CN1140753A - Textile machinery part with embedded solid lubricant - Google Patents
Textile machinery part with embedded solid lubricant Download PDFInfo
- Publication number
- CN1140753A CN1140753A CN96108033.7A CN96108033A CN1140753A CN 1140753 A CN1140753 A CN 1140753A CN 96108033 A CN96108033 A CN 96108033A CN 1140753 A CN1140753 A CN 1140753A
- Authority
- CN
- China
- Prior art keywords
- parts
- mentioned
- described parts
- metal
- nitride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
In a textile machine component, in which at least the wear region or the surface has a matrix of metal-phosphorus, metal-boron or alloyed metal (steel), a soft nitride, which is softer than the matrix, is incorporated as solid lubricant in the matrix.
Description
The present invention relates to a kind of at least at its friction area or the textile machinery part of---phosphorus or metal---boron or alloyed metal (steel) matrix that has metal on its surface at least.
The present invention is to be a kind of improvement of parts of the patent application of the CH-2758/94 that the patent application of DE-A1 4335539.0 on October 19th, 93 and the applying date is on September 9th, 94 to the applying date.
The urgent service performance (behavior under the condition of doing) of utilizing solid lubricant to improve heavily stressed parts is known, and is for example disclosed in following publication:
——JP-OS?5-179522
——JP-OSGM-4-92567
——US-PS-5,086,615
——JP-OS-2-182926
——JP-OSGM-5-777
---select from " PRAXIS-FORUM " book paper " the NI-P-BN dispersion coating of roll body (NI-P-BN Dispersion Coating forCylinder) " (one of author is, Suzuki Mortor Company, Limited).
The described solid lubricant of above-mentioned publication only is applicable to above-mentioned textile machinery part to a certain extent.Known solid lubricant---for example, teflon, molybdenumdisulphide etc.---can not resist high machinery or temperature stress, this is one of solid lubricant reason of being negated up to now.
Task of the present invention is to improve the heavily stressed parts of weaving loom, makes its urgent service performance (behavior under the condition of doing) be higher than existing grade.Particularly determine a kind of solid lubricant with high thermal resistance.
Task of the present invention be by provide a kind of at least its rubbed the zone or have metal on its surface at least---phosphorus, or metal---boron, or the matrix of alloyed metal (steel), utilize nitride softer than matrix, embedding is finished as the method for the textile manufacturing machine parts of the tufftride thing of lubricant in the matrix.
According to textile manufacturing machine parts of the present invention, its all or part of surface is by metal---phosphorus or metal---, and boron constitutes,---phosphorus---adds the solid lubricant that a kind of tufftride thing forms in matrix or metal---boron---matrix to utilize nitride than soft this characteristic of matrix, at metal.Can increase the intensity of matrix greatly by suitable thermal treatment.The increase of hardness reaches by means of the formation of ceramic precipitate in metallic matrix.Therefore, described matrix is at---pottery---matrix hereinafter referred to as metal.Disclosed a kind of hard nitride among clear 4-194031 of Japanese Patent Application Laid-Open and the 2-182927, for example a kind of three-dimensional boron nitride is not suitable as solid lubricant, but it can add to strengthen matrix.Solid lubricant can be used as a kind of dispersion and embeds metal---pottery---in the matrix.In parts coating situation, the parts that are made of any kind of material can be immersed in the coating bath.Parts can partly or entirely be formed by sintering, and for this reason, matrix is that pulverous steel alloy and solid lubricant constitute by original state before it is shaped.Can be with the such tufftride thing of hexagonal boron nitride for example and chromium nitride and nitrided iron as the independent body lubricant.If apply the surface of parts, coat-thickness is preferably 5 to 100mm.Can consider to use nickel, cobalt, the composition of iron or described metal be as metallic substance, but best be iron.Except solid lubricant, metal---pottery---can also contain for example reinforcement material of fine ceramics particle, particularly silicon carbide in the matrix.Can be selected from any material as the solid support material of metal---pottery---matrix that scribbles nitride, aluminium for example, magnesium-zinc alloy or plastics, they can be use packing material, preferably the fiber reinforcement.The base mateiral of textile machinery part can be to use machining, reshapes processing or by the shaping of molded method.The add-on of phosphorus and boron are as metal---pottery---matrix integral part preferably is respectively 1-15%, 0.5-5%.Because according to wearing and tearing, friction oxidation, corrosion or fatigue wait the friction total stress approach of shear strength of this class, and a certain specific phosphorus in the specialized range of listing or the percentage composition of boron are best, therefore stipulated that phosphorus, the component content of boron are respectively 1 to 15% and 0.5 to 5% so bigger scope.
Above-mentioned parts are preferably made the spinning ring and the Steel Traveler of ring spinning frame, the rotor of rotor spinner, rotor spindle, rotor lid or expander, or the nozzle and the roller of guiding fiber or yarn.Material according to the invention also can be made unlubricated sleeve bearing.
As noted, whole parts can be by the alloyed metal that has solid lubricant---body material (steel) is made, rather than applies a coating on parts.Operable powder metallurgy process has been described among Japanese patent application JP-OS-4-241125 or the JP-OS-63-35832.
As the granular size of the nitride of solid lubricant preferably between 0.1 and 5 μ m, 2 μ m particularly.In order to obtain the effect of nitride as solid lubricant, its hardness must be determined like this: when owing to operational stresses induced nitride being come out, described nitride can play the effect that reduces stress, thereby the effect of reduction stress all is identical for matrix and counterpart.Preferably when nitride was exposed to the surface, it changed a protectiveness lubricant film respectively on matrix and component.
Claims (17)
1. textile machinery part, at least at its zone that is rubbed or the body material of provide a kind of metal on its surface at least---phosphorus or metal---boron or alloyed metal (steel), it is characterized in that, utilize nitride than soft this characteristic of body material, in body material, embed a kind of tufftride thing as solid lubricant.
2. parts as claimed in claim 1 is characterized in that solid lubricant is embedded in the matrix with the dispersion form.
3. parts as claimed in claim 1 or 2 is characterized in that, matrix and solid lubricant be sintering together.
4. as the described parts of one of above-mentioned claim, it is characterized in that nitride is made of hexagonal boron nitride or chromium nitride or aluminium nitride or nitrided iron.
5. as the described parts of one of above-mentioned claim, it is characterized in that applied a layer thickness in its surface and be 5 to 100mm body material, base material layer is applied on the base mateiral.
6. parts as claimed in claim 1 or 2 is characterized in that, the material that is used as metal comprises: nickel, and cobalt or iron, the composition of described metal, that is, and nickel---cobalt, cobalt---iron, nickel---iron or nickel---cobalt---iron.
7. as one of above-mentioned claim described parts, it is characterized in that, utilize the dispersion of pottery and/or metal to strengthen this layer.
8. parts as claimed in claim 7 is characterized in that, have embedded hard and tiny ceramic particle in base layer, preferably silicon-carbide particle.
9. as one of above-mentioned claim described parts, it is characterized in that the base mateiral of parts comprises: have or do not have packing material respectively, the aluminium of fiber or magnesium or zinc alloy, or plastics.
10. described parts one of as in the above-mentioned claim 5 to 9 is characterized in that the base mateiral of parts is by machining, reshape or molded method is shaped.
11. as above-mentioned claim 1 to 4 and 6 to 8 in one of described parts, it is characterized in that it is to be made of the steel that has solid lubricant.
12. as one of above-mentioned claim described parts, it is characterized in that the part of phosphorus accounts for 1 to 15% in body material, the part of boron accounts for 0.5 to 5%.
13., it is characterized in that described parts are spinning ring or Steel Traveler of a ring spinning frame as one of above-mentioned claim described parts.
14. as above-mentioned claim 1 to 12 in one of described parts, it is characterized in that described parts are a kind of rotor of rotor spinner, rotor spindle, rotor lid or expander.
15., it is characterized in that parts are a nozzle or a roll body or a fibre guide element as one of above-mentioned claim described parts.
16., it is characterized in that the hardness of nitride is between 50 to 1000HV as one of above-mentioned claim described parts.
17., it is characterized in that the size of nitride particles is between 0.1 and 5 μ m as one of above-mentioned claim described parts.