CN1146033A - Anti-fake marmem mark and its prodn process - Google Patents
Anti-fake marmem mark and its prodn process Download PDFInfo
- Publication number
- CN1146033A CN1146033A CN 95112701 CN95112701A CN1146033A CN 1146033 A CN1146033 A CN 1146033A CN 95112701 CN95112701 CN 95112701 CN 95112701 A CN95112701 A CN 95112701A CN 1146033 A CN1146033 A CN 1146033A
- Authority
- CN
- China
- Prior art keywords
- shape
- marmem
- fake
- mark
- crooked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention applies marmem in the prodn of anti-fake mark. In the said method, the anti-fake mark with the required anti-fake pattern is struck onto commodity after training settling and being changed into other form. During inspection, the anti-fake mark is heated to set temp to restore the set anti-fake pattern. The said anti-fake mark is not easy to imitate and its identification is a dynamical observation course. The present invention is movel and practical and has application prospect.
Description
The present invention relates to anti-fake mark and method for making.
At present, the low-quality goods of copying famous brand, quality product both at home and abroad is a lot, and in order to prevent personation, various anti-false trademarks also arise at the historic moment.Known has: printing ink is false proof, laser anti-counterfeit, color-changing anti-counterfeit, watermark are false proof etc.But and then the anti-false trademark of Fang Zaoing has also been gone on market thereupon.
The objective of the invention is to, a kind of be difficult for imitated anti-fake marmem mark and method for making are provided.
Marmem (being called for short SMA) is a kind of special and novel functional material, as long as suitably adjust composition and processing procedure, can make it to show: SME; Super-elasticity; This three big characteristic of high damping ability.The present invention is exactly with these characteristics of marmem, applies on the anti-false trademark dexterously.The inventive method is because of the composition difference of marmem, and the employing diverse ways.
1. when using NiTi (NiTi) base marmem, training method is: with the silk material or the sheet material of NiTi base, put into shaper by customer requirements, make one of shape that "---" font can be crooked, put into vacuum drying oven, heating-up temperature is from room temperature to 400 ℃--and 800 ℃, insulation timeliness 0.5--20 hour, with stove cooling or take out in the room temperature water of quenching, the NiTi marmem is promptly finalized the design.The NiTi marmem that to finalize the design then bends to another and sets shape, promptly is mark of the present invention.
2. when using copper (Cu) base marmem, training method is: copper-based shape memory alloy is put into shaper by customer requirements make one of shape that "---" font can be crooked, put into 750 ℃--950 ℃ hot stove, insulation timeliness 10--30 minute, quench 90 ℃ after the taking-up--in 210 ℃ the liquid medium, be incubated 20 seconds--20 minutes, quench again after the taking-up in the room temperature water, the copper-based shape memory alloy typing, and then the copper-based shape memory alloy that will finalize the design changes over another and sets shape, the present invention.
The present invention is with shape memory alloy material, after the requirement setting by the user, also it can be changed over another shape, and be attached on the commodity, the consumer buys commodity, during the check true and false, only need the present invention is heated to 20 ℃--between 120 ℃, the present invention promptly reverts to the shape of typing.
Characteristics of the present invention are that the manufacture craft of mark is not easy to grasp, thereby are difficult for imitation, and mark revert to another after the heating and set shape, and the process of distinguishing true from false is the dynamic process that can view and admire attached to being a kind of shape on the commodity in addition.With anti-fake mark novelty, the uniqueness that the inventive method is manufactured, can be accepted by consumers in general.Embodiment 1: the marmem of making NiTi (NiTi) base, the silk material of NiTi base is fixed in the shaper, make " W " shape, put into vacuum drying oven, furnace temperature rises to 500 ℃ from room temperature, and insulation timeliness 1 hour is with deciding to become the NiTi silk material of " W " type to take out from mould after the stove cooling, to decide to become the NiTi marmem of " W " shape to bend to " O " shape then, mark of the present invention.During the subscriber checking commodity true and false, only need " O " shape mark is heated to more than 50 ℃, " O " shape promptly becomes " W " shape, and these explanation commodity are genuine.
Embodiment 2: make copper (Cu) base marmem Cu-Zn-Al, at first by customer requirements the Cu-Zn-Al silk is fixed in the shaper, make serpentine, put into 800 ℃ of hot stoves, be incubated 10 minutes, in the 110 ℃ of hot machine oil of quenching again, be incubated 5 minutes, quench again in the room temperature water, the Cu-Zn-Al silk of typing is taken out from mould, finish typing, made serpentine Cu-Zn-Al, then it is changed into " L " shape, can be attached on the commodity.When the user detects the true and false, only need the heating of " L " shape more than 100 ℃, " L " promptly becomes the serpentine trade mark, and commodity are genuine.
Claims (2)
1. an anti-fake marmem mark is characterized in that, is to make the figure that "---" font can be crooked with shape-memory alloy wire.
2. the method for making of anti-fake marmem mark is characterized in that:
A. Ni-Ti-based shape memory alloy is that the niti-shaped memorial alloy silk is put into shaper, makes one of shape that "---" font can be crooked, put into vacuum drying oven, be heated to 400 ℃--800 ℃, insulation timeliness 0.5--20 hour bends to it another again and sets shape after the cooling;
B. copper (Cu) base marmem, be that copper base shape memory alloy wire is put into shaper, make one of shape that "---" font can be crooked, put into 750 ℃--950 ℃ hot stove, be incubated timeliness 10--30 minute, quench 90 ℃ after the taking-up--in 210 ℃ the liquid medium, being incubated 20 seconds--2 minutes, take out in the room temperature water of quenching again, and then it is bent to another setting shape.