CN114524960A - 无墨打印聚丙烯标识板 - Google Patents
无墨打印聚丙烯标识板 Download PDFInfo
- Publication number
- CN114524960A CN114524960A CN202011257401.7A CN202011257401A CN114524960A CN 114524960 A CN114524960 A CN 114524960A CN 202011257401 A CN202011257401 A CN 202011257401A CN 114524960 A CN114524960 A CN 114524960A
- Authority
- CN
- China
- Prior art keywords
- layer
- inkless
- dye layer
- resin
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及无墨打印聚丙烯标识板，包括聚丙烯标识板、预涂层一、预涂层二、无墨涂层和保护层，所述预涂层一、预涂层二、无墨涂层和保护层从下至上依次涂敷于所述聚丙烯标识板上，所述预涂层一包括A组分和B组分，所述A组分包括氰基丙稀酸乙酯，羟基丙烯酸树脂、丁酮、甲苯和消泡剂，所述B组分包括甲苯二异氰酸酯或二苯基甲烷二异氰酸酯；所述预涂层二包括氯醋树脂、丁酮和甲苯。本发明打印出的标识板表面有保护层，防水、防油、防腐蚀、耐刮性好，使用寿命长，耐老化性能好、耐高温、密度低。
Description
技术领域
本发明涉及打印耗材技术领域，具体是一种无墨打印聚丙烯标识板。
背景技术
标识牌，即指示方向的牌子，日常生活中都离不开它，制作标识牌的材料非常多，常用的有不锈钢板、铝板、镀锌板、亚克力板、聚氯乙烯板等。而常用的制作工艺有烤漆、丝印、腐蚀、焊接、激光、电镀等。通常为了能够达到更好的视觉效果，会将材质与工艺组合起来使用。总体来说，加工流程长、生产效率低、浪费严重，不利于未来标识牌的发展。
聚丙烯标识板优点：耐老化性能好、耐高温(比聚氯乙烯耐温性能更好)、密度低。
日常生活中，标识牌随处可见，传统的标识牌先将标识图文用墨水、墨粉或碳带的方式打印出来，再粘贴在金属铝板或不锈钢板上；近年来，高分子聚丙烯逐渐取代了金属板材，即更多的是将打印好的柔性标识用喷墨打印机、激光打印机或热转印打印机打印后，再根据板材的大小裁剪好后进行粘贴。其缺点是：工序多、时间长、流程复杂；且打印过程会产生废弃的墨盒或色带不易回收、污染环境；裁剪过程中会产生边角料的浪费；户外经风吹日晒粘贴的标识存在起皮、脱落的情况。
发明内容
为了克服这些缺点，本发明提供一种不需要墨盒或色带、不需要粘贴，可直接打印的无墨打印聚丙烯标识板。
本发明提供的具体解决方案如下：
本发明提供了一种无墨打印聚丙烯标识板，包括聚丙烯标识板、预涂层一、预涂层二、无墨涂层和保护层，所述预涂层一、预涂层二、无墨涂层和保护层从下至上依次涂敷于所述聚丙烯标识板上；
所述预涂层一包括A组分和B组分，所述A组分包括氰基丙稀酸乙酯，羟基丙烯酸树脂、丁酮、甲苯和消泡剂，所述B组分包括甲苯二异氰酸酯或二苯基甲烷二异氰酸酯；
所述预涂层二包括氯醋树脂、丁酮和甲苯；
所述无墨涂层包括至少三个热敏层，从上至下分别为热敏显青色层、热敏显红色层和热敏显黄色层，所述热敏显青色层选自青色三芳甲烷类染料层、青色荧烷类染料层、青色螺吡喃类染料层、青色呋喃酮类染料层、青色吡啶类染料层中的一种或多种；所述热敏显红色层选自红色三芳甲烷类染料层、红色荧烷类染料层、红色螺吡喃类染料层、红色呋喃酮类染料层、红色吡啶类染料层中的一种或多种；所述热敏显黄色层选自黄色三芳甲烷类染料层、黄色荧烷类染料层、黄色螺吡喃类染料层、黄色呋喃酮类染料层、黄色吡啶类染料层中的一种或多种；
所述保护层包括氟碳树脂、附着力促进剂、溶剂和助剂，所述氟碳树脂选自聚四氟乙烯树脂、聚偏二氟乙烯树脂、聚三氟氯乙烯树脂、乙烯基醚树脂和聚氟乙烯树脂中的一种或多种，所占质量百分比为5～30％，所述附着力促进剂选自钛酸四乙酯和钛酸正丁酯中的一种或多种，所占质量百分比为0～2％，所述溶剂为水，所占质量百分比为60～85％，所述助剂选自苯二甲酸二丁酯、苯二甲酸二甲酯、聚乙烯蜡、二甲基硅酮油中的一种或多种，所占质量百分比为2～5％。
优选地，所述无墨涂层中各热敏层的厚度范围为5-30μm。
优选地，所述保护层的厚度为10-20μm。
优选地，所述预涂层的厚度为5-30μm。
优选地，还包括中间间隔层，为树脂和填料的混合物，涂敷于热敏层之间。
优选地，所述预涂层二中氯醋树脂的型号为K50。
基于发明的技术方案具有以下有益效果：
(1)本发明的无墨打印聚丙烯板打印标识操作简单、生产效率高；
(2)打印后表面光滑、色彩鲜活、层次分明，分辨率高；
(3)表面有保护层，防水、防油、防腐蚀、耐刮性好，使用寿命长；
(4)耐老化性能好、耐高温、密度低(比聚氯乙烯更好)。
具体实施方式
下面详细描述本发明的实施例，旨在用于解释本发明，而不能理解为对本发明的限制。
本发明提供了一种无墨打印聚丙烯标识板，包括聚丙烯标识板、预涂层一、预涂层二、无墨涂层和保护层，所述预涂层一、预涂层二、无墨涂层和保护层从下至上依次涂敷于所述聚丙烯标识板上；
所述预涂层一包括A组分和B组分，所述A组分包括氰基丙稀酸乙酯，羟基丙烯酸树脂、丁酮和消泡剂，所述B组分包括甲苯二异氰酸酯或二苯基甲烷二异氰酸酯、丁酮和甲苯；
所述预涂层二包括氯醋树脂、丁酮和甲苯；所述氯醋树脂的型号为K50。
所述预涂层一和预涂层二的厚度范围为5-30μm。
所述无墨涂层包括至少三个热敏层，从上至下分别为热敏显青色层、热敏显红色层和热敏显黄色层，所述热敏显青色层选自青色三芳甲烷类染料层、青色荧烷类染料层、青色螺吡喃类染料层、青色呋喃酮类染料层、青色吡啶类染料层中的一种或多种；所述热敏显红色层选自红色三芳甲烷类染料层、红色荧烷类染料层、红色螺吡喃类染料层、红色呋喃酮类染料层、红色吡啶类染料层中的一种或多种；所述热敏显黄色层选自黄色三芳甲烷类染料层、黄色荧烷类染料层、黄色螺吡喃类染料层、黄色呋喃酮类染料层、黄色吡啶类染料层中的一种或多种；所述无墨涂层中各热敏层的厚度范围为5-30μm。
所述保护层包括氟碳树脂、附着力促进剂、溶剂和助剂，所述氟碳树脂选自聚四氟乙烯树脂、聚偏二氟乙烯树脂、聚三氟氯乙烯树脂、乙烯基醚树脂和聚氟乙烯树脂中的一种或多种，所占质量百分比为5～30％，所述附着力促进剂选自钛酸四乙酯和钛酸正丁酯中的一种或多种，所占质量百分比为0～2％，所述溶剂为水，所占质量百分比为60～85％，所述助剂选自苯二甲酸二丁酯、苯二甲酸二甲酯、聚乙烯蜡、二甲基硅酮油中的一种或多种，所占质量百分比为2～5％。所述保护层的厚度为10-20μm。
本发明还包括中间间隔层，为树脂和填料的混合物，涂敷于热敏层之间。这样做能够起到间隔作用，将层与层之间分隔开，减少温度相应对每一层的影响。
所述热敏显青色层、热敏显红色层和热敏显黄色层从下到上依次涂敷于所述预涂层上，各涂层的响应温度分别为：80-120℃，100-150℃，140-200℃，可以显示青色(C)、红色(M)、黄色(Y)三原色的叠加，最终输出彩色图文。打印头的温度决定了各热敏染料层的理论颜色，从而决定叠加后的图文的理论颜色，在实际应用中，各层的变色温度以及响应速度与热敏染料层的位置也紧密相关，而将响应温度最高(温度敏感性差的)热敏染料置于最上层，将响应温度最低(温度敏感性高)的热敏染料置于最下层，从而保证良好的图文效果输出。
所述热敏显青色层为7,7-二(4-(二乙胺基)-2-乙氧苯基)呋喃并[3,4-b]吡啶-5(7H)-酮染料层，所述热敏显红色层为6′-二乙氨基-1′,3′-二甲基苯丙呋喃染料层，所述热敏显黄色层为3',6'-二甲氧基荧烷染料层，采用这三种热敏染料层可带来较好的显色效果和较宽的色值。
具体实施例一预涂层一配比：A组分氰基丙稀酸乙酯25g、羟基丙烯酸树脂20g、助剂0.05g，助剂选用消泡剂、丁酮30g和甲苯25g；B组分二苯基甲烷二异氰酸酯(MDI)5g、丁酮2.5g和甲苯2.5g。
实验步骤：取A组分10g加入5g B组分中，搅拌半小时，然后进行涂布。
预涂层二配比：氯醋树脂K5020g、丁酮40g、甲苯40g。充分溶解后，进行涂布。
基于发明的技术方案具有以下有益效果：
(1)本发明的无墨打印聚丙烯板打印标识操作简单、生产效率高；
(2)打印后表面光滑、色彩鲜活、层次分明，分辨率高；
(3)表面有保护层，防水、防油、防腐蚀、耐刮性好，使用寿命长；
(4)耐老化性能好、耐高温、密度低(比聚氯乙烯更好)。
尽管上面已经详细描述了本发明的实施例，本领域的普通技术人员可以理解：在不脱离本本发明的原理和宗旨的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由权利要求及其等同物限定。
Claims (6)
1.一种无墨打印聚丙烯标识板，其特征在于，包括聚丙烯标识板、预涂层一、预涂层二、无墨涂层和保护层，所述预涂层一、预涂层二、无墨涂层和保护层从下至上依次涂敷于所述聚丙烯标识板上；
所述预涂层一包括A组分和B组分，所述A组分包括氰基丙稀酸乙酯，羟基丙烯酸树脂、丁酮、甲苯和消泡剂，所述B组分包括甲苯二异氰酸酯或二苯基甲烷二异氰酸酯；
所述预涂层二包括氯醋树脂、丁酮和甲苯；
所述无墨涂层包括至少三个热敏层，从上至下分别为热敏显青色层、热敏显红色层和热敏显黄色层，所述热敏显青色层选自青色三芳甲烷类染料层、青色荧烷类染料层、青色螺吡喃类染料层、青色呋喃酮类染料层、青色吡啶类染料层中的一种或多种；所述热敏显红色层选自红色三芳甲烷类染料层、红色荧烷类染料层、红色螺吡喃类染料层、红色呋喃酮类染料层、红色吡啶类染料层中的一种或多种；所述热敏显黄色层选自黄色三芳甲烷类染料层、黄色荧烷类染料层、黄色螺吡喃类染料层、黄色呋喃酮类染料层、黄色吡啶类染料层中的一种或多种；
所述保护层包括氟碳树脂、附着力促进剂、溶剂和助剂，所述氟碳树脂选自聚四氟乙烯树脂、聚偏二氟乙烯树脂、聚三氟氯乙烯树脂、乙烯基醚树脂和聚氟乙烯树脂中的一种或多种，所占质量百分比为5～30％，所述附着力促进剂选自钛酸四乙酯和钛酸正丁酯中的一种或多种，所占质量百分比为0～2％，所述溶剂为水，所占质量百分比为60～85％，所述助剂选自苯二甲酸二丁酯、苯二甲酸二甲酯、聚乙烯蜡、二甲基硅酮油中的一种或多种，所占质量百分比为2～5％。
2.根据权利要求1所述的无墨打印聚丙烯标识板，其特征在于，所述无墨涂层中各热敏层的厚度范围为5-30μm。
3.根据权利要求1所述的无墨打印聚丙烯标识板，其特征在于，所述保护层的厚度为10-20μm。
4.根据权利要求1所述的无墨打印聚丙烯标识板，其特征在于，所述预涂层的厚度为5-30μm。
5.根据权利要求1所述的无墨打印聚丙烯标识板，其特征在于，还包括中间间隔层，为树脂和填料的混合物，涂敷于热敏层之间。
6.根据权利要求1所述的无墨打印聚丙烯标识板，其特征在于，所述预涂层二中氯醋树脂的型号为K50。