CN114085576A - Water-based yellow-sealing coating and preparation method thereof - Google Patents
Water-based yellow-sealing coating and preparation method thereof Download PDFInfo
- Publication number
- CN114085576A CN114085576A CN202111580748.XA CN202111580748A CN114085576A CN 114085576 A CN114085576 A CN 114085576A CN 202111580748 A CN202111580748 A CN 202111580748A CN 114085576 A CN114085576 A CN 114085576A
- Authority
- CN
- China
- Prior art keywords
- water
- yellow
- agent
- acrylic acid
- sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based yellow-sealing coating, which is characterized in that: the paint comprises water-based yellow-sealing self-crosslinking acrylic acid, water-based yellow-sealing solvent-free self-crosslinking acrylic acid, a film-forming cosolvent, water, a defoaming agent, a flatting agent, a wetting agent, powder and a thickening agent, wherein the components in percentage by mass are as follows: 20-22.5% of water-based yellow-sealing self-crosslinking acrylic acid, 20-22.5% of water-based yellow-sealing solvent-free self-crosslinking acrylic acid, 2.0-2.5% of film-forming cosolvent, 5-6% of water, 0.3-0.8% of defoaming agent, 0.2-1.5% of wetting agent, 0.2-1.5% of flatting agent, 40-42.5% of powder and 0.3-1.5% of thickening agent. The water-based paint disclosed by the invention takes water as a solvent, so that the use of an organic solvent is effectively reduced, and the discharge of VOCs is low; and the waterborne self-crosslinking acrylic acid can be used for sealing yellow without adding any curing agent and crosslinking agent, and the wetting agent and the leveling agent are added in the formula system to drive the whole paint liquid system to wet and flatly spread on the medium density fiberboard, so that the whole paint film has excellent compactness on the medium density fiberboard, and the yellow sealing effect is achieved.
Description
Technical Field
The invention relates to the technical field of coatings, in particular to a water-based yellow-sealing coating and a preparation method thereof.
Background
With the rapid development of social economy in China, the requirements of consumers on the quality of life are higher and higher, and the demand on high-grade solid wood furniture is greatly improved compared with the demand desire on plate-type furniture or artificial board furniture in home decoration and furniture purchase.
The water paint is a high molecular material using water as a dispersion medium instead of an organic solvent in the traditional oily paint, and has the advantages of no toxicity, no pollution, low odor, no combustion, no explosion and the like. However, the water-based paint on the market has single function, the hand feeling of a coating film and the smoothness of the coating film are improved mainly through the water-based polymer, and the water-based paint does not have the excellent yellow sealing function on a medium density fiberboard. Therefore, the invention provides the special yellow sealing coating for the surface decoration of the medium density fiberboard, and improves the surface decoration and comfort of the medium density fiberboard.
Disclosure of Invention
In view of the above, the present invention is directed to a water-based yellow-sealing coating and a preparation method thereof, wherein the coating liquid system of the water-based yellow-sealing coating is capable of providing an excellent yellow-sealing effect on medium density fiberboard.
In order to achieve the purpose, the invention adopts the following technical scheme:
a water-based yellow-sealing coating comprises water-based yellow-sealing self-crosslinking acrylic acid, water-based yellow-sealing solvent-free self-crosslinking acrylic acid, a film-forming cosolvent, water, a defoaming agent, a leveling agent, a wetting agent, powder and a thickening agent, wherein the water-based yellow-sealing self-crosslinking acrylic acid comprises the following components in percentage by mass:
preferably, the type of the water-based yellow-sealing self-crosslinking acrylic acid is WA-631.
Preferably, the type of the water-based solvent-free yellow-sealing self-crosslinking acrylic acid is PA-4850.
Preferably, the film-forming cosolvent is one or a combination of dipropylene glycol methyl ether, dipropylene glycol butyl ether, propylene glycol butyl ether and tripropylene glycol butyl ether.
Preferably, the water is purified water or deionized water.
Preferably, the defoaming agent is polydimethylsiloxane which is one or a combination of BYK024, BYK028, TEGO825 and TEGO 902W.
Preferably, the wetting agent is polyether modified siloxane or multifunctional modified siloxane, and the type of the wetting agent is one or a combination of TEGO270, BYK346 and TEGO 4100.
Preferably, the leveling agent is polyether siloxane copolymer, and the type of the polyether siloxane copolymer is TEGO410 or BYK333 or a combination of the TEGO410 and the BYK 333.
As a preferred scheme, the powder material is an inorganic substance which is one or more of CC902 calcium carbonate and R895 titanium dioxide; the thickener is an associated polyurethane thickener, and the model number of the thickener is Coapurxs 71.
The preparation method of the water-based yellow-sealing coating comprises the following steps
(1) Preparing raw materials, which comprise the following components in percentage by weight:
20-22.5% of water-based yellow-sealing self-crosslinking acrylic acid, 20-22.5% of water-based solvent-free yellow-sealing self-crosslinking acrylic acid, 2-2.5% of film-forming cosolvent, 7-8% of water, 0.3-0.8% of defoaming agent, 0.2-1.5% of flatting agent, 0.2-1.5% of wetting agent, 40-42.5% of powder and 0.3-1.5% of thickening agent;
(2) under the condition of normal temperature, adding aqueous yellow-sealed self-crosslinking acrylic acid and aqueous solvent-free yellow-sealed self-crosslinking acrylic acid in percentage into a high-speed dispersion machine, adding a mixed solution of a film-forming cosolvent and water, a defoaming agent, a wetting agent, a leveling agent, powder and a thickening agent at a medium speed, and stirring for 20-30 minutes;
(3) the detection fineness is less than or equal to 40 micrometers;
(4) detecting the pH value to be 7.5-9;
(5) spraying other bad paint film effects without shrinkage cavity;
(6) and taking out the finished product after the detection is qualified.
Compared with the prior art, the invention has obvious advantages and beneficial effects, and specifically, the technical scheme includes that:
the water-based paint disclosed by the invention takes water as a solvent, so that the use of an organic solvent is effectively reduced, and the discharge of VOCs is low; and the waterborne self-crosslinking acrylic acid can be used for sealing yellow without adding any curing agent and crosslinking agent, and the wetting agent and the leveling agent are added in the formula system to drive the whole paint liquid system to wet and flatly spread on the medium density fiberboard, so that the whole paint film has excellent compactness on the medium density fiberboard, and the yellow sealing effect is achieved.
To more clearly illustrate the features and effects of the present invention, the present invention is described in detail below with reference to specific examples.
Detailed Description
The invention discloses a water-based yellow-sealing coating, which comprises water-based yellow-sealing self-crosslinking acrylic acid, water-based yellow-sealing solvent-free self-crosslinking acrylic acid, a film-forming cosolvent, water, a defoaming agent, a flatting agent, a wetting agent, powder and a thickening agent, wherein the water-based yellow-sealing self-crosslinking acrylic acid comprises the following components in percentage by mass:
the type of the water-based yellow-sealing self-crosslinking acrylic acid is WA-631.
The type of the water-based solvent-free yellow-sealing self-crosslinking acrylic acid is PA-4850.
The film-forming cosolvent is one or a combination of dipropylene glycol methyl ether, dipropylene glycol butyl ether, propylene glycol butyl ether and tripropylene glycol butyl ether.
The water is purified water or deionized water.
The defoaming agent is polydimethylsiloxane which is one or a combination of BYK024, BYK028, TEGO825 and TEGO 902W.
The wetting agent is polyether modified siloxane or multifunctional modified siloxane, and the type of the wetting agent is one or a combination of TEGO270, BYK346 and TEGO 4100.
The leveling agent is polyether siloxane copolymer, and the number of the polyether siloxane copolymer is one or two of TEGO410 and BYK 333.
The powder material is an inorganic substance and is one or more of CC902 calcium carbonate and R895 titanium dioxide; the thickener is an associated polyurethane thickener, and the model number of the thickener is Coapurxs 71.
The invention also discloses a preparation method of the water-based yellow-sealing coating, which comprises the following steps
(1) Preparing raw materials, which comprise the following components in percentage by weight:
20-22.5% of water-based yellow-sealing self-crosslinking acrylic acid, 20-22.5% of water-based solvent-free yellow-sealing self-crosslinking acrylic acid, 2-2.5% of film-forming cosolvent, 7-8% of water, 0.3-0.8% of defoaming agent, 0.2-1.5% of flatting agent, 0.2-1.5% of wetting agent, 40-42.5% of powder and 0.3-1.5% of thickening agent.
(2) Under the condition of normal temperature, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in percentage into a high-speed dispersion machine, adding a mixed solution of a film-forming cosolvent and water, a defoaming agent, a wetting agent, a leveling agent, powder and a thickening agent at a medium speed, and stirring for 20-30 minutes.
(3) The detection fineness is less than or equal to 40 micrometers.
(4) The pH value is detected to be 7.5-9.
(5) The spraying has no shrinkage cavity and other bad paint film effects.
(6) And taking out the finished product after the detection is qualified.
The following is a more detailed description with reference to specific examples.
Example 1
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
Example 2
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
Example 3
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
Example 4
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
Example 5
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
Example 6
A water-based yellow-sealing coating and a preparation method thereof are disclosed, which comprises the following components:
preparing raw materials, adding aqueous yellow-sealing self-crosslinking acrylic acid and aqueous solvent-free yellow-sealing self-crosslinking acrylic acid in a conventional high-speed dispersion machine at 25 ℃, adding a mixed solution of a film-forming aid and water, a defoaming agent, a wetting agent, a leveling agent, a hydrophobic agent, powder and a thickening agent at a medium speed, stirring for 20-30 minutes, detecting that the fineness is less than or equal to 40 micrometers, the pH value is 7.5-9, spraying other poor paint film effects without shrinkage cavities, and taking out a finished product after the detection is qualified.
The above examples, when compared to conventional wood coating products and examined, gave the results of the following table, the experimental board selected was a medium density fiberboard:
the test items in the tables are basically detected according to the national standard GB/T23999-. VOC volatilization was measured as described in GB 18582-2001.
The cold-hot circulation experiment result and the detection experiment method obtain: the coating is sprayed on the upper surface of a medium density fiberboard according to the specified mixture ratio and the coating weight of 110 g/square meter multiplied by 3 times, and the medium density fiberboard is dried at room temperature for 48 hours and then placed into a cold-hot circulation machine for testing, wherein the cold-hot circulation setting mode is as follows: freezing at-20 deg.C for 2 hr; raising the temperature to 25 ℃ and placing for 2 hours; raising the temperature to 50 ℃ and baking for 2 hours; these three steps are completed as one cycle. The 6 cycles are repeated, and the paint film is checked for cracks or other abnormal phenomena, and the conclusion is that the embodiment of the invention does not crack or generate other abnormal phenomena.
The above description is only a preferred embodiment of the present invention, and is not intended to limit the technical scope of the present invention, so that any minor modifications, equivalent changes and modifications made to the above embodiment according to the technical spirit of the present invention are within the technical scope of the present invention.
Claims (10)
1. The water-based yellow-sealing coating is characterized by comprising the following components in parts by weight: the paint comprises water-based yellow-sealing self-crosslinking acrylic acid, water-based yellow-sealing solvent-free self-crosslinking acrylic acid, a film-forming cosolvent, water, a defoaming agent, a flatting agent, a wetting agent, powder and a thickening agent, wherein the components in percentage by mass are as follows:
20-22.5% of water-based yellow-sealing self-crosslinking acrylic acid;
20-22.5% of water-based yellow-sealing solvent-free self-crosslinking acrylic acid;
2.0 to 2.5 percent of film-forming cosolvent;
7-8% of water;
0.3 to 0.8 percent of defoaming agent;
0.2 to 1.5 percent of wetting agent;
0.2 to 1.5 percent of flatting agent;
40-42.5% of powder;
0.3 to 1.5 percent of thickening agent.
2. The aqueous yellow-blocking paint according to claim 1, characterized in that: the type of the water-based yellow-sealing self-crosslinking acrylic acid is WA-631.
3. The aqueous yellow-blocking paint according to claim 1, characterized in that: the type of the water-based solvent-free yellow-sealing self-crosslinking acrylic acid is PA-4850.
4. The aqueous yellow-blocking paint according to claim 1, characterized in that: the film-forming cosolvent is one or a combination of dipropylene glycol methyl ether, dipropylene glycol butyl ether, propylene glycol butyl ether and tripropylene glycol butyl ether.
5. The aqueous yellow-blocking paint according to claim 1, characterized in that: the water is purified water or deionized water.
6. The aqueous yellow-blocking paint according to claim 1, characterized in that: the defoaming agent is polydimethylsiloxane which is one or a combination of BYK024, BYK028, TEGO825 and TEGO 902W.
7. The aqueous yellow-blocking paint according to claim 1, characterized in that: the wetting agent is polyether modified siloxane or multifunctional modified siloxane, and the type of the wetting agent is one or a combination of TEGO270, BYK346 and TEGO 4100.
8. The aqueous yellow-blocking paint according to claim 1, characterized in that: the leveling agent is polyether siloxane copolymer, and the number of the polyether siloxane copolymer is one or two of TEGO410 and BYK 333.
9. The aqueous yellow-blocking paint according to claim 1, characterized in that: the powder material is an inorganic substance and is one or more of CC902 calcium carbonate and R895 titanium dioxide; the thickener is an associated polyurethane thickener, and the model number of the thickener is Coapurxs 71.
10. A method of preparing the aqueous yellow-blocking paint according to any one of claims 1 to 9, characterized in that: comprises the following steps
(1) Preparing raw materials, which comprise the following components in percentage by weight:
20-22.5% of water-based yellow-sealing self-crosslinking acrylic acid, 20-22.5% of water-based solvent-free yellow-sealing self-crosslinking acrylic acid, 2-2.5% of film-forming cosolvent, 7-8% of water, 0.3-0.8% of defoaming agent, 0.2-1.5% of flatting agent, 0.2-1.5% of wetting agent, 40-42.5% of powder and 0.3-1.5% of thickening agent;
(2) under the condition of normal temperature, adding aqueous yellow-sealed self-crosslinking acrylic acid and aqueous solvent-free yellow-sealed self-crosslinking acrylic acid in percentage into a high-speed dispersion machine, adding a mixed solution of a film-forming cosolvent and water, a defoaming agent, a wetting agent, a leveling agent, powder and a thickening agent at a medium speed, and stirring for 20-30 minutes;
(3) the detection fineness is less than or equal to 40 micrometers;
(4) detecting the pH value to be 7.5-9;
(5) spraying other bad paint film effects without shrinkage cavity;
(6) and taking out the finished product after the detection is qualified.