CN114437608A - 一种抗菌粉末涂料及制备方法 - Google Patents
一种抗菌粉末涂料及制备方法 Download PDFInfo
- Publication number
- CN114437608A CN114437608A CN202111616163.9A CN202111616163A CN114437608A CN 114437608 A CN114437608 A CN 114437608A CN 202111616163 A CN202111616163 A CN 202111616163A CN 114437608 A CN114437608 A CN 114437608A
- Authority
- CN
- China
- Prior art keywords
- powder coating
- antibacterial
- pigment
- parts
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明一种抗菌粉末涂料及制备方法，其粉末涂料各组成原料按质量份计为：环氧树脂25‑35份、聚酯树脂25‑35份、流平剂1份、增光剂0.5份、抗菌助剂0.3‑2份、颜填料25‑45份，本发明制备简单，抗菌效果好，粒径在38‑42微米的粉末涂料附着性好，易于涂刷，粉末涂料中的抗菌助剂分散均匀，对金黄色葡萄球菌和大肠杆菌达到98％以上的有效杀菌，且消杀效果持续时间长，避免人们频繁喷洒消毒剂。
Description
技术领域
本发明涉及涂料制备技术领域，具体为一种抗菌粉末涂料及制备方法。
背景技术
粉末涂料是一种新型的不含溶剂的固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。粉末涂料是以树脂和颜填料为基础，加入必要的固化剂、添加剂等按照一定比例的混合，熔融挤出后的分散体进行冷却，然后按照既定的粒度进行微分碎，最后进行分级筛选，从而制成的粉末状涂料。
细菌是危害人类健康的杀手，细菌的繁殖和传播可导致流行病的发生。人类普遍使用喷雾型消毒剂来对室内外的细菌进行杀灭，但其毒性大、有异味、对环境污染大，而且时效短，对细菌易产生抗药性，需要每天进行消毒操作，基于此提供一种抗菌粉末涂料。
发明内容
基于上述技术缺陷，本发明提供一种抗菌粉末涂料及制备方法，解决了上述技术问题中的技术缺陷。
本发明一种抗菌粉末涂料，其粉末涂料各组成原料按质量份计为：环氧树脂25-35份、聚酯树脂25-35份、流平剂1份、增光剂0.5份、抗菌助剂0.3-2份、颜填料25-45份。
进一步，所述抗菌助剂为无机纳米银系抗菌剂，其活性成分为纳米银或银溶胶。
进一步，纳米银的存在形式可以为银的化合物，如Agcl、AgBr，或银的络合物，或银离子Ag+，纳米银以包覆或游离的形式与载体结合。
进一步，所述颜填料为无机颜料炭黑、氧化铁颜料、铬系颜料，有机颜料酞菁蓝、有机黄、有机红中的一种或多种。
进一步，所述颜填料钛白粉﹑碳酸钙﹑硫酸钡﹑滑石粉﹑膨润土﹑石英粉中的一种或多种。
本发明抗菌粉末涂料制备方法，包括以下步骤：
S1、将配方中原料按照其对应的质量份投入混料桶内混合，得到初始混合物；
S2、采用双螺杆挤出机对初始混合物进行熔融混炼均匀分散挤出，双螺杆挤出机的挤出口对其进行压片，得到压片材料；
S3、所述挤出温度为90-110度，所述双螺杆挤出机的螺杆转速38- 50HZ；
S4、将上述步骤制成的压片材料，通过磨粉机将压片材料磨成粉末状；
S5、通过旋风机分离器或筛子将超微粉末颗粒分级筛选，其粉末粒径D50 在38-42微米的粉末涂料；
S6、通过自动装袋机将制成的粉末涂料装袋存储。
本发明一种抗菌粉末涂料及制备方法，制备简单，抗菌效果好，粒径在38-42微米的粉末涂料附着性好，易于涂刷，粉末涂料中的抗菌助剂分散均匀，对金黄色葡萄球菌和大肠杆菌达到98％以上的有效杀菌，且消杀效果持续时间长，避免人们频繁喷洒消毒剂。
具体实施方式
本发明一种抗菌粉末涂料，其粉末涂料各组成原料按质量份计为：环氧树脂25-35份、聚酯树脂25-35份、流平剂1份、增光剂0.5份、抗菌助剂0.3-2份、颜填料25-45份。
进一步，所述抗菌助剂为无机纳米银系抗菌剂，其活性成分为纳米银或银溶胶。
进一步，纳米银的存在形式可以为银的化合物，如Agcl、AgBr，或银的络合物，或银离子Ag+，纳米银以包覆或游离的形式与载体结合。
进一步，所述颜填料为无机颜料炭黑、氧化铁颜料、铬系颜料，有机颜料酞菁蓝、有机黄、有机红中的一种或多种。
进一步，所述颜填料钛白粉﹑碳酸钙﹑硫酸钡﹑滑石粉﹑膨润土﹑石英粉中的一种或多种。
所述环氧树脂耐化学品性优良，尤其是耐碱性，漆膜附着力强，特别是对金属，具有较好的耐热性和电绝缘性，漆膜保色性较好。
聚酯树脂固化后的胶层硬度大、透明性好、光亮度高、可室温加压快速固化、耐热性较好
所述流平剂是一种常用的涂料助剂，它能促使涂料在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。能有效降低涂饰液表面张力，提高其流平性和均匀性的一类物质。可改善涂饰液的渗透性，能减少刷涂时产生斑点和斑痕的可能性，增加覆盖性，使成膜均匀、自然。
无机纳米银系抗菌剂对金黄色葡萄球菌和大肠杆菌具有98％以上的杀菌效果，将抗菌剂加入粉末涂料中可实现长久有效的杀菌效果，避免人们频繁喷洒消毒剂对环境和人体健康造成损害。
所述颜填料为无机颜料炭黑、氧化铁颜料、铬系颜料，有机颜料酞菁蓝、有机黄、有机红中的一种或多种；所述颜填料钛白粉﹑碳酸钙﹑硫酸钡﹑滑石粉﹑膨润土﹑石英粉中的一种或多种，多种可选颜填料实现粉末涂料多种可选择性，增强了涂料的可观赏性，有利于产品推广。
本发明抗菌粉末涂料制备方法，包括以下步骤：
S1、将配方中原料按照其对应的质量份投入混料桶内混合，得到初始混合物；
S2、采用双螺杆挤出机对初始混合物进行熔融混炼均匀分散挤出，双螺杆挤出机的挤出口对其进行压片，得到压片材料；
S3、所述挤出温度为90-110度，所述双螺杆挤出机的螺杆转速38- 50HZ；
S4、将上述步骤制成的压片材料，通过磨粉机将压片材料磨成粉末状；
S5、通过旋风机分离器或筛子将超微粉末颗粒分级筛选，其粉末粒径D50 在38-42微米的粉末涂料；
S6、通过自动装袋机将制成的粉末涂料装袋存储。
其粉末粒径D50不限于38-42微米，本技术方案中粉末粒径D50根据应用场景涂覆的物品表面不同，应用不同的粉末粒径，38-42微米的粒径相对于其他粒径附着性较好。
环氧树脂采用聚酯改性环氧树脂，在树脂材料中添加流平剂可以获得 40微米以下的平滑膜层。
实施例1，采用环氧树脂26.5份，聚酯树脂25份、流平剂1份、增光剂0.5份、抗菌助剂2份、颜填料45份，通过该配比制成的抗菌粉末涂料对金黄色葡萄球菌和大肠杆菌达到98％以上的有效杀菌，且消杀效果持续时间长。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所述技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于本发明的保护范围。
Claims (7)
1.一种抗菌粉末涂料，其特征在于：其粉末涂料各组成原料按质量份计为：环氧树脂25-35份、聚酯树脂25-35份、流平剂1份、增光剂0.5份、抗菌助剂0.3-2份、颜填料25-45份。
2.根据权利要求1所述的抗菌粉末涂料，其特征在于：所述抗菌助剂为无机纳米银系抗菌剂，其成分为纳米银或银溶胶。
3.根据权利要求2所述的抗菌粉末涂料，其特征在于：所述纳米银为银的化合物Agcl或AgBr，或银的络合物，或银离子Ag+，纳米银以包覆形式与载体结合。
4.根据权利要求1所述的抗菌粉末涂料，其特征在于：所述颜填料为无机颜料炭黑、氧化铁颜料、铬系颜料，有机颜料酞菁蓝、有机黄、有机红中的一种或多种。
5.根据权利要求1所述的抗菌粉末涂料，其特征在于：所述颜填料钛白粉﹑碳酸钙﹑硫酸钡﹑滑石粉﹑膨润土﹑石英粉中的一种或多种。
6.根据权利要求1所述的抗菌粉末涂料，其特征在于：所述环氧树脂采用聚酯改性环氧树脂。
7.根据权利要求1-6任一项所述的抗菌粉末涂料制备方法，其特征在于：包括以下步骤：
S1、将配方中原料按照其对应的质量份投入混料桶内混合，得到初始混合物；
S2、采用双螺杆挤出机对初始混合物进行熔融混炼均匀分散挤出，双螺杆挤出机的挤出口对其进行压片，得到压片材料；
S3、所述挤出温度为90-110度，所述双螺杆挤出机的螺杆转速38-50HZ；
S4、将上述步骤制成的压片材料，通过磨粉机将压片材料磨成粉末状；
S5、通过旋风机分离器或筛子将超微粉末颗粒分级筛选，其粉末粒径D50在38-42微米的粉末涂料；
S6、通过自动装袋机将制成的粉末涂料装袋存储。