂,甘油二酯,甘油单酯,酯蜡,硅油,以及其混合物等。
例如,所述烃类物质的碳原子数为10、20、30、40、50、60或其之间的任意自然数。
角鲨烷的碳原子数为30,矿物油的碳原子数为12-24,矿脂的碳原子数为28-52。
本发明使用上述所述的疏水性物质与透明质酸以及乳化剂进行混合,涂布在纸巾表面,能够提供透明质酸在纸巾摩擦过程中的迁移性。
在一些实施方式中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
在一些实施方式中,所述透明质酸或其盐为交联的透明质酸或其盐。
所述交联的透明质酸或其盐指的是透明质酸或其盐在化学修饰以后构成的一种衍生物,通过交联剂进行修饰后将线性的透明质酸分子连接成空间网络结构。
所述透明质酸的盐指的是透明质酸的金属盐,例如可以为透明质酸钠、透明质酸镁、透明质酸锌等,优选为透明质酸钠。
例如,所述透明质酸或其盐的分子量可以为1wDa、5wDa、10wDa、20wDa、30wDa、40wDa、50wDa、60wDa、70wDa、80wDa、90wDa、100wDa、110wDa、120wDa、130wDa、140wDa、150wDa等。
在一些实施方式中,所述组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
在一些实施方式中,所述透明质酸或其盐在纸巾中的含量为5-5000ppm,优选为300-900ppm,进一步优选为300-500ppm。
对于透明质酸或其盐在纸巾中的含量测定,其可以按照CN109298112A公开的方法进行测定。
例如,所述透明质酸或其盐在纸巾中的含量可以为5ppm、10ppm、20ppm、30ppm、40ppm、50ppm、100ppm、200ppm、300ppm、400ppm、500ppm、600ppm、700ppm、800ppm、900ppm、1000ppm、2000ppm、3000ppm、4000ppm、5000ppm等。
在一些实施方式中,所述疏水性物质在纸巾中的含量为0.1-6%,优选为2-5%。
对于所述疏水性物质在纸巾中的含量测定,其可以按照化学纤维含油率的国标测量方法GB/T 6504,但在此方法中,将对纤维的操作,变成对纸巾的操作:可先用有机溶剂,比如异丙醇或丙酮,对纸巾上疏水性物质进行萃取,再对萃取液进行液相色谱与质谱联用的方法进行测定。
例如,所述疏水性物质在纸巾中的含量可以为0.1%、0.5%、1%、2%、3%、4%、5%、6%等。
对于乳化剂在纸巾中的含量,本发明不作任何限制,本领域技术人员可以根据需要进行选择,例如,乳化剂在纸巾中的含量可以为0.2-2%。
在一些实施方式中,所述组合物还包含甘油。
对于甘油在纸巾中的含量,本发明不作任何限制,其可以根据需要进行选择,例如,甘油在纸巾中的含量可以为0.1-20%。
所述甘油可以提升纸巾柔软度的手感。
在一些实施方式中,所述组合物还包含水溶性活性成分,优选的,所述水溶性活性成分选自依克多因、麦角硫因、γ-氨基丁酸、氨基酸和蛋白质中的一种或两种以上。
对于水溶性活性成分在纸巾中的含量,本发明不作任何限制,其可以根据需要进行选择。
所述水溶性活性成分可以增加纸巾的护肤性能。
在一些实施方式中,所述透明质酸或其盐的迁移率≥1%,优选≥5%。
所述迁移率指的是在摩擦测试过程中,HA迁移到仿皮上的效率,其计算公式如下:
迁移率=摩擦后仿皮上的HA量/摩擦前正方体接触面上纸巾的HA含量。
在一些实施方式中,所述纸巾中含有纤维素纤维,优选的,所述纤维素纤维的含量≥50%。
所述纸巾指的纸巾基材,例如可以使用中顺洁柔的纸巾基材。
在一些实施方式中,所述纸巾包含透明质酸或其盐和疏水性物质的组合物。在一些实施方式中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。
在一些实施方式中,所述纸巾包含透明质酸或其盐和疏水性物质的组合物。在一些实施方式中,所述疏水性物质为油脂或蜡,优选的,所述油脂为烃类物质或者烃类物质与非烃类物质的混合物。在一些实施方式中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。
在一些实施方式中,所述纸巾包含透明质酸或其盐和疏水性物质的组合物。在一些实施方式中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。在一些实施方式中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。在一些实施方式中,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
在一些实施方式中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
在一些实施方式中,所述透明质酸或其盐为交联的透明质酸或其盐。
在一些实施方式中,所述组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自硬脂酰谷氨酸钠、月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
在一些实施方式中,所述透明质酸或其盐在整理液中的含量为0.01-0.5%,优选为0.1-0.2%。
在一些实施方式中,所述疏水性物质在整理液中的含量为0.5-25%,优选为5-20%。
在一些实施方式中,所述透明质酸或其盐在纸巾中的含量为5-5000ppm,优选为300-900ppm,进一步优选为300-500ppm。
在一些实施方式中,所述疏水性物质在纸巾中的含量为0.1-6%,优选为2-5%。
在一些实施方式中,所述组合物还包含甘油。
在一些实施方式中,所述组合物还包含水溶性活性成分,优选的,所述水溶性活性成分选自依克多因、麦角硫因、γ-氨基丁酸、氨基酸和蛋白质中的一种或两种以上。
在一些实施方式中,所述透明质酸或其盐的迁移率≥1%,优选≥5%。
本发明提供了一种整理液组合物,其包含透明质酸或其盐和疏水性物质。
本发明将整理液组合物涂布在纸巾上,疏水性物质能够降低透明质酸和纸巾纤维素间的氢键,从而可以显著提升透明质酸在纸巾摩擦过程中的迁移性。
对于涂布方法,本发明不作任何限制,本领域技术人员可以根据需要进行选择,例如,可以采用辊涂的方法进行涂布,例如将整理液置于料槽中,其中料槽具有加热功能,将整理液温度控制在60~80℃,浸渍辊部分浸渍在料槽的整理液中,通过顺时针旋转,将整理液带起;
转移辊逆时针旋转,并且通过与浸渍辊的接触,将整理液均匀地铺展于转移辊的表面;纸巾基材从挤压辊与转移辊中间通过,其中转移辊逆时针旋转,挤压辊顺时针旋转,从而将整理液均匀地涂布在纸巾表面。
对于涂布在纸巾中的涂布量,本发明不作任何限制,本领域技术人员可以根据需要进行选择,在本发明中,使用的涂布量为30%,其计算公式为W2–W1/W1*100%。其中,W1为纸巾基材的原始质量,W2为涂布后纸巾的含水总质量。
在一些实施方式中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。在一些实施方式中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。在一些实施方式中,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
例如,所述烃类物质的碳原子数为10、20、30、40、50、60或其之间的任意自然数。
在一些实施方式中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
在一些实施方式中,所述透明质酸或其盐为交联的透明质酸或其盐。
例如,所述透明质酸的盐指的是透明质酸的金属盐,例如可以为透明质酸钠、透明质酸镁、透明质酸锌等,优选为透明质酸钠。
例如,所述透明质酸或其盐的分子量可以为1wDa、5wDa、10wDa、20wDa、30wDa、40wDa、50wDa、60wDa、70wDa、80wDa、90wDa、100wDa、110wDa、120wDa、130wDa、140wDa、150wDa等。
在一些实施方式中,所述整理液组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自硬脂酰谷氨酸钠、月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
在一些实施方式中,以在组合物中所占的质量百分比计,所述透明质酸或其盐为0.01-0.5%,优选为0.1-0.2%;
优选的,所述疏水性物质为0.5-25%,进一步优选为5-20%。
例如,以在组合物中所占的质量百分比计,所述透明质酸或其盐可以为0.01%、0.05%、0.1%、0.2%、0.3%、0.4%、0.5%或其之间的任意范围;
所述疏水性物质可以为0.5%、1%、2%、3%、4%、5%、6%、7%、8%、9%、10%、11%、23%、24%、25%或其之间的任意范围。
对于乳化剂在组合物中的含量,本发明不作任何限制,本领域技术人员可以根据需要进行选择,例如,乳化剂在组合物中的含量可以为0.5-10%。
在一些实施方式中,所述组合物还包含甘油。
对于甘油在组合物中的含量,本发明不作任何限制,其可以根据需要进行选择,例如,甘油在组合物中的含量可以为0.1-80%。
在一些实施方式中,所述组合物还包含水溶性活性成分,优选的,所述水溶性活性成分选自依克多因、麦角硫因、γ-氨基丁酸、氨基酸和蛋白质中的一种或两种以上。
对于水溶性活性成分在纸巾中的含量,本发明不作任何限制,其可以根据需要进行选择。
本发明将整理液组合物涂布在纸巾上,可以显著提高透明质酸在纸巾摩擦过程中的迁移性,透明质酸的迁移率在1%以上,优选在5%以上,进一步优选在10%以上,说明将本发明所述的整理液组合物涂布在纸巾,可以显著提高透明质酸的迁移率。
实施例
本发明对试验中所用到的材料以及试验方法进行一般性和/或具体的描述,在下面的实施例中,如果无其他特别的说明,%表示wt%,即重量百分数。所用试剂或仪器未注明生产厂商者,均为可以通过市购获得的常规试剂产品,其中,实施例和对比例中所述的原料来源如表1所示。
表1原料来源
其中,辛癸酸甘油酯为甘油三酯,碳原子数为21,椰子油为甘油三酯,碳原子数为39,棕榈油为甘油三酯,碳原子数为51,辛酸乙酯为甘油单酯,碳原子数为10,棕榈酸异辛酯为甘油单酯,碳原子数为24,霍霍巴油为甘油单酯,碳原子数为38-44。
实施例1
(1)将HA粉末与甘油预混,形成悬浮液RM-1;
(2)将乳化剂加入水中,加热至60℃搅拌至透明澄清溶液RM-2;
(3)将疏水性物质缓慢加入RM-2中进行搅拌,并且控制体系温度为60℃,形成乳液RM-3;
(4)将RM-1加入RM-3中,控制体系温度为60℃,均质混合30min,形成最终的整理液,其中,各种组分的含量如表2中的编号C1-C22所示,余量为水。
对比例1
按照与实施例1相同的方法进行制备,各种组分的含量如表2中的编号C23-C24所示。
表2各种组分的含量表
实施例2纸巾的制备
如图1所示,将实施例1所得到的整理液放在料槽9中,浸渍辊8部分浸渍在料槽9的整理液中使其温度保持在60-80℃,通过顺时针旋转,将整理液带起,转移辊7逆时针旋转,并且通过与浸渍辊8的接触,将整理液均匀地铺展于转移辊7的表面,纸巾基材1通过第一导辊2、第二导辊3和挤压辊6接触,从而在纸巾基材上涂布整理液,涂布量为30%,涂布量的计算公式为:W2–W1/W1*100%,其中,W1为纸巾基材的原始质量,W2为涂布后纸巾的含水总质量,所得到的纸巾的编号为Nap1-Nap22,各个组分的含量如表3所示。
其中,HA的测定方法按照CN109298112A公开的方法进行测定;
疏水性物质的测定方法按照化学纤维含油率的国标测量方法GB/T 6504,但在此方法中,将对纤维的操作,变成对纸巾的操作:可先用有机溶剂,比如异丙醇或丙酮,对纸巾上疏水性物质进行萃取,再对萃取液进行液相色谱与质谱联用的方法进行测量;
乳化剂和甘油的含量可以按照本领域常规的方法进行测量。
对比例2
采用与实施例2相同的方法使用对比例1所述的整理液组合物进行涂布,得到纸巾,其编号为Nap23-Nap24,各个组分的含量如表3所示。
表3纸巾中不同组分的含量表
实验例1透明质酸的迁移率的测定
实验材料:尺寸为5cm×12cm的硅胶仿皮、质量为300g尺寸为5cm×5cm正方体方块、量程为5N的拉力计以及皮筋。
操作方法:
1)用去离子水清洗仿皮表面后,室温晾干表面水分;
2)使用分析天平,精确记录仿皮的质量;
3)使用喷雾器,在仿皮表面均匀喷0.1g去离子水;
4)用酒精将实验桌面擦干净,将5cm×12cm的硅胶仿皮固定于光滑的水平桌面上;
5)将编号为Nap1-Nap24的纸巾固定于正方体重块一面,并将固定有纸巾的那一面置于仿皮正上方,正方体重块重心与仿皮一端竖直方向对齐,重物的边与仿皮边缘对齐,如图2A和图2B所示;
6)使用拉力计水平匀速拖动重块,直到拖动重块重心至仿皮末端结束,如此重复5次;
7)将仿皮剪成小碎块,置于窄口玻璃瓶中,检测仿皮中HA的含量;
8)计算HA从纸巾到仿皮中的迁移率,其结果如表4所示,其中,迁移率的计算公式为:
迁移率=摩擦测试后仿皮中HA量/摩擦测试前正方体接触面积上纸巾的HA含量
仿皮中HA含量检测方法如下:
(1)试剂以及材料:
磷酸二氢钠(国药基团化学试剂有限公司)、磷酸氢二钠(国药基团化学试剂有限公司)、磷酸(国药基团化学试剂有限公司)、透明质酸对照品(华熙生物科技股份有限公司)和透明质酸酶(华熙生物科技股份有限公司)
(2)色谱条件
色谱柱:MCI GEL CK08EH色谱柱(8×300mm,9μm),流动相:1%磷酸;流速:0.6ml/min;进样量:20μL;柱温:40℃;检测波长:232nm
(3)溶液配制
A)酶解缓冲液:
称取磷酸二氢钠(NaH2PO4·2H2O)27.4g、磷酸氢二钠(Na2HPO4·12H2O)8.8g置1000mL容量瓶中,加水稀释至刻度,摇匀,得0.2mol/L NaH2PO4-Na2HPO4缓冲液,将该缓冲液稀释40倍后得到酶解缓冲液(5mM/L NaH2PO4-Na2HPO4缓冲液,pH6.0)
B)对照溶液:
精密称取透明质酸钠对照品约50mg于50mL容量瓶中,酶解缓冲液溶解并定容至刻度,混匀。取上述溶液0.5mL置于10mL容量瓶中,加入5mL酶解缓冲液和0.5mL透明质酸酶,混匀,密封,42℃酶解2h,煮沸2min使酶失活,酶解缓冲液定容至刻度,0.22μm滤膜过滤,即得对照品溶液。
C)固体供试品:
称取仿皮15-18g,置于窄口玻璃瓶中,精确记录仿皮质量,加入酶解缓冲液,缓冲液体积以能浸没仿皮为准,加入0.5mL透明质酸酶,混匀、密封,42℃酶解2h,煮沸2min使酶失活,酶解缓冲液定容至刻度,0.22μm滤膜过滤,即得供试品溶液,平行制备两份。
D)测定:
分别取对照品溶液和供试品溶液20μL进样,记录色谱图,按下式计算仿皮中HA的含量(μg/g)
式中:As为供试品溶液峰面积,Mr为对照品称样量(mg);Z为对照品含量;h%为对照品干燥失重;Vr为对照品溶液体积(mL);Ar为对照品溶液峰面积;M仿皮为仿皮的质量。
表4HA的迁移率
注:纸巾中透明质酸的迁移率达到5%以上认定是合格的,迁移率在5%以下达不到护肤效果。
以上所述,仅是本发明的较佳实施例而已,并非是对本发明作其它形式的限制,任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型,仍属于本发明技术方案的保护范围。
Claims (10)
1.一种整理液组合物,其包含透明质酸或其盐和疏水性物质。
2.根据权利要求1所述的组合物,其中,所述疏水性物质为油脂或蜡,优选的,所述油脂或蜡为烃类物质或者烃类物质与非烃类物质的混合物。
3.根据权利要求2所述的组合物,其中,所述烃类物质的碳原子数为10-60,优选为28-52,进一步优选的,所述烃类物质为角鲨烷、矿物油和/或矿脂,优选为矿脂。
4.根据权利要求2或3所述的组合物,其中,所述非烃类物质为植物来源、动物来源和/或人工合成的非烃类物质,优选的,所述非烃类物质选自甘油三酯、甘油二酯、甘油单酯、酯蜡和硅油中的一种或两种以上。
5.根据权利要求1-4中任一项所述的组合物,其中,所述透明质酸或其盐的分子量为1w-150wDa,优选为20w-80wDa。
6.根据权利要求1-4中任一项所述的组合物,其中,所述透明质酸或其盐为交联的透明质酸或其盐。
7.根据权利要求1-6中任一项所述的组合物,其中,所述整理液组合物还包含乳化剂,优选的,所述乳化剂为非离子或阴离子表面活性剂,优选的,所述非离子表面活性剂选自吐温-20、吐温-80、鲸蜡硬脂醇聚醚-6、鲸蜡硬脂醇聚醚-25、鲸蜡硬脂醇橄榄油酸酯和山梨坦橄榄油酸酯中的一种或两种以上,优选的,所述阴离子表面活性剂选自硬脂酰谷氨酸钠、月桂酸钠、十二烷基苯磺酸钠、十二烷基硫酸钠和油酸钠中的一种或两种以上。
8.根据权利要求1-7中任一项所述的组合物,其中,以在组合物中所占的质量百分比计,所述透明质酸或其盐为0.01-0.5%,优选为0.1-0.2%;
优选的,所述疏水性物质为0.5-25%,进一步优选为5-20%。
9.权利要求1-8中任一项所述的组合物在纸品中的用途。
10.一种纸巾,其包含透明质酸或其盐和疏水性物质的组合物。