CN113927000A - Thin strip continuous casting structure and method for removing cold steel on surface of molten pool thereof - Google Patents
Thin strip continuous casting structure and method for removing cold steel on surface of molten pool thereof Download PDFInfo
- Publication number
- CN113927000A CN113927000A CN202010602928.2A CN202010602928A CN113927000A CN 113927000 A CN113927000 A CN 113927000A CN 202010602928 A CN202010602928 A CN 202010602928A CN 113927000 A CN113927000 A CN 113927000A
- Authority
- CN
- China
- Prior art keywords
- molten pool
- flow distributor
- thin strip
- distributor
- cold steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a thin strip continuous casting structure and a method for removing cold steel on the surface of a molten pool thereof, and the thin strip continuous casting structure comprises a tundish, wherein a water gap is formed at the bottom of the tundish, a flow distributor is arranged below the water gap, a pair of crystallization rollers are arranged below the flow distributor, the crystallization rollers and side sealing plates enclose a molten pool, and the distance between a spitting hole on the flow distributor and the surface of the molten pool is set to be H1; the cloth stream device is provided with a bracket mechanism, the bracket mechanism drives the cloth stream device to move vertically, and a vertical movement curve equation Y of the cloth stream device is as follows: y ═ ASin (ω X + Φ) or Y ═ ACos (ω X + Φ), where a is the amplitude, ω is the frequency, and X is the time. The invention utilizes the micromotion of the flow distributor to improve the flow distribution on the surface of the molten pool, and simultaneously blocks the generation and growth of cold steel on the surface of the flow distributor, thereby avoiding the formation of larger cold steel blocks on the surface of the molten pool.
Description
Technical Field
The invention relates to a twin-roll thin strip continuous casting technology, in particular to a thin strip continuous casting structure and a method for removing cold steel on the surface of a molten pool thereof.
Background
The twin-roll thin strip continuous casting adopts two casting rolls rotating in opposite directions as crystallizers, and liquid metal is directly produced into thin strip steel with the thickness of less than 10 mm. Compared with the traditional thin strip production process, the technology has the advantages of shortening the process flow, saving energy, reducing the production cost, improving the mechanical property of a strip blank and the like, so the technology is considered to be one of the most promising near-net shape continuous casting technologies in the 21 st century.
The strip casting process is a casting and rolling process which is not only related to but also distinguished from the traditional continuous casting. Referring to fig. 1, a conventional thin strip continuous casting structure is mainly manufactured by injecting molten steel 1 into a tundish 2, distributing the molten steel 1 into a distributor 4 through a nozzle 3, injecting the molten steel into a molten pool surrounded by two water-cooled crystallization rolls 5 and side sealing plates through the distributor 4, gradually solidifying the molten steel 1 on the surfaces of the two water-cooled crystallization rolls 5 to form a shell, and after the molten steel is completely solidified near a connecting line of the two water-cooled crystallization rolls 5, performing a rolling action through reverse rotation of the two water-cooled crystallization rolls 5 to form a dense metal strip 6 with a certain thickness and width.
The main problems of the prior art are as follows:
the control method of the casting process is complex, the solidification speed of the molten steel has close relation with factors such as the rotation speed of a crystallizing roller, the liquid level of a molten pool, the roll gap of the crystallizing roller, the quality of the molten steel and the like in the casting process, and the problem of complexity is solved if the optimal matching of various process parameters is sought;
in addition, the strip continuous casting molten pool is much smaller than the traditional production process, and in order to improve the surface quality of the cast strip, the uniform distribution of the molten steel in the molten pool must be ensured, a flow distributor is additionally arranged in the molten pool, and a side sealing plate is additionally arranged at the edge part. After the molten steel is cast into a molten pool, the molten steel is further influenced by the cooling effect of the flow distributor and the side sealing plates and the heat dissipation of the molten steel into air besides the cooling effect of the crystallizing roller, so that the supercooling of the molten steel in the molten pool and the heat dissipation of the molten steel into air are easily caused, the supercooling of the molten steel in the molten pool is easily caused, cold steel is formed on the flow distributor and the side sealing plates, meanwhile, the cold steel is also formed in the molten pool due to unstable fluctuation of the liquid level of the molten pool in the casting process, the cold steel falls into the bottom of the molten pool when the cold steel grows to a certain degree, the casting force is suddenly changed when the cold steel reaches the position of a roll gap, cold-insulated cracks and other defects are easily formed on the surface of a casting strip, the surface quality of the casting strip is seriously influenced, the strip breakage can be formed in serious cases, and the production process is interrupted. Such abrupt changes in rolling force may also impact the crystallization roller, reducing the service life of the crystallization roller.
In order to reduce the adverse effect of cold steel on the continuous casting production of thin strips, domestic and foreign scholars adopt various methods to heat and preserve heat of local supercooling areas so as to prevent cold steel caused by supercooling of the local supercooling areas.
One of the important methods is to use an electromagnetic induction heating method, and in WO2000037199, JP2155543 and the like, an induction generator is additionally arranged behind a side sealing plate of a thin strip continuous casting bath to heat molten steel near the side sealing plate, so as to prevent cold steel from being formed on the side sealing plate.
Chinese patent CN98229485.9 proposes a hot side sealing device for a twin-roll thin strip casting machine, which is characterized in that a set of resistance heater is added behind the side sealing plate of the molten pool for heating, so that the side sealing plate can keep a high temperature state during the casting process, and the formation of cold steel is prevented.
JP7290202 discloses a side heat-insulating cover for a molten pool, namely, a parabolic heat-insulating cover is arranged above a thin-strip continuous casting side molten pool, and a meniscus on a side sealing plate is just positioned above the focus of the parabolic heat-insulating cover, so that the radiation heat reflection of molten steel in the molten pool is converged on the focus, the temperature near the meniscus is kept high, the steel is prevented from being cooled, and the casting process can be carried out for a long time.
In addition, chinese patent CN 101564761a proposes a method and a device for heating meniscus in a twin-roll thin-strip continuous casting molten pool, the main content of which is to arrange a reflector and a corresponding quartz glass panel above the thin-strip continuous casting molten pool, install a heating lamp tube at the focal point position in the reflector, the inner wall of the reflector is oval, the focal point of an ellipsoid formed by the inner wall of the reflector is located at the meniscus position of a flow distributor or a side closure plate in the molten pool, so as to realize online heating and heat preservation of the side closure plate and the meniscus on the flow distributor at the position where cold steel is easily solidified in the thin-strip continuous casting molten pool.
The above patent solves the problem of the cold steel at the local position of the molten pool to a certain extent, but the uniformity of the overall temperature of the molten pool is difficult to improve, and the implementation angle has great uncertainty.
Disclosure of Invention
Aiming at the defects in the prior art, the invention aims to provide a thin strip continuous casting structure and a method for removing cold steel on the surface of a molten pool thereof.
In order to achieve the purpose, the invention adopts the following technical scheme:
on one hand, the thin strip continuous casting structure comprises a tundish, wherein a water gap is formed in the bottom of the tundish, a flow distributor is arranged below the water gap, a pair of crystallization rollers are arranged below the flow distributor, the crystallization rollers and side sealing plates form a molten pool in a surrounding manner,
the distance between a spitting hole on the flow distributor and the surface of the molten pool is set to be H1;
the cloth stream device is provided with a bracket mechanism, the bracket mechanism drives the cloth stream device to move vertically, and a vertical movement curve equation Y of the cloth stream device is as follows:
Y=ASin(ωX+φ)
or Y ═ ACos (ω X + φ)
In the formula, A is amplitude, ω is frequency, X is time, and φ is start position.
Preferably, the distance H1 between the discharge hole of the distributor and the surface of the molten pool is set between 5mm and 15 mm.
Preferably, the amplitude a ranges from 0.33 to 0.5H 1.
Preferably, the value range of the frequency omega is between 1 and 2.
Preferably, the bracket mechanism has a pair of brackets, which are respectively and symmetrically arranged on two sides of the upper end of the flow distributor.
Preferably, the bracket mechanism comprises a sliding groove arranged on the side part of the current distributor, and a bracket body hinged in the sliding groove through a shaft, the front end of the bracket body is contacted with the upper end part of the current distributor, and the rear end of the bracket body is connected with a motor.
In another aspect, a method for removing cold steel from the surface of a molten pool based on the thin strip continuous casting structure comprises the following steps:
1) setting a distance H1 between a spitting hole on the flow distributor and the surface of the molten pool;
2) selecting the amplitude A of the vertical movement of the current distributor;
3) selecting the vertical moving frequency omega of the current distributor;
4) selecting a curve equation Y for the vertical movement of the current distributor, and substituting the amplitude A in the step 2) and the frequency omega in the step 3) into the curve equation Y;
5) and in the casting process, putting the curve equation Y of the step 4) into a control program for vertically moving the flow distributor.
Preferably, the surface distance H1 is selected to be between 8mm and 12 mm.
Preferably, the amplitude A is selected to be 0.33-0.5H 1.
Preferably, the frequency ω is selected to be between 1 and 2.
The thin strip continuous casting structure and the method for removing cold steel on the surface of the molten pool thereof provided by the invention also have the following beneficial effects:
1) the up-down micro motion is realized through the flow distributor, so that the temperature distribution on the surface of a molten pool can be improved, and the temperature on the surface of the molten pool is increased;
2) the up-down micro motion is realized through the flow distributor, so that the cold solidifying point can be prevented from being formed on the surface of the flow distributor;
3) the up-down jogging is realized through the flow distributor, so that the cold steel blocks which start to solidify and grow up can be blocked;
4) the temperature distribution in the molten pool can be improved and the whole activity of the molten pool is increased by the up-and-down micro motion of the flow distributor.
Drawings
FIG. 1 is a schematic view of a prior art thin strip casting structure;
FIG. 2 is a schematic view of a thin strip casting structure of the present invention;
FIG. 3 is a schematic flow chart of the method for removing cold steel from the surface of the molten pool.
Detailed Description
The technical scheme of the invention is further explained by combining the drawings and the embodiment.
Referring to fig. 2, the thin strip continuous casting structure provided by the present invention includes a tundish 8 for containing molten steel 7, a nozzle 9 is provided at the bottom of the tundish 8, a distributor 10 is provided below the nozzle 9, a pair of crystallization rollers 11 is provided below the distributor 10, and the crystallization rollers 11 and side sealing plates enclose a molten pool 12.
The distance between the discharge hole 13 on the flow distributor 10 and the surface of the molten pool 12 is set to be H1, H1 is set to be between 8mm and 12mm, and H1 is optimally set to be 10 mm.
The bracket mechanism is arranged on the flow distributor 10, the bracket mechanism drives the up-and-down micro motion of the flow distributor 10, and a curve equation Y of the up-and-down micro motion of the flow distributor 10 is as follows:
Y=ASin(ωX+φ)
or Y ═ ACos (ω X + φ)
In the formula, A is amplitude and the value range is 0.33-0.5H 1;
omega is frequency, and the value range is 1-2;
x is time;
phi is the starting position.
The bracket mechanism is provided with a pair of brackets which are respectively and symmetrically arranged at two sides of the upper end part of the flow distributor.
The bracket mechanism comprises sliding grooves 14 arranged at two side parts of the flow distributor 10, and a bracket body 16 hinged in the sliding grooves 14 through a shaft 15, wherein the front end of the bracket body 16 is contacted with the upper end part of the flow distributor 10, and the rear end of the bracket body 16 is connected with a motor 17.
In the casting process, molten steel 7 passes through a water inlet 9 of a tundish 8 and is then distributed into a distributor 10 through the water inlet 9, the distributor 10 is fixed through a bracket body 16, the bracket body 16 is fixed in a chute 14 through a shaft 15 capable of moving up and down, a motor 17 drives the shaft 15 to move in the chute 14 to realize the up and down micro movement of the bracket body 16 and the distributor 10, and a discharge hole 13 on the distributor 10 is immersed in a certain distance below a molten pool 12.
The invention also provides a molten pool surface cold steel removing method based on the thin strip continuous casting structure, which comprises the following steps:
1) setting the surface distance H1 between the discharge hole 13 on the flow distributor 10 and the molten pool 12; since the spout hole 13 is buried below the liquid level of the molten bath 12, the molten steel flowing out of the spout hole 13 functions to activate the surface of the molten bath 12, so that the distance H1 cannot be too large, and if the spout hole 13 is buried too deeply, the molten steel level on the surface of the molten bath 12 is too calm, which may cause cold steel to appear; if the discharge hole 13 is buried too shallow, the liquid surface of the molten pool 12 becomes too active to form a micro-crack.
2) Selecting the amplitude A of the vertical movement of the current distributor 10; the amplitude A affects the distance H1 between the spitting hole 13 of the stream distributor 10 and the liquid surface of the upper molten pool 12, so the range does not exceed the set distance H1 between the spitting hole 13 and the liquid surface of the upper molten pool 12 by controlling the amplitude between 0.33 and 0.5H 1.
3) Selecting the vertical moving frequency omega of the current distributor 10; the frequency omega can be used for micro-motion to obtain better probability for preventing cold steel from appearing.
4) Selecting a curve equation Y for the vertical movement of the current distributor 10, and substituting the amplitude A in the step 2) and the frequency omega in the step 3) into the curve equation Y; the curve equation is selected as the curve equation of the movement of the flow distributor 10, on one hand, the curve equation can be easily set and realized in a rotating mechanism, and in addition, the amplitude A and the repeatability with time are better.
5) During the casting process, putting the curve equation Y of the step 4) into a control program of the vertical movement of the flow distributor 10.
Example 1
A molten pool surface cold steel removing method based on a thin strip continuous casting structure comprises the following steps:
1) in the casting process, the distance H1 between the spitting hole 13 on the flow distributor 10 and the surface of the molten pool 12 is set to be 8 mm;
2) selecting the amplitude A of the vertical movement of the flow distributor 10 to be 4 mm;
3) selecting the vertical moving frequency omega of the current distributor 10 as 1;
4) selecting a curve equation Y ═ ASin (ω X + Φ) for the vertical movement of the flow distributor 10, and substituting the amplitude a of step 2) of 4mm and the frequency ω of step 3) of 1 into the curve equation Y ═ ASin (ω X + Φ) to obtain: y ═ 4Sin (X + Φ);
5) during the casting process, the curve equation Y of step 4) is 4Sin (X + Φ) and put into the control program of the vertical movement of the current distributor 10.
Example 2
A molten pool surface cold steel removing method based on a thin strip continuous casting structure comprises the following steps:
1) in the casting process, the distance H1 between the spitting hole 13 on the flow distributor 10 and the surface of the molten pool 12 is set to be 10 mm;
2) selecting the amplitude A of the vertical movement of the flow distributor 10 to be 5 mm;
3) selecting a frequency omega of the vertical movement of the current distributor 10 to be 2;
4) selecting a curve equation Y ═ ASin (ω X + Φ) for the vertical movement of the flow distributor 10, and substituting the amplitude a of step 2) of 5mm and the frequency ω ═ 2 of step 3) into the curve equation Y ═ ASin (ω X + Φ) to obtain: y ═ 5Sin (2X + Φ);
5) during casting, the curve equation Y of step 4) is 5Sin (2X + Φ) and put into the control program for controlling the vertical movement of the distributor 10.
Example 3
A molten pool surface cold steel removing method based on a thin strip continuous casting structure comprises the following steps:
1) in the casting process, the distance H1 between the spitting hole 13 on the flow distributor 10 and the surface of the molten pool 12 is set to be 12 mm;
2) selecting the amplitude A of the vertical movement of the flow distributor 10 to be 3 mm;
3) selecting the vertical moving frequency omega of the current distributor 10 to be 1.5;
4) selecting a curve equation Y ═ ASin (ω X + Φ) for the vertical movement of the flow distributor 10, and substituting the curve equation Y ═ ASin (ω X + Φ) for the amplitude a of step 2) of 3mm and the frequency ω of step 3) of 1.5 into the curve equation Y ═ ASin (ω X + Φ): y ═ 3Sin (1.5X + Φ);
5) during casting, the curve equation Y of step 4) is 3Sin (1.5X + Φ) and put into the control program of the vertical movement of the distributor 10.
It should be understood by those skilled in the art that the above embodiments are only for illustrating the present invention and are not to be used as a limitation of the present invention, and that changes and modifications to the above described embodiments are within the scope of the claims of the present invention as long as they are within the spirit and scope of the present invention.
Claims (10)
1. The utility model provides a thin strip continuous casting structure, includes the tundish, the bottom of tundish has the mouth of a river, the below at the mouth of a river is equipped with the flow distributor, the below of flow distributor is equipped with a pair of crystallization roller, the crystallization roller encloses into the molten bath with the side seal board, its characterized in that:
the distance between a spitting hole on the flow distributor and the surface of the molten pool is set to be H1;
the cloth stream device is provided with a bracket mechanism, the bracket mechanism drives the cloth stream device to move vertically, and a vertical movement curve equation Y of the cloth stream device is as follows:
Y=ASin(ωX+φ)
or Y ═ ACos (ω X + φ)
In the formula, A is amplitude, ω is frequency, X is time, and φ is start position.
2. The thin strip cast structure as claimed in claim 1 wherein: the distance H1 between the discharge hole on the flow distributor and the surface of the molten pool is set between 8mm and 12 mm.
3. The thin strip cast structure as claimed in claim 2 wherein: the amplitude A ranges from 0.33 to 0.5H 1.
4. The thin strip cast structure as claimed in claim 1 wherein: the value range of the frequency omega is 1-2.
5. The thin strip cast structure as claimed in claim 1 wherein: the bracket mechanism is provided with a pair of brackets which are respectively and symmetrically arranged on two sides of the upper end part of the flow distributor.
6. The thin strip cast structure as claimed in claim 5 wherein: the bracket mechanism comprises a sliding groove arranged on the side part of the current distributor, and a bracket body hinged in the sliding groove through a shaft, wherein the front end of the bracket body is contacted with the upper end part of the current distributor, and the rear end of the bracket body is connected with a motor.
7. A method for removing cold steel from the surface of a molten bath based on the thin strip casting structure according to any one of claims 1 to 6, comprising the steps of:
1) setting a distance H1 between a spitting hole on the flow distributor and the surface of the molten pool;
2) selecting the amplitude A of the vertical movement of the current distributor;
3) selecting the vertical moving frequency omega of the current distributor;
4) selecting a curve equation Y for the vertical movement of the current distributor, and substituting the amplitude A in the step 2) and the frequency omega in the step 3) into the curve equation Y;
5) and in the casting process, putting the curve equation Y of the step 4) into a control program for vertically moving the flow distributor.
8. The method for removing cold steel from the surface of a molten pool according to claim 7, wherein: the surface distance H1 is selected to be between 8mm and 12 mm.
9. The method for removing cold steel from the surface of a molten pool according to claim 7, wherein: the amplitude A is selected to be 0.33-0.5H 1.
10. The method for removing cold steel from the surface of a molten pool according to claim 7, wherein: the frequency omega is selected to be between 1 and 2.