CN114685154B - High-frequency wide-temperature ultralow-loss ferrite material and preparation process thereof - Google Patents

High-frequency wide-temperature ultralow-loss ferrite material and preparation process thereof Download PDF

Info

Publication number
CN114685154B
CN114685154B CN202210455385.5A CN202210455385A CN114685154B CN 114685154 B CN114685154 B CN 114685154B CN 202210455385 A CN202210455385 A CN 202210455385A CN 114685154 B CN114685154 B CN 114685154B
Authority
CN
China
Prior art keywords
temperature
ball milling
formula
main formula
ferrite material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202210455385.5A
Other languages
Chinese (zh)
Other versions
CN114685154A (en
Inventor
黄刚
廖继红
李崇华
刘海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Magnetic Electronic Technology Co ltd
Original Assignee
China Magnetic Electronic Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Magnetic Electronic Technology Co ltd filed Critical China Magnetic Electronic Technology Co ltd
Priority to CN202210455385.5A priority Critical patent/CN114685154B/en
Publication of CN114685154A publication Critical patent/CN114685154A/en
Application granted granted Critical
Publication of CN114685154B publication Critical patent/CN114685154B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a high-frequency wide-temperature ultralow-loss ferrite material which comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight: fe 2 O 3 70-72 mol%, mnO 20-22 mol%, znO 6-10 mol%, the total proportion of the main formula is 100mol%; relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows: caCO 3 1～1000PPM、SnO 2 100～300PPM、Co 2 O 3 50～80PPM、Bi 2 O 3 50-100 PPM nano SiO 2 50-100 PPM and CCTO 50-100 PPM. The invention aims to provide a ferrite material with high Bs value, high frequency, wide temperature and low loss.

Description

High-frequency wide-temperature ultralow-loss ferrite material and preparation process thereof
Technical Field
The invention relates to the technical field of soft magnetic ferrite cores, in particular to a high-frequency wide-temperature ultralow-loss ferrite material.
Background
At present, most of domestic enterprises engaged in ferrite material production are still in PC95 material level or below. The high-performance low-loss ferrite material products are fewer, and the performance difference with the foreign similar products is larger. As for the high-frequency low-loss material capable of being produced in quantity, the market blank is more, so that domestic autonomous power supply manufacturing industry can only produce low-end products, and high-end products depend on the high-frequency ferrite core material of imported foreign well-known enterprises. The situation seriously restricts the development of the electronic information industry in China. More seriously, in recent years, china is continuously subjected to scientific and technological sanctions abroad, and the science and technology sanctions from communication enterprises to scientific research colleges and research institutions all suffer from serious impact. Under such a large environment, the independent high-frequency wide-temperature ultralow-power-loss soft magnetic ferrite material in China is researched and developed, and the method has great significance for the development of the electronic information industry in China.
Therefore, it is necessary to develop an ultra-low loss ferrite material having a high Bs value and a low high frequency loss at a high frequency and a wide temperature.
Disclosure of Invention
The invention aims to provide a ferrite material with high Bs value, low high frequency loss, high width and low temperature and ultra-low loss.
The technical purpose of the invention is realized by the following technical scheme:
the high-frequency wide-temperature ultralow-loss ferrite material is characterized by comprising a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 70～72mol％
MnO 20～22mol％
ZnO 6～10mol％
the proportion of each main formula is 100mol%;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 1～1000PPM
SnO 2 100～300PPM
Co 2 O 3 50～80PPM
Bi 2 O 3 50～100PPM
nano SiO 2 2 50～100PPM
CCTO 50～100PPM。
By adopting the technical scheme, co is added into the adulterant formula of the invention 2 O 3 ，Co 2 O 3 The metal ions in the MnZn ferrite are doped with Fe which can replace the B site of the MnZn ferrite 3+ And Mn 3+ Therefore, the exchange effect of the A-B ultrasonic is increased, the heat resistance of the material is improved, the working temperature of the material is widened, the Curie temperature of the material is improved, the density of the sintered ferrite is also improved, and the saturation magnetic induction intensity of the material is effectively improved. And the CCTO is added in the doping formula, when the CCTO is adopted for doping to prepare the ferrite, the CCTO can be enriched in the crystal boundary of the MnZn power ferrite, and the speed of reducing the grain resistance along with the temperature can be slowed down due to the characteristic of high resistivity, so that the speed of increasing the high-frequency loss along with the temperature is slowed down, and the high-frequency loss and energy consumption of the material are effectively reduced.
As a further improvement of the invention, the dopant formula also comprises YBCO 10-50 PPM in percentage by weight.
By adopting the technical proposal, the utility model has the advantages that,Co 2 O 3 although the saturation flux density of the soft magnet can be improved during doping, the microstructure of the soft magnet is easy to grow discontinuously and the crystal is irregular, and bubbles are generated in each area inside the crystal, so that the initial permeability and the power loss performance of the material are influenced, therefore, when the added YBCO is sintered, the YBCO melting point is low, the YBCO can be preferentially melted and permeated, the connection force among crystal grains is improved, the crystal form of the material grows continuously, the generation of pores in the material is effectively reduced, the hysteresis loss of the material is effectively reduced, and the purpose of improving the connection force between Co and Co 2 O 3 The total power loss of the material is reduced under the condition that the guaranteed high Bs value of doping is high.
As a further improvement of the invention, the main formula comprises the following components in percentage by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
CCTO 80PPM
YBCO 30PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to a certain temperature in the air atmosphere, preserving the temperature for 1-3 h, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing CCTO and YBCO by stirring to form a mixture, adding polysiloxane into the mixture, and stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a binder to form small particles, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
By adopting the technical scheme, when the dopant formula is added for secondary burdening, the polysiloxane is added, and can improve the mixing dispersibility of the main formula and the dopant formula, so that the uniformity of CCTO enriched in the crystal boundary of MnZn power ferrite during the preparation of the ferrite is improved, the increasing effect of the CCTO on the resistivity of the prepared ferrite is improved, the eddy current loss of the material is further reduced, the high-frequency power loss of the material is reduced, in the process of preparing the ferrite material again, the step of rapid heating is also adopted after secondary ball milling, the additive polysiloxane in the ferrite can be removed at high temperature, the purity and density of the sintered ferrite are improved, and the saturation magnetic induction intensity of the material is improved.
As a further development of the invention, the polysiloxane in step S4 is PSX700.
As a further improvement of the present invention, step S5' is further included between step S5 and step S6: removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, and heating for 20-30min;
as a further improvement of the invention, the mixture is put into an oven to be heated to 400-500 ℃.
As a further improvement of the invention, PVA solution with 7-10 wt% of adhesive is added during granulation in step S6, and the mixture is sieved after being spray-dried into small granules.
As a further improvement of the invention, the temperature of the pre-burning in the step S3 is 900-1050 ℃.
As a further improvement of the invention, the sintering temperature in the step S8 is 900-1370 ℃.
The invention has the beneficial effects that:
1. co is added into the adulterant formula of the invention 2 O 3 ，Co 2 O 3 The metal ions in the MnZn ferrite are doped with Fe which can replace the B site of the MnZn ferrite 3+ And Mn 3+ Therefore, the exchange effect of the A-B ultrasonic is increased, the heat resistance of the material is improved, the working temperature of the material is widened, the Curie temperature of the material is improved, the density of the sintered ferrite is also improved, and the saturation magnetic induction intensity of the material is effectively improved.
2. According to the invention, the CCTO is added in the doping formula, when the CCTO is adopted for doping to prepare the ferrite, the CCTO can be enriched in the crystal boundary of the MnZn power ferrite, and due to the characteristic of high resistivity, the speed of reducing the resistance of crystal grains along with the temperature can be slowed down, so that the increasing speed of high-frequency loss along with the temperature is delayed, and the high-frequency loss energy consumption of the material is effectively reduced.
3. According to the invention, when the main formula and the dopant formula are added for mixing, polysiloxane is added, and the mixing dispersibility of the main formula and the dopant formula can be improved by the polysiloxane, so that the uniformity of CCTO enriched in the crystal boundary of MnZn power ferrite during the preparation of the ferrite is improved, the increasing effect of the CCTO on the resistivity of the prepared ferrite is improved, the eddy current loss of the material is further reduced, and the high-frequency power loss of the material is reduced.
4. In the preparation process, yttrium barium copper oxide YBCO and Co are added 2 O 3 Although the saturation magnetic flux density of the soft magnet can be improved during doping, the microstructure of the soft magnet is easy to grow discontinuously and the crystal is irregular, and each area in the crystal is easy to growThe influence of bubbles is generated, so that the initial permeability and the power loss performance of the material are influenced, the added YBCO has low melting point during sintering, can be preferentially melted and permeated to improve the connection force among crystal grains, ensure the crystal form of the material to grow continuously, effectively reduce the generation of pores in the material, effectively reduce the hysteresis loss of the material and achieve the aim of improving the initial permeability and the power loss performance of the material in Co 2 O 3 Under the condition of ensuring high Bs value of doping, the total power loss of the material is reduced.
Detailed Description
The technical solution of the present invention will be clearly and completely described below with reference to specific embodiments. It is to be understood that the described embodiments are merely a few embodiments of the invention, and not all embodiments. All other embodiments obtained by a person skilled in the art without any inventive work based on the embodiments of the present invention are within the scope of the present invention, and for the sake of experimenting, the samples of the embodiments were prepared as standard rings with a mean outer diameter of 25 × inner diameter of 15 × height of 7.5.
1. Examples of the invention
Example 1
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 70mol％
MnO 20mol％
ZnO 10mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 1PPM
SnO 2 100PPM
Co 2 O 3 50PPM
Bi 2 O 3 50PPM
nano SiO 2 2 50PPM
CCTO 50PPM
YBCO 10PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 900 ℃ in the air atmosphere, preserving the heat for 1h, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing CCTO and YBCO to form a mixture, adding polysiloxane PSX700 into the mixture, and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 400 ℃, and keeping for 20min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 7wt% of a binding agent, performing spray drying to form small particles, and sieving;
step S7: and (3) compression molding: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere at 900 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Example 2
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 72mol％
MnO 22mol％
ZnO 6mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 1000PPM
SnO 2 300PPM
Co 2 O 3 80PPM
Bi 2 O 3 100PPM
nano SiO 2 100PPM
CCTO 100PPM
YBCO 50PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 1050 ℃ in the air atmosphere, preserving the heat for 3 hours, and cooling the powder along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to pre-sinter powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing and stirring CCTO and YBCO to form a mixture, adding polysiloxane PSX700 into the mixture, and stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: placing the mixture after the secondary ball milling into an oven, heating to 500 ℃, and keeping for 30min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 10wt% of a binding agent, performing spray drying to form small particles, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles on pressing equipment into annular raw blanks;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere at 1370 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Example 3
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
CCTO 80PPM
YBCO 30PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary material preparation: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling along with the furnace to obtain pre-sintered powder;
step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing and stirring CCTO and YBCO to form a mixture, adding polysiloxane PSX700 into the mixture, and stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles on pressing equipment into annular raw blanks;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 1
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol%;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Bi 2 O 3 80PPM
nano SiO 2 2 80PPM
CCTO 80PPM
YBCO 30PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling the powder along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to pre-sinter powder 3 、SnO 2 、Bi 2 O 3 Nano SiO 2 Mixing and stirring CCTO and YBCO to form a mixture, adding polysiloxane PSX700 into the mixture, and stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 2
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
CCTO 80PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary material preparation: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed evenly in a preliminary way;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing and stirring CCTO to form a mixture, adding polysiloxane PSX700 into the mixture, and stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: placing the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 3
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
CCTO 80PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed evenly in a preliminary way;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling the powder along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Bi 2 O 3 Nano SiO 2 Mixing the mixture with CCTO to form a mixture, adding polysiloxane PSX700 into the mixture, and stirring and mixingForming a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 4
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
YBCO 30PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly；
Step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 2 Mixing YBCO to form a mixture, adding polysiloxane PSX700 into the mixture, and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 5
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM
CCTO 80PPM
YBCO 30PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing CCTO and YBCO to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S5': removing impurities at high temperature: putting the mixture subjected to the secondary ball milling into an oven, heating to 450 ℃, and keeping for 25min;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, forming small particles by adopting spray drying, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
Comparative example 6
A high-frequency wide-temperature ultralow-loss ferrite material comprises a main formula and a dopant formula, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 71mol％
MnO 21mol％
ZnO 8mol％
the proportion of each main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Bi 2 O 3 80PPM
nano SiO 2 80PPM。
The invention also provides a preparation process of the high-frequency wide-temperature ultralow-loss ferrite material, which comprises the following steps of:
step S1: primary burdening: weighing the materials according to the proportioning requirement to prepare the main formula raw material Fe 2 O 3 MnO and ZnO powder are mixed uniformly;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to 950 ℃ in the air atmosphere, preserving the heat for 2 hours, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Bi 2 O 3 Nano SiO 2 Stirring and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a PVA solution added with 8wt% of a binding agent, performing spray drying to form small particles, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles into annular raw blanks on pressing equipment;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere of 1200 ℃ to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
The soft magnetic ferrite materials prepared in examples 1 to 3 and comparative examples 1 to 6 were subjected to a magnetic property test using a standard ring sample of outer diameter 25 x inner diameter 15 x height 7.5 and compared with the properties of TDK PC95 of japan corporation, and the results are as follows 1:
TABLE 1 magnetic Property results for the respective samples
Figure BDA0003618549150000131
Figure BDA0003618549150000141
The principles and embodiments of the present invention are explained herein using specific examples, which are set forth only to help understand the method and its core ideas of the present invention. It should be noted that, for those skilled in the art, it is possible to make various improvements and modifications to the present invention without departing from the principle of the present invention, and those improvements and modifications also fall within the scope of the claims of the present invention.

Claims (8)

1. The high-frequency wide-temperature ultralow-loss ferrite material is characterized by comprising a main formula, a dopant formula and polysiloxane, wherein the main formula comprises the following components in parts by weight:
Fe 2 O 3 70~72mol%
MnO 20~22mol%
ZnO 6~10mol%
the proportion of the main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 1~1000PPM
SnO 2 100~300PPM
Co 2 O 3 50~80PPM
Bi 2 O 3 50~100PPM
nano SiO 2 50~100PPM
CCTO 50~100PPM
YBCO 10~50PPM。
2. The high-frequency wide-temperature ultralow-loss ferrite material as claimed in claim 1, wherein the main formula comprises the following components in percentage by weight:
Fe 2 O 3 71mol%
MnO 21mol%
ZnO 8mol%
the proportion of the main formula is 100mol percent;
relative to the total amount of the main formula, the components and the weight percentages in the dopant formula are respectively as follows:
CaCO 3 500PPM
SnO 2 200PPM
Co 2 O 3 70PPM
Bi 2 O 3 80PPM
nano SiO 2 2 80PPM
CCTO 80PPM
YBCO 30PPM。
3. A process for preparing a high frequency wide temperature ultra low loss ferrite material according to claim 1, comprising the steps of:
step S1: primary burdening: weighing the main formula raw material Fe according to the proportioning requirement 2 O 3 MnO and ZnO powder are mixed evenly in a preliminary way;
step S2: primary ball milling: putting the main formula powder which is preliminarily and uniformly mixed in the step S1 into a ball mill, and performing ball milling to obtain primary ball-milled powder;
and step S3: pre-burning: heating the powder obtained by ball milling in the step S2 to a certain temperature in the air atmosphere, preserving the heat for 1 to 3 hours, and cooling along with the furnace to obtain pre-sintered powder;
and step S4: secondary burdening: addition of CaCO to the presintered powder 3 、SnO 2 、Co 2 O 3 、Bi 2 O 3 Nano SiO 2 Mixing CCTO and YBCO to form a mixture, adding polysiloxane into the mixture, and mixing to form a mixture;
step S5: secondary ball milling: putting the mixture obtained in the step S4 into a ball mill for secondary ball milling;
step S6: and (3) granulation: adding the mixture subjected to secondary ball milling into a binder to form small particles, and sieving;
step S7: and (3) pressing and forming: pressing the granulated small particles on pressing equipment into annular raw blanks;
step S8: and (3) secondary sintering: and sintering and molding the annular raw blank in an air atmosphere to obtain the target high-frequency wide-temperature ultralow-loss ferrite material.
4. The preparation process of the high-frequency wide-temperature ultra-low loss ferrite material as claimed in claim 3, further comprising a step S5' between the step S5 and the step S6: removing impurities at high temperature: and putting the mixture subjected to the secondary ball milling into an oven, and heating for 20-30min.
5. The preparation process of the high-frequency wide-temperature ultralow-loss ferrite material as claimed in claim 4, wherein the mixture is placed in an oven and heated to 400-500 ℃.
6. The preparation process of the high-frequency wide-temperature ultralow-loss ferrite material as claimed in claim 3, wherein a PVA solution with a binder of 7wt% -10 wt% is added during granulation in step S6, and the mixture is formed into small particles by spray drying and then sieved.
7. The preparation process of the high-frequency wide-temperature ultralow-loss ferrite material according to claim 3, wherein the pre-sintering temperature in the step S3 is 900-1050 ℃.
8. The process for preparing a high-frequency wide-temperature ultra-low loss ferrite material according to claim 3, wherein the sintering temperature in step S8 is 900-1370 ℃.
CN202210455385.5A 2022-04-27 2022-04-27 High-frequency wide-temperature ultralow-loss ferrite material and preparation process thereof Active CN114685154B (en)