CN113979834B - Photocuring initiator, preparation method thereof and photocuring composition containing photocuring initiator - Google Patents
Photocuring initiator, preparation method thereof and photocuring composition containing photocuring initiator Download PDFInfo
- Publication number
- CN113979834B CN113979834B CN202111336692.3A CN202111336692A CN113979834B CN 113979834 B CN113979834 B CN 113979834B CN 202111336692 A CN202111336692 A CN 202111336692A CN 113979834 B CN113979834 B CN 113979834B
- Authority
- CN
- China
- Prior art keywords
- reaction
- solution
- photocuring
- solvent
- hexafluorophosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a photocuring initiator which is polysubstituted diaryl iodonium hexafluorophosphate and has a structure shown in a formula I, wherein a substituent group R is selected from any one of methyl, ethyl, isopropyl, tert-butyl, methoxy, p-dimethyl, chlorine and bromine. The invention also provides a preparation method of the photocuring initiator, which comprises the following steps: (1) Taking substituted benzene and elemental iodine as reaction raw materials, adding acid, then adding a first solvent, and then adding an oxidant for reaction to obtain an intermediate; (2) And (2) dissolving the intermediate obtained in the step (1) in a second solvent to form a solution, dropwise adding a saturated potassium hexafluorophosphate solution for reaction, and performing suction filtration to obtain the polysubstituted diaryl iodonium hexafluorophosphate after solids are separated out from the solution. The invention also provides a photocuring composition which comprises the photocuring initiator. The method can reduce the process cost, and byproducts generated in the synthesis process are easy to treat and easy to realize industrial mass production.
Description
Technical Field
The invention relates to the technical field of photocuring materials, in particular to a photocuring initiator, a preparation method thereof and a photocuring composition containing the photocuring initiator.
Background
The ultraviolet curing technology is a process for rapidly converting a liquid substance with chemical reaction activity into a solid substance by utilizing ultraviolet initiation. The technology has the characteristics of high curing speed, high efficiency, wide adaptability, economy, energy conservation, less pollution, low toxicity and environmental friendliness, and is widely applied to the fields of printing plate making, photoresists, printing inks, coatings, adhesives, rapid forming, food packaging and medical biomaterials.
The light-cured system generally comprises four parts of a prepolymer, a photoinitiator, a reactive diluent and an additive. The photoinitiator which is the most core photoinitiator in the photocuring technology naturally has high research and application values, and the existing photoinitiators are mainly divided into two types, namely a free radical type photoinitiator and a cationic photoinitiator according to the initiation mechanism. Among them, diaryliodonium salts have been the most widely used cationic polymerization photoinitiators so far because of their advantages such as good photosensitivity, thermal stability and photoinitiation activity.
In 2007, the Olofsson topic group developed a method for synthesizing diaryliodonium trifluoromethanesulfonate using iodobenzene and aromatic hydrocarbon as raw materials and m-chloroperoxybenzoic acid as an oxidizing agent. (adv. Synth. Catal.2007,349, 2610-2618.)
In 2008, the Olofsson subject group developed a new method for synthesizing diaryl iodonium p-toluenesulfonate by using anisole and iodine as raw materials and m-chloroperoxybenzoic acid as an oxidizing agent. (Synlett 2008,4, 592-596.)
However, in the above methods in the prior art for synthesizing diaryl iodonium salts, m-chloroperoxybenzoic acid is used as an oxidant, which is very expensive, and the process for treating m-chlorobenzoic acid, a by-product generated by the reaction, is very complicated, and the recycling difficulty is high. In addition, the method is difficult to realize a large amount of industrial production requirements. Therefore, it is of great significance to develop a new method for synthesizing diaryl iodonium salt with lower cost and easy processing of byproducts.
Disclosure of Invention
The invention aims to solve the technical problems that the synthesis process of diaryl iodonium salt in the prior art is high in cost, byproducts generated in the process are not easy to treat, and industrial mass production is difficult to realize. The invention provides a photocuring initiator, a preparation method thereof and a photocuring composition containing the photocuring initiator, which can reduce the preparation cost of the photocuring initiator, and by-products generated in the synthesis process are easy to treat and easy to realize industrial mass production.
In order to solve the above technical problems, an embodiment of the present invention discloses a photocuring initiator, which is a polysubstituted diaryl iodonium hexafluorophosphate and has a structure represented by formula I:
wherein, the substituent group R is selected from any one of methyl, ethyl, isopropyl, tert-butyl, methoxy, p-dimethyl, chlorine and bromine.
According to another specific embodiment, the present invention discloses a photo-curing initiator, and the substituent group R is selected from any one or more of methyl, ethyl, isopropyl, tert-butyl, methoxy, p-dimethyl, chlorine and bromine.
The embodiment of the invention also discloses a preparation method of the photocuring initiator, which comprises the following steps:
(1) Taking substituted benzene and elemental iodine as reaction raw materials, adding acid, then adding a first solvent, and then adding an oxidant for reaction to obtain an intermediate;
(2) And (2) dissolving the intermediate obtained in the step (1) in a second solvent to form a solution, dropwise adding a saturated potassium hexafluorophosphate solution, and performing suction filtration to obtain the polysubstituted diaryl iodonium hexafluorophosphate after solids are precipitated from the solution.
According to another specific embodiment of the invention, the embodiment of the invention discloses a preparation method of the photocuring initiator, in the step (1), the substituted benzene is any one of toluene, ethylbenzene, cumene, tert-butylbenzene, anisole, p-xylene, chlorobenzene and bromobenzene.
According to another specific embodiment of the present invention, in step (1), the molar ratio of the substituted benzene to the elemental iodine is from 4 to 8, the molar ratio between the acid addition and the elemental iodine is from 2 to 1.
According to another specific embodiment of the present invention, the embodiment of the present invention discloses a preparation method of a photo-curing initiator, in the step (2), the molar ratio of the saturated potassium hexafluorophosphate solution to the intermediate is 1.
According to another specific embodiment of the invention, the embodiment of the invention discloses a preparation method of a photocuring initiator, wherein the acid is any one of p-toluenesulfonic acid, trifluoromethanesulfonic acid, hydrochloric acid, sulfuric acid and acetic acid;
the first solvent is any one of dichloromethane, dichloroethane, methanol, ethyl acetate, acetone and methyl tert-butyl ether.
According to another specific embodiment of the invention, the embodiment of the invention discloses a preparation method of a photocuring initiator, and the oxidant is any one of 50% hydrogen peroxide, sodium perborate, sodium persulfate, potassium monopersulfate, ammonium persulfate, benzoyl peroxide and 55% tert-butyl hydroperoxide.
According to another specific embodiment, the embodiment of the invention discloses a preparation method of the photo-curing initiator, and the second solvent is any one of acetonitrile, methanol, ethanol and isopropanol.
According to another embodiment of the present invention, a method for preparing a photo-curing initiator is disclosed, wherein in the step (1), the reaction temperature is controlled to be 30-80 ℃ and the reaction time is controlled to be 48 hours.
The embodiment of the invention also discloses a photocuring composition which comprises the photocuring initiator.
Compared with the prior art, the invention has the following effects:
the photocuring initiator and the preparation method can reduce the preparation cost of the photocuring initiator, and byproducts generated in the synthesis process are easy to treat, thereby being easy to realize industrial mass production.
Detailed Description
The following description of the embodiments of the present invention is provided for illustrative purposes, and other advantages and effects of the present invention will become apparent to those skilled in the art from the present disclosure. While the invention will be described in conjunction with the preferred embodiments, it is not intended that features of the invention be limited to these embodiments. On the contrary, the invention is described in connection with the embodiments for the purpose of covering alternatives or modifications that may be extended based on the claims of the present invention. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. The invention may be practiced without these particulars. Moreover, some of the specific details have been omitted from the description in order not to obscure or obscure the focus of the present invention. It should be noted that the embodiments and features of the embodiments may be combined with each other without conflict.
The invention relates to a specific synthesis process as follows, the polysubstituted diaryl iodonium hexafluorophosphate is prepared by the method comprising the following steps:
example 1
The related synthesis process comprises the following steps:
11.1g of toluene, 5.1g of elementary iodine, 10.3g of p-toluenesulfonic acid and 50mL of dichloroethane were sequentially added to a 250mL round-bottom flask, then 10.3g of 50% hydrogen peroxide was slowly added dropwise under stirring, and the mixture was heated to 60 ℃ to react for 48 hoursAfter the reaction is finished, filtering to remove solids, washing the filtrate with water, and desolventizing to obtain 16.3g of intermediate bis (4-methylphenyl) iodonium p-toluenesulfonate; 16.3g of the intermediate bis (4-methylphenyl) iodonium p-toluenesulfonate thus obtained was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and the mixture was stirred at room temperature for 2 hours, after a solid precipitated from the solution, it was filtered by suction to obtain 15.2g of the product bis (4-methylphenyl) iodonium hexafluorophosphate in a yield of 84%. Of the resulting product 1 H NMR(500MHz,CDCl 3 )δ8.02(d,J=8.5Hz,4H),7.28(d,J=7.8Hz,4H),2.38(s,6H); 13 C NMR(125MHz,CDCl 3 ) Delta 141.8,136.0,132.3,111.2,21.3. The above results confirmed that the obtained product was the objective product.
Example 2
The related synthesis process comprises the following steps:
adding 12.7g of ethylbenzene, 5.1g of elemental iodine, 10.3g of p-toluenesulfonic acid and 50mL of dichloroethane into a 250mL round-bottom flask in sequence, slowly dropwise adding 10.3g of 50% hydrogen peroxide under the stirring condition, heating to 60 ℃ for reaction for 48 hours, filtering to remove solids after the reaction is finished, and washing and desolventizing filtrate to obtain 15.3g of intermediate bis (4-ethylphenyl) iodonium p-toluenesulfonic acid salt; 15.3g of the intermediate bis (4-ethylphenyl) iodonium p-toluenesulfonate obtained was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and the mixture was stirred at room temperature for 2 hours, after a solid precipitated from the solution, the mixture was filtered by suction to obtain 14.5g of the product bis (4-ethylphenyl) iodonium hexafluorophosphate in a yield of 75%. Of the resulting product 1 H NMR(500MHz,CDCl 3 )δ8.07(d,J=8.5Hz,4H),7.38(d,J=8.4Hz,4H),2.70(q,J=7.3Hz,4H),1.26(t,J=7.2Hz,6H); 13 C NMR(125MHz,CDCl 3 ) Delta 147.0,135.6,130.9,112.4,28.7,15.4. The above results confirmed that the obtained product was the objective product.
Example 3
The related synthesis process comprises the following steps:
adding 14.4g of cumene, 5.1g of elementary iodine, 10.3g of p-toluenesulfonic acid and 50mL of dichloroethane into a 250mL round-bottom flask in sequence, then slowly dropwise adding 10.3g of 50% hydrogen peroxide under the stirring condition, heating to 60 ℃ for reaction for 48 hours, filtering to remove solids after the reaction is finished, and washing and desolventizing filtrate to obtain 16.5g of intermediate bis (4-isopropylphenyl) iodonium p-toluenesulfonic acid salt; 16.5g of the intermediate bis (4-isopropylphenyl) iodonium p-toluenesulfonate was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and the mixture was stirred at room temperature for 2 hours, after solids were precipitated from the solution, the mixture was filtered by suction to obtain 15.5g of the product bis (4-isopropylphenyl) iodonium hexafluorophosphate in a yield of 76%. 1H NMR (500mhz, cdcl3) δ 8.06 (d, J =8.4hz, 4H), 7.28 (d, J =7.5hz, 4H), 2.89-2.73 (m, 2H), 1.26 (d, J =6.6hz, 12h) of the resulting product; 13C NMR (125MHz, CDCl3) delta 150.6,135.6,129.3,113.2,33.9,23.9. The above results confirmed that the obtained product was the objective product.
Example 4
The related synthesis process comprises the following steps:
adding 16.1g of tert-butylbenzene, 5.1g of elemental iodine, 10.3g of p-toluenesulfonic acid and 50mL of dichloroethane into a 250mL round-bottom flask in sequence, then slowly dropwise adding 10.3g of 50% hydrogen peroxide under the stirring condition, heating to 60 ℃ for reaction for 48 hours, filtering to remove solids after the reaction is finished, and washing and desolventizing filtrate to obtain 15.8g of intermediate bis (4-tert-butylphenyl) iodonium p-toluenesulfonic acid; 15.8g of the obtained intermediate bis (4-tert-butylphenyl) iodonium p-toluenesulfonate was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of hexapotassium hexafluorophosphate solution) was added dropwise thereto with stirringPotassium fluorophosphate was dissolved in 200mL of water), stirred at room temperature for 2 hours, and after a solid precipitated from the solution, the solution was filtered by suction to obtain 14.9g of bis (4-tert-butylphenyl) iodonium hexafluorophosphate, a yield of 69%. Of the resulting product 1 H NMR(500MHz,CDCl 3 )δ8.05(d,J=8.5Hz,4H),7.50(d,J=8.5Hz,4H),1.36(s,18H); 13 C NMR(125MHz,CDCl 3 ) Delta 154.9,135.7,128.2,113.4,34.6,31.2. The above results confirmed that the obtained product was the objective product.
Example 5
The related synthesis process comprises the following steps:
13.0g of anisole, 5.1g of iodine, 10.3g of p-toluenesulfonic acid and 50mL of dichloroethane were sequentially added to a 250mL round-bottom flask, then 10.3g of 50% hydrogen peroxide was slowly added dropwise with stirring, and then the mixture was heated to 60 ℃ to react for 48 hours. After the reaction, the solid was removed by filtration, and the filtrate was washed with water and desolventized to obtain 16.8g of intermediate bis (4-methoxyphenyl) iodonium p-toluenesulfonate. The intermediate bis (4-methoxyphenyl) iodonium p-toluenesulfonate, which was obtained in an amount of 16.8g, was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and the mixture was stirred at room temperature for 2 hours, after a solid precipitated from the solution, it was filtered by suction to obtain the product bis (4-methoxyphenyl) iodonium hexafluorophosphate, 15.8g, in a yield of 81%. 1H NMR (500mhz, cdcl3) δ 8.05 (d, J =8.5hz, 4h), 7.03 (d, J =8.4hz, 4h), 3.79 (s, 6H) of the resulting product; 13C NMR (125MHz, CDCl3) delta 162.9,137.4,117.5,107.1,55.4. The above results confirmed that the obtained product was the objective product.
Example 6
The related synthesis process comprises the following steps:
to a 250mL round bottom flask were added 12.7g of p-xylene, 5.1g of elemental iodine, and 10.3g of p-toluene in that orderSulfonic acid and 50mL dichloroethane, then slowly dropwise adding 10.3g of 50% hydrogen peroxide under the condition of stirring, then heating to 60 ℃ for reacting for 48 hours, filtering to remove solids after the reaction is finished, and washing and desolventizing the filtrate to obtain 13.2g of intermediate bis (2, 5-dimethylphenyl) iodonium p-toluenesulfonate; 13.2g of the obtained intermediate bis (2, 5-dimethylphenyl) iodonium p-toluenesulfonate was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and stirred at room temperature for 2 hours, and after a solid precipitated from the solution, 12.3g of the product bis (2, 5-dimethylphenyl) iodonium hexafluorophosphate was obtained by suction filtration at a yield of 64%. Of the resulting product 1 H NMR(500MHz,CDCl 3 )δ7.97(s,2H),7.14(s,4H),2.41(s,6H),2.36(s,6H); 13 C NMR(125MHz,CDCl 3 ) Delta 139.8,137.2,134.8,132.1,131.2,110.8,27.3,21.0. The above results confirmed that the obtained product was the objective product.
Example 7
The related synthesis process comprises the following steps:
13.5g of chlorobenzene, 5.1g of elemental iodine, 9g of trifluoromethanesulfonic acid and 50mL of dichloroethane are sequentially added into a 250mL round-bottom flask, then 10.3g of 50% hydrogen peroxide is slowly dripped under the stirring condition, then the mixture is heated to 60 ℃ to react for 48 hours, after the reaction is finished, the solid is removed by filtration, and after washing and desolventizing are carried out on the filtrate, 16.4g of intermediate bis (4-chlorophenyl) iodonium trifluoromethanesulfonate is obtained; the obtained 16.4g of intermediate bis (4-chlorophenyl) iodonium trifluoromethanesulfonate was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and stirred at room temperature for 2 hours, and after a solid precipitated from the solution, 16.7g of the product bis (4-chlorophenyl) iodonium hexafluorophosphate was obtained by suction filtration at a yield of 82%. 1H NMR (500mhz, cdcl3) δ 8.09 (d, J =8.4hz, 4H), 7.55 (d, J =8.5hz, 4H) of the resulting product; 13C NMR (125MHz, CDCl3) delta 137.4,137.3,131.9,112.3. The above results confirmed that the obtained product was the objective product.
Example 8
The related synthesis process comprises the following steps:
adding 18.8g of bromobenzene, 5.1g of elemental iodine, 9g of trifluoromethanesulfonic acid and 50mL of dichloroethane into a 250mL round-bottom flask in sequence, then slowly dropwise adding 10.3g of 50% hydrogen peroxide under the stirring condition, heating to 60 ℃ for reacting for 48 hours, filtering to remove solids after the reaction is finished, and washing and desolventizing filtrate to obtain 19.3g of intermediate bis (4-bromophenyl) iodonium trifluoromethanesulfonate; 19.3g of the intermediate bis (4-bromophenyl) iodonium trifluoromethanesulfonate thus obtained was dissolved in 10mL of ethanol, and then a saturated potassium hexafluorophosphate solution (14.7 g of potassium hexafluorophosphate dissolved in 200mL of water) was added dropwise thereto with stirring, and the mixture was stirred at room temperature for 2 hours, and after a solid precipitated from the solution, 19.6g of the product bis (4-bromophenyl) iodonium hexafluorophosphate was obtained by suction filtration at a yield of 82%. Of the resulting product 1 H NMR(500MHz,CDCl 3 )δ8.08(d,J=8.5Hz,4H),7.65(d,J=8.5Hz,4H); 13 C NMR(125MHz,CDCl 3 ) Delta 137.5,134.5,125.4,113.2. The above results confirmed that the obtained product was the objective product.
The invention provides a new way for synthesizing polysubstituted diaryl iodonium hexafluorophosphate, which has high photoinitiation activity; the oxidant used in the method is cheap and easy to obtain, and meanwhile, the generated by-product is easy to treat, the reaction condition is mild, and the industrial production requirement can be met.
While the invention has been described with reference to certain preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing is illustrative of the present invention and is not to be construed as limited to the specific embodiments disclosed. Various changes in form and detail, including simple deductions or substitutions, may be made by those skilled in the art without departing from the spirit and scope of the invention.
Claims (4)
1. A method for preparing a photo-curing initiator, wherein the initiator is a polysubstituted diaryl iodonium hexafluorophosphate, and the polysubstituted diaryl iodonium hexafluorophosphate has a structure shown in formula I:
formula I
Wherein, the substituent group R is selected from any one of methyl, ethyl, isopropyl, tert-butyl, methoxy, p-dimethyl, chlorine and bromine;
the preparation method of the photoinitiator comprises the following steps:
(1) Taking substituted benzene and elemental iodine as reaction raw materials, adding acid, then adding a first solvent, and then adding an oxidant for reaction, wherein the reaction temperature is controlled to be 30-80 ℃, and the reaction time is controlled to be 48 hours, so as to obtain an intermediate;
wherein the acid is p-toluenesulfonic acid; the first solvent is any one of dichloromethane, dichloroethane, methanol, ethyl acetate, acetone and methyl tert-butyl ether; the oxidant is 50% hydrogen peroxide;
(2) Dissolving the intermediate obtained in the step (1) in a second solvent to form a solution, dropwise adding a saturated potassium hexafluorophosphate solution for reaction, and performing suction filtration to obtain the polysubstituted diaryl iodonium hexafluorophosphate after solids are separated out from the solution;
wherein the second solvent is any one of acetonitrile, methanol, ethanol and isopropanol.
2. The method for preparing the photo-curing initiator according to claim 1, wherein in the step (1), the substituted benzene is any one of toluene, ethylbenzene, cumene, tert-butylbenzene, anisole, p-xylene, chlorobenzene, and bromobenzene.
3. The method for preparing the photo-curing initiator according to claim 1, wherein in step (1), the molar ratio of the substituted benzene to the elemental iodine is 4.
4. The method for preparing the photo-curing initiator according to claim 1, wherein in the step (2), the molar ratio of the saturated potassium hexafluorophosphate solution to the intermediate is 1.