CN114437776B - Method and system for preparing cracking raw material from waste plastic oil and/or waste tire oil - Google Patents
Method and system for preparing cracking raw material from waste plastic oil and/or waste tire oil Download PDFInfo
- Publication number
- CN114437776B CN114437776B CN202011193313.5A CN202011193313A CN114437776B CN 114437776 B CN114437776 B CN 114437776B CN 202011193313 A CN202011193313 A CN 202011193313A CN 114437776 B CN114437776 B CN 114437776B
- Authority
- CN
- China
- Prior art keywords
- waste
- oil
- metal
- content
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a method and a system for preparing cracking raw materials from waste plastic oil and/or waste tire oil, wherein the waste plastic oil and/or waste tire oil is contacted with a waste hydrogenation catalyst in a impurity removal reactor, impurity removal reaction is carried out under impurity removal reaction conditions, obtained reaction effluent enters a hydrofining reactor to be contacted with the hydrofining catalyst for reaction, gas-phase materials and liquid-phase materials are obtained after the reaction effluent is separated, and all or part of the obtained liquid-phase materials are cracking raw materials for preparing ethylene by steam cracking. The invention can effectively remove the impurities in the waste plastic oil and/or the waste tire oil, provides high-quality cracking raw materials for the process of preparing ethylene by steam cracking, and has low cost and long operation period.
Description
Technical Field
The invention relates to the technical field of hydrocarbon raw material treatment, in particular to a method and a system for preparing cracking raw materials from waste plastic oil and/or waste tire oil.
Background
With the continuous development of urban process in China, urban population rises year by year, the living standard of people is continuously improved, the yield of urban household garbage is continuously increased, and the current urban garbage treatment method mainly comprises landfill, incineration and the like. There are a series of subsequent environmental protection issues, whether incineration or landfill.
The chemical conversion method can convert the plastic garbage into industrial raw materials or fuel oil with utilization value, not only can eliminate environmental pollution, but also can realize sustainable development and utilization of resources, and is an effective way for treating white pollution. At present, the waste plastic oil refining industry has developed a situation of blooming throughout China, and some enterprises build pyrolysis demonstration devices with smaller scale, but the problem of high-value utilization of waste plastic pyrolysis products is still to be effectively solved.
The waste plastic oil, the waste tire oil and the traditional petroleum-based oil converted by various processes have large difference, and the high impurity content, especially the high silicon content, brings great trouble to the subsequent processing. At present, few researches are conducted on deep processing of waste plastic oil and waste tire oil, and much research focuses on the influence of chlorine impurities in the waste plastic oil on post-processing of the waste plastic oil, and the situation that other impurities such as silicon impurities and metal impurities are also contained in the waste plastic oil is not realized, and the serious influence of the impurities on the subsequent processing technology is not realized.
CN104611060a discloses a method for producing clean fuel oil from waste plastics and high aromatic components. After the high aromatic component is mixed with the waste plastic oil, the waste plastic oil passes through a thermal cracking reaction zone, and the thermal cracking reaction zone adopts a mode of combining gradual heating and constant temperature operation; and (3) the obtained pyrolysis gas enters a catalytic reaction zone to be contacted with a catalyst in the catalytic reaction zone for catalytic reaction, and the obtained reaction effluent enters gas-liquid separation to obtain a gas product and a liquid-phase oil product.
CN104726134a discloses a method for producing high-quality gasoline and diesel oil from chlorine-containing plastic oil. The method is characterized in that chlorine-containing plastic oil is injected into a high-temperature dechlorination tower filled with active aluminum oxide for high-temperature dechlorination, a small amount of NaOH aqueous solution is sprayed on the top of the high-temperature dechlorination tower, and the dechlorinated plastic oil enters a catalytic distillation tower filled with a molecular sieve/aluminum oxide catalyst for reaction and rectification; the plastic oil after catalytic distillation enters a hydrogenation refining tower through pressurization, the distillate oil after hydrogenation refining is distilled at a constant pressure, the distillate oil is cut into gasoline and diesel oil according to the distillation temperature, and the heavy oil at the bottom of the tower is mixed with the raw material chlorine-containing plastic oil for re-reaction. The dechlorination catalyst and the sulfide catalyst used in the invention are prepared by selecting proper methods according to the composition and the performance of the plastic oil.
CN102942951a discloses a method for preparing clean diesel oil by hydrogenation of plastic oil, which comprises the following steps: a. mixing the plastic oil and hydrogen, and entering a pre-hydrogenation reactor filled with a hydrogenation protecting catalyst for chemical reaction; b. the effluent of the pre-hydrogenation reactor enters a hot high-pressure separator for separation and gas stripping, and the effluent at the bottom of the hot high-pressure separator and the gas at the top of the cold high-pressure separator enter a main hydrogenation reactor for chemical reaction; c. the effluent of the main hydrogenation reactor enters a cold high-pressure separator for gas-liquid separation, the effluent at the bottom of the cold high-pressure separator enters a cold low-pressure separator for mixing with light oil extracted from the middle part of the cold high-pressure separator, and then enters a fractionating tower for separation, and clean diesel oil fractions with sulfur content less than 5 mug/g and cetane number higher than 50 can be extracted from the lateral line of the fractionating tower.
CN102226103a discloses a method for producing gasoline and diesel oil by using plastic oil. The process is characterized in that firstly, the plastic oil is distilled to obtain a fraction smaller than 300 ℃ and a fraction larger than 300 ℃, then the fraction smaller than 300 ℃ is hydrofined on a sulfide catalyst, the mono-olefin is removed through hydrogenation saturation reaction of mono-olefin, no peculiar smell is produced by desulfurizing, removing nitrogen and removing colloid, and the gasoline and diesel oil mixed oil with high quality is obtained through distillation. The distillate with the distillation temperature of more than 300 ℃ is subjected to reactive distillation and then hydrofining or mixing with plastic oil for re-reaction. The sulfide catalyst used in the invention is prepared by selecting a proper carrier according to the composition and the performance of the pyrolysis plastic oil through a liquid phase method.
The prior art mainly focuses on the dechlorination and refining processes of waste plastic oil, and is not aware that silicon compounds in the waste plastic oil can have serious toxic effects on the hydrogenation catalyst in the prior art and catalysts in other subsequent processes, so that the operation period of the subsequent processes is short, or industrial operation cannot be realized in fact.
Disclosure of Invention
The invention aims to solve the problem of short processing period when waste plastic oil and/or waste tire oil raw materials are processed in the prior art, and provides a method and a system for preparing cracking raw materials from the waste plastic oil and/or the waste tire oil.
The first aspect of the invention provides a method for preparing cracking raw materials from waste plastic oil and/or waste tire oil, comprising the following steps:
(1) The waste plastic oil and/or the waste tire oil enter a impurity removal reactor to contact with a waste hydrogenation catalyst in the presence of hydrogen, and the impurity removal reaction is carried out under the impurity removal reaction condition, wherein the silicon content of a liquid phase material in the obtained reaction effluent is less than 1 mug/g, and the metal content is less than 5 mug/g;
(2) And (3) a hydrofining unit, wherein the reaction effluent obtained in the step (1) enters a hydrofining reactor to be contacted with a hydrofining catalyst, hydrofining reaction is carried out under the condition of hydrofining reaction, and after the reaction effluent is separated, a gas-phase material and a liquid-phase material are obtained, and all or part of the obtained liquid-phase material is a cracking raw material for preparing ethylene by steam cracking.
In one embodiment of the invention, the waste plastic oil is hydrocarbon materials obtained by one or more conversion methods of thermal cracking, catalytic cracking and dissolution liquefaction of waste plastic; the distillation range of the waste plastic oil is 30-700 ℃, the silicon content is less than 10000 mug/g, the chlorine content is less than 10000 mug/g, and the metal content is less than 10000 mug/g. The composition of the waste plastic oil comprises olefin with volume fraction of 5-80%, preferably 5-60%, aromatic hydrocarbon with volume fraction of less than 90%, preferably 2-60%, and alkane with volume fraction of less than 90%, preferably 5-60%.
In the invention, the waste plastic is one or more of waste plastic in fresh household garbage, waste plastic in industrial and agricultural production and waste plastic in aged garbage, and the waste plastic is one or more selected from PE, PP, PS, PVC.
In one embodiment of the invention, the junked tire oil is a hydrocarbon material obtained by one or more conversion methods of thermal cracking, catalytic cracking and dissolution liquefaction of junked tires; the distillation range of the waste tire oil is 30-700 ℃, the silicon content is less than 10000 mug/g, the chlorine content is less than 10000 mug/g, and the metal content is less than 10000 mug/g. The composition of the waste tire oil comprises 5-80% of olefin, preferably 5-60% of aromatic hydrocarbon, less than 90% of aromatic hydrocarbon, preferably 2-60% of aromatic hydrocarbon, and less than 90% of alkane, preferably 5-60% of alkane.
In the invention, the junked tires are various junked tires prepared from natural rubber and/or synthetic rubber.
In the invention, the thermal cracking and thermal cracking reaction refers to a reaction that hydrocarbon molecules including waste plastics and junked tires are decomposed into smaller molecules under the condition of isolating air at high temperature. Depending on the reaction temperature, 600℃or less will be referred to as thermal cracking reaction, and 600℃or more will be referred to as thermal cracking reaction.
In the present invention, the catalytic cracking and catalytic cracking reaction refers to a reaction in which hydrocarbon molecules including waste plastics and junked tires are decomposed into smaller molecules under high temperature conditions and in the presence of a catalyst. Depending on the reaction products, the reaction using low-carbon olefins (ethylene, propylene, and butene) as the target products is called a catalytic cracking reaction, and the reaction using motor gasoline as the target products is called a catalytic cracking reaction.
In the present invention, the dissolution and liquefaction reaction means a reaction in which waste plastics and junked tires are converted from a solid state to a liquid state in the presence of solvent oil and/or an organic solvent.
In one embodiment of the invention, the de-hybridization reactor is at least one fixed bed hydrogenation reactor and/or at least one moving bed hydrogenation reactor. And filling a waste hydrogenation catalyst in the fixed bed hydrogenation reactor and/or the moving bed reactor, and carrying out desilication, dechlorination, demetallization and other impurity removal reactions on the waste plastic oil and/or the waste tire oil through at least one fixed bed hydrogenation reactor and/or at least one moving bed hydrogenation reactor.
In one embodiment of the invention, the impurity removal reactor is more than two fixed bed hydrogenation reactors connected in parallel, each reactor is filled with a waste hydrogenation catalyst, waste plastic oil and/or waste tire oil is subjected to impurity removal reaction through at least one fixed bed hydrogenation reactor, and when the waste hydrogenation catalyst in the fixed bed hydrogenation reactor is saturated with silicon or saturated with metal, the waste plastic oil and/or waste tire oil is fed into other fixed bed hydrogenation reactors in a switching way.
In one embodiment of the invention, the waste hydrogenation catalyst in the dehazing reactor is considered to be saturated with silicon or with metal when the silicon content of the liquid phase material in the reaction effluent is greater than or equal to 1 μg/g or when the metal content is greater than or equal to 5 μg/g.
In one embodiment of the invention, the waste hydrogenation catalyst is one or more selected from the group consisting of a protecting agent used from the end of any fixed bed hydrogenation process device in the hydrocarbon oil processing field, a catalyst at the end of the fixed bed hydrogenation process device, a regenerated protecting agent and a regenerated catalyst.
In one embodiment of the invention, the equivalent diameter of the spent hydrogenation catalyst is from 0.5 to 16mm, preferably from 1 to 10mm. The shape of the waste hydrogenation catalyst is not limited, and for example, the shape of the waste hydrogenation catalyst comprises a sphere, and various different shapes such as strip clover, butterfly, raschig ring, honeycomb shape and the like.
In one embodiment of the invention, the waste hydrogenation catalyst comprises, based on the total weight of the waste hydrogenation catalyst, 0-50% by weight of hydrogenation active metal oxide, 0-50% by weight of carbon and 0-40% by weight of sulfur, wherein the hydrogenation active metal is selected from one or more of VIII group metals and VIB group metals.
In one embodiment of the invention, the waste hydrogenation catalyst comprises, based on the total weight of the waste hydrogenation catalyst, 0-50 wt% of molybdenum oxide and/or tungsten oxide, 0-40 wt% of nickel oxide and/or cobalt oxide, 0-30 wt% of carbon and 0-30 wt% of sulfur.
In one embodiment of the invention, the waste hydrogenation catalyst comprises 1-40 wt% of hydrogenation active metal oxide and 20 wt% or less of carbon based on the total weight of the waste hydrogenation catalyst, wherein the hydrogenation active metal is selected from one or more of VIII group metal and VIB group metal.
In one embodiment of the invention, a plurality of waste hydrogenation catalysts are filled in layers, the equivalent diameter of the waste hydrogenation catalysts is gradually reduced along the material flow direction, the pore diameter is gradually reduced, and the active metal content is gradually increased.
In one embodiment of the invention, the impurity removal reactor is also filled with a dechlorinating agent, and the filling volume ratio of the dechlorinating agent to the waste catalyst is 1-80: 20 to 99. The waste hydrogenation catalyst and the dechlorinating agent are uniformly mixed and filled or layered filled.
In one embodiment of the invention, the waste hydrogenation catalyst and the dechlorinating agent are filled in layers, and the dechlorinating agent is filled downstream of the waste hydrogenation catalyst according to the material flow direction.
In one embodiment of the present invention, the dechlorinating agent is one or more, and when the dechlorinating agent is a plurality of dechlorinating agents, the dechlorinating agents can be packed in a graded combination or a mixed packing.
In one embodiment of the invention, the hydrogenation reactor is at least one moving bed hydrogenation reactor, and the waste hydrogenation catalyst and the dechlorinating agent are filled in the moving bed hydrogenation reactor. The waste hydrogenation catalyst and the dechlorinating agent are mechanically mixed according to a certain proportion.
In one embodiment of the invention, the dechlorinating agent comprises at least one group IA metal compound and/or at least one group IIA metal compound, optionally one or more metal oxides selected from Cu, fe, zn, and a carrier and/or binder;
the carrier and/or the binder is selected from one or more of silicon oxide, aluminum oxide, silicon oxide-aluminum oxide, zirconium oxide and clay. The clay is one or more selected from kaolin, illite, montmorillonite and bentonite; the kaolin comprises halloysite.
In the present invention, "optional" means optional, and the optional metal oxide or oxides selected from Cu, fe, zn means that the metal oxide or oxides selected from Cu, fe, zn is/are optional components of the dechlorinating agent.
In the present invention, the dechlorinating agent is preferably a high-temperature dechlorinating agent and/or a medium-temperature dechlorinating agent. The invention has no limitation to high-temperature dechlorinating agent and medium-temperature dechlorinating agent, and the invention can be realized by conventional high-temperature dechlorinating agent and medium-temperature dechlorinating agent. Further preferred are high temperature dechlorinating agents and/or medium temperature dechlorinating agents having a large chlorine capacity.
In one embodiment of the invention, the chlorine content of the liquid phase material in the reaction effluent of step (1) is less than 0.5 μg/g.
In one embodiment of the invention, the stripping reaction conditions are: hydrogen partial pressure of 0.5-20.0 MPa, reaction temperature of 60-500 ℃ and volume space velocity of 0.1-30 h -1 Hydrogen oil volume ratio of 5-1000 Nm 3 /m 3 。
The preferred conditions for the stripping reaction are: hydrogen partial pressure of 1-12 MPa, reaction temperature of 100-450 ℃ and volume space velocity of 0.2-20 h -1 Hydrogen oil volume ratio of 5-800 Nm 3 /m 3 。
In the hydrofining unit of the step (2), the reaction effluent obtained in the impurity removal unit of the step (1) directly enters a hydrofining reactor, and is contacted with a hydrofining catalyst for reaction under the condition of hydrofining reaction, so that impurities such as sulfur, nitrogen and the like are removed, and olefin is hydrogenated and saturated.
In one embodiment of the present invention, the hydrofinishing reaction conditions are: hydrogen partial pressure of 1.0-20.0 MPa, reaction temperature of 250-430 ℃ and volume space velocity of 0.5-20 h -1 The volume ratio of hydrogen to oil is 50-1000 Nm 3 /m 3 ;
The preferred hydrofining reaction conditions are: hydrogen partial pressure of 1.0-12 MPa, reaction temperature of 280-400 ℃ and volume space velocity of 0.5-15 h -1 The volume ratio of hydrogen to oil is 100-800 Nm 3 /m 3 。
In one embodiment of the invention, the hydrofining catalyst comprises a hydrogenation metal active component and a carrier, wherein the content of the hydrogenation metal active component is 5-50 wt% based on the total weight of the hydrofining catalyst and calculated as oxide.
In a preferred case, the hydrogenation metal active component is at least one metal element selected from the group consisting of group VIB metal elements and at least one metal element selected from the group consisting of group VIII metal elements, wherein the group VIB metal elements are molybdenum and/or tungsten, and the group VIII metal elements are cobalt and/or nickel; the content of the group VIB metal element is 4 to 40 wt%, preferably 8 to 35 wt%, and the content of the group VIII metal element is 1 to 10 wt%, preferably 2 to 5 wt%, based on the total weight of the hydrofining catalyst, calculated as oxide.
After separation of the reaction effluent from the hydrofining reactor, a gaseous and a liquid phase are obtained, in one embodiment of the invention, the olefin content in the obtained liquid phase is less than or equal to 2 mass%, the sulfur content is less than 50 μg/g, the nitrogen content is less than 50 μg/g, the silicon content is less than 1 μg/g, the chlorine content is less than 0.5 μg/g, and the metal content is less than 1 μg/g. The obtained liquid phase material has low sulfur, low nitrogen and low olefin, and all or part of the liquid phase material can be a cracking raw material for preparing ethylene by steam cracking.
The invention also provides a system for any method, which comprises a impurity removal unit and a hydrofining unit, wherein the impurity removal unit is provided with an impurity removal reactor filled with waste hydrogenation catalyst, the impurity removal reactor is provided with at least one waste plastic oil and/or waste tire oil inlet and at least one reaction effluent outlet, and the waste hydrogenation catalyst is one or more selected from a protective agent and a catalyst from the end of any fixed bed hydrogenation process device in the hydrocarbon oil processing field to the end, and a regenerated protective agent and a regenerated catalyst;
the reaction effluent outlet of the impurity removal unit is communicated with the feed inlet of the hydrofining unit, the hydrofining unit is provided with a hydrofining reactor filled with hydrofining catalyst, the reaction effluent outlet of the hydrofining reactor is communicated with the inlet of the separation unit, and the separation unit is provided with at least one gas-phase material outlet and at least one liquid-phase material outlet.
In one embodiment of the invention, the de-hybridization reactor is at least one fixed bed hydrogenation reactor and/or at least one moving bed hydrogenation reactor.
In one embodiment of the invention, the impurity removal reactor is more than two fixed bed hydrogenation reactors connected in parallel, each fixed bed hydrogenation reactor is filled with a waste hydrogenation catalyst, and each fixed bed hydrogenation reactor is provided with at least one waste plastic oil and/or waste tire oil inlet and at least one reaction effluent outlet.
The invention is characterized in that:
1. the invention can treat waste plastic oil and waste tyre oil converted by various processes, and provides high-quality cracking raw materials for preparing ethylene by steam cracking after the waste plastic oil and the waste tyre oil are treated by a impurity removing unit and a hydrofining unit.
2. The invention effectively removes impurities, especially silicon impurities, chlorine impurities and metal impurities, in the waste plastic oil and the waste tire oil in the impurity removal unit, avoids the influence of the impurities on the hydrofining catalyst in the hydrofining unit, and prolongs the whole operation period.
3. The invention uses the waste hydrogenation catalyst, and has low cost and good impurity removal effect. In the preferred embodiment of the invention, a moving bed or two fixed bed reactors which are connected in parallel and alternately switched are adopted for pretreatment, so that the purposes of long-period deep desilication, demetallization and dechlorination are realized.
Drawings
FIG. 1 is a schematic diagram of one embodiment of a process for preparing a pyrolysis feedstock from waste plastic oil and/or scrap tire oil provided by the present invention.
Detailed Description
The invention will be further described with reference to the accompanying drawings, without thereby limiting the invention.
FIG. 1 is a schematic diagram of one embodiment of a method for preparing cracking raw materials from waste plastic oil and/or waste tire oil, wherein as shown in FIG. 1, after the waste plastic oil and/or waste tire oil from a pipeline 1 is boosted by a feed pump 2, the waste plastic oil and/or waste tire oil enters a heating furnace 4 from a pipeline 3 together with new hydrogen from a pipeline 17 and circulating hydrogen from a pipeline 16 to be heated, the heated hydrogen-mixed material enters a impurity removing unit through a pipeline 5, the impurity removing unit is provided with two parallel fixed bed hydrogenation reactors 8 and 9, a catalyst bed layer A is arranged in the fixed bed hydrogenation reactor 8, waste hydrogenation catalyst is filled in a grading manner, a catalyst bed layer B is arranged in the fixed bed hydrogenation reactor 9, and waste hydrogenation catalyst is filled in a grading manner. In one embodiment, the hydrogen mixed material enters a fixed bed hydrogenation reactor 8 through a pipeline 6, contacts with the waste hydrogenation catalyst filled in a grading way, and carries out the impurity removal reaction under the impurity removal reaction condition, and the fixed bed hydrogenation reactor 9 is used for standby. After the waste hydrogenation catalyst in the fixed bed hydrogenation reactor 8 is saturated with silicon or metal, the hydrogen mixed material enters the fixed bed hydrogenation reactor 9 through a pipeline 7 to react, the fixed bed hydrogenation reactor 8 is cut out of the reaction system, and then the waste hydrogenation catalyst in the catalyst bed A is replaced.
The reaction effluent obtained from the impurity removal unit enters a hydrofining reactor 12 through pipelines 10 and 11 to be contacted with hydrofining catalyst for reaction, the reaction effluent enters a high-pressure separator 14 through a pipeline 13 to be subjected to gas-liquid separation, the obtained liquid phase material is extracted through a pipeline 18, and the obtained gas phase material is returned to the inlet of a heating furnace 4 through a pipeline 16 after being boosted by a circulating hydrogen compressor 15.
The invention is further illustrated by the following examples, which are not intended to limit the invention in any way.
In the examples, the silicon content in the hydrocarbon material was measured by the method of measuring single wavelength dispersive X-ray fluorescence (SH/T0993-2019) of silicon content in gasoline and related products.
In the examples, the chlorine content in the liquid material was measured by coulometry, specifically by the method of "measuring the total chlorine content in crude oil by coulometry" (RIPP 64-90) in "petrochemical analysis method" (RIPP test method). The instrument used was a microcoulomb analyzer and the sample was a liquid material.
The dechlorinating agent used in examples and comparative examples was an industrially practiced dechlorinating agent RDY-100, manufactured by Jinan Ruidong Utility Co., ltd.
The reforming prehydrogenation end catalyst D used in the examples, the support was alumina, butterfly-shaped, equivalent diameter 1.6mm, composition comprising: 18% by weight of tungsten oxide, 2% by weight of nickel oxide, 0.04% by weight of cobalt oxide, 5.0% by weight of carbon and 6% by weight of sulfur;
the end catalyst E carrier of the gasoline hydrogenation used in the examples is alumina, butterfly-shaped, with equivalent diameter of 1.6mm, and the composition comprises: 10% by weight of molybdenum oxide, 3.5% by weight of cobalt oxide, 8.0% by weight of carbon and 7.0% by weight of sulfur;
the end catalyst F for diesel hydrofining used in the examples has a carrier of alumina, butterfly shape and equivalent diameter of 1.6mm, and comprises the following components: 26% of molybdenum oxide, 4.0% of nickel oxide, 20% of carbon content and 15% of sulfur content;
the end hydrogenation catalyst G used in the examples is a residuum hydrogenation protecting agent end catalyst, the carrier is alumina, raschig rings, equivalent diameter 6.0mm, the composition includes: 2% by weight of molybdenum oxide, 0.5% by weight of nickel oxide, 40% by weight of carbon and 5% by weight of sulfur;
the hydrofining catalyst H used in the examples has a carrier of alumina, a butterfly shape and an equivalent diameter of 1.6mm, and comprises the following components: 26% by weight of molybdenum oxide and 4.0% by weight of nickel oxide.
The properties of the raw materials are shown in Table 1, wherein the raw material I is waste plastic oil, J is waste plastic oil and waste tire oil in a ratio of 80:20 by weight, and the raw material K is waste plastic oil and waste tire oil in a ratio of 40:60 by weight.
TABLE 1
Examples 1 to 5
After the waste plastic oil and/or the waste tire oil are mixed with hydrogen, the mixture enters a impurity removal reactor to be contacted with a waste hydrogenation catalyst, impurity removal reaction is carried out under impurity removal reaction conditions, and the catalyst filling condition, reaction conditions and reaction results of the impurity removal units are shown in table 2. As can be seen from Table 2, the liquid phase material in the reaction effluent from the impurity removal unit had a silicon content of less than 1. Mu.g/g, a chlorine content of less than 0.5. Mu.g/g, and a metal content of less than 5. Mu.g/g.
The reaction effluent obtained by the impurity removal unit enters a hydrofining reactor to contact with a hydrofining catalyst, hydrofining reaction is carried out under the hydrofining reaction condition, and gas-phase materials and liquid-phase materials are obtained after the reaction effluent is separated, and the catalyst loading condition, the reaction condition and the reaction result of the hydrofining unit are shown in Table 3.
As can be seen from Table 3, the obtained liquid phase material has low impurity content and BMCI value, and is a pyrolysis raw material for preparing ethylene by high-quality steam pyrolysis.
TABLE 2
TABLE 3 Table 3
Example 6
In this example, two parallel fixed bed hydrogenation reactors 1 and 2 were set up, and the feedstock J was used as a feed, and the catalyst loading conditions, the impurity removal reaction conditions and the reaction results were as shown in Table 4.
When the reactor 1 was operated for 800 hours, the metal content of the liquid phase material in the reaction effluent was more than 5. Mu.g/g, and at this time, the reactor was switched to the reactor 2, and the metal content of the liquid phase material was reduced to less than 1. Mu.g/g. The catalyst is replaced for the reactor 1, and thus the cycle achieves a long period of operation.
TABLE 4 Table 4
Example 7
In this example, two parallel fixed bed hydrogenation reactors 1 and 2 were set up, and the raw material K was used as the feed, and the catalyst loading conditions, the impurity removal reaction conditions and the reaction results were as shown in Table 5.
When the reactor 1 is operated for 1000 hours, the silicon content of the liquid phase material in the reaction effluent is more than 1 mug/g, the metal content is more than 8 mug/g, the reactor is switched to the reactor 2, and the silicon content and the metal content of the liquid phase material are reduced to be less than 1 mug/g. The catalyst is replaced for the reactor 1, and thus the cycle achieves a long period of operation.
TABLE 5
Example 8
The moving bed reactor of the stripping unit in this example, which uses the feedstock I as the feed, the catalyst loading conditions, the stripping reaction conditions and the reaction results are shown in Table 6.
As can be seen from Table 6, by adopting the method of the present invention, the raw material I with higher impurity content is treated by adopting a moving bed in the impurity removal unit, the silicon content of the obtained liquid phase reaction effluent is less than 1 mug/g, the chlorine content is less than 0.5 mug/g, the metal content is less than 5 mug/g, and the dosage consumption is 10.2 kg/ton of oil.
TABLE 6
Impurity removing unit | Moving bed reactor |
Catalyst | D |
Raw oil | Raw material I |
Reaction pressure, MPa | 1.6 |
Reaction temperature, DEG C | 380 |
Hydrogen to oil ratio, nm 3 /m 3 | 50 |
Consumption of agent, kg/ton oil | 10.2 |
Liquid phase reaction effluent | |
Silicon content, μg/g | <1 |
Chlorine content, μg/g | <0.5 |
Metal content, μg/g | <5 |
It should be noted that the above-mentioned embodiments of the present invention are merely examples, and are not intended to limit the present invention, and various modifications and variations of the present invention will be apparent to those skilled in the art. Any modification, equivalent replacement, improvement, etc. made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (21)
1. A method for preparing cracking raw materials from waste plastic oil and/or junked tire oil, comprising the following steps:
(1) The waste plastic oil and/or the waste tire oil enter a impurity removal reactor to contact with a waste hydrogenation catalyst in the presence of hydrogen, and the impurity removal reaction is carried out under the impurity removal reaction condition, wherein the silicon content of a liquid phase material in the obtained reaction effluent is less than 1 mug/g, and the metal content is less than 5 mug/g; the waste hydrogenation catalyst is a protective agent and a catalyst which are selected from the end of any fixed bed hydrogenation process device in the hydrocarbon oil processing field, wherein the waste hydrogenation catalyst comprises 0-50% by weight of hydrogenation active metal oxide, 5-50% by weight of carbon and 6-40% by weight of sulfur based on the total weight of the waste hydrogenation catalyst, and the hydrogenation active metal is selected from one or more of VIII group metal and VIB group metal; the impurity removal reaction conditions are as follows: hydrogen partial pressure of 0.5-20.0 MPa, reaction temperature of 60-500 ℃ and volume space velocity of 0.1-30 h -1 Hydrogen oil volume ratio of 5-1000 Nm 3 /m 3 ;
(2) And (3) a hydrofining unit, wherein the reaction effluent obtained in the step (1) enters a hydrofining reactor to be contacted with a hydrofining catalyst, hydrofining reaction is carried out under the condition of hydrofining reaction, and after the reaction effluent is separated, a gas-phase material and a liquid-phase material are obtained, and all or part of the obtained liquid-phase material is a cracking raw material for preparing ethylene by steam cracking.
2. The method according to claim 1, wherein the waste plastic oil is a hydrocarbon material obtained by one or more conversion methods of thermal cracking, catalytic cracking, and dissolution liquefaction of waste plastic; the distillation range of the waste plastic oil is 30-700 ℃, the silicon content is less than 10000 mug/g, the chlorine content is less than 10000 mug/g, and the metal content is less than 10000 mug/g.
3. The method according to claim 2, wherein the waste plastics are one or more of fresh household garbage, industrial and agricultural production and aged garbage, and the waste plastics are one or more selected from PE, PP, PS, PVC.
4. The method according to claim 1, wherein the junked tire oil is a hydrocarbon material obtained by one or more conversion methods of thermal cracking, catalytic cracking, and dissolution liquefaction of junked tires; the distillation range of the waste tire oil is 30-700 ℃, the silicon content is less than 10000 mug/g, the chlorine content is less than 10000 mug/g, and the metal content is less than 10000 mug/g.
5. The method according to claim 4, wherein the scrap tires are various scrap tires made of natural rubber and/or synthetic rubber.
6. The process according to claim 1, characterized in that the de-hybridization reactor is at least one fixed bed hydrogenation reactor and/or at least one moving bed hydrogenation reactor.
7. The method according to claim 1, wherein the impurity removal reactor is two or more fixed bed hydrogenation reactors connected in parallel, each reactor is filled with a waste hydrogenation catalyst, the waste plastic oil and/or waste tire oil is subjected to impurity removal reaction through at least one fixed bed hydrogenation reactor, and when the waste hydrogenation catalyst in the fixed bed hydrogenation reactor is saturated with silicon or saturated with metal, the waste plastic oil and/or waste tire oil is fed into the other fixed bed hydrogenation reactors in a switching manner.
8. The process of claim 7, wherein the waste hydrogenation catalyst in the hydrogenation reactor is considered to be saturated with silicon or metal when the silicon content of the liquid phase material in the reaction effluent is 1 μg/g or more or when the metal content is 5 μg/g or more.
9. The method according to claim 1, wherein the equivalent diameter of the spent hydrogenation catalyst is 0.5-16 mm.
10. The method according to claim 1, wherein the waste hydrogenation catalyst comprises, based on the total weight of the waste hydrogenation catalyst, 0-50 wt% of molybdenum oxide and/or tungsten oxide, 0-40 wt% of nickel oxide and/or cobalt oxide, 5-30 wt% of carbon, and 6-30 wt% of sulfur.
11. The method according to claim 1, wherein the waste hydrogenation catalyst comprises 1-40 wt% of hydrogenation active metal oxide and 5-20 wt% of carbon based on the total weight of the waste hydrogenation catalyst, and the hydrogenation active metal is selected from one or more of group VIII metal and group VIB metal.
12. The method according to claim 1, wherein the impurity removal reactor is further filled with a dechlorinating agent, and the filling volume ratio of the dechlorinating agent to the waste catalyst is 1-80: 20 to 99.
13. The method according to claim 12, wherein the dechlorinating agent comprises at least one group IA metal compound and/or at least one group IIA metal compound, optionally one or several metal oxides selected from Cu, fe, zn, and a carrier and/or a binder;
the carrier and/or the binder is selected from one or more of silicon oxide, aluminum oxide, silicon oxide-aluminum oxide, zirconium oxide and clay.
14. The process of claim 12, wherein the chlorine content of the liquid phase material in the reaction effluent of step (1) is less than 0.5 μg/g.
15. The method according to claim 1, wherein the stripping reaction conditions are: hydrogen partial pressure of 1-12 MPa, reaction temperature of 100-450 ℃ and volume space velocity of 0.2-20 h -1 Hydrogen oil volume ratio of 5-800 Nm 3 /m 3 。
16. The process of claim 1, wherein the hydrofinishing catalyst of step (2) comprises a hydrofinishing metal active component and a support, the hydrofinishing metal active component being present in an amount of from 5 to 50 wt% on an oxide basis based on the total weight of the hydrofinishing catalyst.
17. The process according to claim 16, characterized in that the hydrogenating metal active component is at least one metal element selected from the group consisting of group VIB metal elements and at least one metal element selected from the group consisting of group VIII metal elements, the group VIB metal elements being molybdenum and/or tungsten and the group VIII metal elements being cobalt and/or nickel; the total weight of the hydrofining catalyst is taken as a reference, the content of the metal element of the VIB group is 4-40 wt% and the content of the metal element of the VIII group is 1-10 wt% based on oxide.
18. The process according to claim 17, wherein the group VIB metal element content is 8 to 35 wt.% and the group VIII metal element content is 2 to 5 wt.% on an oxide basis based on the total weight of the hydrofinishing catalyst.
19. The process of claim 1, wherein the hydrofinishing reaction conditions of step (2) are: hydrogen partial pressure of 1.0-20.0 MPa, reaction temperature of 250-430 ℃ and volume space velocity of 0.5-20 h -1 The volume ratio of hydrogen to oil is 50-1000 Nm 3 /m 3 。
20. The process of claim 1, wherein the hydrofinishing reaction conditions of step (2) are: hydrogen partial pressure of 1.0-12 MPa, reaction temperature of 280-400 ℃ and volume space velocity of 0.5-15 h -1 The volume ratio of hydrogen to oil is 100-800 Nm 3 /m 3 。
21. The process according to claim 1, wherein the liquid phase material obtained in step (2) has an olefin content of 2 mass% or less, a sulfur content of < 50. Mu.g/g, a nitrogen content of < 50. Mu.g/g, a silicon content of < 1. Mu.g/g, a chlorine content of < 0.5. Mu.g/g and a metal content of < 1. Mu.g/g.