CN113926479B - Potassium molybdenum sulfur/nickel nitride composite material and preparation method and application thereof - Google Patents
Potassium molybdenum sulfur/nickel nitride composite material and preparation method and application thereof Download PDFInfo
- Publication number
- CN113926479B CN113926479B CN202010669431.2A CN202010669431A CN113926479B CN 113926479 B CN113926479 B CN 113926479B CN 202010669431 A CN202010669431 A CN 202010669431A CN 113926479 B CN113926479 B CN 113926479B
- Authority
- CN
- China
- Prior art keywords
- potassium
- sulfur
- molybdenum
- nickel nitride
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a potassium-molybdenum-sulfur/nickel nitride composite material, a preparation method and application thereof, wherein the potassium-molybdenum-sulfur/nickel nitride composite material comprises potassium-molybdenum-sulfur KMoS 2 And nickel nitride Ni 3 N, and a part of potassium, molybdenum and sulfur and nickel nitride have sulfur-nickel chemical bonds between the potassium, molybdenum and sulfur.
Description
Technical Field
The invention relates to a catalyst material for oxygen evolution reaction and hydrogen evolution reaction, in particular to a potassium-molybdenum-sulfur/nickel nitride composite material and a preparation method and application thereof, belonging to the field of materials science.
Background
Since the 21 st century, with the development of global economy, the consumption of energy is increasing, the shortage of fossil fuel and environmental pollution are becoming more serious, and the research on new energy materials is becoming more concerned. Therefore, researchers are urged to urgently need to find a renewable energy source which is rich, durable, zero-emission and eco-friendly as an alternative energy source, so that the dependence on fossil fuels is greatly reduced. Full water splitting is an environment-friendly energy conversion technology due to high energy conversion efficiency and environmentHas small pollution and wide application prospect and is widely concerned. The total decomposition water is divided into two half-reactions, one is the Hydrogen Evolution Reaction (HER) and one is the Oxygen Evolution Reaction (OER), the main purpose of which is to produce pure hydrogen (H) 2 ) And oxygen (O) 2 ) In practice, full hydrolysis requires an effective catalyst to promote both reactions. Currently, platinum (Pt) -based catalysts are the most effective catalysts for HER, while iridium (Ir) and ruthenium (Ru) -based catalysts are highly effective catalysts for OER. However, noble metals such as Pt, Ir and Ru are expensive, scarce in reserves and poor in durability, which hinders further applications. In recent years, researchers have prepared a number of low cost HER electrocatalysts that are highly effective in accelerating the HER reaction. However, OER is a very demanding step involving a four-electron reaction and the formation of an oxygen-oxygen bond, and therefore the reaction kinetics of OER is inherently slower than HER. Therefore, efficient non-noble metal electrocatalysts are needed to be researched to reduce the OER over-potential (eta) so as to improve the energy conversion efficiency of the fully hydrolyzed water. Currently conventional catalyst RuO 2 And IrO 2 Commonly used for OER electrocatalysis, but its high price hinders its further applications due to poor stability and its presence of the noble metals Ru and Ir. Therefore, non-noble metal materials are better substitutes.
Potassium molybdenum sulfide (KMoS) 2 ) Has higher electron transfer rate and arouses great interest. However, KMoS 2 The low catalytic activity hinders the popularization of the catalyst in practical application. In recent years, nickel nitride (Ni) has been a representative transition metal nitride 3 N) not only has a stable structure, but also has good bonding strength with hydroxyl free radicals (OH) on the surface, and is a potential catalyst for oxygen evolution reaction and hydrogen evolution reaction. Therefore, a single material has the disadvantages of low electron transfer rate, insufficient active sites, unstable material or insufficient hydroxyl groups, and the like, and the catalytic performance of the material is limited.
Disclosure of Invention
The invention provides a potassium-molybdenum-sulfur/nickel nitride composite material and a preparation method and application thereof, aiming at solving the technical problems of low catalytic activity and high price of catalysts for oxygen evolution reaction and hydrogen evolution reaction in the prior art.
In one aspect, the present invention provides a potassium molybdenum sulfur/nickel nitride composite comprising a potassium molybdenum sulfur KMoS 2 And nickel nitride Ni 3 N, and a sulfur-nickel chemical bond is formed between part of the potassium-molybdenum-sulfur and the nickel nitride.
In the disclosure, the potassium-molybdenum-sulfur/nickel nitride composite material combines the high conductivity of potassium-molybdenum-sulfur and the stability of nickel nitride, and sulfur-nickel chemical bonds are formed between S in part of potassium-molybdenum-sulfur and Ni in nickel nitride, so as to form a potassium-molybdenum-sulfur/nickel nitride heterojunction, which can further regulate and control an electronic structure, improve the stability of the electronic structure, and further improve the performance of an electrocatalyst.
Preferably, the potassium molybdenum sulfur/nickel nitride composite material has a laminated structure, wherein nickel nitride is compounded in laminated potassium molybdenum sulfur KMoS 2 In addition, the method is favorable for forming sulfur-nickel chemical bonds, accelerates the electron transfer rate and improves the oxygen evolution reaction and hydrogen evolution reaction performances.
Preferably, the mass ratio of the potassium, molybdenum and sulfur to the nickel nitride material is 1:0.5 to 2.5.
On the other hand, the invention also provides a preparation method of the potassium-molybdenum-sulfur/nickel nitride composite material, which comprises the steps of dispersing potassium-molybdenum-sulfur and nickel nitride in a reaction kettle filled with deionized water or alkaline solution, and carrying out hydrothermal reaction at 60-170 ℃ to obtain the potassium-molybdenum-sulfur/nickel nitride composite material.
In the invention, potassium-molybdenum-sulfur and nickel nitride are placed in a hydrothermal kettle (or called reaction kettle) filled with deionized water or alkaline solution, S exposed in the potassium-molybdenum-sulfur and Ni exposed in the nickel nitride form bonds at high temperature/high pressure of the reaction kettle in the hydrothermal reaction process at 60-170 ℃, and finally the potassium-molybdenum-sulfur/nickel nitride composite material with sulfur-nickel bonds is obtained. Preferably, the mode of dispersion is ultrasonic treatment; more preferably, the power of ultrasonic treatment is 100-150W, and the time is 10-30 minutes. More preferably, the filling ratio of the reaction kettle can be 50-70 vol%.
Preferably, the particle size of the potassium molybdenum sulfur is 500 nm-5 μm; the particle size of the nickel nitride is 50 nm-0.5 mu m.
Preferably, the mass ratio of the potassium, molybdenum and sulfur to the nickel nitride is 1: 0.5-2.5, and the optimal ratio is 1: 2.
Preferably, the alkaline solution is at least one selected from a sodium hydroxide solution, a potassium hydroxide solution and ammonia water, and preferably has a pH of 8-12.
Preferably, the hydrothermal reaction time is 12-24 hours.
In another aspect, the invention also provides an application of the potassium-molybdenum-sulfur/nickel nitride composite material in oxygen evolution reaction and hydrogen evolution reaction.
Compared with the prior art, the invention has the following beneficial effects:
the invention adopts a hydrothermal method under alkaline conditions for the first time, so that the potassium-molybdenum-sulfur material and the nickel nitride material are subjected to heat treatment at 60-170 ℃ to form the potassium-molybdenum-sulfur/nickel nitride composite material, and the potassium-molybdenum-sulfur/nickel nitride composite material has good electrocatalytic activity in alkaline oxygen evolution reaction. The invention effectively improves the electrochemical activity and stability of the catalyst in the alkaline oxygen evolution reaction, has simple and clear preparation process, is suitable for large-scale production and has certain use value.
Drawings
FIG. 1 shows X-ray diffraction patterns (XRD) of a synthetic K-Mo-S material, a nickel nitride material and a synthetic K-Mo-S/Ni nitride composite material synthesized by hydrothermal method in example 1;
FIG. 2 shows X-ray photoelectron spectroscopy (XPS) of a potassium-molybdenum-sulfur material, a nickel nitride material synthesized according to the present invention, and a potassium-molybdenum-sulfur/nickel nitride composite synthesized according to example 1 by a hydrothermal method;
FIG. 3 shows the S2 p peaks of X-ray photoelectron spectroscopy (XPS) of the synthesized K-Mo-S material of the present invention and the synthesized K-Mo-S/Ni nitride composite of example 1 by hydrothermal method;
FIG. 4 shows a Scanning Electron Micrograph (SEM) of a potassium molybdenum sulfide/nickel nitride composite synthesized by hydrothermal method in example 1;
FIG. 5 shows a Transmission Electron Micrograph (TEM) of a potassium molybdenum sulfide/nickel nitride composite synthesized by a hydrothermal method according to example 1;
FIG. 6 shows an energy dispersive x-ray spectroscopy mapping (EDS-mapping) of a potassium molybdenum sulfur/nickel nitride composite synthesized in example 1 using a hydrothermal method;
FIG. 7 shows the LSV and overpotential plots for OER testing in 1M KOH for the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method in examples 1-5;
FIG. 8 shows the LSV and overpotential plots for HER tests in 1M KOH for the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method in examples 1-5;
FIG. 9 shows Tafel slope plots of the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method in examples 1-5 in 1M KOH;
FIG. 10 shows EIS impedance plots of the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method in examples 1-5 in 1M KOH;
FIG. 11 shows the LSV and overpotential plots for OER testing in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1, 2, respectively;
FIG. 12 shows the LSV and overpotential plots for the HER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1, 2, respectively;
FIG. 13 shows Tafel slope plots of the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1, 2, respectively, in 1M KOH;
FIG. 14 shows EIS impedance plots of potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1, 2, respectively, in 1M KOH;
FIG. 15 shows the LSV and overpotential plots for OER testing in 1M KOH for the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal methods at different temperatures for examples 1, 8, and 9;
FIG. 16 shows the LSV and overpotential plots for HER tests in 1M KOH for potassium molybdenum sulfide/nickel nitride composites synthesized by different temperature hydrothermal methods for examples 1, 8 and 9;
FIG. 17 shows Tafel slope plots of the potassium molybdenum sulfide/nickel nitride composites of examples 1, 8, 9 synthesized using different temperature hydrothermal methods in 1M KOH;
FIG. 18 shows EIS impedance plots of potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method at different temperatures in examples 1, 8 and 9 in 1M KOH.
Detailed Description
The present invention is further illustrated by the following examples, which are to be understood as merely illustrative and not restrictive.
In this disclosure, the potassium molybdenum sulfur/nickel nitride composite is: the catalyst is prepared by taking potassium molybdenum sulfide and nickel nitride as raw materials, placing the raw materials in deionized water or an alkaline strip solution, and adopting a hydrothermal method.
The potassium molybdenum sulfur/nickel nitride composite material provided by the present invention is exemplarily illustrated below.
The preparation of the potassium molybdenum sulfide comprises but is not limited to synthesis through high-temperature solid-phase reaction. Mixing the potassium source, the molybdenum source and the sulfur source material according to the molar ratio of 1:1:1, and fully grinding in an agate mortar for 0.5-2 h. Then pressing the mixed powder into small balls, sealing the small balls in a quartz tube in vacuum, annealing the small balls in a muffle furnace for 12 to 36 hours at the heating rate of 5 to 10 ℃ per minute -1 . And then, after the sample is naturally cooled to room temperature and taken out, dispersing the sample in deionized water, and performing vacuum drying at room temperature to obtain the potassium-molybdenum-sulfur. Wherein the potassium source, the molybdenum source and the sulfur source are respectively K 2 S 2 Powder, Mo powder, MoS 2 And (3) powder. The potassium-molybdenum-sulfur material is obtained based on solid-phase high-temperature calcination, and the annealing temperature is 600-1000 ℃. The grain size of the obtained potassium, molybdenum and sulfur can be 500 nm-5 mu m.
The preparation of the nickel nitride comprises, but is not limited to, the preparation by first hydrothermal and then calcining in a tube furnace. Adding a nickel source and a nitrogen source into deionized water, and then carrying out hydrothermal heating in a hydrothermal kettle for 4-12 h. And after the sample is naturally cooled to room temperature, taking out, carrying out suction filtration, and carrying out vacuum drying at 60 ℃. And then putting the sample into a muffle furnace, and calcining for 2-6h under an air atmosphere. Then taking out the sample after the sample is naturally cooled to room temperature, and putting the sample in a tube furnace NH 3 Calcining for 1h in the atmosphere, with the heating rate of 5-10 ℃ min -1 . And finally, naturally cooling the product to room temperature and collecting the product to obtain the nickel nitride. Wherein, the nitrogen source and the nickel source material can be nickel chloride hexahydrate and ammonium fluoride or/and urea respectively. Preparing nickel nitride, namely preparing a precursor on the basis of first hydrothermal preparation, wherein the hydrothermal temperature can be 80-160 ℃. Calcining the obtained nickel nitride precursor in a muffle furnace in air atmosphere at the calcining temperature of 200-3 DEG CAt 00 ℃. Or putting the nickel nitride precursor into a tube furnace NH 3 Calcining at the temperature of 250-450 ℃ in the atmosphere. The particle size of the obtained nickel nitride is 50 nm-0.5 μm.
The potassium molybdenum sulfur material and the nickel nitride material are prepared by a hydrothermal method under the deionized water or alkaline condition, and then are washed, filtered, collected and dried to obtain the potassium molybdenum sulfur/nickel nitride composite material. The raw materials are mixed and dispersed by ultrasonic treatment (the power can be 100-150W, and the time can be 10-30 minutes). Mixed into a mixed solution and then placed in a reaction kettle, and the filling ratio of the reaction kettle is preferably controlled to be 50-70 vol%. Wherein the mass ratio of the potassium molybdenum sulfide material to the nickel nitride material can be 1: 0.5-2.5. For example, the potassium-molybdenum-sulfur/nickel nitride composite material is obtained by respectively centrifugally washing with ethanol and deionized water for 2-6 times, carrying out suction filtration and collection, and drying the product. The alkaline condition is sodium hydroxide, potassium hydroxide or ammonia water solution. The preferred hydrothermal temperature is 60-170 deg.C, preferably 80-160 deg.C, more preferably 100-140 deg.C, and most preferably 120 deg.C. If the hydrothermal reaction temperature is too high, a large amount of potassium molybdenum sulfur/nickel nitride composite material is agglomerated, so that the impedance is increased, and the catalytic performance is reduced. If the hydrothermal reaction temperature is too low, the potassium molybdenum sulfur material and the nickel nitride material do not react or react incompletely, no or only a small amount of sulfur-nickel bonds are formed, and the reduction of impedance cannot be realized, so that the catalytic activity is caused. If the addition amount of potassium, molybdenum and sulfur is too much, the active sites are insufficient, the bonding strength of the active sites and the coded hydroxyl radicals is weak, and the catalytic performance is reduced; if the amount of nickel nitride added is too large, the electron transfer rate is reduced, resulting in a decrease in catalytic performance. The hydrothermal treatment time may be 12 to 24 hours. For example, the drying may be one of a freeze drying method, a vacuum drying method, and an air drying method.
In the invention, sulfur-nickel bonds are formed between part of potassium-molybdenum-sulfur and nickel nitride in the potassium-molybdenum-sulfur/nickel nitride composite material to form a heterojunction, so that the oxygen evolution reaction and the hydrogen evolution reaction can be improved.
The present invention will be described in detail by way of examples. It is also to be understood that the following examples are illustrative of the present invention and are not to be construed as limiting the scope of the invention, and that certain insubstantial modifications and adaptations of the invention by those skilled in the art may be made in light of the above teachings. The specific process parameters and the like of the following examples are also only one example of suitable ranges, i.e., those skilled in the art can select the appropriate ranges through the description herein, and are not limited to the specific values exemplified below.
Examples of the preparation of potassium molybdenum sulfide and nickel nitride
(1) Preparation of potassium molybdenum sulfide: will K 2 S 2 Powder, Mo powder, MoS 2 The powders are mixed according to the molar ratio of 1:1:1 and fully ground in an agate mortar for 0.5 to 2 hours. Then pressing the mixed powder into small balls, sealing the small balls in a quartz tube in vacuum, annealing the small balls in a muffle furnace at the temperature of 600 ℃ and 1000 ℃ for 12 to 36 hours at the heating rate of 5 to 10 ℃ for min -1 . And then, after the sample is naturally cooled to room temperature and taken out, dispersing the sample in deionized water, and performing vacuum drying at room temperature to obtain the potassium-molybdenum-sulfur.
Preparation of nickel nitride: 1.118g of nickel chloride hexahydrate, 0.37g of ammonium fluoride and 1.5g of urea are added into 60mL of deionized water, and then are heated in a hydrothermal kettle at 80-160 ℃ for 4-12h in a hydrothermal mode. And after the sample is naturally cooled to room temperature, taking out, carrying out suction filtration, and carrying out vacuum drying at 60 ℃. And then the sample is put into a muffle furnace to be calcined for 2-6h at the temperature of 200-300 ℃ under the air atmosphere. Then taking out the sample after the sample is naturally cooled to room temperature, and putting the sample in a tube furnace NH 3 Calcining for 1h at the temperature of 250-450 ℃ under the atmosphere, and the heating rate is 5-10 ℃ min -1 . And finally, naturally cooling the product to room temperature and collecting the product to obtain the nickel nitride.
Example 1
(1) To a solution of 50mL of ammonia at pH 11(± 0.5), 50mg of potassium molybdenum sulfide and 100mg of nickel nitride were added;
(2) adding the mixed solution of potassium, molybdenum, sulfur and nickel nitride into a lining (the filling ratio is 60%) of a reaction kettle, and ultrasonically stirring for 30min at 120W until the mixed solution is uniformly dispersed;
(3) after ultrasonic stirring, carrying out hydrothermal heating on the uniformly mixed potassium-molybdenum-sulfur and nickel nitride solution at 120 ℃ for 16 hours by a hydrothermal method, taking out the solution, and collecting the solution after the sample is naturally cooled to room temperature;
(4) and carrying out suction filtration and washing on the collected solution. In the washing process, the black sample is washed with ethanol for three times, then washed with deionized water for three times, and then placed in an oven at 60 ℃ for vacuum drying for 12 hours. And finally, collecting the potassium-molybdenum-sulfur/nickel nitride composite material.
Example 2
(1) Adding 50mg of potassium molybdenum sulfur and 50mg of nickel nitride into 50mL of ammonia water solution with the pH value of 11 (+ -0.5);
(2) adding the mixed solution of potassium, molybdenum, sulfur and nickel nitride into a lining (the filling ratio is 60%) of a reaction kettle, and ultrasonically stirring for 30min at 120W until the mixed solution is uniformly dispersed;
(3) after ultrasonic stirring, carrying out hydrothermal heating on the uniformly mixed potassium-molybdenum-sulfur and nickel nitride solution at 120 ℃ for 16 hours by a hydrothermal method, taking out the solution, and collecting the solution after the sample is naturally cooled to room temperature;
(4) and carrying out suction filtration and washing on the collected solution. In the washing process, the black sample is washed with ethanol for three times, then washed with deionized water for three times, and then placed in an oven at 60 ℃ for vacuum drying for 12 hours. And finally, collecting the potassium-molybdenum-sulfur/nickel nitride composite material.
Example 3
(1) To a solution of 50mL of ammonia at pH 11(± 0.5) was added 100mg of potassium molybdenum sulfide and 50mg of nickel nitride;
(2) adding the mixed solution of potassium, molybdenum, sulfur and nickel nitride into a lining (the filling ratio is 60%) of a reaction kettle, and ultrasonically stirring for 30min at 120W until the mixed solution is uniformly dispersed;
(3) after ultrasonic stirring, carrying out hydrothermal heating on the uniformly mixed potassium-molybdenum-sulfur and nickel nitride solution at 120 ℃ for 16 hours by a hydrothermal method, taking out the solution, and collecting the solution after the sample is naturally cooled to room temperature;
(4) and carrying out suction filtration and washing on the collected solution. In the washing process, the black sample is washed with ethanol for three times, then washed with deionized water for three times, and then placed in an oven at 60 ℃ for vacuum drying for 12 hours. And finally, collecting the potassium-molybdenum-sulfur/nickel nitride composite material.
Example 4
(1) To a solution of 50mL of ammonia at pH 11(± 0.5) was added 50mg of potassium molybdenum sulfide and 75mg of nickel nitride;
(2) adding the mixed solution of potassium, molybdenum, sulfur and nickel nitride into a lining (the filling ratio is 60%) of a reaction kettle, and ultrasonically stirring for 30min at 120W until the mixed solution is uniformly dispersed;
(3) after ultrasonic stirring, carrying out hydrothermal heating on the uniformly mixed potassium-molybdenum-sulfur and nickel nitride solution at 120 ℃ for 16 hours by a hydrothermal method, taking out the solution, and collecting the solution after the sample is naturally cooled to room temperature;
(4) and carrying out suction filtration and washing on the collected solution. In the washing process, the black sample is washed with ethanol for three times, then washed with deionized water for three times, and then placed in an oven at 60 ℃ for vacuum drying for 12 hours. And finally, collecting the potassium-molybdenum-sulfur/nickel nitride composite material.
Example 5
(1) To a solution of 50mL of ammonia at pH 11(± 0.5), 50mg of potassium molybdenum sulfide and 125mg of nickel nitride were added;
(2) adding the mixed solution of potassium, molybdenum, sulfur and nickel nitride into a lining (the filling ratio is 60%) of a reaction kettle, and ultrasonically stirring for 30min at 120W until the mixed solution is uniformly dispersed;
(3) after ultrasonic stirring, carrying out hydrothermal heating on the uniformly mixed potassium-molybdenum-sulfur and nickel nitride solution at 120 ℃ for 16 hours by a hydrothermal method, taking out the solution, and collecting the solution after the sample is naturally cooled to room temperature;
(4) and carrying out suction filtration and washing on the collected solution. In the washing process, the black sample is washed with ethanol for three times, then washed with deionized water for three times, and then placed in an oven at 60 ℃ for vacuum drying for 12 hours. And finally, collecting the potassium-molybdenum-sulfur/nickel nitride composite material.
Example 6
See example 1 for the preparation of the potassium molybdenum sulfide/nickel nitride composite material in this example 6, except that: the alkaline solution was replaced with deionized water.
Example 7
See example 1 for the preparation of the potassium molybdenum sulfide/nickel nitride composite material in this example 7, except that: the pH of the alkaline solution was 9.
Example 8
See example 1 for the preparation of the potassium molybdenum sulfide/nickel nitride composite material in this example 8, except that: the hydrothermal temperature is 160 ℃ and the time is 12 h.
Example 9
The preparation process of the potassium molybdenum sulfur/nickel nitride composite material in this example 11 is as shown in example 1, except that: the hydrothermal temperature is 80 ℃ and the hydrothermal time is 12 h.
The examples are given solely for the purpose of further illustrating the invention and are not to be construed as limiting thereof. For example, the alkaline solution can be at least one of sodium hydroxide, potassium hydroxide or ammonia water solution, the temperature of the hydrothermal treatment is distributed between 80 ℃ and 160 ℃, and the time of the hydrothermal treatment can be adjusted between 8 hours and 24 hours, so that the potassium-molybdenum-sulfur/nickel nitride composite material can be prepared.
Comparative example 1
For the preparation of the potassium molybdenum sulfur/nickel nitride composite of this comparative example 1, see example 1, except that: standing at room temperature 25 deg.C for 12 h.
Comparative example 2
For the preparation of the potassium molybdenum sulfur/nickel nitride composite of this comparative example 2, see example 1, except that: the mixture is heated at 180 ℃ for 12 h.
FIG. 1 shows X-ray diffraction spectra (XRD) of a potassium-molybdenum-sulfur material, a nickel nitride material and a potassium-molybdenum-sulfur/nickel nitride composite material synthesized by a hydrothermal method in example 1. from FIG. 1, it can be observed that characteristic peaks of the potassium-molybdenum-sulfur material are consistent with XRD standard cards JCPDS No.18-1064 of potassium-molybdenum-sulfur, and characteristic peaks of the nickel nitride material are consistent with XRD standard cards JCPDS No.10-0280 of nickel nitride, which confirms that the potassium-molybdenum-sulfur and nickel nitride materials are successfully prepared;
FIG. 2 shows X-ray photoelectron spectroscopy (XPS) of the synthesized K-Mo-S material, Ni-N material and the synthesized K-Mo-S/Ni-N composite material of example 1 by hydrothermal method, and it can be seen from FIG. 2 that characteristic peaks of O, K, Mo, S, Ni and N elements all exist, thus proving successful synthesis of the K-Mo-S/Ni-N composite material;
FIG. 3 shows the S2 p peaks of X-ray photoelectron spectroscopy (XPS) of the potassium-molybdenum-sulfur material synthesized by the present invention and the potassium-molybdenum-sulfur/nickel nitride composite synthesized by hydrothermal method of example 1. from FIG. 3, it can be seen that sulfur-nickel chemical bonds exist in the potassium-molybdenum-sulfur/nickel nitride composite, thus demonstrating that sulfur-nickel chemical bonds are formed between part of potassium-molybdenum-sulfur and nickel nitride;
FIG. 4 shows a Scanning Electron Microscope (SEM) of the potassium molybdenum sulfide/nickel nitride composite material synthesized by hydrothermal method in example 1, and it can be seen from FIG. 4 that the morphology of the potassium molybdenum sulfide/nickel nitride composite material is mainly a layered material;
FIG. 5 shows a Transmission Electron Micrograph (TEM) of a potassium molybdenum sulfur/nickel nitride composite synthesized in example 1 by a hydrothermal method, from a typical TEM image in FIG. 5a, a potassium molybdenum sulfur/nickel nitride composite is seen, which is composed of layered potassium molybdenum sulfur and nickel nitride having a smooth surface, and an HRTEM image (FIG. 5b) clearly shows lattice fringes with a interplanar spacing of 0.203nm and Ni 3 The N (111) planes correspond;
FIG. 6 shows the energy dispersive x-ray spectroscopy mapping (EDS-mapping) of the potassium molybdenum sulfur/nickel nitride composite synthesized in example 1 by a hydrothermal method, from which it can be seen that Mo, S, Ni and N elements are uniformly distributed in the potassium molybdenum sulfur/nickel nitride composite;
FIG. 7 shows the LSV and overpotential curves of the OER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method in examples 1-5. As can be seen from the LSV and overpotential curves, the overpotential of the catalyst is the lowest for the example 1 sample and the overpotential curve is 10cm at the anode current density in the case of the potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method in examples 1-5 -2 The overpotentials of the catalysts of the samples of examples 2 to 5 were 233mV, and the overpotentials of the catalysts of the samples of examples 2 to 5 were 264, 293, 262 and 251mV, respectively, thereby demonstrating that the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 has higher catalytic performance for OER;
FIG. 8 shows the LSV and overpotential curves of HER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method in examples 1-5, and it can be seen from the LSV and overpotential curves of HER test in hydrothermal method in examples 1-5Of the samples of material, the catalyst of the sample of example 1 had the lowest overpotential and had a current density at the anode of-10 cm -2 The overpotentials were 89mV versus 148, 208, 158, and 119mV for the catalysts of the samples of examples 2-5, respectively, demonstrating the higher catalytic performance of the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 for HER;
FIG. 9 shows the Tafel slope plots of the potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method in examples 1-5 in 1M KOH, and it can be seen that the Tafel slope of the catalyst in example 1 is 66mV dec -1 Whereas the overpotentials of the catalysts of the samples of examples 2-5 were 95, 84, 83 and 88mV dec, respectively -1 Thus, the electrocatalytic activity of the potassium molybdenum sulfur/nickel nitride composite catalyst in example 1 was again demonstrated to be higher than that of the other samples;
FIG. 10 shows EIS impedance plots of the potassium molybdenum sulfur/nickel nitride composite materials synthesized by hydrothermal method in examples 1-5 in 1M KOH, and it can be seen from the EIS impedance of the catalyst sample in example 1 is 7.925 Ω, while the EIS impedance of the catalyst samples in examples 2-5 are 47.15, 53.51, 19.36 and 18.99 Ω, respectively, thereby proving that the potassium molybdenum sulfur/nickel nitride composite material catalyst in example 1 is more beneficial to electron transmission and improving OER catalytic activity.
FIG. 11 shows the LSV and overpotential graphs of OER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1-2, respectively, from which it can be seen that, in the samples of the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1-2, respectively, the overpotential of the catalyst of example 1 is the lowest and the current density at the anode is 10cm -2 The overpotentials of the catalysts of examples 6 and 7 and comparative examples 1 to 2 were 233mV, and 288, 281, 336 and 308mV, respectively, thereby demonstrating that the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 has higher catalytic performance for OER;
FIG. 12 shows the LSV and overpotential patterns of HER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1-2, respectively, from which it can be seen that the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1-21-2, respectivelyOf the samples of the K-Mo-S/Ni-nitride composite, the catalyst of the sample of example 1 had the lowest overpotential and the current density at the anode was-10 cm -2 The overpotentials of the sample catalysts of examples 6, 7 and comparative examples 1 to 21 to 2 were 89mV, while the overpotentials of the sample catalysts of examples 6, 7 and comparative examples 1 to 21 to 2 were 176, 163, 231 and 210mV, respectively, thereby demonstrating the higher catalytic performance of the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 for HER;
FIG. 13 shows the Tafel slopes of the potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1-2, respectively, in 1M KOH, from which it can be seen that the Tafel slope of the catalyst of example 1 is 66mV dec as a minimum -1 Whereas the overpotentials of the catalysts of the samples of examples 6, 7 and comparative examples 1-2 were 84, 79, 100 and 119mV dec, respectively -1 Thus, the electrocatalytic activity of the potassium molybdenum sulfur/nickel nitride composite catalyst in example 1 was again demonstrated to be higher than that of the other samples;
fig. 14 shows EIS impedance plots of potassium molybdenum sulfur/nickel nitride composites synthesized in examples 1, 6, 7 and comparative examples 1 to 2, respectively, in 1M KOH, and it can be seen from the graphs that the EIS impedance of the sample catalyst of example 1 is 7.925 Ω, and the impedances of the sample catalysts of examples 6, 7 and comparative examples 1 to 2 are 45.74, 31.36, 76.93 and 59.05 Ω, respectively, thus proving that the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 is more advantageous for electron transport and for improving the OER catalytic activity.
FIG. 15 shows the LSV and overpotential curves of OER test in 1M KOH for the potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method at different temperatures in examples 1, 8 and 9. it can be seen from these plots that, in the samples of the potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method in examples 1, 8 and 9, the overpotential of the catalyst in the sample of example 1 is the lowest, and the current density at the anode is 10cm -2 The overpotential of the catalyst is 233mV, while the overpotentials of the catalysts of the samples in examples 8 and 9 are 306 mV and 266mV, respectively, so that the potassium-molybdenum-sulfur/nickel nitride composite catalyst in example 1 has higher catalytic performance for OER;
FIG. 16 shows the LSV and overpotential for HER test of potassium molybdenum sulfide/nickel nitride composites synthesized by hydrothermal method at different temperatures in 1M KOH according to examples 1, 8 and 9The bitmap shows that in the samples of the potassium molybdenum sulfide/nickel nitride composite materials synthesized by the hydrothermal method in the examples 1, 8 and 9, the overpotential of the catalyst of the sample of the example 1 is the lowest, and the current density at the anode is-10 cm -2 The overpotentials of the catalysts of examples 8 and 9 were 187 and 181mV, respectively, thereby demonstrating that the potassium molybdenum sulfur/nickel nitride composite catalyst of example 1 has higher catalytic performance for HER;
FIG. 17 shows the Tafel slopes of the K-Mo-S/Ni-nitride composites synthesized by hydrothermal method at different temperatures in examples 1, 8 and 9 in 1M KOH, and it can be seen from the graphs that the Tafel slope of the catalyst sample in example 1 is 66mV dec -1 Whereas the overpotentials of the catalysts of the samples of examples 8 and 9 were 147 mV dec and 149mV dec, respectively -1 Thus, the electrocatalytic activity of the potassium molybdenum sulfur/nickel nitride composite catalyst in example 1 was again demonstrated to be higher than that of the other samples;
FIG. 18 shows EIS impedance plots of potassium molybdenum sulfur/nickel nitride composites synthesized by hydrothermal method at different temperatures in examples 1, 8 and 9 in 1M KOH, and it can be seen from the EIS impedance of the catalyst sample in example 1 is 7.925 Ω, while the impedance of the catalyst samples in examples 8 and 9 is 47.3 Ω and 43.1 Ω, respectively, thereby proving that the catalyst potassium molybdenum sulfur/nickel nitride composite in example 1 is more beneficial to electron transmission and improving OER catalytic activity.
Table 1 shows the preparation process and performance parameters of the potassium molybdenum sulfide/nickel nitride composite material prepared according to the present invention:
industrial applicability
The potassium molybdenum sulfur/nickel nitride composite material prepared by the method greatly reduces the overpotentials of HER and OER, and both the Tafel slope and EIS impedance are obviously reduced, thereby being beneficial to the electrocatalysis of HER and OER. Therefore, the potassium molybdenum sulfur/nickel nitride composite catalyst effectively improves the electrochemical activity of HER and OER, and the preparation of the material has low requirement on equipment, short preparation period and easy operation of the preparation process, and is suitable for large-scale production.
Claims (8)
1. The potassium-molybdenum-sulfur/nickel nitride composite material is characterized by comprising potassium-molybdenum-sulfur KMoS 2 And nickel nitride Ni 3 N, and a sulfur-nickel chemical bond is formed between part of the potassium-molybdenum-sulfur and the nickel nitride; the mass ratio of the potassium, molybdenum and sulfur to the nickel nitride material is 1:0.5 to 2.5;
the preparation method of the potassium molybdenum sulfur/nickel nitride composite material comprises the following steps: and dispersing potassium molybdenum sulfur and nickel nitride in a reaction kettle filled with deionized water or alkaline solution, and carrying out hydrothermal reaction at the temperature of 60-170 ℃ to prepare the potassium molybdenum sulfur/nickel nitride composite material.
2. The potassium molybdenum sulfur/nickel nitride composite of claim 1, wherein the potassium molybdenum sulfur/nickel nitride composite has a layered structure in which nickel nitride is composited in a layered potassium molybdenum sulfur KMoS 2 The above.
3. The potassium molybdenum sulfur/nickel nitride composite material of claim 1, wherein the particle size of the potassium molybdenum sulfur is 500nm to 5 μm; the particle size of the nickel nitride is 50 nm-0.5 mu m.
4. The potassium molybdenum sulfur/nickel nitride composite material of claim 1, wherein the dispersion is by sonication; the power of ultrasonic treatment is 100-150W, and the time is 10-30 minutes.
5. The potassium molybdenum sulfur/nickel nitride composite of claim 1, wherein the alkaline solution is selected from at least one of a sodium hydroxide solution, a potassium hydroxide solution, and ammonia.
6. The potassium molybdenum sulfur/nickel nitride composite material of claim 5, wherein the pH of the alkaline solution is 8-12.
7. The potassium molybdenum sulfur/nickel nitride composite material according to any one of claims 1 to 6, wherein the hydrothermal reaction time is 8 to 24 hours.
8. Use of a potassium molybdenum sulphur/nickel nitride composite material according to any of claims 1 to 7 in oxygen evolution reactions and hydrogen evolution reactions.