CN113981694A - Waterproof cloth and preparation process thereof - Google Patents
Waterproof cloth and preparation process thereof Download PDFInfo
- Publication number
- CN113981694A CN113981694A CN202111169381.2A CN202111169381A CN113981694A CN 113981694 A CN113981694 A CN 113981694A CN 202111169381 A CN202111169381 A CN 202111169381A CN 113981694 A CN113981694 A CN 113981694A
- Authority
- CN
- China
- Prior art keywords
- cloth
- parts
- waterproof cloth
- waterproof
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof cloth which comprises an inner waterproof cloth, a base cloth, a breathable cloth and an outer waterproof cloth which are sequentially arranged from inside to outside, wherein the inner waterproof cloth and the outer waterproof cloth are prepared by mixing the following raw materials in parts by weight: 5-10 parts of polyvinyl chloride resin, 1-3 parts of softener, 4-8 parts of nano titanium dioxide, 2-4 parts of chitin fiber, 1-3 parts of mineral powder, 1-2 parts of flatting agent, 2-4 parts of potassium hydroxide and 5-10 parts of water. The waterproof cloth has two waterproof surfaces, the breathable cloth is arranged on the base cloth, and the waterproof cloth has strong waterproof performance and good crease resistance when being matched with the waterproof cloth on the two surfaces.
Description
Technical Field
The invention relates to the field of waterproof cloth, in particular to waterproof cloth and a preparation process thereof.
Background
The waterproof fabric is a novel textile fabric, and the components of the waterproof fabric are formed by a macromolecular waterproof breathable material (PTFE membrane) and a cloth composite fabric. The cloth with the waterproof film simply coated on the outer layer of the cloth has long time, and the waterproof film on the outer layer is easy to fall off under the repeated folding and compression, so that the waterproof effect is influenced.
Disclosure of Invention
The purpose of the invention is as follows: the invention aims to solve the technical problem of the prior art and provides a waterproof cloth and a preparation process thereof.
In order to solve the technical problem, the invention discloses a waterproof cloth which comprises an inner waterproof cloth, a base cloth, a breathable cloth and an outer waterproof cloth which are sequentially arranged from inside to outside, wherein the inner waterproof cloth and the outer waterproof cloth are prepared by mixing the following raw materials in parts by weight: 5-10 parts of polyvinyl chloride resin, 1-3 parts of softener, 4-8 parts of nano titanium dioxide, 2-4 parts of chitin fiber, 1-3 parts of mineral powder, 1-2 parts of flatting agent, 2-4 parts of potassium hydroxide and 5-10 parts of water.
In the invention, the mineral powder is kaolin.
In the invention, the breathable layer is made of bamboo charcoal fibers.
The invention also discloses a preparation process of the waterproof cloth, which is characterized by comprising the following steps of:
step 1: hot-pressing the base cloth and the breathable cloth;
step 2: adding polyvinyl chloride resin, a softening agent, nano titanium dioxide, chitin fiber, mineral powder, a flatting agent, potassium hydroxide and water into a stirrer according to a ratio, uniformly stirring and pouring out;
and step 3: soaking the cloth obtained in the step 1 into the mixed liquid obtained in the step 2, taking out and drying;
and 4, step 4: immersing the cloth dried in the step 3 into the mixed solution again, taking out and drying;
and 5: and obtaining the finished waterproof cloth.
In the invention, the drying temperature of the step 3 and the step 4 is 100 ℃.
In the invention, the temperature of the mixed solution in the step 2 is 50 ℃, and the material soaking time is 5 min.
In the invention, the temperature of the mixed solution in the step 3 is 60 ℃, and the material soaking time is 10 min.
Has the advantages that: the waterproof cloth has two waterproof surfaces, the breathable cloth is arranged on the base cloth, and the waterproof cloth has strong waterproof performance and good crease resistance when being matched with the waterproof cloth on the two surfaces.
Detailed Description
Example (b):
the embodiment provides a waterproof cloth, including interior tarpaulin, base cloth, ventilative cloth, the outer tarpaulin that sets gradually from inside to outside, wherein interior tarpaulin is mixed with outer tarpaulin by following parts by weight raw materials component and is made: 5-10 parts of polyvinyl chloride resin, 1-3 parts of softener, 4-8 parts of nano titanium dioxide, 2-4 parts of chitin fiber, 1-3 parts of mineral powder, 1-2 parts of flatting agent, 2-4 parts of potassium hydroxide and 5-10 parts of water.
The embodiment specifically includes:
in this embodiment, the mineral powder is kaolin.
In this embodiment, the breathable layer is made of bamboo charcoal fiber.
The invention also discloses a preparation process of the waterproof cloth, which is characterized by comprising the following steps of:
step 1: hot-pressing the base cloth and the breathable cloth;
step 2: adding polyvinyl chloride resin, a softening agent, nano titanium dioxide, chitin fiber, mineral powder, a flatting agent, potassium hydroxide and water into a stirrer according to a ratio, uniformly stirring and pouring out;
and step 3: soaking the cloth obtained in the step 1 into the mixed liquid obtained in the step 2, taking out and drying;
and 4, step 4: immersing the cloth dried in the step 3 into the mixed solution again, taking out and drying;
and 5: and obtaining the finished waterproof cloth.
In this embodiment, the drying temperature in the step 3 and the step 4 is 100 ℃.
In this embodiment, the temperature of the mixture in step 2 is 50 ℃, and the soaking time is 5 min.
In this embodiment, the temperature of the mixture in step 3 is 60 ℃, and the soaking time is 10 min.
The invention provides a waterproof cloth and a preparation process thereof, and a method and a way for realizing the technical scheme are numerous, the above description is only a preferred embodiment of the invention, and it should be noted that, for a person skilled in the art, a plurality of improvements and decorations can be made without departing from the principle of the invention, and these improvements and decorations should also be regarded as the protection scope of the invention. All the components not specified in the present embodiment can be realized by the prior art.
Claims (7)
1. The waterproof cloth is characterized by comprising an inner waterproof cloth, a base cloth, a breathable cloth and an outer waterproof cloth which are sequentially arranged from inside to outside, wherein the inner waterproof cloth and the outer waterproof cloth are prepared by mixing the following raw material components in parts by weight: 5-10 parts of polyvinyl chloride resin, 1-3 parts of softener, 4-8 parts of nano titanium dioxide, 2-4 parts of chitin fiber, 1-3 parts of mineral powder, 1-2 parts of flatting agent, 2-4 parts of potassium hydroxide and 5-10 parts of water.
2. The waterproof fabric of claim 1, wherein the mineral powder is kaolin.
3. The waterproof fabric as claimed in claim 1, wherein the breathable layer is bamboo charcoal fiber.
4. The preparation process of the waterproof cloth is characterized by comprising the following steps of:
step 1: hot-pressing the base cloth and the breathable cloth;
step 2: adding polyvinyl chloride resin, a softening agent, nano titanium dioxide, chitin fiber, mineral powder, a flatting agent, potassium hydroxide and water into a stirrer according to a ratio, uniformly stirring and pouring out;
and step 3: soaking the cloth obtained in the step 1 into the mixed liquid obtained in the step 2, taking out and drying;
and 4, step 4: immersing the cloth dried in the step 3 into the mixed solution again, taking out and drying;
and 5: and obtaining the finished waterproof cloth.
5. The preparation process of the waterproof cloth material according to claim 4, wherein the drying temperature in the step 3 and the step 4 is 100 ℃.
6. The preparation process of the waterproof cloth material according to claim 4, wherein the temperature of the mixed liquid in the step 2 is 50 ℃, and the soaking time is 5 min.
7. The preparation process of the waterproof cloth material according to claim 4, wherein the temperature of the mixed liquid in the step 3 is 60 ℃, and the soaking time is 10 min.