CN1140888A - Sealing element of special high-voltage electric appliance - Google Patents
Sealing element of special high-voltage electric appliance Download PDFInfo
- Publication number
- CN1140888A CN1140888A CN 95107847 CN95107847A CN1140888A CN 1140888 A CN1140888 A CN 1140888A CN 95107847 CN95107847 CN 95107847 CN 95107847 A CN95107847 A CN 95107847A CN 1140888 A CN1140888 A CN 1140888A
- Authority
- CN
- China
- Prior art keywords
- rubber
- sealing element
- seal
- electric appliance
- voltage electric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The sealing element is esp suitable for transformer, and it uses rubber as main material and has in its components rubber, carbon black, promoter, peroxide, sulphur, pretreated short staple and other rubber additives. It can reach schopper hardness of 80 degrees, tension strength of 20.5 MPa and elongation at rupture of 50%.
Description
The present invention relates to a kind of sealing element of special high-voltage electric appliance take rubber as main component, be particularly suitable for doing the seal of transformer.
Some High-Voltage Electrical Appliances particularly seal of transformer are different from other seal, and main cause is that this seal environment for use is abominable, and relevant performance requirement is very harsh. The transformer seal, long-term exposing outside is exposed to the elements, exposure in sunshine, and be in for a long time under the very high pressure state, so the sizing material of seal must have higher resistance to weathering energy and electrical insulation capability, and little compression set must be arranged. In addition, because the higher-pressure region of transformer has than high-intensity magnetic field, can produce electric arc when meeting rainy weather, magnetic field and electric arc all can intensify the oxygen in the transformer surrounding air, thereby produce ion-oxygen, i.e. ozone, and therefore, seal piece size also must have ozone resistance. In addition, also require the transformer seal to have UV resistant irradiation, transformer oil resistant, the performance such as cold-resistant, pollute transformer oil and adapt to severe cold area preventing.
For above requirement, northwest rubber research institute and transformer research center, Shenyang, jointly developed successfully the seal piece size prescription of code name for " P815 ", but seal does not still reach desirable reliability and durability, still can not satisfy the harsh requirement of transformer sealing. In recent years, the applicant had developed the another kind of sizing compound formula that is better than " P815 " prescription, but seal be full of cracks and transformer oil impregnate problem still do not obtain radical cure.
Therefore, task of the present invention is on the basis of existing technology, and a kind of new seal piece size prescription and corresponding sealing element of special high-voltage electric appliance are provided, and improves durability and the reliability of seal.
Sealing element of special high-voltage electric appliance, its sizing material composition comprises acrylonitrile-butadiene rubber, neoprene, carbon black, promoter, peroxide, Sulfur, pretreated short fibre and the industrial compounding ingredient of other ordinary rubber, when rubber content (by weight) is 100 parts, content of carbon black is 10-70 part, promoter 2-5 part, peroxide 0.9-2.2 part, Sulfur 0.1-0.6 part, pretreated short fibre 10-50 part.
The seal piece size prescription is to guarantee the seal inherent quality, determines the main aspect of its reliability and durability. The main raw material(s) of above-mentioned prescription has adopted acrylonitrile-butadiene rubber and good neoprene and the usefulness of ozone resistance of the good middle high acrylonitrile content of oil resistance. Vulcanizing system then is the high short vulcanizing system of low-sulfur and peroxide vulcanizing system and uses, the high short vulcanizing system of low-sulfur (being the promoter+a small amount of Sulfur of higher amount) exists the shortcoming that time of scorch is short, compression is large, and during peroxide cure, the high temperature tear resistance is poor, two vulcanizing systems are also used, both solve the problem that the sizing material time of scorch is short, compression is large, also improved the high temperature resistant tear resistance of sizing material.
Bare bones of the present invention is the selection of reinforcing agent, has especially used pretreated short fibre as reinforcing agent. Pretreated short fibre is a kind of filler by the common development of Beijing University of Chemical Technology and Heilongjiang Province's Fujin City rubber plant. This filler reinforcing property is high, processing performance is good, gives birth to low, the easy dispersion of heat. The present invention selects pretreated short fibre as reinforcing agent, has effectively improved the physical property of seal.
Method and result that the seal that makes according to sizing compound formula of the present invention is made a service test are as follows:
One, test material and the place of production
1, produce in neoprene Qingdao
2, produce in acrylonitrile-butadiene rubber Qingdao
3, carbon black plant, carbon black Luoyang
4, pretreated short fibre Fujin rubber plant
5, the industrial compounding ingredient of other ordinary rubber
Two, testing equipment
1, mixing: 6 cun mills
2, sulfuration: 25 tons of vulcanizing presses
3, XU-strength tester (Changsha product)
4, ageing oven
Three, test method
1, hardness test: undertaken by GB531-83
2, strength and extension property test: undertaken by GB523-81
3, density measurement: undertaken by GB533-81
4, resistance to liquid can be tested: undertaken by GB1690-82
5, permanent compression test: undertaken by GB1683-81
Four, result of the test
1, (1) Shao Er A type hardness tester (degree) 80; (2) hot strength (MPa) 20.5; (3) elongation at break (%) 50%.
2, air oven aging test (100 ℃ * 161h): (1) hardness 82; (2) hot strength 18.5; (3) elongation at break 40%.
3, anti-liquid (transformer oil resistant) test (100 ℃ * 70h): (1) hot strength 19; (2) elongation at break 45%; (3) weight change+4.7.
4, permanent compression test (100 ℃ * 70h, hot-air 20%): 25%.
Five, the actual qualification test of using
Suppress respectively glue pearl exemplar (50 of the present invention's prescription of three kinds of specifications (φ 12 * 25 * 14, φ 16 * 35 * 14, φ 11.5 * 28.5 * 16) with equal dies by sizing compound formula of the present invention and prior art formula, 15 of prior art formula), offer applying unit (Jinan will friend limited company, Zhengzhou transformer factory and Liuzhou transformer factory) carry out reliability and durability contrast test, result of the test is as shown in table 1.
By 9 months Continuous Observation test, the sealing element of special high-voltage electric appliance exemplar all passed through to satisfy 250 days life test, has satisfied instructions for use, proves that the reliability of the seal and durability are significantly improved.
Show according to above test, the physical property of sealing element of special high-voltage electric appliance provided by the present invention, the technical merit that has not only surpassed " P815 " prescription and applicant's original formulation, make inherent quality, reliability and the durability of seal that by a relatively large margin raising be arranged, satisfied the harsh requirement of transformer and the sealing of other High-Voltage Electrical Appliances, and opened up new road for the quality and the technical merit that improve the transformer sealing, established new basis.
The below describes the present invention.
The sizing material composition of sealing element of special high-voltage electric appliance, when rubber content (weight portion) was 100 parts, content of carbon black was 10-70 part, 2-5 parts of promoter, peroxide 0.9-2.2 part, Sulfur 0.1-0.6 part, pretreated short fibre 10-50 part; State and contain an amount of industrial compounding ingredient of other ordinary rubber. Table 2 provides the content range of four groups of concrete formulation datas and each composition.
Sizing compound formula provided by the invention, the breakthrough of most critical are to have added pretreated short fibre, and this is the basis that guarantees the seal inherent quality. In addition, acrylonitrile-butadiene rubber and neoprene and usefulness, the high short vulcanizing system of low-sulfur and peroxide vulcanizing system and usefulness also are the main points of prescription of the present invention.
Promoter is adopted acrylonitrile-butadiene rubber Vulcanization accelerator TMTD (thiuram disulphide) and the DM (disulfide group propyl benzene thiazole) commonly used that oil resistivity is good, compression set is low; Peroxide adopts DCP (cumyl peroxide). In sizing compound formula, also contain an amount of activator (magnesia, zinc oxide, stearic acid), plasticizer (bizinc resin DBP, dibutylester DOP) and age resistor (MB 4010NA).
The conditions of vulcanization of sizing compound formula of the present invention is: (13-18) ' * (165 ± 5 ℃), generally speaking, best conditions of vulcanization is 165 ℃ * 15 '.
The production technology of seal can be carried out with reference to traditional handicraft of the prior art, and is as shown in table 3. Table 1 actual service test result
Four groups of concrete formulation datas of table 2 and each component content scope (weight portion)
Table 3 sealing element of special high-voltage electric appliance production technology
| Service time | The exemplar of prior art sizing compound formula | The exemplar of sizing compound formula of the present invention |
| 3 months | Slight be full of cracks | Without be full of cracks |
| 6 months | The be full of cracks aggravation | Be full of cracks is slightly arranged, and naked eyes can be debated |
| 9 months | Oil impregnate | Be full of cracks obviously can be debated |
| Acrylonitrile-butadiene rubber | 50 | 40 | 70 | 80 | 80-40 |
| Neoprene | 50 | 60 | 30 | 20 | 20-60 |
| Age resistor | 3 | 3 | 2 | 2.5 | 0-3.5 |
| Magnesia | 4 | 4 | 5 | 3 | 3-6 |
| Zinc oxide | 5 | 5 | 6 | 4 | 3-6 |
| Stearic acid | 1 | 1 | 1.5 | 2 | 1-3 |
| Carbon black (high wear-resistant carbon black and semi-reinforcing hydrocarbon black) | 40 | 50 | 30 | 20 | 10-70 |
| Cold resistant plasticizer | 10 | 12 | 8 | 7 | 7-15 |
| Sulfur | 0.2 | 0.2 | 0.3 | 0.3 | 0.1-0.6 |
| Peroxide | 1.8 | 1.8 | 1.6 | 1.5 | 0.9-2.2 |
| Promoter | 3 | 3 | 2.5 | 3.5 | 2-5 |
| Pretreated short fibre | 30 | 35 | 40 | 45 | 10-50 |
| Composition | The first assembly side | The second assembly side | The 3rd assembly side | The 4th assembly side | Range of variables |
| Cut glue-→ weighing-→ rubber close refining-→ add short fiber-→ add promoter-→ add 50% carbon black-→ add 50% plasticizer-→ add other 50% carbon black-→ add other 50% plasticizer-→ add small powder (other compounding ingredient)-→ Sulfur-→ slice (sizing material)-→ park from lack cooling in 24 hours stand-by → turn refining-→ slice-→ extrude-→ weighing-→ sulfuration-→ deburring-→ check-→ packing-→ warehouse-in. |
Claims (2)
1, a kind of sealing element of special high-voltage electric appliance, its sizing material composition comprises acrylonitrile-butadiene rubber, neoprene, carbon black, promoter, peroxide, Sulfur, pretreated short fibre and the industrial compounding ingredient of other ordinary rubber, when rubber content is (by weight) 100 parts, content of carbon black is 10-70 part, promoter 2-5 part, peroxide 0.9-2.2 part, 0.1-0.6 part of Sulfur, pretreated short fibre 10-50 part.
2, by seal claimed in claim 1, it is characterized in that: the content of other compounding ingredient is in the sizing material, age resistor 0-3.5 part, magnesia 3-6 part, zinc oxide 3-6 part, stearic acid 1-3 part, cold resistant plasticizer 7-15 part.