CN114181591A - Drum set paint surface material and spraying method - Google Patents
Drum set paint surface material and spraying method Download PDFInfo
- Publication number
- CN114181591A CN114181591A CN202210140190.1A CN202210140190A CN114181591A CN 114181591 A CN114181591 A CN 114181591A CN 202210140190 A CN202210140190 A CN 202210140190A CN 114181591 A CN114181591 A CN 114181591A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- spraying
- drum
- paint surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a paint surface material for a drum set, which belongs to the technical field of paint surface spraying processing of the drum set and comprises the following components in parts by weight: main materials: 30-50 parts; auxiliary materials: 60-80 parts; diacetone acrylamide: 5-8 parts; polyacrylate material: 2-5 parts; dispersing agent: 1-3 parts; curing agent: 1-3 parts; water-based color paste: 30-40 parts; aqueous anticorrosive agent: 1-3 parts; an adhesion promoter: 3-5 parts; deionized water: 30-45 parts of the paint surface material prepared by the invention has stronger wear resistance and strength, and also has waterproof and anticorrosion functions, the service life of the paint surface material after spraying is prolonged, and the normal work of the drum set is not influenced.
Description
Technical Field
The invention relates to the technical field of spraying and processing of a drum set paint surface, in particular to a drum set paint surface material and a spraying method.
Background
Drum sets are jazz drums, which are very important percussion instruments in jazz bands.
In the production and processing process of the drum kit, the drum kit needs to be painted and protected, however, due to long-term working and knocking friction of the drum kit, the painted surface is affected, if the painted surface is poor in performance, the service life of the painted surface is affected, and the drum kit is also affected.
Disclosure of Invention
In order to achieve the purpose, the invention provides the following technical scheme: the shelf drum paint surface material comprises the following components in parts by weight:
main materials: 30-50 parts;
auxiliary materials: 60-80 parts;
diacetone acrylamide: 5-8 parts;
polyacrylate material: 2-5 parts;
dispersing agent: 1-3 parts;
curing agent: 1-3 parts;
water-based color paste: 30-40 parts;
aqueous anticorrosive agent: 1-3 parts;
an adhesion promoter: 3-5 parts;
deionized water: 30-45 parts.
Preferably, the main material comprises alumina particles, chromium oxide particles and composite alpha-ceramic micro powder.
Preferably, the auxiliary material consists of aqueous epoxy resin emulsion, styrene-acrylic emulsion and aqueous hydroxy acrylic emulsion.
Preferably, the method for spraying the drum set paint surface material comprises the following steps:
the first step is as follows: mixing the raw materials to prepare a required paint material, uniformly stirring the paint material, and adding the paint material into spraying equipment for later use;
the second step is that: cleaning a drum set to be sprayed, and airing;
the third step: then, shielding the areas which do not need to be sprayed on the drum set by using a shielding object;
the fourth step: spraying paint on the area to be sprayed of the drum kit by using spraying equipment, and uniformly spraying the paint surface material on the outer wall of the drum kit;
the fifth step: after the spraying is finished, standing the drum set, and airing the paint surface material;
and a sixth step: and detecting the drum set after the spraying is finished by using detection equipment, detecting the thickness of the sprayed paint surface, and carrying out processing treatment on unqualified paint surfaces again to ensure the processing quality of the paint surface of the drum set.
Compared with the prior art, the invention has the beneficial effects that: the paint surface material prepared by the invention has stronger wear resistance and strength, and also has waterproof and anticorrosion functions, the service life of the paint surface material after spraying is prolonged, and the normal work of the drum set is not influenced.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides a technical scheme that: the shelf drum paint surface material comprises the following components in parts by weight:
example 1:
main materials: 30 parts of (1);
auxiliary materials: 60 parts;
diacetone acrylamide: 5 parts of a mixture;
polyacrylate material: 2 parts of (1);
dispersing agent: 1 part;
curing agent: 1 part;
water-based color paste: 30 parts of (1);
aqueous anticorrosive agent: 1 part;
an adhesion promoter: 3 parts of a mixture;
deionized water: 30 parts of.
The main material comprises alumina particles, chromium oxide particles and composite alpha-ceramic micro powder.
The auxiliary material consists of aqueous epoxy resin emulsion, styrene-acrylic emulsion and aqueous hydroxy acrylic emulsion;
the preparation method of the paint surface material comprises the following steps: drying the alumina particles, the chromium oxide particles and the composite alpha-ceramic micro powder of the main material, then putting the dried particles into a ball mill for ball milling to control the particle size of the mixture to be 50-100 nanometers, then adding the water-based epoxy resin emulsion, the styrene-acrylic emulsion and the water-based hydroxy acrylic emulsion of the auxiliary material for mixing, then adding diacetone acrylamide, a polyacrylate material, a dispersing agent, a curing agent, water, a color paste, a water-based anticorrosive agent, an adhesion promoter and deionized water for mixing to prepare the required paint surface material.
A spraying method of a drum set paint surface material comprises the following steps:
the first step is as follows: mixing the raw materials to prepare a required paint material, uniformly stirring the paint material, and adding the paint material into spraying equipment for later use;
the second step is that: cleaning a drum set to be sprayed, and airing;
the third step: then, shielding the areas which do not need to be sprayed on the drum set by using a shielding object;
the fourth step: spraying paint on the area to be sprayed of the drum kit by using spraying equipment, and uniformly spraying the paint surface material on the outer wall of the drum kit;
the fifth step: after the spraying is finished, standing the drum set, and airing the paint surface material;
and a sixth step: and detecting the drum set after the spraying is finished by using detection equipment, detecting the thickness of the sprayed paint surface, and carrying out processing treatment on unqualified paint surfaces again to ensure the processing quality of the paint surface of the drum set.
Example 2:
main materials: 40 parts of a mixture;
auxiliary materials: 70 parts of (B);
diacetone acrylamide: 6 parts of (1);
polyacrylate material: 3 parts of a mixture;
dispersing agent: 2 parts of (1);
curing agent: 2 parts of (1);
water-based color paste: 35 parts of (B);
aqueous anticorrosive agent: 3 parts of a mixture;
an adhesion promoter: 4 parts of a mixture;
deionized water: 38 parts of the raw materials.
The main material comprises alumina particles, chromium oxide particles and composite alpha-ceramic micro powder.
The auxiliary material consists of aqueous epoxy resin emulsion, styrene-acrylic emulsion and aqueous hydroxy acrylic emulsion;
the preparation method of the paint surface material comprises the following steps: drying the alumina particles, the chromium oxide particles and the composite alpha-ceramic micro powder of the main material, then putting the dried particles into a ball mill for ball milling to control the particle size of the mixture to be 50-100 nanometers, then adding the water-based epoxy resin emulsion, the styrene-acrylic emulsion and the water-based hydroxy acrylic emulsion of the auxiliary material for mixing, then adding diacetone acrylamide, a polyacrylate material, a dispersing agent, a curing agent, water, a color paste, a water-based anticorrosive agent, an adhesion promoter and deionized water for mixing to prepare the required paint surface material.
A spraying method of a drum set paint surface material comprises the following steps:
the first step is as follows: mixing the raw materials to prepare a required paint material, uniformly stirring the paint material, and adding the paint material into spraying equipment for later use;
the second step is that: cleaning a drum set to be sprayed, and airing;
the third step: then, shielding the areas which do not need to be sprayed on the drum set by using a shielding object;
the fourth step: spraying paint on the area to be sprayed of the drum kit by using spraying equipment, and uniformly spraying the paint surface material on the outer wall of the drum kit;
the fifth step: after the spraying is finished, standing the drum set, and airing the paint surface material;
and a sixth step: and detecting the drum set after the spraying is finished by using detection equipment, detecting the thickness of the sprayed paint surface, and carrying out processing treatment on unqualified paint surfaces again to ensure the processing quality of the paint surface of the drum set.
Example 3:
main materials: 50 parts of a mixture;
auxiliary materials: 80 parts of a mixture;
diacetone acrylamide: 8 parts of a mixture;
polyacrylate material: 5 parts of a mixture;
dispersing agent: 3 parts of a mixture;
curing agent: 3 parts of a mixture;
water-based color paste: 40 parts of a mixture;
aqueous anticorrosive agent: 3 parts of a mixture;
an adhesion promoter: 5 parts of a mixture;
deionized water: 45 parts of the raw materials.
The main material comprises alumina particles, chromium oxide particles and composite alpha-ceramic micro powder.
The auxiliary material consists of aqueous epoxy resin emulsion, styrene-acrylic emulsion and aqueous hydroxy acrylic emulsion;
the preparation method of the paint surface material comprises the following steps: drying the alumina particles, the chromium oxide particles and the composite alpha-ceramic micro powder of the main material, then putting the dried particles into a ball mill for ball milling to control the particle size of the mixture to be 50-100 nanometers, then adding the water-based epoxy resin emulsion, the styrene-acrylic emulsion and the water-based hydroxy acrylic emulsion of the auxiliary material for mixing, then adding diacetone acrylamide, a polyacrylate material, a dispersing agent, a curing agent, water, a color paste, a water-based anticorrosive agent, an adhesion promoter and deionized water for mixing to prepare the required paint surface material.
A spraying method of a drum set paint surface material comprises the following steps:
the first step is as follows: mixing the raw materials to prepare a required paint material, uniformly stirring the paint material, and adding the paint material into spraying equipment for later use;
the second step is that: cleaning a drum set to be sprayed, and airing;
the third step: then, shielding the areas which do not need to be sprayed on the drum set by using a shielding object;
the fourth step: spraying paint on the area to be sprayed of the drum kit by using spraying equipment, and uniformly spraying the paint surface material on the outer wall of the drum kit;
the fifth step: after the spraying is finished, standing the drum set, and airing the paint surface material;
and a sixth step: detecting the painted drum by using detection equipment, detecting the thickness of the painted surface, and reprocessing the unqualified drum to ensure the processing quality of the painted surface of the drum;
according to the invention, the added raw materials are matched to prepare the paint surface material, so that the paint surface sprayed on the outer wall of the drum set is good in wear resistance and hardness, and has the functions of corrosion resistance and water resistance, the damage probability of the paint surface is reduced, the service life of the paint surface is prolonged, and the service life of the drum set is ensured;
the parameters of the prepared paint surface material are shown in the following chart:
| compressive strength (MPa) | Rub for 1h damage weight/g | Hardness (HRC) | |
| Example 1 | 92 | 0.81 | 66 |
| Example 2 | 88 | 0.83 | 65 |
| Example 3 | 84 | 0.79 | 68 |
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (4)
1. A drum set finish material, characterized by: comprises the following components by weight:
main materials: 30-50 parts;
auxiliary materials: 60-80 parts;
diacetone acrylamide: 5-8 parts;
polyacrylate material: 2-5 parts;
dispersing agent: 1-3 parts;
curing agent: 1-3 parts;
water-based color paste: 30-40 parts;
aqueous anticorrosive agent: 1-3 parts;
an adhesion promoter: 3-5 parts;
deionized water: 30-45 parts.
2. The drum kit paint surface material of claim 1, wherein: the main material comprises alumina particles, chromium oxide particles and composite alpha-ceramic micro powder.
3. The drum kit paint surface material of claim 1, wherein: the auxiliary material consists of aqueous epoxy resin emulsion, styrene-acrylic emulsion and aqueous hydroxy acrylic emulsion.
4. The method of claim 1, wherein the step of spraying the paint on the drum comprises: the method comprises the following steps:
the first step is as follows: mixing the raw materials to prepare a required paint material, uniformly stirring the paint material, and adding the paint material into spraying equipment for later use;
the second step is that: cleaning a drum set to be sprayed, and airing;
the third step: then, shielding the areas which do not need to be sprayed on the drum set by using a shielding object;
the fourth step: spraying paint on the area to be sprayed of the drum kit by using spraying equipment, and uniformly spraying the paint surface material on the outer wall of the drum kit;
the fifth step: after the spraying is finished, standing the drum set, and airing the paint surface material;
and a sixth step: and detecting the drum set after the spraying is finished by using detection equipment, detecting the thickness of the sprayed paint surface, and carrying out processing treatment on unqualified paint surfaces again to ensure the processing quality of the paint surface of the drum set.