CN113956067A - 一种泡沫水泥吸音板 - Google Patents
一种泡沫水泥吸音板 Download PDFInfo
- Publication number
- CN113956067A CN113956067A CN202111400301.XA CN202111400301A CN113956067A CN 113956067 A CN113956067 A CN 113956067A CN 202111400301 A CN202111400301 A CN 202111400301A CN 113956067 A CN113956067 A CN 113956067A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- foaming agent
- foam
- foam cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种泡沫水泥吸音板及其制备方法，该吸音板材料包括胶凝材料、水、耐火材料、保温材料、稳泡剂、发泡剂以及憎水剂。其中所述胶凝材料为普通硅酸盐水泥、粉煤灰、磷酸盐水泥中的一种或多种,所述耐火材料为熟铝矾土，所述保温材料为聚丙烯腈纤维及膨胀蛭石，所述稳泡剂为硅酮酰胺，所述发泡剂为双氧水发泡剂，所述憎水剂为甲基硅酸钠。与现有技术相比，本发明的泡沫水泥吸音板的吸音隔音效果好，强度高，轻质，热胀冷缩反应小，防潮，耐火性能及保温效果好，施工工艺便捷特别适用于隧道工程。
Description
技术领域
本发明涉及一种泡沫水泥吸音板及其制备方法，尤其是涉及一种隧道工程用吸音板及其制备方法，属于建筑材料技术领域。
背景技术
目前，市面上采用的吸音板多应用于房建工程中，很少有应用到隧道工程中的吸音板。常用的的吸音板多为矿棉吸音板、木质吸音板、石膏吸音板等。这类材料存在强度低，自重大，热胀冷缩反应大，吸水率高，施工工艺多的缺点。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供的一种吸音隔音效果好，强度高，轻质，防潮，耐火性能好，保温效果好的泡沫水泥吸音板及其制备方法。
本发明的目的可以通过以下技术方案来实现
一种泡沫水泥吸音板，由以下成分及重量百分比含量的原料制成：
该泡沫水泥吸音板所含成分优选以下重量百分比：
所述的胶凝材料为普通硅酸盐水泥、粉煤灰、磷酸盐水泥中的一种或多种。
所述的耐火材料为熟铝矾土。
所述的保温材料为聚丙烯腈纤维及膨胀蛭石。
所述的稳泡剂为硅酮酰胺。
所述的发泡剂为双氧水发泡剂。
所述的憎水剂为甲基硅酸钠。
一种泡沫水泥吸音板的制备方法，该方法包括以下步骤：
按照以下成分及重量百分比含量备料：胶凝材料150、水50～63、耐火材料11～12.3、保温材料6.4～7.5、稳泡剂5.5～6.2、发泡剂4～6.5憎水剂2～3：
将稳泡剂和憎水剂加入容器，进行人工搅拌形成预混料；
将胶凝、水、耐火材料、保温材料、预混料依次加入搅拌机中，进行均匀搅拌形成浆料；
将发泡剂发泡后加入上述所得的浆料中，搅拌均匀后浇筑到模具中，成形后经过脱模和养护得到吸音板；
一种泡沫水泥吸音板的应用：经上述程序制备所得泡沫水泥吸音板可用于隧道工程中。
与现有技术相比，本发明具有以下优点及有益效果；
本发明的泡沫水泥吸音板以普通硅酸盐水泥、粉煤灰。磷酸盐水泥为主要成分。通过在吸音板原料中加入双氧水发泡剂来降低吸音板容重及导热系数，并在吸音板中形成蜂窝状结构达到轻质、保温、吸音的目的；加入熟铝矾土可以提高吸音板的耐火性能从而达到防火要求；加入聚丙烯腈纤维既可以加强吸音板的整体性也可以与膨胀蛭石相结合从而提升吸音板的保温性能；加入硅酮酰胺可以与双氧水发泡剂相结合从而提升双氧水发泡剂的稳定性；通过加入甲基硅酸钠，可以使吸音板及内部生成不溶性的防水高分子化合物，从而达到防水目的；将胶凝材料与上述各种材料相混合可以显著改善吸音板的各项综合性能。制取的吸音板吸音隔音效果好，强度高，热胀冷缩反应小，防潮，耐火性能及保温效果好，施工工艺便捷。
具体实施方式
下面将结合具体的实施例对本发明进行详细说明
以下实施例中取得的试件采用如下方法进行测试：
根据JC/T2122-2012来测得吸音板吸声系数；根据JC/T266-2011来测得密度、抗压强度及吸水率；根据GB/T10294来测得导热系数；根据GB/T5464-2010来测得燃烧性能。
实施例1
一种泡沫水泥吸音板，由以下成分及重量百分比含量的原料制成：
一种泡沫水泥吸音版的制备方法，该方法包括以下步骤：
(1)按照以下成分及重量百分比含量备料：普通硅酸盐水泥130、粉煤灰20、水58、熟铝矾土11.6、聚丙烯腈纤维3.4、膨胀蛭石3.5、硅酮酰胺6.0、双氧水发泡剂6.4、甲基硅酸钠2.5；
(2)将硅酮酰胺和甲基硅酸钠加入容器，进行人工搅拌形成预混料；
(3)将普通硅酸盐水泥、粉煤灰、水、熟铝矾土、聚丙烯腈纤维、膨胀蛭石、双氧水发泡剂及预混料依次加入搅拌机中，进行均匀搅拌5min形成浆料。
(4)将双氧水发泡剂加入上述所得浆料中，搅拌均匀后浇筑到模具中。浇筑前模具应均匀涂刷脱模剂以此来保证试件不沾模。浇筑完成后把所得试件放入养护室中进行发泡，试件成型后进行脱模，脱模后继续养护28天，养护完成后获得此试件。
脱模后制取的吸音板密度357kg/m3，导热系数为0.038W/(m·K),吸水率5％，抗压强度0.83Mpa,吸音板吸声系数详见(表1)，吸音板防火等级为A1级别。
实施例2
一种泡沫水泥吸音版，由以下成分及重量百分比含量的原料制成：
一种泡沫水泥吸音版的制备方法，该方法包括以下步骤：
(1)按照以下成分及重量百分比含量备料：普通硅酸盐水泥113、磷酸盐水泥27、水62、熟铝矾土12.3、聚丙烯腈纤维3.1、膨胀蛭石4.4、硅酮酰胺5.8、双氧水发泡剂5.6、甲基硅酸钠2.2；
(2)将硅酮酰胺和甲基硅酸钠加入容器，进行人工搅拌形成预混料；
(3)将普通硅酸盐水泥、粉煤灰、水、熟铝矾土、聚丙烯腈纤维、膨胀蛭石、双氧水发泡剂及预混料依次加入搅拌机中，进行均匀搅拌5min形成浆料。
(4)将双氧水发泡剂加入上述所得浆料中，搅拌均匀后浇筑到模具中。浇筑前模具应均匀涂刷脱模剂以此来保证试件不沾模。浇筑完成后把所得试件放入养护室中进行发泡，试件成型后进行脱模，脱模后继续养护28天，养护完成后获得此试件。
脱模后制取的吸音板密度363kg/m3，导热系数为0.04W/(m·K),吸水率5.0％，抗压强度0.81Mpa,吸音板吸声系数详见(表1)，吸音板防火等级为A1级别。
实施例3
一种泡沫水泥吸音版，由以下成分及重量百分比含量的原料制成：
一种泡沫水泥吸音版的制备方法，该方法包括以下步骤：
(1)按照以下成分及重量百分比含量备料：普通硅酸盐水泥95、磷酸盐水泥27、粉煤灰23、水55、熟铝矾土11.5、聚丙烯腈纤维3.75、膨胀蛭石3.75、硅酮酰胺5.8、双氧水发泡剂6.0、甲基硅酸钠2.1；
(2)将硅酮酰胺和甲基硅酸钠加入容器，进行人工搅拌形成预混料；
(3)将普通硅酸盐水泥、粉煤灰、水、熟铝矾土、聚丙烯腈纤维、膨胀蛭石、双氧水发泡剂及预混料依次加入搅拌机中，进行均匀搅拌5min形成浆料。
(4)将双氧水发泡剂加入上述所得浆料中，搅拌均匀后浇筑到模具中。浇筑前模具应均匀涂刷脱模剂以此来保证试件不沾模。浇筑完成后把所得试件放入养护室中进行发泡，试件成型后进行脱模，脱模后继续养护28天，养护完成后获得此试件。
脱模后制取的吸音板密度349kg/m3，导热系数为0.038W/(m·K),吸水率4.8％，抗压强度0.83Mpa,吸音板吸声系数详见(表1)，吸音板防火等级为A1级别。
表1
由实施例1-3的数据可见，经过在不同频率下进行测试，采用实施例3时，泡沫水泥吸音板的吸声效果最好。
Claims (9)
1.一种泡沫水泥吸音板，其特征在于：该吸音板由以下成分及重量百分比含量的原料制成：
2.根据权利要求1所述的一种泡沫水泥吸音板：其特征在于：该泡沫剂所含成分优选以下重量百分比：
3.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述胶凝材料选自普通硅酸盐水泥、粉煤灰、磷酸盐水泥中的一种或多种。
4.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述耐火材料为熟铝矾土。
5.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述保温材料为聚丙烯腈纤维及膨胀蛭石。
6.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述的稳泡剂选自硅酮酰胺。
7.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述的发泡剂选自双氧水发泡剂。
8.根据权利1或2所述的一种泡沫水泥吸音板，其特征在于：所述憎水剂甲基硅酸钠。
9.根据要求1～8所述的一种泡沫水泥吸音板的制备方法，其特征在于：按照以下成分及重量百分比含量备料：
(1)胶凝材料150、水50～63、耐火材料11～12.3、保温材料6.4～7.5、稳泡剂5.5～6.2、发泡剂4～6.5、憎水剂2～3。
(2)将稳泡剂和憎水剂加入容器，进行人工搅拌形成预混料。
(3)将胶凝材料、水、耐火材料、保温材料、预混料依次加入搅拌机中，进行均匀搅拌形成浆料。
(4)将发泡剂发泡后加入上述所得的浆料中，搅拌均匀后浇筑到模具中，成形后经过脱模和养护得到吸音板。