CN114191315A - 一种种植义齿用牙冠复合材料及其制备方法 - Google Patents
一种种植义齿用牙冠复合材料及其制备方法 Download PDFInfo
- Publication number
- CN114191315A CN114191315A CN202210003929.4A CN202210003929A CN114191315A CN 114191315 A CN114191315 A CN 114191315A CN 202210003929 A CN202210003929 A CN 202210003929A CN 114191315 A CN114191315 A CN 114191315A
- Authority
- CN
- China
- Prior art keywords
- powder
- agent
- mixing
- composite
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于口腔生物材料领域，具体的涉及一种种植义齿用牙冠复合材料及其制备方法，解决了传统的种植义齿用材料具有机械力学性能欠缺、生物相容性较差、不具备抗菌效果的问题，该种种植义齿用牙冠复合材料，其特征在于，包括以下质量百分数原料，70‑80％聚合物复合剂、8‑12％陶瓷复合剂、5‑8％活化剂和1‑3％抗菌剂。本发明技术方案中，通过将聚甲基丙烯酸甲酯和聚醚醚酮按比例混合得到复合材料的主体，结合了甲基丙烯酸甲酯的自然美观色泽、易加工性和聚醚醚酮的优异机械力学性能，相比于传统材料具有更优异的机械力学性能、耐磨性和美观度。
Description
技术领域
本发明属于口腔生物材料领域，具体的涉及一种种植义齿用牙冠复合材料及其制备方法。
技术背景
现今社会，口腔健康问题日益突出，严重影响了人们的生活质量。尤其在中老年人群当中，牙齿缺失的比例逐渐增加，因此临床上对义齿的需求日益增加。好的义齿在恢复正常的功能和美观的同时，还必须具有优异的力学性能、抗菌性能，这样才能保证义齿在复杂的空腔环境及使用过程中保持最佳的舒适感，才能实现最佳的修复效果。
对于缺失牙齿的修复方法，即义齿的安装方法一般可以分为三大类：分别是活动义齿、固定义齿和种植牙。其中活动义齿是指患者可以自行摘取的义齿，可以进行方便的清洗，但是咀嚼效率较低，舒服度较差。固定义齿是指利用确实牙齿两侧的完好牙齿作为基底对确实部位进行修复，其无需每次饭后进行拆卸清洗，但是安装过程中需要对确实部位两侧的完好牙齿进行部分磨除，对人体自身有一定的损害。种植义齿是近些年发展较快的技术，其具有不损伤邻近牙、稳定牢靠、小巧舒适、适应性更广等优点而逐渐受到广大医患的青睐。但是现有的大多数种植义齿用材料具有机械力学性能欠缺、生物相容性较差、不具备抗菌效果等问题。因此开发一种性能优良，患者舒适感佳的种植义齿用牙冠材料具有重要的意义和应用前景。
发明内容
针对现有技术的不足，本发明提供一种种植义齿用牙冠复合材料及其制备方法，解决了传统的种植义齿用材料具有机械力学性能欠缺、生物相容性较差、不具备抗菌效果的问题。
为实现上述目的，本发明是通过如下方案实现的：
一种种植义齿用牙冠复合材料，包括以下质量百分数原料，70-80％聚合物复合剂、8-12％陶瓷复合剂、5-8％活化剂和1-3％抗菌剂。
优选的，所述聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末以质量比为5-7:3-5混合而成。
优选的，所述陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末以质量比为55-65:10-20:5-10:3-5混合而成。
优选的，所述活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸粉末以质量比为5-8:2-3:2-3:1-2混合而成。
优选的，所述抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末以质量比为1-2:4-5:2-3:2-3混合而成。
一种种植义齿用牙冠复合材料的制备方法，包括以下步骤：
S1、按上述配比称取物料，将聚合物复合剂、陶瓷复合剂在无溶剂条件下进行混合球磨或者砂磨，得到混合粉末；
S2、将活化剂、抗菌剂加入上述混合粉末中进行混合球磨，得到最终的复合粉末；
S3、将复合粉末加热至160-210℃再进行保温1-2h，使各组分原料充分混合分散均匀，得到的混合物料在模具中挤压成型，然后室温冷却干燥，即得成品。
与现有技术相比，本发明方法的有益效果是：
(1)本发明技术方案中，通过将聚甲基丙烯酸甲酯和聚醚醚酮按比例混合得到复合材料的主体，结合了甲基丙烯酸甲酯的自然美观色泽、易加工性和聚醚醚酮的优异机械力学性能，相比于传统材料具有更优异的机械力学性能、耐磨性和美观度。此外，在原材料中添加活化剂，表面吸附有氨基酸的羟基磷灰石溶胶、生物玻璃溶胶、生物陶瓷溶胶，三者相互协同作用增强了材料的生物相容性，避免了后期的排异反应，增强了病患的使用舒适度。
(2)本发明技术方案中，通过在原材料中添加了新型了抗菌剂，该抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末组合而成，避免了小分子抗菌剂后期泄露毒害的问题，而且加入上转换纳米材料，可以将吸收的自然光转化为可以杀菌的紫外光，有机硅季铵盐不仅可以增强材料表面的抗菌性能，而且可以增强各组分之间的协同能力，更大的提高材料的抗菌性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种种植义齿用牙冠复合材料，包括以下质量百分数原料，70％聚合物复合剂、8％陶瓷复合剂、5％活化剂和1％抗菌剂；
聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末以质量比为5:3混合，再通过混合球磨的方式充分研磨而成；
陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末以质量比为55:10:5:3混合，再通过混合球磨的方式充分研磨而成；
活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸混合粉末以质量比为5:2:2:1混合，与pH值为7.4的生理盐水以质量比1:1的比例混合，在温度37℃条件下机械搅拌24h，过滤得到滤渣，将滤渣在75℃条件下风干，再通过混合球磨的方式充分研磨混合而成；
抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末以质量比为1:4:2:2混合，通过混合球磨的方式充分研磨而成，所述的上转换纳米材料可以将吸收的自然光转化为紫外光。
一种种植义齿用牙冠复合材料的制备方法，包括以下步骤：
S1、按上述配比称取物料，将聚合物复合剂、陶瓷复合剂在无溶剂条件下进行混合球磨或者砂磨，得到混合粉末；
S2、将活化剂、抗菌剂加入上述混合粉末中进行混合球磨，得到最终的复合粉末；
S3、将复合粉末加热至160℃再进行保温2h，使各组分原料充分混合分散均匀，得到的混合物料在模具中挤压成型，然后室温冷却干燥，即得成品。
实施例2
一种种植义齿用牙冠复合材料，包括以下质量百分数原料，75％聚合物复合剂、10％陶瓷复合剂、7％活化剂和2％抗菌剂；
聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末以质量比为6:4混合，通过混合球磨的方式充分研磨而成；
陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末以质量比为60:15:7:4混合，通过混合球磨的方式充分研磨而成；
活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸混合粉末以质量比为6:2.5:2.5:1.5混合，与pH值为7.4的生理盐水以质量比1:1的比例混合，在温度37℃条件下机械搅拌24h，过滤得到滤渣，将滤渣在75℃条件下风干，再通过混合球磨的方式充分研磨混合而成；
抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末以质量比为1.5:4.5:2.5:2.5混合，通过混合球磨的方式充分研磨而成，所述的上转换纳米材料可以将吸收的自然光转化为紫外光。
一种种植义齿用牙冠复合材料的制备方法，包括以下步骤：
S1、按上述配比称取物料，将聚合物复合剂、陶瓷复合剂在无溶剂条件下进行混合球磨或者砂磨，得到混合粉末；
S2、将活化剂、抗菌剂加入上述混合粉末中进行混合球磨，得到最终的复合粉末；
S3、将复合粉末加热至180℃再进行保温1.5h，使各组分原料充分混合分散均匀，得到的混合物料在模具中挤压成型，然后室温冷却干燥，即得成品。
实施例3
一种种植义齿用牙冠复合材料，包括以下质量百分数原料，80％聚合物复合剂、12％陶瓷复合剂、8％活化剂和3％抗菌剂；
聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末以质量比为7:5混合，通过混合球磨的方式充分研磨而成；
陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末以质量比为65:20:10:5混合，通过混合球磨的方式充分研磨而成；
活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸混合粉末以质量比为8:3:3:2混合，与pH值为7.4的生理盐水以质量比1:1的比例混合，在温度37℃条件下机械搅拌24h，过滤得到滤渣，将滤渣在75℃条件下风干，再通过混合球磨的方式充分研磨混合而成；
抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末以质量比为2:5:3:3混合，通过混合球磨的方式充分研磨而成，所述的上转换纳米材料可以将吸收的自然光转化为紫外光。
一种种植义齿用牙冠复合材料的制备方法，包括以下步骤：
S1、按上述配比称取物料，将聚合物复合剂、陶瓷复合剂在无溶剂条件下进行混合球磨或者砂磨，得到混合粉末；
S2、将活化剂、抗菌剂加入上述混合粉末中进行混合球磨，得到最终的复合粉末；
S3、将复合粉末加热至210℃再进行保温1h，使各组分原料充分混合分散均匀，得到的混合物料在模具中挤压成型，然后室温冷却干燥，即得成品。
按照本发明上述方案所提供的一种种植义齿用牙冠复合材料的原材料及制备方法，所制得的复合材料自然亮白，且具有一定的透明性，具有很好的机械力学性能和耐磨性，生物相容性好。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (6)
1.一种种植义齿用牙冠复合材料，其特征在于，包括以下质量百分数原料，70-80％聚合物复合剂、8-12％陶瓷复合剂、5-8％活化剂和1-3％抗菌剂；
所述聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末通过混合球磨的方式充分研磨而成；
所述陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末通过混合球磨的方式充分研磨而成；
所述活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸混合粉末与pH值为7.4的生理盐水以质量比1:1的比例混合，在温度37℃条件下机械搅拌24h，过滤得到滤渣，将滤渣在75℃条件下风干，再通过混合球磨的方式充分研磨混合而成；
所述抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末通过混合球磨的方式充分研磨而成，所述的上转换纳米材料可以将吸收的自然光转化为紫外光。
2.根据权利要求1所述的一种种植义齿用牙冠复合材料，其特征在于，所述聚合物复合剂是由聚甲基丙烯酸甲酯粉末/聚醚醚酮粉末以质量比为5-7:3-5混合而成。
3.根据权利要求1所述的一种种植义齿用牙冠复合材料，其特征在于，所述陶瓷复合剂是由氧化锆陶瓷粉末/氧化锌陶瓷粉末/氧化铱陶瓷粉末/氧化钙粉末以质量比为55-65:10-20:5-10:3-5混合而成。
4.根据权利要求1所述的一种种植义齿用牙冠复合材料，其特征在于，所述活化剂是由羟基磷灰石溶胶/生物玻璃溶胶/生物陶瓷溶胶/氨基酸粉末以质量比为5-8:2-3:2-3:1-2混合而成。
5.根据权利要求1所述的一种种植义齿用牙冠复合材料，其特征在于，所述抗菌剂是由上转换纳米材料/纳米氧化锌/纳米银/有机硅季铵盐粉末以质量比为1-2:4-5:2-3:2-3混合而成。
6.一种如权利要求1-5任一项所述的种植义齿用牙冠复合材料的制备方法，其特征在于，包括以下步骤：
S1、按上述配比称取物料，将聚合物复合剂、陶瓷复合剂在无溶剂条件下进行混合球磨或者砂磨，得到混合粉末；
S2、将活化剂、抗菌剂加入上述混合粉末中进行混合球磨，得到最终的复合粉末；
S3、将复合粉末加热至160-210℃再进行保温1-2h，使各组分原料充分混合分散均匀，得到的混合物料在模具中挤压成型，然后室温冷却干燥，即得成品。