CN113802394A - 一种纺织品 - Google Patents
一种纺织品 Download PDFInfo
- Publication number
- CN113802394A CN113802394A CN202010533693.6A CN202010533693A CN113802394A CN 113802394 A CN113802394 A CN 113802394A CN 202010533693 A CN202010533693 A CN 202010533693A CN 113802394 A CN113802394 A CN 113802394A
- Authority
- CN
- China
- Prior art keywords
- textile
- polyamide fiber
- polyamide
- content
- dye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纺织品。该纺织品由100%聚酰胺纤维形成，聚酰胺纤维上附着有酸性染料；且该纺织品经还原清洗处理后残液的吸光度峰值大于0.02且小于2.00。本发明的纺织品具有优异的发色效果。
Description
技术领域
本发明属于纺织品领域，具体涉及一种发色性优异的聚酰胺纤维纺织品。
背景技术
聚酰胺纤维具有拉伸强度高、轻质、手感光滑、穿着舒适等优点，在民用纺织品及高级奢侈品领域均具有良好的应用前景。为进一步提高聚酰胺纤维纺织品的应用性，在聚酰胺纤维的纺丝过程中一般都会添加一些无机粒子，使其具有抗紫外线、遮热等性能，增加纺织品的功能性。但是，无机粒子添加后，因其所具备的较高的反射率，提高了纺织品表面对光的反射率，使得进入人眼的光线变多，纺织品颜色相对变浅，无法满足深色服装的需求。
为了提高聚酰胺纤维纺织品的深染效果，如专利文献CN106012597A中公开了一种仿色织锦纶面料的染色方法，纬纱采用高氨基锦纶，氨基含量达90wt%，利用高氨基锦纶中含有更多的带正电荷的氨基与酸性染料中的阴离子发生反应，提高深染效果，但是此种方法不适用于普通聚酰胺纤维纺织品，应用十分受限。
又如，在专利文献CN110791979A中公开了一种提升高强尼龙6的染色方法，将织物在染色加工前采用氢氧化钠和酸性渗透剂进行预处理，以提高上染率，但是此种方法增加了加工工程，增加了成本，同时可能会影响聚酰胺纤维纺织品的物性。
再如，日本专利文献特开2007-321247中公开了一种聚酰胺纤维构造物，利用酸性染料及金属复合盐染料进行染色，并将羧基的脂肪族聚合物作为染料固着剂，所得纤维构造物在维持鲜明色相、良好耐光坚牢度的基础上，湿润坚牢度也得到提高，但是同样没有解决深染的问题。
发明内容
本发明的目的在于提供一种加工工艺简单，成本低廉，即便是普通聚酰胺纤维作为原料也能具有优异发色性能的纺织品。
本发明的技术解决方案是：
本发明的纺织品由100%聚酰胺纤维形成，聚酰胺纤维上附着有酸性染料；且该纺织品还原清洗处理后残液的吸光度峰值大于0.02且小于2.00。
本发明的纺织品具有优异的发色性，浓染效果好，适用范围广。
具体实施方式
本发明的纺织品由100%聚酰胺纤维形成，聚酰胺纤维上附着有酸性染料；且该纺织品还原清洗处理后残液的吸光度峰值大于0.02且小于2.00。吸光度峰值在此范围时，酸性染料不仅与聚酰胺纤维的末端氨基发生反应，还与聚酰胺纤维的酰胺键发生反应，聚酰胺纤维上的酸性染料附着量高，具有深染的效果，发色性优越。本发明的聚酰胺纤维为非改性的普通聚酰胺纤维。
这里的聚酰胺纤维上附着有酸性染料是指单纤维表面上及单纤维内部均存在有酸性染料，其中，酸性染料可以根据EN14582：2016标准中规定的离子色谱IC测定纺织品上是否含有硫元素来确定。如果含有硫元素则认定聚酰胺纤维上附着有酸性染料。
这里的还原清洗是指在氢氧化钠和保险粉（连二亚硫酸钠）的水溶液中，60℃条件下处理20分钟。
一般来说，聚酰胺纤维的末端氨基染座含量为30～80mmol/kg。本发明中，优选末端氨基含量为30～50mmol/kg的聚酰胺纤维，当末端氨基含量高于50mmol/kg时，与之发生离子键结合的酸性染料使用量较多，剩余可以与酰胺键产生的第二染座结合的染料量减少，纺织品颜色变深的效果有降低的趋势。
本发明中，优选聚酰胺纤维中无机粒子的含量为0.5～5.0wt%。前述无机粒子的种类没有特别限定，可以是如二氧化钛（TiO2）、氧化锌、三氧化二铝、硫化锌、氧化锆等中的一种或几种，可根据需要进行选择。无机粒子含量如果低于0.5wt%的话，纺织品的抗紫外线、遮热等功能性有下降的趋势，而含量如果大于5.0wt%的话，成本提高，而且对抗紫外线、遮热等功能性并没有提高。
本发明中，优选总纤度为10～40旦尼尔（简称D）的聚酰胺纤维，由这样的聚酰胺纤维编织得到的纺织品具有轻薄、轻量的优点，比较适合用于制作夏季服装及冬季轻量羽绒服装等。
一般地，聚酰胺纤维采用酸性染料染色时，染液pH值为4-5，此时，聚酰胺纤维末端氨基发生质子化，带有正电荷，与酸性染料离解的负电荷磺酸基团，发生离子键结合，从而上染聚酰胺纤维。本发明中，利用pH值小于3的染液，氢离子除了吸附在末端氨基上，还会吸附在酰胺键上，使酰胺键成为第二种染座。增加的染座可以结合更多的酸性染料，从而提高上染率，使得纺织品的颜色变深。其中，调节染液pH值所用的酸不做特别限定，可以是柠檬酸、乳酸、琥珀酸、脂肪酸等。
本发明中聚酰胺纤维纺织品可以是机织物，也可以是针织物等，没有特别限定。
下面结合实施例及比较例对本发明作进一步说明。
本发明所涉及的各参数的测试方法如下：
（1）吸光度峰值
①称量0.063g氢氧化钠和0.21g保险粉加入105mL去离子水中，搅拌均匀配置成还原清洗液；
②称量3.5g聚酰胺纤维纺织品，放入上述还原清洗液中；
（2）末端氨基含量
将1g聚酰胺纤维纺织品溶解于25mL的苯酚-甲醇混合溶液（苯酚-甲醇的重量比为7：3）中，使得聚酰胺分子链末端自由氨基水解出来，再用体积比1：4的盐酸-乙醇混合溶液对自由氨基进行滴定，消耗的盐酸-乙醇溶液的量等同于自由氨基的量，即末端氨基的含量。
（3）无机粒子的含量
称取5g聚酰胺纤维纺织品作为试样，选用100mL甲酸将试样充分溶解，过滤干燥，称取无机粒子的重量，并计算出含量。
（4）耐水色牢度
GB/T 5713-2013标准。
（5）L*值
采用Datacolor 650测色仪，在D65光源、10℃角、100%UV。光条件下，将长度、宽度均为20cm的纺织品折叠成4层后测试。
（6）UPF紫外线保护等级
AS/NZS 4399-1996标准。
实施例1
选用由10D/24f的普通聚酰胺6FDY作为经纬纱形成的机织物作为待加工品，其中，普通聚酰胺6FDY中末端氨基含量为30mmol/kg、无机粒子二氧化钛含量为0.5wt%。
先将1g/L匀染剂、10g/L乳酸和去离子水混合均匀形成助剂溶液（浴比1：20），然后将5.00%o.w.f.的酸性染料加入助剂溶液中，搅拌均匀形成pH值为2.8的整理液，再将待加工品与整理液一并放入染色机中，在95℃下保温30分钟后取出得到染色后的纺织品。接着将5%o.w.f.单宁酸类固色剂和去离子水混合均匀得到固色剂溶液（浴比1：20），将染色后的纺织品与固色剂溶液放入染色机中，在80℃下保温20分钟，制得本发明的纺织品。
所得纺织品的各性能参数见表1。
实施例2
普通聚酰胺6 FDY为20D/24f，末端氨基含量为40mmol/kg，其余同实施例1，得到本发明的纺织品，其各性能参数见表1。
实施例3
普通聚酰胺6 FDY为40D/24f，末端氨基含量为50mmol/kg，其余同实施例1，得到本发明的纺织品，其各性能参数见表1。
实施例4
普通聚酰胺6 FDY为60D/24f，末端氨基含量为80mmol/kg，其余同实施例1，得到本发明的纺织品，其各性能参数见表1。
实施例5
聚酰胺纤维中无机粒子二氧化钛含量为2wt%，其余同实施例1，得到本发明的纺织品，其各项性能见表1。
实施例6
聚酰胺纤维中无机粒子二氧化钛含量为5wt%，其余同实施例1，得到本发明的纺织品，其各项性能见表1。
实施例7
聚酰胺纤维中无机粒子二氧化钛含量为6wt%，其余同实施例1，得到本发明的纺织品，其各项性能见表1。
实施例8
整理液的pH值为2.6，其余同实施例1，得到本发明的纺织品，其各项性能见表1。
实施例9
整理液的pH值为2.1，其余同实施例1，得到本发明的纺织品，其各项性能见表1。
比较例
整理液的pH值为3.3，其余同实施例4，得到纺织品，其各项性能见表1。
表1
根据表1，
（1）由实施例1和实施例2可知，同等条件下，二氧化钛含量为0.5wt%的聚酰胺FDY形成的纺织品与二氧化钛含量为0.4wt%的聚酰胺FDY形成的纺织品相比，两者的L*值、耐水色牢度以及克重均相当，但前者的UPF高于后者，即前者的紫外线防护效果比后者好。
（2）由实施例6和实施例7可知，同等条件下，二氧化钛含量为5.0wt%的聚酰胺FDY形成的纺织品与二氧化钛含量为6.0wt%的聚酰胺FDY形成的纺织品相比，即便二氧化钛含量增加了，UPF也没有变化，而且两者的耐水色牢度以及克重均相当，但前者的L*值略低于后者，也就是说前者比后者颜色略深。
（3）由实施例3和实施例4可知，同等条件下，末端氨基含量为50 mmol/kg的聚酰胺FDY形成的纺织品与末端氨基含量为60mmol/kg的聚酰胺FDY形成的纺织品相比，两者的UPF和克重相当，虽然后者的耐水色牢度优于后者，但前者的L*值比后者低，即前者比后者上色深。
（4）由实施例3和实施例5可知，同等条件下，40D聚酰胺FDY形成的纺织品与50D聚酰胺FDY形成的纺织品相比，两者的L*值、耐水色牢度以及UPF均相当，但前者的克重低于后者，即前者比后者轻。
（5）由比较例和实施例4可知，同等条件下，残液的吸光度峰值为0.01的纺织品与残液的吸光度峰值为0.03的纺织品相比，两者的UPF以及克重均相当，前者的耐水色牢度优于后者，但前者的L*值很高，上色效果较差。
Claims (5)
1.一种纺织品，由100%聚酰胺纤维形成，其特征是：所述聚酰胺纤维上附着有酸性染料；且所述纺织品还原清洗后的残液的吸光度峰值大于0.02且小于2.00。
2.根据权利要求1所述纺织品，其特征是：所述聚酰胺纤维的末端氨基含量为30～50mmol/kg。
3.根据权利要求1所述纺织品，其特征是：所述聚酰胺纤维中无机粒子的含量为0.5～5.0wt%。
4.根据权利要求1所述纺织品，其特征是：所述聚酰胺纤维的总纤度为10～40旦尼尔。
5.根据权利要求1～4中任一项所述纺织品，其特征是：根据GB/T 5713-2013标准，所述纺织品的耐水色牢度在3-4级以上。