CN113829460A - Wood craft anti-corrosion treatment method - Google Patents
Wood craft anti-corrosion treatment method Download PDFInfo
- Publication number
- CN113829460A CN113829460A CN202111169535.8A CN202111169535A CN113829460A CN 113829460 A CN113829460 A CN 113829460A CN 202111169535 A CN202111169535 A CN 202111169535A CN 113829460 A CN113829460 A CN 113829460A
- Authority
- CN
- China
- Prior art keywords
- wooden
- artware
- wood
- polishing
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a wood craft anticorrosion treatment method, which comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; the invention improves the corrosion resistance of the wooden handicraft, so that the wooden handicraft is more beautiful; the two corrosion prevention modes are comprehensively applied, so that the corrosion prevention capability of the wood craft is greatly improved, and the service life is prolonged; simple steps, low cost and convenient large-scale production.
Description
Technical Field
The invention relates to the technical field of artware, in particular to a wood artware anticorrosion treatment method.
Background
The handicraft combines culture and art, the wooden handicraft is widely applied to multiple fields such as gifts, home decoration, outdoor decoration and the like, and the processing and the manufacturing are very perfect. The wooden crafts can be divided into large furniture such as tables, chairs, beds, cabinets and the like and small appliances such as flowerpot racks, crutches, pen containers, hanging decorations and various wooden appliances for containing and using according to the purposes, and the manufacturing process is not complicated.
The wood is mainly composed of cellulose and hemicellulose, wherein the cellulose plays a skeleton role in the wood cell wall, and the chemical property and the supermolecular structure of the cellulose have important influence on the strength of the wood. Hydroxyl groups in cellulose and water molecules can also form hydrogen bonds, and the hydrogen bonds existing between the hydroxyl groups at different positions directly influence the moisture absorption and desorption processes of the wood. A large number of hydrogen bonds can improve the strength of wood, reduce hygroscopicity, reduce chemical reactivity and the like, and the hygroscopicity of cellulose directly influences the size stability and strength of limiting. After the wood is carbonized, the concentration of hydroxyl groups is reduced, and the chemical structure is changed complexly, so that the moisture absorption of the wood is reduced. The hemicellulose is a substance tightly connected with cell membranes in cell walls, plays a role of bonding, is a matrix substance, has strong hygroscopicity, poor heat resistance and easy hydrolysis, is easy to change under the action of external conditions, is a component with the largest hygroscopicity in wood, is one of factors for causing moisture absorption expansion and deformation cracking of wood, can be destroyed by carbonization, can reduce the hygroscopicity of the wood, reduces the expansion and contraction of the wood, and ensures that the wood has excellent effects of corrosion prevention and biological attack resistance
At present, the wood artware is subjected to an anticorrosion method by adopting a soaking or spraying method, but the method is single, the wood artware is difficult to be thoroughly anticorrosion, the integral attractiveness is influenced once the wood artware is corroded, and the service life of the wood artware is shortened.
Disclosure of Invention
The invention aims to provide a wood craft anticorrosion treatment method to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; wherein:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
Further, the sand paper in the first step is wood sand paper.
And furthermore, the bracket in the second step is a stainless steel bracket, and a rubber pad is arranged on the contact surface of the bracket and the wooden handicraft.
Further, the formula of the preservative in the third step comprises the following components in parts by weight: 30-40 parts of diammonium phosphate, 60-80 parts of amine oxide, 20-30 parts of boric acid, 75-95 parts of ethylene glycol, 2-8 parts of zinc halide and 37-49 parts of imidazoles, and then dissolving the raw materials in 1000 parts of water to prepare the preservative solution.
Further, the strong light in the fourth step is one of sunlight or a strong light.
Compared with the prior art, the invention has the beneficial effects that:
1. the corrosion resistance degree of the wooden handicraft is improved, so that the wooden handicraft is more attractive;
2. the two corrosion prevention modes are comprehensively applied, so that the corrosion prevention capability of the wood craft is greatly improved, and the service life is prolonged;
3. simple steps, low cost and convenient large-scale production.
Detailed Description
The technical solutions in the embodiments of the present invention are clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
a wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; wherein:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
Further, the sand paper in the first step is wood sand paper.
Example two:
a wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; wherein:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
And furthermore, the bracket in the second step is a stainless steel bracket, and a rubber pad is arranged on the contact surface of the bracket and the wooden handicraft.
Example three:
a wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; wherein:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
Further, the formula of the preservative in the third step comprises the following components in parts by weight: 30-40 parts of diammonium phosphate, 60-80 parts of amine oxide, 20-30 parts of boric acid, 75-95 parts of ethylene glycol, 2-8 parts of zinc halide and 37-49 parts of imidazoles, and then dissolving the raw materials in 1000 parts of water to prepare the preservative solution.
Example four:
a wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; wherein:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
Further, the strong light in the fourth step is one of sunlight or a strong light.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (5)
1. A wood craft anticorrosion treatment method comprises the following steps: step one, polishing; step two, placing; step three, soaking; step four, drying; step five, painting; step six, polishing; step seven, storing; the method is characterized in that:
in the first step, the artware to be preserved is polished, firstly, 600# abrasive paper is used for rough polishing, then 1000# abrasive paper is used for fine polishing, and finally 1200# abrasive paper is used for carefully polishing dead corners until the surfaces of the artware are smooth;
in the second step, the wooden artwork polished in the first step is placed on a support and is firmly bound;
in the third step, the wood artware and the bracket which are placed in the second step are soaked in a preservative solution for 3-4 days;
in the fourth step, the wooden artware soaked in the third step is fished out and is placed in a strong light environment for solarization until the wooden artware is dried;
in the fifth step, the wooden handicraft dried in the fourth step is painted, and the surface of the wooden handicraft is evenly sprayed with anticorrosive paint;
in the sixth step, polishing the wooden artwork after the paint spraying in the fifth step to make the surface smooth and glossy;
and step seven, placing the polished wood artware in the step six into a dry warehouse for storage.
2. The wood craft anticorrosion treatment method according to claim 1, wherein: the sand paper in the first step is wood sand paper.
3. The wood craft anticorrosion treatment method according to claim 1, wherein: and the bracket in the second step is a stainless steel bracket, and a rubber pad is arranged on the contact surface of the bracket and the wooden handicraft.
4. The wood craft anticorrosion treatment method according to claim 1, wherein: the formula of the preservative in the third step comprises the following components in parts by weight: 30-40 parts of diammonium phosphate, 60-80 parts of amine oxide, 20-30 parts of boric acid, 75-95 parts of ethylene glycol, 2-8 parts of zinc halide and 37-49 parts of imidazoles, and then dissolving the raw materials in 1000 parts of water to prepare the preservative solution.
5. The wood craft anticorrosion treatment method according to claim 1, wherein: the strong light in the fourth step is sunlight or a strong light.