CN114128955B - 一种基于红外原理的保健鞋及其制备方法 - Google Patents

一种基于红外原理的保健鞋及其制备方法 Download PDF

Info

Publication number
CN114128955B
CN114128955B CN202111312699.1A CN202111312699A CN114128955B CN 114128955 B CN114128955 B CN 114128955B CN 202111312699 A CN202111312699 A CN 202111312699A CN 114128955 B CN114128955 B CN 114128955B
Authority
CN
China
Prior art keywords
layer
antistatic
far infrared
antibacterial
mass concentration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202111312699.1A
Other languages
English (en)
Other versions
CN114128955A (zh
Inventor
刘昭霞
彭飘林
吕美莲
李政仕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liming Vocational University
Original Assignee
Liming Vocational University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liming Vocational University filed Critical Liming Vocational University
Priority to CN202111312699.1A priority Critical patent/CN114128955B/zh
Publication of CN114128955A publication Critical patent/CN114128955A/zh
Application granted granted Critical
Publication of CN114128955B publication Critical patent/CN114128955B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及保健鞋产品制备技术领域，具体涉及一种基于红外原理的保健鞋及其制备方法。其中，保健鞋包括鞋帮、鞋垫和鞋底，鞋帮和鞋垫固定连接形成保健鞋整体结构；鞋垫从上到下依次包括固定为一体结构的抗菌层、抗静电层、网格布、加强层、保暖层以及稳固层；抗静电层、网格布以及加强层之间固定安装有对应人体脚底穴位的磁疗器；网格布的表面涂覆有纳米远红外材料，网格布外部的纳米远红外材料涂层表面固定设置有用于防止汗液渗透的透明防水膜；抗菌层以及抗静电层上均阵列开设有多个用于远红外线释放的通孔。本申请结构新颖，抗菌效果及远红外保健效果较好，具有较好的实用价值及推广价值。

Description

一种基于红外原理的保健鞋及其制备方法
技术领域
本发明涉及保健鞋产品制备技术领域，具体涉及一种基于红外原理的保健鞋及其制备方法。
背景技术
远红外线是太阳光谱的一部分，远红外能量光谱已被科学证明为“声明光波”。远红外线渗入人体后，会引起人体细胞的原子和分子共振，并使人体的微血管扩张，进而达到活化组织细胞，加速血液循环，防止组织细胞老化，加强人体的免疫系统之目的。
许多产品利用电子仪器发射远红外波，并利用一定的材料介质，制成远红外理疗产品，但在穿戴设备上，则实现起来即为不便利。一些日常产品虽然也使用了远红外技术，但是功效的长久性以及使用的便捷性成为一个技术难点。
经过发明人调研发现：近年来采用远红外光谱制备鞋垫，并且提供足疗保健的技术逐渐受到人们的广泛重视。目前有申请号为201620756878.2的中国专利公布了一种纳米远红外保健鞋垫，该鞋垫采用有纳米远红外材料作为红外放射源，结合网布构建鞋垫，以对人体进行红外足疗。
但是，发明人进一步分析认为：目前提供的纳米远红外保健鞋垫能够实现远红外足疗，但是在具体使用过程中，仍然存在一些不足：主要集中在鞋垫没有考虑磁疗技术手段，其足疗功效需要进一步改善；同时，发明人在实际生活穿鞋体验中还发现，现有的鞋垫在垫入鞋子内部之后，在人体步行的过程中，在脚力的作用下有时容易导致鞋垫向后移动，严重的时候会导致软质鞋垫的尾部移动翻出鞋子，使鞋子的脚尖位置空出位置，给人体穿鞋带来不舒适的感觉；进一步地，现有鞋垫不具备抗菌功能，其功能相对比较单一。
为此，本申请提供一种基于红外原理的保健鞋及其制备方法，在保证远红外保健足疗效果的同时，还进一步实现磁疗按摩和提高鞋垫安装的稳定性，进而有效解决现有技术存在的不足和缺陷。
发明内容
本发明的目的就在于：针对目前存在的上述问题，提供一种基于红外原理的保健鞋及其制备方法，在保证远红外保健足疗效果的同时，还进一步实现磁疗按摩和提高鞋垫安装的稳定性，进而有效解决现有技术存在的不足和缺陷。
为了实现上述目的，本发明采用的技术方案是：
一种基于红外原理的保健鞋，包括鞋帮、鞋垫和鞋底，鞋帮和鞋垫固定连接形成保健鞋整体结构；所述鞋垫从上到下依次包括固定为一体结构的抗菌层、抗静电层、网格布、加强层、保暖层以及稳固层；所述抗静电层、网格布以及加强层之间固定安装有对应人体脚底穴位的磁疗器；所述网格布的表面涂覆有纳米远红外材料，网格布外部的纳米远红外材料涂层表面固定设置有用于防止汗液渗透的透明防水膜；所述抗菌层以及抗静电层上均阵列开设有多个用于远红外线释放的通孔；所述稳固层底面设置有多个向脚后跟方向倾斜的斜柱，鞋底的上表面开设有多个与所述斜柱相匹配的斜孔；所述鞋垫与鞋底之间通过斜柱嵌入斜孔内部进行稳定安装。
优选的，所述抗菌层为香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维混纺而成的面料层；所述香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维的质量比为2:2:3:1；所述抗菌层通过抗菌染整处理之后固定粘接设置于所述抗静电层的外表面。设置抗菌层的作用在于，能够有效提高鞋垫的抗菌效果，尤其在男性穿戴者方面，部分男性脚底通常容易感染一些细菌，从而引起脚臭或者脚痒等情况发生。为此，设置抗菌层能够在一定程度上抑制细菌的滋生，有效保持鞋子内部的抗菌效果及安全性。
优选的，所述抗静电层为抗静电丝、涤纶纤维以及氨纶纤维混纺而成的面料层，所述抗静电层的表面通过抗静电剂进行处理并烘干；所述抗静电丝、涤纶纤维以及氨纶纤维的质量比为5:2:2。抗静电层的设置，主要为了解决现有毛鞋垫表面容易产生静电的不足。尤其在冬季比较干燥，采用表面带有绒毛或者易带静电的鞋垫时，容易产生类似毛衣表面静电现象的情况，因此现有鞋垫也需解决静电问题，提高其抗静电效果。
优选的，所述网格布的网孔为蜂巢孔结构，网格布的网孔内部填充有纳米远红外材料，防水膜对称设置在网格布的上层面和下层面。采用网格布的好处在于：一方面便于纳米远红外材料涂覆在表面，并且便于在网孔内部填充一些纳米远红外材料；另一方面，蜂巢结构具有较好的强度，利于保持鞋垫的抗压能力。
优选的，所述加强层为高强度芳纶纤维与聚氨酯纤维、腈纶纤维以及锦纶纤维混纺而成的面料层；所述芳纶纤维、聚氨酯纤维、腈纶纤维以及锦纶纤维的质量比为5:1:1:2；所述保暖层为棉纤维面料层；所述稳固层为橡胶材料层或硅胶材料层；所述鞋底的底面设置有“人”字形结构或“W”字形结构的防滑纹；鞋底内部设置有多个气泡孔，气泡孔内部充满流质胶体。一方面，加强层的设置主要为了提高鞋垫的整体强度，保证鞋垫的整体耐用性；另一方面，鞋底上表面以及鞋垫底面的结构设计，利于保证鞋垫安装的稳定性。当斜柱嵌入斜孔内部之后，人体在穿鞋并安装鞋垫行走时，脚底步行对鞋垫产生的向后作用力能够得到斜柱和斜孔配合结构的承受，避免在该作用力下导致鞋垫后移，保证鞋垫安装的稳定性，避免出现鞋垫尾部后移而引起的脚尖位置空位情况发生。
优选的，所述抗静电层、网格布以及加强层上开设有安装孔，所述磁疗器配合嵌入所述安装孔中进行固定安装；所述磁疗器的顶部为磁石，磁石底部固定连接圆筒结构的内筒；磁疗器的底部为底盖，所述底盖的顶部固定连接圆筒结构的外筒，所述内筒配合嵌入所述外筒中进行可相对滑动的配合安装；所述磁石的底面以及底盖的顶面中心位置通过弹簧固定连接，所述弹簧位于内筒以及外筒内部；所述磁石以及底盖的外形均为圆形片结构，圆形片的外表面为球形面，圆形片连接弹簧的一面为水平面。磁疗器的主要作用在于：将磁疗器按照人体穴位的方位进行排布，人体穿上带有该鞋垫的鞋子之后，足底除了能够接受远红外治疗保养之外，还能够接受一定程度的足底磁疗按摩。通过弹簧以及磁石的设置，能够让人体在行走时，结合足底对鞋垫的作用力对磁石进行按压，得到一定的学位按摩，并且当力度较大时，结合弹簧的作用能够将磁石向下按压一定距离，从而利于调节磁石按压人体穴位的力度，避免因为磁石按压人体足底力度过大而引起的不适。
如上所述的一种基于红外原理的保健鞋的制备方法，包括如下步骤：
步骤1：鞋体制备：制备鞋帮和鞋底，将鞋帮和鞋底通过缝制方式缝合为一体结构；将鞋帮和鞋底相互缝合的位置浸入补鞋用粘胶，将缝合位置的缝隙进行密封粘连；
步骤2：鞋垫制备：抗菌层进行抗菌染整处理并烘干；抗静电层进行抗静电剂处理并烘干；将抗菌层和抗静电层进行固定粘连；在抗静电层的底面开设若干用于安装磁石的内嵌凹槽；
将加强层、保暖层以及稳固层进行固定粘接；在加强层上开设用于安装底盖的内嵌凹槽；
准备网格布，在网格布上涂覆纳米远红外材料，并在网格布的网孔内同时填充纳米远红外材料；然后在网格布的上表面固定粘接防水膜，并在网格布上开设安装孔；
将磁疗器穿过安装孔进行安装，保证磁石位于网格布上方，底盖位于网格布下方；
随后将磁石嵌入抗静电层的内嵌凹槽内，将底盖嵌入加强层的内嵌凹槽中；然后将网格布分别与抗静电层和加强层固定粘接为一体结构；
步骤3：鞋垫安装：将鞋垫放入保健鞋内，让稳固层底部的斜柱嵌入斜孔内部进行配合安装。
优选的，所述步骤2中，抗菌层(3)通过抗菌整理剂进行抗菌处理；抗菌整理剂按照质量组分准备质量浓度0.6％-0.8％的蓖麻油酸丁酯硫酸钠2份，1.5％-1.7％的2-甲基-4-异噻唑啉-3-酮3份，0.02％-0.08％的双氧水2份，0.1％-0.2％的2-羟基-4-正辛氧基二苯甲酮2份，0.02％-0.05％的硫酸铜溶液1份，0.18％-0.3％的脂肪醇聚氧乙烯丙基磺酸2份，0.05％-0.09％的聚乙烯醇2份，0.12％-0.15％的十二烷基羧甲基钠型咪唑啉醋酸盐1份和1.5％-1.8％的二甲基二烯丙基氯化铵-丙烯酰胺共聚物1份，以上组分按质量比1:5与水混合均匀后得到。
优选的，所述步骤2中，所述抗静电层(4)采用抗静电助剂进行处理；
抗静电助剂的制备步骤为：首先按照质量组分准备质量浓度30％-50％的环氧乙烷1份、10％-15％的十二醇2份、5％-10％的双氧水1份、5％-8％的五氧化二磷3份、3％-8％的甲醇2份、5％-10％的十六硫醇1份和3％-5％的氢氧化钠1份；然后将反应釜预热至95摄氏度并保持6-8分钟，向其中加入十二醇和氢氧化钠，在此温度下将其混合搅匀；然后缓慢加入甲醇、十六硫醇及五氧化二磷，再次混合均匀之后抽真空脱水至反应釜内无水馏出，并注入氮气将反应釜内残余的空气驱除；再向其中通入环氧乙烷，加压至0.3Mpa，且反应温度控制在150-160摄氏度，并在反应150分钟后将得到的料液冷却至80摄氏度；将其转移至酯化釜中，同时往酯化釜中加入五氧化二磷以及双氧水，在此温度下反应120分钟后，趁热用100目的不锈钢筛过滤，再将滤液用氢氧化钾水溶液中和后，静置、冷却以得到抗静电助剂。
涂覆有纳米远红外材料的网格布可以发射远红外线。所述网格布的网格结构为蜂巢结构，利于涂覆及网孔填充纳米远红外材料。这种材料能够持续发出4～16微米的远红外光波。这种涂覆在网格布上并使网格布具有发射远红外光波的材料可以是生物炭、碳纤维制品等纳米远红外材料。
同时，网格布嵌入鞋垫基底的上表面，而网格布由若干筋条交错而成，这些筋条形成一个个的远红外发射点。在具体使用时，所述通孔的孔径均可以设置为2mm～3mm。每个通孔都成为远红外线的发射源点，还使得人体足部得到舒适的远红外保健治疗。人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
由于采用了上述技术方案，本发明的有益效果是：
一方面，本申请能够保证保健鞋的远红外保健效果，使人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
另一方面，抗菌层以及抗静电层的设计，能够有效解决现有鞋垫存在的抗菌效果及抗静电效果较差的不足和缺陷，提高鞋垫的抗菌及抗静电综合性能，提高人体穿戴的安全性及舒适性。
再一方面，本申请通过磁疗器的设置，能够对人体脚底的学位进行一定程度的按摩，尤其在人体行走的过程中，一按一松的节奏，利于人体足底的按摩效果保证，提高鞋垫的整体磁疗功能。而设置在磁疗器内部的弹簧结构，利于缓冲足底受到的按摩压力调节，避免压力过大而引起人体不适。
最后，本申请保健效果较好，通过鞋垫与鞋底的整体配合，能够保证鞋垫安装的稳定性及限制鞋垫向后位移，具有较好的实用价值及推广价值。
附图说明
图1为本发明的磁石排布结构示意图；
图2为本发明的保健鞋俯视结构示意图；
图3为本发明的保健鞋剖视结构示意图；
图4为本发明图3的局部示意图A；
图5为本发明的网格布结构示意图。
图中：1、鞋帮；2、鞋垫；3、抗菌层；4、抗静电层；5、网格布；6、加强层；7、保暖层；8、稳固层；9、鞋底；10、通孔；11、气泡孔；12、流质胶体；13、斜孔；14、斜柱；15、磁疗器；16、安装孔；17、磁石；18、内筒；19、外筒；20、弹簧；21、防水膜；22、底盖。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例，基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1，如图1-5所示：
一种基于红外原理的保健鞋，包括鞋帮1、鞋垫2和鞋底9，鞋帮1和鞋垫2固定连接形成保健鞋整体结构；所述鞋垫2从上到下依次包括固定为一体结构的抗菌层3、抗静电层4、网格布5、加强层6、保暖层7以及稳固层8；所述抗静电层4、网格布5以及加强层6之间固定安装有对应人体脚底穴位的磁疗器15；所述网格布5的表面涂覆有纳米远红外材料，网格布5外部的纳米远红外材料涂层表面固定设置有用于防止汗液渗透的透明防水膜21；所述抗菌层3以及抗静电层4上均阵列开设有多个用于远红外线释放的通孔10；所述稳固层8底面设置有多个向脚后跟方向倾斜的斜柱14，鞋底9的上表面开设有多个与所述斜柱14相匹配的斜孔13；所述鞋垫2与鞋底9之间通过斜柱14嵌入斜孔13内部进行稳定安装。
优选的，所述抗菌层3为香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维混纺而成的面料层；所述香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维的质量比为2:2:3:1；所述抗菌层3通过抗菌染整处理之后固定粘接设置于所述抗静电层4的外表面。设置抗菌层3的作用在于，能够有效提高鞋垫2的抗菌效果，尤其在男性穿戴者方面，部分男性脚底通常容易感染一些细菌，从而引起脚臭或者脚痒等情况发生。为此，设置抗菌层3能够在一定程度上抑制细菌的滋生，有效保持鞋子内部的抗菌效果及安全性。
优选的，所述抗静电层4为抗静电丝、涤纶纤维以及氨纶纤维混纺而成的面料层，所述抗静电层4的表面通过抗静电剂进行处理并烘干；所述抗静电丝、涤纶纤维以及氨纶纤维的质量比为5:2:2。抗静电层4的设置，主要为了解决现有毛鞋垫2表面容易产生静电的不足。尤其在冬季比较干燥，采用表面带有绒毛或者易带静电的鞋垫2时，容易产生类似毛衣表面静电现象的情况，因此现有鞋垫2也需解决静电问题，提高其抗静电效果。
优选的，所述网格布5的网孔为蜂巢孔结构，网格布5的网孔内部填充有纳米远红外材料，防水膜21对称设置在网格布5的上层面和下层面。采用网格布5的好处在于：一方面便于纳米远红外材料涂覆在表面，并且便于在网孔内部填充一些纳米远红外材料；另一方面，蜂巢结构具有较好的强度，利于保持鞋垫2的抗压能力。
优选的，所述加强层6为高强度芳纶纤维与聚氨酯纤维、腈纶纤维以及锦纶纤维混纺而成的面料层；所述芳纶纤维、聚氨酯纤维、腈纶纤维以及锦纶纤维的质量比为5:1:1:2；所述保暖层7为棉纤维面料层；所述稳固层8为橡胶材料层或硅胶材料层；所述鞋底9的底面设置有“人”字形结构或“W”字形结构的防滑纹；鞋底9内部设置有多个气泡孔11，气泡孔11内部充满流质胶体12。一方面，加强层6的设置主要为了提高鞋垫2的整体强度，保证鞋垫2的整体耐用性；另一方面，鞋底9上表面以及鞋垫2底面的结构设计，利于保证鞋垫2安装的稳定性。当斜柱14嵌入斜孔13内部之后，人体在穿鞋并安装鞋垫2行走时，脚底步行对鞋垫2产生的向后作用力能够得到斜柱14和斜孔13配合结构的承受，避免在该作用力下导致鞋垫2后移，保证鞋垫2安装的稳定性，避免出现鞋垫2尾部后移而引起的脚尖位置空位情况发生。
鞋底内部设置气泡，并且在气泡内部填充流质胶体，其主要目的在于防止鞋底开裂。万一在鞋底出现开裂情况时，流质胶体能够及时将开裂缝隙堵住，从而保证鞋底的正常耐用性及抗裂性。防滑纹的设置则主要为了提高鞋底的防滑效果。
优选的，所述抗静电层4、网格布5以及加强层6上开设有安装孔16，所述磁疗器15配合嵌入所述安装孔16中进行固定安装；所述磁疗器15的顶部为磁石17，磁石17底部固定连接圆筒结构的内筒18；磁疗器15的底部为底盖22，所述底盖22的顶部固定连接圆筒结构的外筒19，所述内筒18配合嵌入所述外筒19中进行可相对滑动的配合安装；所述磁石17的底面以及底盖22的顶面中心位置通过弹簧20固定连接，所述弹簧20位于内筒18以及外筒19内部；所述磁石17以及底盖22的外形均为圆形片结构，圆形片的外表面为球形面，圆形片连接弹簧20的一面为水平面。磁疗器15的主要作用在于：将磁疗器15按照人体穴位的方位进行排布，人体穿上带有该鞋垫2的鞋子之后，足底除了能够接受远红外治疗保养之外，还能够接受一定程度的足底磁疗按摩。通过弹簧20以及磁石17的设置，能够让人体在行走时，结合足底对鞋垫2的作用力对磁石17进行按压，得到一定的学位按摩，并且当力度较大时，结合弹簧20的作用能够将磁石17向下按压一定距离，从而利于调节磁石17按压人体穴位的力度，避免因为磁石17按压人体足底力度过大而引起的不适。
如上所述的一种基于红外原理的保健鞋的制备方法，包括如下步骤：
步骤1：鞋体制备：制备鞋帮1和鞋底9，将鞋帮1和鞋底9通过缝制方式缝合为一体结构；将鞋帮1和鞋底9相互缝合的位置浸入补鞋用粘胶，将缝合位置的缝隙进行密封粘连；
步骤2：鞋垫2制备：抗菌层3进行抗菌染整处理并烘干；抗静电层4进行抗静电剂处理并烘干；将抗菌层3和抗静电层4进行固定粘连；在抗静电层4的底面开设若干用于安装磁石17的内嵌凹槽；
将加强层6、保暖层7以及稳固层8进行固定粘接；在加强层6上开设用于安装底盖22的内嵌凹槽；
准备网格布5，在网格布5上涂覆纳米远红外材料，并在网格布5的网孔内同时填充纳米远红外材料；然后在网格布5的上表面固定粘接防水膜21，并在网格布5上开设安装孔16；
将磁疗器15穿过安装孔16进行安装，保证磁石17位于网格布5上方，底盖22位于网格布5下方；
随后将磁石17嵌入抗静电层4的内嵌凹槽内，将底盖22嵌入加强层6的内嵌凹槽中；然后将网格布5分别与抗静电层4和加强层6固定粘接为一体结构；
步骤3：鞋垫2安装：将鞋垫2放入保健鞋内，让稳固层8底部的斜柱14嵌入斜孔13内部进行配合安装。
优选的，所述步骤2中，抗菌层(3)通过抗菌整理剂进行抗菌处理；抗菌整理剂按照质量组分准备质量浓度0.6％-0.8％的蓖麻油酸丁酯硫酸钠2份，1.5％-1.7％的2-甲基-4-异噻唑啉-3-酮3份，50％-70％的双氧水2份，0.1％-0.2％的2-羟基-4-正辛氧基二苯甲酮2份，0.02％-0.05％的硫酸铜溶液1份，0.18％-0.3％的脂肪醇聚氧乙烯丙基磺酸2份，0.05％-0.09％的聚乙烯醇2份，0.12％-0.15％的十二烷基羧甲基钠型咪唑啉醋酸盐1份和1.5％-1.8％的二甲基二烯丙基氯化铵-丙烯酰胺共聚物1份，以上组分按质量比1:5与水混合均匀后得到。
优选的，所述步骤2中，所述抗静电层(4)采用抗静电助剂进行处理；
抗静电助剂的制备步骤为：首先按照质量组分准备质量浓度30％-50％的环氧乙烷1份、10％-15％的十二醇2份、50％-70％的双氧水1份、5％-8％的五氧化二磷3份、3％-8％的甲醇2份、5％-10％的十六硫醇1份和3％-5％的氢氧化钠1份；然后将反应釜预热至95摄氏度并保持6-8分钟，向其中加入十二醇和氢氧化钠，在此温度下将其混合搅匀；然后缓慢加入甲醇、十六硫醇及五氧化二磷，再次混合均匀之后抽真空脱水至反应釜内无水馏出，并注入氮气将反应釜内残余的空气驱除；再向其中通入环氧乙烷，加压至0.3Mpa，且反应温度控制在150-160摄氏度，并在反应150分钟后将得到的料液冷却至80摄氏度；将其转移至酯化釜中，同时往酯化釜中加入五氧化二磷以及双氧水，在此温度下反应120分钟后，趁热用100目的不锈钢筛过滤，再将滤液用氢氧化钾水溶液中和后，静置、冷却以得到抗静电助剂。
涂覆有纳米远红外材料的网格布5可以发射远红外线。所述网格布5的网格结构为蜂巢结构，利于涂覆及网孔填充纳米远红外材料。这种材料能够持续发出4～16微米的远红外光波。这种涂覆在网格布5上并使网格布5具有发射远红外光波的材料可以是生物炭、碳纤维制品等纳米远红外材料。
同时，网格布5嵌入鞋垫2基底的上表面，而网格布5由若干筋条交错而成，这些筋条形成一个个的远红外发射点。在具体使用时，所述通孔10的孔径均可以设置为2mm～3mm。每个通孔10都成为远红外线的发射源点，还使得人体足部得到舒适的远红外保健治疗。人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
由于采用了上述技术方案，本发明的有益效果是：
一方面，本申请能够保证保健鞋的远红外保健效果，使人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
另一方面，抗菌层3以及抗静电层4的设计，能够有效解决现有鞋垫2存在的抗菌效果及抗静电效果较差的不足和缺陷，提高鞋垫2的抗菌及抗静电综合性能，提高人体穿戴的安全性及舒适性。
再一方面，本申请通过磁疗器15的设置，能够对人体脚底的学位进行一定程度的按摩，尤其在人体行走的过程中，一按一松的节奏，利于人体足底的按摩效果保证，提高鞋垫2的整体磁疗功能。而设置在磁疗器15内部的弹簧20结构，利于缓冲足底受到的按摩压力调节，避免压力过大而引起人体不适。
最后，本申请保健效果较好，通过鞋垫2与鞋底9的整体配合，能够保证鞋垫2安装的稳定性及限制鞋垫2向后位移，具有较好的实用价值及推广价值。
实施例2，如图1-5所示：
一种基于红外原理的保健鞋的制备方法，包括如下步骤：
步骤1：鞋体制备：制备鞋帮1和鞋底9，将鞋帮1和鞋底9通过缝制方式缝合为一体结构；将鞋帮1和鞋底9相互缝合的位置浸入补鞋用粘胶，将缝合位置的缝隙进行密封粘连；
步骤2：鞋垫2制备：抗菌层3进行抗菌染整处理并烘干；抗静电层4进行抗静电剂处理并烘干；将抗菌层3和抗静电层4进行固定粘连；在抗静电层4的底面开设若干用于安装磁石17的内嵌凹槽；
将加强层6、保暖层7以及稳固层8进行固定粘接；在加强层6上开设用于安装底盖22的内嵌凹槽；
准备网格布5，在网格布5上涂覆纳米远红外材料，并在网格布5的网孔内同时填充纳米远红外材料；然后在网格布5的上表面固定粘接防水膜21，并在网格布5上开设安装孔16；
将磁疗器15穿过安装孔16进行安装，保证磁石17位于网格布5上方，底盖22位于网格布5下方；
随后将磁石17嵌入抗静电层4的内嵌凹槽内，将底盖22嵌入加强层6的内嵌凹槽中；然后将网格布5分别与抗静电层4和加强层6固定粘接为一体结构；
步骤3：鞋垫2安装：将鞋垫2放入保健鞋内，让稳固层8底部的斜柱14嵌入斜孔13内部进行配合安装。
优选的，所述步骤2中，抗菌层(3)通过抗菌整理剂进行抗菌处理；抗菌整理剂按照质量组分准备质量浓度0.6％的蓖麻油酸丁酯硫酸钠2份，1.5％的2-甲基-4-异噻唑啉-3-酮3份，50％的双氧水2份，0.1％的2-羟基-4-正辛氧基二苯甲酮2份，0.02％的硫酸铜溶液1份，0.18％的脂肪醇聚氧乙烯丙基磺酸2份，0.05％的聚乙烯醇2份，0.12％的十二烷基羧甲基钠型咪唑啉醋酸盐1份和1.5％的二甲基二烯丙基氯化铵-丙烯酰胺共聚物1份，以上组分按质量比1:5与水混合均匀后得到。
优选的，所述步骤2中，所述抗静电层(4)采用抗静电助剂进行处理；
抗静电助剂的制备步骤为：首先按照质量组分准备质量浓度30％的环氧乙烷1份、10％的十二醇2份、50％的双氧水1份、5％的五氧化二磷3份、3％的甲醇2份、5％的十六硫醇1份和3％的氢氧化钠1份；然后将反应釜预热至95摄氏度并保持6分钟，向其中加入十二醇和氢氧化钠，在此温度下将其混合搅匀；然后缓慢加入甲醇、十六硫醇及五氧化二磷，再次混合均匀之后抽真空脱水至反应釜内无水馏出，并注入氮气将反应釜内残余的空气驱除；再向其中通入环氧乙烷，加压至0.3Mpa，且反应温度控制在150摄氏度，并在反应150分钟后将得到的料液冷却至80摄氏度；将其转移至酯化釜中，同时往酯化釜中加入五氧化二磷以及双氧水，在此温度下反应120分钟后，趁热用100目的不锈钢筛过滤，再将滤液用氢氧化钾水溶液中和后，静置、冷却以得到抗静电助剂。
涂覆有纳米远红外材料的网格布5可以发射远红外线。所述网格布5的网格结构为蜂巢结构，利于涂覆及网孔填充纳米远红外材料。这种材料能够持续发出4～16微米的远红外光波。这种涂覆在网格布5上并使网格布5具有发射远红外光波的材料可以是生物炭、碳纤维制品等纳米远红外材料。
同时，网格布5嵌入鞋垫2基底的上表面，而网格布5由若干筋条交错而成，这些筋条形成一个个的远红外发射点。在具体使用时，所述通孔10的孔径均可以设置为2mm。每个通孔10都成为远红外线的发射源点，还使得人体足部得到舒适的远红外保健治疗。人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
由于采用了上述技术方案，本发明的有益效果是：
一方面，本申请能够保证保健鞋的远红外保健效果，使人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
另一方面，抗菌层3以及抗静电层4的设计，能够有效解决现有鞋垫2存在的抗菌效果及抗静电效果较差的不足和缺陷，提高鞋垫2的抗菌及抗静电综合性能，提高人体穿戴的安全性及舒适性。
再一方面，本申请通过磁疗器15的设置，能够对人体脚底的学位进行一定程度的按摩，尤其在人体行走的过程中，一按一松的节奏，利于人体足底的按摩效果保证，提高鞋垫2的整体磁疗功能。而设置在磁疗器15内部的弹簧20结构，利于缓冲足底受到的按摩压力调节，避免压力过大而引起人体不适。
最后，本申请保健效果较好，通过鞋垫2与鞋底9的整体配合，能够保证鞋垫2安装的稳定性及限制鞋垫2向后位移，具有较好的实用价值及推广价值。
实施例3，如图1-5所示：
一种基于红外原理的保健鞋，包括鞋帮1、鞋垫2和鞋底9，鞋帮1和鞋垫2固定连接形成保健鞋整体结构；所述鞋垫2从上到下依次包括固定为一体结构的抗菌层3、抗静电层4、网格布5、加强层6、保暖层7以及稳固层8；所述抗静电层4、网格布5以及加强层6之间固定安装有对应人体脚底穴位的磁疗器15；所述网格布5的表面涂覆有纳米远红外材料，网格布5外部的纳米远红外材料涂层表面固定设置有用于防止汗液渗透的透明防水膜21；所述抗菌层3以及抗静电层4上均阵列开设有多个用于远红外线释放的通孔10；所述稳固层8底面设置有多个向脚后跟方向倾斜的斜柱14，鞋底9的上表面开设有多个与所述斜柱14相匹配的斜孔13；所述鞋垫2与鞋底9之间通过斜柱14嵌入斜孔13内部进行稳定安装。
如上所述的一种基于红外原理的保健鞋的制备方法，包括如下步骤：
步骤1：鞋体制备：制备鞋帮1和鞋底9，将鞋帮1和鞋底9通过缝制方式缝合为一体结构；将鞋帮1和鞋底9相互缝合的位置浸入补鞋用粘胶，将缝合位置的缝隙进行密封粘连；
步骤2：鞋垫2制备：抗菌层3进行抗菌染整处理并烘干；抗静电层4进行抗静电剂处理并烘干；将抗菌层3和抗静电层4进行固定粘连；在抗静电层4的底面开设若干用于安装磁石17的内嵌凹槽；
将加强层6、保暖层7以及稳固层8进行固定粘接；在加强层6上开设用于安装底盖22的内嵌凹槽；
准备网格布5，在网格布5上涂覆纳米远红外材料，并在网格布5的网孔内同时填充纳米远红外材料；然后在网格布5的上表面固定粘接防水膜21，并在网格布5上开设安装孔16；
将磁疗器15穿过安装孔16进行安装，保证磁石17位于网格布5上方，底盖22位于网格布5下方；
随后将磁石17嵌入抗静电层4的内嵌凹槽内，将底盖22嵌入加强层6的内嵌凹槽中；然后将网格布5分别与抗静电层4和加强层6固定粘接为一体结构；
步骤3：鞋垫2安装：将鞋垫2放入保健鞋内，让稳固层8底部的斜柱14嵌入斜孔13内部进行配合安装。
优选的，所述步骤2中，抗菌层(3)通过抗菌整理剂进行抗菌处理；抗菌整理剂按照质量组分准备质量浓度0.8％的蓖麻油酸丁酯硫酸钠2份，1.7％的2-甲基-4-异噻唑啉-3-酮3份，70％的双氧水2份，0.2％的2-羟基-4-正辛氧基二苯甲酮2份，0.05％的硫酸铜溶液1份，0.3％的脂肪醇聚氧乙烯丙基磺酸2份，0.09％的聚乙烯醇2份，0.15％的十二烷基羧甲基钠型咪唑啉醋酸盐1份和1.8％的二甲基二烯丙基氯化铵-丙烯酰胺共聚物1份，以上组分按质量比1:5与水混合均匀后得到。
优选的，所述步骤2中，所述抗静电层(4)采用抗静电助剂进行处理；
抗静电助剂的制备步骤为：首先按照质量组分准备质量浓度50％的环氧乙烷1份、15％的十二醇2份、70％的双氧水1份、8％的五氧化二磷3份、8％的甲醇2份、10％的十六硫醇1份和5％的氢氧化钠1份；然后将反应釜预热至95摄氏度并保持8分钟，向其中加入十二醇和氢氧化钠，在此温度下将其混合搅匀；然后缓慢加入甲醇、十六硫醇及五氧化二磷，再次混合均匀之后抽真空脱水至反应釜内无水馏出，并注入氮气将反应釜内残余的空气驱除；再向其中通入环氧乙烷，加压至0.3Mpa，且反应温度控制在160摄氏度，并在反应150分钟后将得到的料液冷却至80摄氏度；将其转移至酯化釜中，同时往酯化釜中加入五氧化二磷以及双氧水，在此温度下反应120分钟后，趁热用100目的不锈钢筛过滤，再将滤液用氢氧化钾水溶液中和后，静置、冷却以得到抗静电助剂。
涂覆有纳米远红外材料的网格布5可以发射远红外线。所述网格布5的网格结构为蜂巢结构，利于涂覆及网孔填充纳米远红外材料。这种材料能够持续发出4～16微米的远红外光波。这种涂覆在网格布5上并使网格布5具有发射远红外光波的材料可以是生物炭、碳纤维制品等纳米远红外材料。
同时，网格布5嵌入鞋垫2基底的上表面，而网格布5由若干筋条交错而成，这些筋条形成一个个的远红外发射点。在具体使用时，所述通孔10的孔径均可以设置为3mm。每个通孔10都成为远红外线的发射源点，还使得人体足部得到舒适的远红外保健治疗。人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
由于采用了上述技术方案，本发明的有益效果是：
一方面，本申请能够保证保健鞋的远红外保健效果，使人体足部在远红外线的作用下可享受远红外的长期理疗效果，以改善人体的微循环系统，促进人体的新陈代谢，提高人体免疫功能，并进行消炎消肿灭菌等。
另一方面，抗菌层3以及抗静电层4的设计，能够有效解决现有鞋垫2存在的抗菌效果及抗静电效果较差的不足和缺陷，提高鞋垫2的抗菌及抗静电综合性能，提高人体穿戴的安全性及舒适性。
再一方面，本申请通过磁疗器15的设置，能够对人体脚底的学位进行一定程度的按摩，尤其在人体行走的过程中，一按一松的节奏，利于人体足底的按摩效果保证，提高鞋垫2的整体磁疗功能。而设置在磁疗器15内部的弹簧20结构，利于缓冲足底受到的按摩压力调节，避免压力过大而引起人体不适。
最后，本申请保健效果较好，通过鞋垫2与鞋底9的整体配合，能够保证鞋垫2安装的稳定性及限制鞋垫2向后位移，具有较好的实用价值及推广价值。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可轻易想到变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应以权利要求的保护范围为准。

Claims (6)

1.一种基于红外原理的保健鞋，包括鞋帮(1)、鞋垫(2)和鞋底(9)，鞋帮(1)和鞋底(9)固定连接形成保健鞋整体结构；其特征在于：所述鞋垫(2)从上到下依次包括固定为一体结构的抗菌层(3)、抗静电层(4)、网格布(5)、加强层(6)、保暖层(7)以及稳固层(8)；鞋底(9)内部设置有多个气泡孔(11)，气泡孔(11)内部充满流质胶体(12)；
所述抗菌层(3)以及抗静电层(4)上均阵列开设有多个用于远红外线释放的通孔(10)；
所述网格布(5)的表面涂覆有纳米远红外材料，网格布(5)外部的纳米远红外材料涂层表面固定设置有用于防止汗液渗透的透明防水膜(21)；所述网格布(5)的网孔为蜂巢孔结构，网格布(5)的网孔内部填充有纳米远红外材料，防水膜(21)对称设置在网格布(5)的上层面和下层面；
所述抗静电层(4)、网格布(5)以及加强层(6)之间固定安装有对应人体脚底穴位的磁疗器(15)；所述抗静电层(4)、网格布(5)以及加强层(6)上开设有安装孔(16)，所述磁疗器(15)配合嵌入所述安装孔(16)中进行固定安装；所述磁疗器(15)的顶部为磁石(17)，磁石(17)底部固定连接圆筒结构的内筒(18)；磁疗器(15)的底部为底盖(22)，所述底盖(22)的顶部固定连接圆筒结构的外筒(19)，所述内筒(18)配合嵌入所述外筒(19)中进行可相对滑动的配合安装；所述磁石(17)的底面以及底盖(22)的顶面中心位置通过弹簧(20)固定连接，所述弹簧(20)位于内筒(18)以及外筒(19)内部；所述磁石(17)以及底盖(22)的外形均为圆形片结构，圆形片的外表面为球形面，圆形片连接弹簧(20)的一面为水平面；
所述稳固层(8)底面设置有多个向脚后跟方向倾斜的斜柱(14)，鞋底(9)的上表面开设有多个与所述斜柱(14)相匹配的斜孔(13)；所述鞋垫(2)与鞋底(9)之间通过斜柱(14)嵌入斜孔(13)内部进行稳定安装；
所述保健鞋的制备方法包括如下步骤：
步骤1：鞋体制备：制备鞋帮(1)和鞋底(9)，将鞋帮(1)和鞋底(9)通过缝制方式缝合为一体结构；将鞋帮(1)和鞋底(9)相互缝合的位置浸入补鞋用粘胶，将缝合位置的缝隙进行密封粘连；
步骤2：鞋垫制备：抗菌层(3)进行抗菌染整处理并烘干；抗静电层(4)进行抗静电剂处理并烘干；将抗菌层(3)和抗静电层(4)进行固定粘连；在抗静电层(4)的底面开设若干用于安装磁石(17)的内嵌凹槽；将加强层(6)、保暖层(7)以及稳固层(8)进行固定粘接；在加强层(6)上开设用于安装底盖(22)的内嵌凹槽；准备网格布(5)，在网格布(5)上涂覆纳米远红外材料，并在网格布(5)的网孔内同时填充纳米远红外材料；然后在网格布(5)的上表面固定粘接防水膜(21)，并在网格布(5)上开设安装孔(16)；将磁疗器(15)穿过安装孔(16)进行安装，保证磁石(17)位于网格布(5)上方，底盖(22)位于网格布(5)下方；随后将磁石(17)嵌入抗静电层(4)的内嵌凹槽内，将底盖(22)嵌入加强层(6)的内嵌凹槽中；然后将网格布(5)分别与抗静电层(4)和加强层(6)固定粘接为一体结构；
步骤3：鞋垫安装：将鞋垫(2)放入保健鞋内，让稳固层(8)底部的斜柱(14)嵌入斜孔(13)内部进行配合安装。
2.如权利要求1所述的一种基于红外原理的保健鞋，其特征在于：所述抗菌层(3)为香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维混纺而成的面料层；所述香蕉纤维、亚麻纤维、竹炭纤维以及涤纶长丝纤维的质量比为2:2:3:1；所述抗菌层(3)通过抗菌染整处理之后固定粘接设置于所述抗静电层(4)的外表面。
3.如权利要求1或2所述的一种基于红外原理的保健鞋，其特征在于：所述抗静电层(4)为抗静电丝、涤纶纤维以及氨纶纤维混纺而成的面料层，所述抗静电层(4)的表面通过抗静电剂进行处理并烘干；所述抗静电丝、涤纶纤维以及氨纶纤维的质量比为5:2:2。
4.如权利要求1所述的一种基于红外原理的保健鞋，其特征在于：所述加强层(6)为高强度芳纶纤维与聚氨酯纤维、腈纶纤维以及锦纶纤维混纺而成的面料层；所述芳纶纤维、聚氨酯纤维、腈纶纤维以及锦纶纤维的质量比为5:1:1:2；所述保暖层(7)为棉纤维面料层；所述稳固层(8)为橡胶材料层或硅胶材料层；所述鞋底(9)的底面设置有“人”字形结构或“W”字形结构的防滑纹。
5.如权利要求1所述的一种基于红外原理的保健鞋，其特征在于：所述步骤2中，抗菌层(3)通过抗菌整理剂进行抗菌处理；抗菌整理剂按照质量组分准备质量浓度0.6％-0.8％的蓖麻油酸丁酯硫酸钠2份，1.5％-1.7％的2-甲基-4-异噻唑啉-3-酮3份，50％-70％的双氧水2份，0.1％-0.2％的2-羟基-4-正辛氧基二苯甲酮2份，0.02％-0.05％的硫酸铜溶液1份，0.18％-0.3％的脂肪醇聚氧乙烯丙基磺酸2份，0.05％-0.09％的聚乙烯醇2份，0.12％-0.15％的十二烷基羧甲基钠型咪唑啉醋酸盐1份和1.5％-1.8％的二甲基二烯丙基氯化铵-丙烯酰胺共聚物1份，以上组分按质量比1:5与水混合均匀后得到。
6.如权利要求1所述的一种基于红外原理的保健鞋，其特征在于：所述步骤2中，所述抗静电层(4)采用抗静电助剂进行处理；
抗静电助剂的制备步骤为：首先按照质量组分准备质量浓度30％-50％的环氧乙烷1份、10％-15％的十二醇2份、50％-70％的双氧水1份、5％-8％的五氧化二磷3份、3％-8％的甲醇2份、5％-10％的十六硫醇1份和3％-5％的氢氧化钠1份；然后将反应釜预热至95摄氏度并保持6-8分钟，向其中加入十二醇和氢氧化钠，在此温度下将其混合搅匀；然后缓慢加入甲醇、十六硫醇及五氧化二磷，再次混合均匀之后抽真空脱水至反应釜内无水馏出，并注入氮气将反应釜内残余的空气驱除；再向其中通入环氧乙烷，加压至0.3Mpa，且反应温度控制在150-160摄氏度，并在反应150分钟后将得到的料液冷却至80摄氏度；将其转移至酯化釜中，同时往酯化釜中加入五氧化二磷以及双氧水，在此温度下反应120分钟后，趁热用100目的不锈钢筛过滤，再将滤液用氢氧化钾水溶液中和后，静置、冷却以得到抗静电助剂。
CN202111312699.1A 2021-11-08 2021-11-08 一种基于红外原理的保健鞋及其制备方法 Active CN114128955B (zh)