CN113265534A - 一种低品铬铁渣再利用生产工艺 - Google Patents

一种低品铬铁渣再利用生产工艺 Download PDF

Info

Publication number
CN113265534A
CN113265534A CN202110402450.3A CN202110402450A CN113265534A CN 113265534 A CN113265534 A CN 113265534A CN 202110402450 A CN202110402450 A CN 202110402450A CN 113265534 A CN113265534 A CN 113265534A
Authority
CN
China
Prior art keywords
slag
mixture
grade
low
molten iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202110402450.3A
Other languages
English (en)
Other versions
CN113265534B (zh
Inventor
马天荣
廖军
王先武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiayuguan Hongdian Ferroalloy Co ltd
Original Assignee
Jiayuguan Hongdian Ferroalloy Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiayuguan Hongdian Ferroalloy Co ltd filed Critical Jiayuguan Hongdian Ferroalloy Co ltd
Priority to CN202110402450.3A priority Critical patent/CN113265534B/zh
Publication of CN113265534A publication Critical patent/CN113265534A/zh
Application granted granted Critical
Publication of CN113265534B publication Critical patent/CN113265534B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于金属冶炼领域，涉及工业废弃物的再利用，具体涉及一种低品铬铁渣再利用生产工艺，包括如下步骤：S1：将烧结矿、低品铬铁渣、硅石和除尘灰压球按照6:2:1:2的比例混合；S2：将上述物料搭配一定比例焦炭经过配料系统混合上至矿热炉内，通过电极传导电能加热到1300‑1500℃；S3：在高温下通过氧化还原反应，冶炼3‑4小时后打开炉眼，渣铁混合物一起排出至铁水灌内，边出渣铁混合物边沉淀，上层液态渣流出铁水灌嘴直接进入水翠池，铁水滞留在铁水包内，然后由行车吊运进行浇铸，该工艺方法简单、费用低、低品铬铁渣的综合利用率高，解决了现有技术中存在的问题。

Description

一种低品铬铁渣再利用生产工艺
技术领域
本发明属于金属冶炼领域，涉及工业废弃物的再利用，具体涉及一种低品铬铁渣再利用生产工艺。
背景技术
随着铁合金行业的快速发展，铁合金生产产生大量的铁合金炉渣。铁合金炉渣，包括高碳铬铁渣、硅锰渣及硅铁渣等，当然也包含低品铬铁渣，其废弃不仅会造成所含金属的流失，而且还会造成环境污染。目前对铁合金炉渣的处理工艺有：1、破碎跳态法；2、磁选法等，这些方式普遍存在工艺复杂、环节较多，投资较大和只能处理含有的金属颗粒，无法处理渣中金属的氧化物等缺陷。
发明内容
为克服上述现有技术中存在的问题，本发明的目的是提供一种低品铬铁渣再利用生产工艺，该工艺方法简单、费用低、低品铬铁渣的综合利用率高，解决了现有技术中存在的问题。
本发明所采用的技术方案是：
一种低品铬铁渣再利用生产工艺，包括如下步骤：
S1：将烧结矿、低品铬铁渣、硅石和除尘灰压球按照6:2:1:2的比例混合；
S2：将上述物料搭配一定比例焦炭经过配料系统混合上至矿热炉内，通过电极传导电能加热，出炉铁水温度到1300-1500℃；
S3：在高温下通过氧化还原反应，冶炼3-4小时后打开炉眼，渣铁混合物一起排出至铁水灌内，边出渣铁混合物边沉淀，上层液态渣流出铁水灌嘴直接进入水翠池，铁水滞留在铁水包内，然后由行车吊运进行浇铸。
优选的步骤S1中所述的硅石为冶炼硅铁所需硅石的筛下物中的小粒硅石。
优选的步骤S2中所述的矿热炉的电能输入为3000kwh/t。
本发明的有益效果是：
1.整个过程粉尘少，减少了粉尘对环境的污染；
2.水淬后的炉渣稳定好，粒度较小且粒度均匀；
3.机械化、自动化程度高；
4.铁水和炉渣分离效果好；
5.对炉渣的粘度和流动性要求不高；
6.工艺环节少、工艺简单，费用少。
具体实施方式
一种低品铬铁渣的再利用生产工艺，依照下列步骤完成：
S1：将烧结矿、低品铬铁渣、硅石和除尘灰压球按照6:2:1:2的比例混合，硅石为冶炼硅铁所需硅石的筛下物中的小粒硅石；
烧结矿、低品铬铁渣和除尘灰压球中均含有Cr2O3、Fe、MgO、SiO2和Al2O3，在焦炭作为还原剂的前提下，烧结矿、低品铬铁渣、硅石和除尘灰压球按照6:2:1:2的比例混合入炉冶炼，炉渣碱度可调控1.2-1.3之间，能够确保混合物料中有用元素的充分还原，达到对低品铬铁渣中有用金属元素的回收。
S2：将上述物料搭配一定比例焦炭经过配料系统混合上至矿热炉内，通过电极传导电能加热,出炉铁水温度到1300-1500℃，矿热炉的电能输入为3000kwh/t；
S3：在高温下通过氧化还原反应，冶炼3-4小时后打开炉眼，渣铁混合物一起排出至铁水灌内，边出渣铁混合物边沉淀，上层液态渣流出铁水灌嘴直接进入水淬池，水淬渣可以外销，铁水滞留在铁水包内，然后由行车吊运进行浇铸，经过破碎，达到客户需求粒度进行销售。
通过工艺冶炼的反复摸索试验，在出炉铁水温度达到1300-1500℃之间时，铁水的流动性较好，铁水粘包量较少，且炉渣中的Cr2O3含量可控制在2%以下。
试验数据如下：
序号 温度 炉渣Cr2O3 碱度 备注
1 1289 2.78 1.35
2 1261 2.06 1.34
3 1354 1.19 1.30
4 1355 1.32 1.27

Claims (3)

1.一种低品铬铁渣再利用生产工艺，其特征在于包括如下步骤：
S1：将烧结矿、低品铬铁渣、硅石和除尘灰压球按照6:2:1:2的比例混合；
S2：将上述物料搭配一定比例焦炭经过配料系统混合上至矿热炉内，通过电极传导电能加热到1300-1500℃；
S3：在高温下通过氧化还原反应，冶炼3-4小时后打开炉眼，渣铁混合物一起排出至铁水灌内，边出渣铁混合物边沉淀，上层液态渣流出铁水灌嘴直接进入水翠池，铁水滞留在铁水包内，然后由行车吊运进行浇铸。
2.根据权利要求1所述的一种低品铬铁渣再利用生产工艺，其特征在于：步骤S1中所述的硅石为冶炼硅铁所需硅石的筛下物中的小粒硅石。
3.根据权利要求1所述的一种低品铬铁渣再利用生产工艺，其特征在于：步骤S2中所述的矿热炉的电能输入为3000kwh/t。
CN202110402450.3A 2021-04-14 2021-04-14 一种低品铬铁渣再利用生产工艺 Active CN113265534B (zh)