CN113789096A - 一种纳米隔热涂料的制备方法 - Google Patents
一种纳米隔热涂料的制备方法 Download PDFInfo
- Publication number
- CN113789096A CN113789096A CN202111158791.7A CN202111158791A CN113789096A CN 113789096 A CN113789096 A CN 113789096A CN 202111158791 A CN202111158791 A CN 202111158791A CN 113789096 A CN113789096 A CN 113789096A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- heat insulation
- preparation
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种纳米隔热涂料的制备方法，包括以下步骤：原料准备阶段、研磨阶段、初步处理阶段、PH调节阶段、干燥阶段、溶解阶段，通过这些步骤，向纳米隔热涂料中，添加杀菌防霉剂，通过三七粉的杀菌作用，增强涂料的杀菌作用，减少纳米隔热涂料霉变的可能性，且三七粉对人体无害，相比于化学杀菌药剂，更为环保，对人体的健康影响更小，避免影响用户的身体健康，通过设置的氯化橡胶和纳米玻璃微珠等材料，利用其对阳光的反射能力，增强纳米隔热涂料的反光能力，从而在夏天时，对阳光更充分的反光，将部分阳光反射出去，避免涂料过热，从而使得用户的居住环境中的温度不至于过高，避免给用户居住生活带来不便。
Description
技术领域
本发明涉及制备方法领域，特别涉及一种纳米隔热涂料的制备方法。
背景技术
纳米透明隔热涂料是一种陶瓷类隔热保温水性涂料，采用最新复合陶瓷纳米氧化钨隔热材料，设计用来吸收阳光中红外紫外线，纳米透明隔热涂料其独特的环保成分，纳米氧化钨液体、二氧化钛能清除周围环境中的异味，降解甲醛和其他有害物质，纳米透明隔热涂料是一种新型涂料，符合环保涂料的要求和特性，但是纳米材料在实际使用中，其防霉变的效果不好，如公开号CN109266206A公开的一种纳米隔热涂料的制备方法，其反射阳光的能力不好，在炎炎夏日，其大量吸收热量，导致过热，不便于用户。
发明内容
本发明的主要目的在于提供一种纳米隔热涂料的制备方法，可以有效解决背景技术中提出的问题。
为实现上述目的，本发明采取的技术方案为：
一种纳米隔热涂料的制备方法，包括以下步骤：
S1、原料准备阶段，将各种材料按照重量比进行配置；
S2、研磨阶段；
S3、初步处理阶段，将研磨后的纳米填充料加入至水性丙烯酸溶液中，再将纳米高分子树脂、添加剂、纳米玻璃微珠依次加入至水性丙烯酸溶液中，通过超声分散机进行处理；
S4、PH调节阶段，将碱性溶液加入至上一步得到的混合溶液中，将PH调节至中性；
S5、干燥阶段；
S6、溶解阶段；
优选的，S1步骤中，其中纳米填充料30-50份、纳米高分子树脂10-20份、水性丙烯酸溶液90-100份、水100份、碱性溶液50-60份、消泡剂1-2份、分散机1-3份、流平剂2-3份、杀菌防霉剂3-6份、光引发剂5-7份、成膜助剂0-1份，添加剂2-3份，纳米玻璃微珠1-2份，选取的纳米填充料为二氧化硅，选取的杀菌防霉剂为三七粉，选取的添加剂为氯化橡胶。
优选的，S2步骤中，纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠分别从原料中倒出通过研磨机进行研磨，研磨完成后，将其分别放置回原料中，研磨时间不能低于半个小时，研磨完成后的纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠的直径不能大于8um。
优选的，S3步骤中，超声分散机的处理时间不能低于一个小时。
优选的，S4步骤中，将碱性溶液加入至混合液中后，通过超声分散机进行分散搅拌，分散搅拌时间为20分钟左右，搅拌完成后，进行PH测试，确认其为中性，否者继续添加碱性溶液，直至混合溶液为碱性。
优选的，S5步骤中，将上一步得到的混合溶液放置于烘干箱中，干燥处理后得到混合粉末，干燥处理的时间为24h，干燥完成后，需静止降温至室温状态，冷却混合粉末。
优选的，S6步骤中，将水、消泡剂、分散机、流平剂、杀菌防霉剂、光引发剂、成膜助剂依次加入至超声分散机中，进行混合搅拌，然后将前一步得到的混合粉末加入其中，经过高速搅拌，最后过滤包装，超声分散机的处理时间不能低于两个小时，混合完成后，过滤，将其中不容于溶液的杂质筛选出，将过滤后的溶液密封包装，室温储存。
与现有技术相比，本发明一种纳米隔热涂料的制备方法，通过设置的杀菌防霉剂，通过三七粉的杀菌作用，增强涂料的杀菌效果，减少涂料的霉变，通过设置的氯化橡胶和纳米玻璃微珠的反射能力，增强涂料的反光能力，从而在夏天时，对阳光更充分的反光，避免涂料过热，给用户居住生活带来不便。
附图说明
图1为本发明一种纳米隔热涂料的制备方法的制备步骤图。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例一
如图1所示，一种纳米隔热涂料的制备方法，包括以下步骤：
S1、原料准备阶段，将各种材料按照重量比进行配置；
S2、研磨阶段；
S3、初步处理阶段，将研磨后的纳米填充料加入至水性丙烯酸溶液中，再将纳米高分子树脂、添加剂、纳米玻璃微珠依次加入至水性丙烯酸溶液中，通过超声分散机进行处理；
S4、PH调节阶段，将碱性溶液加入至上一步得到的混合溶液中，将PH调节至中性；
S5、干燥阶段；
S6、溶解阶段。
S1步骤中，其中纳米填充料30-50份、纳米高分子树脂10-20份、水性丙烯酸溶液90-100份、水100份、碱性溶液50-60份、消泡剂1-2份、分散机1-3份、流平剂2-3份、杀菌防霉剂3-6份、光引发剂5-7份、成膜助剂0-1份，添加剂2-3份，纳米玻璃微珠1-2份，选取的纳米填充料为二氧化硅，选取的杀菌防霉剂为三七粉，选取的添加剂为氯化橡胶；
实施例二
S2步骤中，纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠分别从原料中倒出通过研磨机进行研磨，研磨完成后，将其分别放置回原料中，研磨时间不能低于半个小时，研磨完成后的纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠的直径不能大于8um；S3步骤中，超声分散机的处理时间不能低于一个小时；S4步骤中，将碱性溶液加入至混合液中后，通过超声分散机进行分散搅拌，分散搅拌时间为20分钟左右，搅拌完成后，进行PH测试，确认其为中性，否者继续添加碱性溶液，直至混合溶液为碱性；S5步骤中，将上一步得到的混合溶液放置于烘干箱中，干燥处理后得到混合粉末，干燥处理的时间为24h，干燥完成后，需静止降温至室温状态，冷却混合粉末；S6步骤中，将水、消泡剂、分散机、流平剂、杀菌防霉剂、光引发剂、成膜助剂依次加入至超声分散机中，进行混合搅拌，然后将前一步得到的混合粉末加入其中，经过高速搅拌，最后过滤包装，超声分散机的处理时间不能低于两个小时，混合完成后，过滤，将其中不容于溶液的杂质筛选出，将过滤后的溶液密封包装，室温储存。
需要说明的是，本发明为一种纳米隔热涂料的制备方法，将各种材料按照重量比进行配置，其中纳米填充料为二氧化硅30-50份、纳米高分子树脂10-20份、水性丙烯酸溶液90-100份、水100份、碱性溶液50-60份、消泡剂1-2份、分散机1-3份、流平剂2-3份、杀菌防霉剂为三七粉3-6份、光引发剂5-7份、成膜助剂0-1份，添加剂为氯化橡胶2-3份，纳米玻璃微珠1-2份，其中纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠分别需要通过研磨机进行处理，研磨时间不能低于半个小时，将其研磨至8um以下时，分被放置会原料桶待用，将纳米填充料加入至水性丙烯酸溶液中，再将纳米高分子树脂、添加剂、纳米玻璃微珠依次加入至水性丙烯酸溶液中，通过超声分散机进行处理，处理时间不能低于一个小时，然后得到混合容易，然后将碱性溶液慢慢加入，边加入边搅拌，然后放置入超声分散机中，通过20分钟左右的分撒搅拌，测试PH值，确认其为中性后，将其取出进行干燥，放置于烘干箱中，最少烘干24h小时，直至得到混合粉末，静止降温至室温后，将其取出待用，然后将水、消泡剂、分散机、流平剂、杀菌防霉剂、光引发剂、成膜助剂依次加入至超声分散机中，进行混合搅拌，混合搅拌的时间不能低于两个小时，然后将前一步得到的混合粉末加入其中，再次高速搅拌，再次经过不低于两个小时的搅拌后，将其过滤，将不溶于溶液的杂质过滤筛选掉，最后密封包装，室温储存。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.一种纳米隔热涂料的制备方法，其特征在于：包括以下步骤：
S1、原料准备阶段，将各种材料按照重量比进行配置；
S2、研磨阶段；
S3、初步处理阶段，将研磨后的纳米填充料加入至水性丙烯酸溶液中，再将纳米高分子树脂、添加剂、纳米玻璃微珠依次加入至水性丙烯酸溶液中，通过超声分散机进行处理；
S4、PH调节阶段，将碱性溶液加入至上一步得到的混合溶液中，将PH调节至中性；
S5、干燥阶段；
S6、溶解阶段。
2.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S1步骤中，其中纳米填充料30-50份、纳米高分子树脂10-20份、水性丙烯酸溶液90-100份、水100份、碱性溶液50-60份、消泡剂1-2份、分散机1-3份、流平剂2-3份、杀菌防霉剂3-6份、光引发剂5-7份、成膜助剂0-1份，添加剂2-3份，纳米玻璃微珠1-2份，选取的纳米填充料为二氧化硅，选取的杀菌防霉剂为三七粉，选取的添加剂为氯化橡胶。
3.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S2步骤中，纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠分别从原料中倒出通过研磨机进行研磨，研磨完成后，将其分别放置回原料中，研磨时间不能低于半个小时，研磨完成后的纳米填充料、纳米高分子树脂、添加剂、杀菌防霉剂、纳米玻璃微珠的直径不能大于8um。
4.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S3步骤中，超声分散机的处理时间不能低于一个小时。
5.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S4步骤中，将碱性溶液加入至混合液中后，通过超声分散机进行分散搅拌，分散搅拌时间为20分钟左右，搅拌完成后，进行PH测试，确认其为中性，否者继续添加碱性溶液，直至混合溶液为碱性。
6.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S5步骤中，将上一步得到的混合溶液放置于烘干箱中，干燥处理后得到混合粉末，干燥处理的时间为24h，干燥完成后，需静止降温至室温状态，冷却混合粉末。
7.根据权利要求1所述的一种纳米隔热涂料的制备方法，其特征在于：所述S6步骤中，将水、消泡剂、分散机、流平剂、杀菌防霉剂、光引发剂、成膜助剂依次加入至超声分散机中，进行混合搅拌，然后将前一步得到的混合粉末加入其中，经过高速搅拌，最后过滤包装，超声分散机的处理时间不能低于两个小时，混合完成后，过滤，将其中不容于溶液的杂质筛选出，将过滤后的溶液密封包装，室温储存。