CN114391478A - 一种可降解型抑菌除味猫砂的制备方法 - Google Patents
一种可降解型抑菌除味猫砂的制备方法 Download PDFInfo
- Publication number
- CN114391478A CN114391478A CN202210052163.9A CN202210052163A CN114391478A CN 114391478 A CN114391478 A CN 114391478A CN 202210052163 A CN202210052163 A CN 202210052163A CN 114391478 A CN114391478 A CN 114391478A
- Authority
- CN
- China
- Prior art keywords
- cat litter
- parts
- powder
- odor
- bacteriostatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可降解型抑菌除味猫砂的制备方法，包括以下步骤：S1、将植物纤维、豆腐渣粉、玉米淀粉、膨化玉米粉混合粉碎，搅拌均匀；S2、在混合物中加入粘合剂、防腐剂和溶剂；S3、在混合液中缓慢加入抑菌除臭粉末，边搅拌边加入，使其均匀的分散溶解在混合液中；S4、将混合液进行造粒，筛选出粒径为(3～5mm)的颗粒进行晾晒，得到初成品；S5、将颗粒进行多次除尘，得到成品。本发明的可降解型抑菌除味猫砂的制备方法，通过选用多种取材丰富的再生资源且可降解的各类原材料进行制备而得的，制备过程简捷，整体制作过程中在配方和工艺上通过自然冷却而非烘干工艺从而促使该豆腐猫砂达到整体含水量内外保持一致，同时对环境友好，不会污染环境。
Description
技术领域
本发明涉及宠物用品技术领域，特别涉及一种可降解型抑菌除味猫砂的制备方法。
背景技术
随着社会的发展，喜欢养猫的人越来越多，在养猫的过程中，每天处理猫的排泄物成为最费时费力的事，为保护家庭环境卫生及猫的健康，猫砂应运而生。猫砂作为猫咪用来掩埋粪便和尿液的垫料，具有一定的吸水和除臭功能，是饲养宠物家庭的常用必备品。
早期的猫砂以不结团的土砂为主，这类型猫砂接触尿液不结团，包裹掩盖性差。随着技术发展，逐渐发展成结团砂。目前市面上，结团砂按材质不同主要分为膨润土猫砂、纸砂、二氧化硅水晶砂、混合猫砂和植物猫砂等等。
(1)膨润土猫砂主要由膨润土组成，这类型产品吸湿性和结团性较好，缺点是不可直接冲厕所和粉尘较大及易被猫带出猫砂盘。
(2)纸砂主要呈颗粒状，由纸屑、木屑组成，一般会负载活性炭或香精等除味成分，具有较好的抑制异味效果。缺点是不结团性、不易清理和不环保。
(3)植物猫砂主要由植物纤维、玉米粉、淀粉等压缩制备而成，相对于不结团的纸砂和不可直接冲厕的膨润土猫砂，具有较好的吸水性、结团性和便捷性，其代表性产品豆腐猫砂逐渐成为国内养猫人士的首选。但是植物猫砂易霉变和易粉化是主要的技术难题。目前的产品主要添加食品常用的一水柠檬酸或苯甲酸钠作为防腐剂，该防腐体系需在酸性条件下才有防腐效果，而植物猫砂一般会添加碳酸钙来提高硬度，猫砂整体偏碱性，故这类防腐剂防腐效果不佳。而且由于猫咪的高蛋白饮食习惯，排泄物中氨类硫类含量较高，导致排泄物气味重，单靠目前植物纤维、玉米粉、淀粉等成分无法有效的消除异味。此外，植物猫砂主要通过提高产品硬度来减少猫砂的粉化，但硬度太高影响产品的吸水速度。
(4)混合猫砂主要由植物猫砂和膨润土猫砂混合而成，兼具较好的结团和除臭效果。例如：专利文献CN106688904B介绍了一种清香型抑菌猫砂，属于膨润土猫砂，主要采用柠檬片等植物提取物和羊奶酪蛋白水解产物的抗菌肽作为抑菌成分添加到膨润土猫砂中，以实现抗菌功能，但多肽原料分离提纯困难和具有靶向性，限制了产品应用。专利文献CN111670819A公开了一种具有除臭性能的植物猫砂，属于植物猫砂，主要通过添加柠檬酸等防腐剂实现防腐效果和添加沸石等实现除臭效果。该专利采用膨润土和植物猫砂进行混合方式进行制备，由于膨润土遇水易自身凝结，在混料加水中易结块，不利于制粒和产品均匀性，工艺上较难实施。此外，其采用常见的柠檬酸、苯甲酸钠等防腐剂需在偏酸性条件才能产生较好的防腐效果。专利文献CN111567412A介绍了一种利用膨化工艺制备的球形植物猫砂，属于植物猫砂，主要通过将香精包裹在颗粒中实现掩盖臭味，但未根源性解决去除异味和抑菌问题。专利文献CN111149710A公开了一种除味抗菌硅藻土猫砂，属于少见的硅藻土猫砂，其通过负载银离子实现抑菌效果和通过改性硅藻土实现除味效果。但银离子类杀菌剂粒径小穿透性强，可能会对宠物有急性毒性作用，且原料成本较高。
目前市面上比较受欢迎的可降解型抑菌除臭猫砂，通过选用多种取材丰富的再生资源且可降解的各类原材料进行制备而得的，制备过程简捷，整体制作过程中在配方和工艺上通过自然冷却而非烘干工艺从而促使该豆腐猫砂达到整体含水量内外保持一致，同时对环境友好，不会污染环境。
发明内容
本发明的主要目的是提供一种可降解型抑菌除味猫砂的制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提出的一种可降解型抑菌除味猫砂的制备方法，包括以下步骤：
S1、将植物纤维、豆腐渣粉、玉米淀粉、膨化玉米粉按照一定的比例混合粉碎，放入搅拌器中搅拌均匀，得到混合物；
S2、在S1中得到的混合物中加入粘合剂、防腐剂和溶剂并搅拌均匀，得到混合液；
S3、在S2中得到的混合液中缓慢加入抑菌除臭粉末，边搅拌边加入，使其均匀的分散溶解在混合液中；
S4、将S3中得到的混合液进行造粒，筛选出粒径为(3～5mm)的颗粒进行晾晒，得到初成品；
S5、将颗粒进行多次除尘，得到成品。
优选地，在所述的S1中，各物质的质量份数分别为：其中
植物纤维5-100份、豆腐渣粉5-100份、玉米淀粉5-100份、膨化玉米粉5-100份。
优选地，在所述的S1中，各物质的质量份数分别为：其中
植物纤维10-50份、豆腐渣粉10-60份、玉米淀粉10-40份、膨化玉米粉5-40份。
优选地，在所述的S2中，各物质的质量份数分别为：其中
粘合剂0.1-3份、防腐剂0.01-1份和溶剂0.1-1份。
优选地，在所述的S3中，所述的抑菌除臭粉末的质量份数为0.1-10份。
优选地，在所述的S3中，所述的抑菌除臭粉末为银钛粉末(Ag/TiO2)。
优选地，所述的银钛粉末(Ag/TiO2)是以水为载体进行合成的。
本发明的可降解型抑菌除味猫砂的制备方法，制备的猫砂为一次成型的，选用多种取材丰富的再生资源且可降解的各类原材料进行制备而得，制备过程简捷，所需设备少，能量消耗显著降低，整体制作过程中在配方和工艺上通过自然冷却而非烘干工艺从而促使该豆腐猫砂达到整体含水量内外保持一致，无需高温烘干从而使产品具有含水量更低，具有更强的吸水性和结团效果，不仅保护了环境，降低了能耗，而且提高了能量利用率，并最大限度的保证了该豆腐猫砂的品质。加入抑菌除臭粉末，使得该猫砂具有抑菌除臭的效果，可以抑制猫砂中黄曲霉素、大肠杆菌等微生物的滋生，同时还可以减少猫尿猫屎中主要臭味物质氨气、硫化氢的产生，从而达到减少恶臭的目的。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图示出的结构获得其他的附图。
图1为本发明实施例提供的一种可降解型抑菌除味猫砂的制备方法流程图。
本发明目的的实现、功能特点及优点将结合实施例，参照附图做进一步说明。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
需要说明，本发明实施例中所有方向性指示(诸如上、下、左、右、前、后……)仅用于解释在某一特定姿态(如附图所示)下各部件之间的相对位置关系、运动情况等，如果该特定姿态发生改变时，则该方向性指示也相应地随之改变。
另外，在本发明中涉及“第一”、“第二”等的描述仅用于描述目的，而不能理解为指示或暗示其相对重要性或者隐含指明所指示的技术特征的数量。由此，限定有“第一”、“第二”的特征可以明示或者隐含地包括至少一个该特征。另外，各个实施例之间的技术方案可以相互结合，但是必须是以本领域普通技术人员能够实现为基础，当技术方案的结合出现相互矛盾或无法实现时应当认为这种技术方案的结合不存在，也不在本发明要求的保护范围之内。
在本发明实施例中，参照图1，该可降解型抑菌除味猫砂的制备方法，为一次成型的，选用多种取材丰富的再生资源且可降解的各类原材料进行制备而得，制备过程简捷，所需设备少，能量消耗显著降低，整体制作过程中在配方和工艺上通过自然冷却而非烘干工艺从而促使该豆腐猫砂达到整体含水量内外保持一致，无需高温烘干从而使产品具有含水量更低，具有更强的吸水性和结团效果，不仅保护了环境，降低了能耗，而且提高了能量利用率，并最大限度的保证了该豆腐猫砂的品质。加入抑菌除臭粉末，使得该猫砂具有抑菌除臭的效果，可以抑制猫砂中黄曲霉素、大肠杆菌等微生物的滋生，同时还可以减少猫尿猫屎中主要臭味物质氨气、硫化氢的产生，从而达到减少恶臭的目的。
实施例1：
S1、将植物纤维30份、豆腐渣粉30份、玉米淀粉30份、膨化玉米粉15份的比例混合粉碎，放入搅拌器中搅拌均匀，得到混合物；
S2、在S1中得到的混合物中加入粘合剂0.5份、防腐剂0.05份和溶剂0.5份，搅拌均匀，得到混合液；
S3、在S2中得到的混合液缓慢加入抑菌除臭粉末3份，边搅拌边加入，使其均匀的分散溶解在混合液中；
S4、将S3中得到的混合液通过造粒机进行造粒，通过筛粒机筛选出粒径为4mm的颗粒进行晾晒，得到初成品；
S5、将颗粒进行多次除尘，得到成品。
实施例2：
S1、将植物纤维20份、豆腐渣粉20份、玉米淀粉20份、膨化玉米粉15份的比例混合粉碎，放入搅拌器中搅拌均匀，得到混合物；
S2、在S1中得到的混合物中加入粘合剂0.3份、防腐剂0.03份和溶剂0.3份，搅拌均匀，得到混合液；
S3、在S2中得到的混合液缓慢加入抑菌除臭粉末1份，边搅拌边加入，使其均匀的分散溶解在混合液中；
S4、将S3中得到的混合液通过造粒机进行造粒，通过筛粒机筛选出粒径为3mm的颗粒进行晾晒，得到初成品；
S5、将颗粒进行多次除尘，得到成品。
实施例3：
S1、将植物纤维50份、豆腐渣粉50份、玉米淀粉50份、膨化玉米粉20份的比例混合粉碎，放入搅拌器中搅拌均匀，得到混合物；
S2、在S1中得到的混合物中加入粘合剂0.6份、防腐剂0.07份和溶剂0.6份，搅拌均匀，得到混合液；
S3、在S2中得到的混合液缓慢加入抑菌除臭粉末5份，边搅拌边加入，使其均匀的分散溶解在混合液中；
S4、将S3中得到的混合液通过造粒机进行造粒，通过筛粒机筛选出粒径为5mm的颗粒进行晾晒，得到初成品；
S5、将颗粒进行多次除尘，得到成品。
可以理解的是，上述实施例1-3中，植物纤维可以是种子纤维，例如棉、木棉等，也可以是韧皮纤维，例如亚麻、苎麻、黄麻、竹纤维等，或者是叶纤维和果实纤维，例如剑麻、蕉麻、椰子纤维等；
黏合剂可以为天然黏合剂或者合成黏合剂，例如淀粉、蛋白质、糊精、动物胶、虫胶、皮胶、松香，水玻璃等无机粘合剂，以及合成树脂、合成橡胶等有机粘合剂；
防腐剂可以为天然防腐剂或者化学防腐剂，例如乳酸链球菌素、如乳酸链球菌素、如乳酸链球菌素等；
溶剂为软水。
在上述实施例中，所述的抑菌除臭粉末为纳米载银二氧化钛(Ag/TiO2)。所述的银钛抑菌除臭粉末是以水为载体进行合成，掺杂了载银二氧化钛水剂。不仅具有零VOC、消毒杀菌的功能，还能有效的分解宠物产生的臭味气体如氨气、硫化氢等易挥发的气体。
为检验上述猫砂的杀菌除臭效果，对上述实施例1-3的方法制备的猫砂进行了试验，并随机抽取1份市售植物猫砂(厂家：浙江省金华市新猫宠物用品实力工厂，产品名称：可降解植物豆腐猫砂，货号：222212，成分：豆腐渣、淀粉、瓜尔豆胶，厂家描述产品特点：自然食材，结团快，低粉尘，低含水量)和1份膨润土猫砂(厂家：深圳市至臻卓越科技有限公司，产品名称：豆腐猫砂，品牌：宠瑾，成分：膨润土，厂家描述产品特点：粉尘少，结团实，除臭，抑菌，香气持久。)作为对比，实验结果如下：
一、杀菌消毒实验数据对比
二、除臭实验数据对比
三、毒性实验数据对比
| 项目名称 | 过敏性 | 经口毒性实验 |
| 实施例1 | 对皮肤无刺激性 | 无毒 |
| 实施例2 | 对皮肤无刺激性 | 无毒 |
| 实施例3 | 对皮肤无刺激性 | 无毒 |
| 对照组植物猫砂 | 对皮肤有稍微刺激性 | 无毒 |
| 对照组膨润土猫砂 | 对皮肤有稍微刺激性 | 无毒 |
四、各性能实验数据对比
从上述对比可以看出，本发明实施例1-3的3猫砂与同为植物猫砂和膨润土猫砂的对照相比较，本发明实施例加入抑菌除臭粉末制备的猫砂，使得该猫砂具有抑菌除臭的效果，可以抑制猫砂中黄曲霉素、大肠杆菌等微生物的滋生，同时还可以减少猫尿猫屎中主要臭味物质氨气、硫化氢的产生，从而达到减少恶臭的目的。而且，具有更强的吸水性和结团效果，不仅保护了环境，降低了能耗，而且提高了能量利用率，并最大限度的保证了该豆腐猫砂的品质。
以上所述仅为本发明的优选实施例，并非因此限制本发明的专利范围，凡是在本发明的发明构思下，利用本发明说明书及附图内容所作的等效结构变换，或直接/间接运用在其他相关的技术领域均包括在本发明的专利保护范围内。
Claims (7)
1.一种可降解型抑菌除味猫砂的制备方法，其特征在于，包括以下步骤：
S1、将植物纤维、豆腐渣粉、玉米淀粉、膨化玉米粉按照一定的比例混合粉碎，放入搅拌器中搅拌均匀，得到混合物；
S2、在S1中得到的混合物中加入粘合剂、防腐剂和溶剂并搅拌均匀，得到混合液；
S3、在S2中得到的混合液中缓慢加入抑菌除臭粉末，边搅拌边加入，使其均匀的分散溶解在混合液中；
S4、将S3中得到的混合液进行造粒，筛选出粒径为(3～5mm)的颗粒进行晾晒，得到初成品；
S5、将颗粒进行多次除尘，得到成品。
2.如权利要求1所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，在所述的S1中，各物质的质量份数分别为：其中
植物纤维5-100份、豆腐渣粉5-100份、玉米淀粉5-100份、膨化玉米粉5-100份。
3.如权利要求2所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，在所述的S1中，各物质的质量份数分别为：其中
植物纤维10-50份、豆腐渣粉10-60份、玉米淀粉10-40份、膨化玉米粉5-40份。
4.如权利要求1所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，在所述的S2中，各物质的质量份数分别为：其中
粘合剂0.1-3份、防腐剂0.01-1份和溶剂0.1-1份。
5.如权利要求1所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，在所述的S3中，所述的抑菌除臭粉末的质量份数为0.1-10份。
6.如权利要求1所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，在所述的S3中，所述的抑菌除臭粉末为银钛粉末(Ag/TiO2)。
7.如权利要求6所述的一种可降解型抑菌除味猫砂的制备方法，其特征在于，所述的银钛粉末(Ag/TiO2)是以水为载体进行合成的。