CN113735458A - 一种玻璃盖板及电子设备 - Google Patents
一种玻璃盖板及电子设备 Download PDFInfo
- Publication number
- CN113735458A CN113735458A CN202110938328.8A CN202110938328A CN113735458A CN 113735458 A CN113735458 A CN 113735458A CN 202110938328 A CN202110938328 A CN 202110938328A CN 113735458 A CN113735458 A CN 113735458A
- Authority
- CN
- China
- Prior art keywords
- cover plate
- antireflection film
- glass cover
- stress
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种玻璃盖板及电子设备，其中，玻璃盖板包括，盖板本体，包括第一面和第二面，第一面的应力小于第二面，第一面受向内弯曲的力，第二面受向外弯曲的力；减反射膜，至少部分覆盖盖板本体的第一面，减反射膜的弹性模量大于盖板本体的弹性模量，减反射膜能够平衡第一面和第二面的应力。本发明在盖板应力小的一面镀减反射膜，且减反射膜的弹性模量大于盖板的弹性模量，极大程度上能够平衡盖板两面的应力差，减轻了盖板的翘曲程度，便于盖板的后期加工，且提高了显示面板的整体视觉效果。
Description
技术领域
本发明涉及显示面板技术领域，尤其涉及一种玻璃盖板及电子设备。
背景技术
车用玻璃盖板，为了增强盖板强度，一般都需要做化学钢化；如图1和图2所示，平整的玻璃10’在化学钢化过程中，正反面的钢化深度往往不一致，第一面11’的应力小于第二面12’从而导致玻璃翘曲。如果不做处理，不利于玻璃10’的后期加工，影响盖板的外观，甚至影响显示面板的显示效果。
有鉴于此，急需对现有的玻璃盖板进行改进，减小钢化后的盖板两面的应力差。
发明内容
本发明公开一种玻璃盖板及电子设备，用于解决现有技术中，钢化后的盖板两面的应力差导致盖板翘曲的问题。
为了解决上述问题，本发明采用下述技术方案：
提供一种玻璃盖板，包括，
盖板本体，包括第一面和第二面，所述第一面的应力小于所述第二面，自然状态下，所述盖板本体向所述第一面弯曲；
减反射膜，至少部分覆盖所述第一面，所述减反射膜的弹性模量大于所述盖板本体的弹性模量，所述减反射膜能够平衡所述第一面和第二面的应力。
在上述方案中，所述盖板本体为钢化玻璃。
在上述方案中，所述减反射膜完全覆盖所述第一面。
在上述方案中，所述盖板本体的弹性模量为60～80GPa。
在上述方案中，所述减反射膜的弹性模量为100～150GPa。
在上述方案中，所述减反射膜由二氧化硅、氮化硅、氧化铌、氧化钛中的一种或多种制成。
在上述方案中，所述减反射膜至少有两层。
在上述方案中，所述减反射膜有5～9层。
在上述方案中，所述减反射膜的反射率小于1％，厚度为200～500nm。
本发明还提供了一种电子设备，包括上述方案中任一项所述的玻璃盖板。
本发明采用的技术方案能够达到以下有益效果：
在盖板应力小的一面镀减反射膜，且减反射膜的弹性模量大于盖板的弹性模量，极大程度上能够平衡盖板两面的应力差，减轻了盖板的翘曲程度，便于盖板的后期加工，且提高了显示面板的整体视觉效果。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，构成本发明的一部分，本发明的示意性实施例及其说明解释本发明，并不构成对本发明的不当限定。在附图中：
图1为现有技术中未钢化的玻璃示意图；
图2为现有技术中玻璃钢化后的示意图；
图3为本发明实施例1公开的玻璃盖板的结构示意图。
具体包括下述附图标记：
现有技术中的玻璃-10’；现有技术中的第一面-11’；现有技术中的第二面-12’；盖板本体-10；第一面-11；第二面-12；减反射膜-20。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合本发明具体实施例及相应的附图对本发明技术方案进行清楚、完整地描述。显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
如图3所示，本发明提供的玻璃盖板，包括，
盖板本体10，包括第一面11和第二面12，第一面11的应力小于第二面12，在自然状态下，第一面11受向内弯曲的力，第二面12受向外弯曲的力，盖板本体10向第一面11弯曲；减反射膜20，至少部分覆盖盖板本体10的第一面11，减反射膜20的弹性模量大于盖板本体10的弹性模量，减反射膜20能够平衡第一面11和第二面12的应力。
本发明在盖板本体10应力小的第一面11镀减反射膜20，且减反射膜20的弹性模量大于盖板本体10的弹性模量，极大程度上能够平衡盖板本体10两面的应力差，减轻了盖板本体10的翘曲程度，便于盖板本体10的后期加工。
盖板本体10为钢化玻璃，钢化玻璃强度高，适用范围广，但是由于玻璃化学钢化过程中正反面的钢化深度往往不一致，从而导致玻璃翘曲。
减反射膜20完全覆盖盖板本体10。能够更好的平衡盖板本体10两面的应力差，使盖板本体10达到最佳使用效果。
本实施例优选的，盖板本体10的弹性模量为60～80GPa。减反射膜20的弹性模量为100～150GPa。弹性模量越大，材料越不容易变形，且刚性越强、硬度越大。因此，在第一面11镀减反射膜20能够改善翘曲。
减反射膜20由二氧化硅、氮化硅、氧化铌、氧化钛中的一种或多种制成。
减反射膜至少有两层，由于单层减反射膜20很难达到预期效果，为了在单波长实现零反射，或在较宽的光谱区达到好的增透效果，因此采用多层减反射膜20。本实施例优选的，减反射膜有5～9层，并且由两种折射率不同的材料堆叠而层，低折射率材料包括二氧化硅，高折射率材料包括氮化硅、氧化铌和氧化钛。
减反射膜20的厚度为200～500nm。
本实施例优选的，减反射膜20的反射率小于1％。消除反射光的效果好。
实施例2
本发明还提供了一种电子设备，包括实施例1中的玻璃盖板。使用这种玻璃盖板的电子设备，由于玻璃盖板的减反射膜20平衡了盖板两面的应力差，使盖板达到大致平整的状态，方便了后续加工，使得显示面板的显示效果更好。
本发明在盖板应力小的一面镀减反射膜，且减反射膜的弹性模量大于盖板的弹性模量，极大程度上能够平衡盖板两面的应力差，减轻了盖板的翘曲程度，便于盖板的后期加工，且提高了显示面板的整体视觉效果。
上面结合附图对本发明的实施例进行了描述，但是本发明并不局限于上述的具体实施方式，上述的具体实施方式仅仅是示意性的，而不是限制性的，本领域的普通技术人员在本发明的启示下，在不脱离本发明宗旨和权利要求所保护的范围情况下，还可做出很多形式，均属于本发明的保护之内。
Claims (10)
1.一种玻璃盖板，其特征在于，包括，
盖板本体，包括第一面和第二面，所述第一面的应力小于所述第二面，自然状态下，所述盖板本体向所述第一面弯曲；
减反射膜，至少部分覆盖所述第一面，所述减反射膜的弹性模量大于所述盖板本体的弹性模量，所述减反射膜能够平衡所述第一面和第二面的应力。
2.根据权利要求1所述的玻璃盖板，其特征在于，所述盖板本体为钢化玻璃。
3.根据权利要求1所述的玻璃盖板，其特征在于，所述减反射膜完全覆盖所述第一面。
4.根据权利要求1所述的玻璃盖板，其特征在于，所述盖板本体的弹性模量为60～80GPa。
5.根据权利要求1所述的玻璃盖板，其特征在于，所述减反射膜的弹性模量为100～150GPa。
6.根据权利要求1所述的玻璃盖板，其特征在于，所述减反射膜由二氧化硅、氮化硅、氧化铌、氧化钛中的一种或多种制成。
7.根据权利要求1所述的玻璃盖板，其特征在于，所述减反射膜至少有两层。
8.根据权利要求7所述的玻璃盖板，其特征在于，所述减反射膜有5～9层。
9.根据权利要求1所述的玻璃盖板，其特征在于，所述减反射膜的反射率小于1%，厚度为200～500nm。
10.一种电子设备，其特征在于，包括权利要求1-9任一项所述的玻璃盖板。