CN1136580A - High grade wall paint - Google Patents
High grade wall paint Download PDFInfo
- Publication number
- CN1136580A CN1136580A CN 96101782 CN96101782A CN1136580A CN 1136580 A CN1136580 A CN 1136580A CN 96101782 CN96101782 CN 96101782 CN 96101782 A CN96101782 A CN 96101782A CN 1136580 A CN1136580 A CN 1136580A
- Authority
- CN
- China
- Prior art keywords
- powder
- water
- calcium carbonate
- high grade
- wall paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The raw material of the high grade wall paint consists of light calcium carbonate, heavy calcium carbonate, lime powder, talc powder, soluble solid gum powder, hexasodium metaphosphate, whitening agent, lithophone, ultra-marine powder and pigment powder. Said invention possesses of the active resuts of high hardness, good properties of cleaning resistance, heat resistance, alkaline resistance and water proof, powerful cohesive force, as bright and clean as porcelain, bright and lustrous, easy construction and low cost.
Description
The invention belongs to building and ornament materials, especially a kind of high grade wall paint.
The building and ornament materials of China develop along with developing rapidly of construction industry at present, building and ornament materials market a slice prosperity, and both production and marketing thrive, and demand increases year by year., the building wall plastering material is continued to use traditional methods such as paper muscle lime, dry powder putty and building coating for many years always.These traditional methods, greatest weakness are, the garnet paper muscle rots, and the putty difference of hardness is met quality problems such as damp efflorescence.
The object of the present invention is to provide a kind of hardness height, anti-wiping, heat-resisting, alkaline-resisting, water resistance is good, cohesive force is strong, pure white as porcelain, high grade wall paint that cost is low.
Technical solution of the present invention is such.The contriver has reached purpose of the present invention through the practice test more than 3 years.Raw material of the present invention includes light calcium carbonate, water-ground limestone, lime powder, talcum powder, solid, water soluble rubber powder, Sodium hexametaphosphate 99, whitening agent, zinc sulfide white and ultramarine powder, pigment powder.
The weight part of above-mentioned various raw materials is: light calcium carbonate 20-30, water-ground limestone 20-28, lime powder 12-18, talcum powder 10-15, solid, water soluble rubber powder 5-10, Sodium hexametaphosphate 99 0.3-1.5, whitening agent 0.4-1.8, zinc sulfide white 5-12, ultramarine powder 0.05-0.1, pigment powder 0.05-0.1.
Light calcium carbonate: generated by calcium hydroxide and calcium dioxide, carbonic acid gas chemical combination, it is a kind of important source material, can make product sliding more tender, increases the fine and smooth sense of metope.The chemical building material shop is on sale.
Water-ground limestone (CaCO
3): another name dry powder, white powder are that natural calcite is directly pulverized to grind through pulverizer and formed, and odorless, free from extraneous odour, are exposed at no change in the air, proportion 2.710, molten point 1339 degree, water-soluble hardly, market is on sale.
Lime powder: white powder, its efficient oxidation calcium and content of magnesia are not less than 80%.Be used for high grade wall paint, strengthen cohesive strength and scrub resistance, reduce cost.Commercially available on sale.
Talcum powder [3MgO, 4SiO
2H
2O]: be the natural silico-aluminate that exists, white or light-colored powder are laminar, and vitreous luster is arranged, and the property softness has soapy feeling, relative density 2.7-2.8, the chemical property torpescence has oilness.Water tolerance, anti acid alkali performance, insulativity also has spanwise effect, so can reduce the water-permeable of filming, reduces cracking and efflorescence that product is filmed.Market is on sale.
The solid hydrosol powder as the main binding agent of wall paint, improves the sticking power of various raw materials to metope.The chemical industry shop is on sale.
Sodium hexametaphosphate 99: be commonly called as sodium phosphate glasses, vitreous solid, having has wettability power more by force, water-soluble, is insoluble to organic solvent.As dispersion agent, starting material are uniformly dispersed, improve the quality of products.The chemical industry shop is on sale.
Whitening agent: be commonly called as white dyestuff, be used for brightening of materials such as textiles, paper pulp, can absorb the ultraviolet ray of daylight and other light source, send blue purple or cyan fluorescent, thereby make material seem pure whiter, and have better water solubility and higher fluorescent effect.Its effect is to make the tender from the coarse to fine and increase light of raw material, makes it porcelainization.The chemical industry shop is on sale.
The ultramarine powder: be a kind of whitening agent that comparatively generally uses, it can with yellow pigment generation chemical reaction in the most of raw materials of this product, yellow is removed, increase whiteness.And can be used as pigment and use.The chemical industry shop is on sale.
Making method of the present invention: various raw materials are weighed by weight, put into stirrer stir the back packaging final prod.Solid, water soluble rubber powder packing in addition wherein, during use, per kilogram is with 18 kilograms of cold water soak, wait dissolve fully after, be 0.35: 1 in sizing material and above-mentioned powder ratio.
The present invention compared with prior art, have hardness height, anti-wiping, thermotolerance, alkaline-resisting, water resistance good, cohesive force is strong, bright and clean as porcelain, lovely luster, be difficult for being stained with dirt, easy construction, cost is low, widely used positively effect.
Most preferred embodiment of the present invention is such, and water-ground limestone and talcum powder are selected the above whiteness of 80 degree, the product that fineness 325 orders are above for use.Various raw materials by weight (is unit with the kilogram) weigh: light calcium carbonate 25, water-ground limestone 24, lime powder 14, talcum powder 12, Sodium hexametaphosphate 99 0.8, whitening agent 0.8, zinc sulfide white 10, ultramarine powder 0.08, pigment 0.08, mix then and put into the stirrer back packaging final prod that stirs.Wherein the solid, water soluble rubber powder is packed in addition, and during use, per kilogram is with 18 kilograms of cold water soak, wait dissolving fully after, be 0.35: 1 in sizing material and above-mentioned powder ratio.
The present invention shows through the test-results more than 3 years, has solved the garnet paper muscle and has easily turned to be yellow, and rots; Dry powder putty,, cohesive strength is poor, hardness is low, meets easily efflorescence of tide, comes off.
The present invention is as follows through Guangxi district construction engineering quality inspection center building materials testing data:
The test subject test-results
Appearance of coat is bright and clean smooth, exquisite in texture
Whiteness 81.9%
Pencil hardness 3H
Cohesive strength 0.73MPa
80 ± 2 ℃ of 5h of thermotolerance do not have cracking, play drum, the shedding phenomenon
Water tolerance immersion 14d has not had drum, shedding, metachromatism
The saturated Ca of alkali resistance (OH)
214d has not had drum, shedding, metachromatism.
Washable wiping is greater than 1000 times
Claims (3)
1, a kind of high grade wall paint, its feature of raw material are to include light calcium carbonate, water-ground limestone, lime powder, talcum powder, solid, water soluble rubber powder, Sodium hexametaphosphate 99, whitening agent, zinc sulfide white, ultramarine powder, pigment powder.
2, high grade wall paint according to claim 1, its feature of raw material are that the weight part of various raw materials is: light calcium carbonate 20-30, water-ground limestone 20-28, lime powder 12-18, talcum powder 10-15, solid, water soluble rubber powder 5-10, Sodium hexametaphosphate 99 0.3-1.5, whitening agent 0.4-1.8, zinc sulfide white 5-12, ultramarine powder 0.05-0.1, pigment powder 0.05-0.1.
3, high grade wall paint according to claim 1 and 2, its feature of raw material are that the weight part that various raw materials contain is: light calcium carbonate 25, water-ground limestone 24, lime powder 14, talcum powder 12, solid, water soluble rubber powder 6.5, Sodium hexametaphosphate 99 0.8, whitening agent 0.8, zinc sulfide white 10, ultramarine powder 0.08, pigment powder 0.08.