CN113265214B - Magnetic glue for manufacturing false eyelashes, method for manufacturing false eyelashes and product - Google Patents

Magnetic glue for manufacturing false eyelashes, method for manufacturing false eyelashes and product Download PDF

Info

Publication number
CN113265214B
CN113265214B CN202110502388.5A CN202110502388A CN113265214B CN 113265214 B CN113265214 B CN 113265214B CN 202110502388 A CN202110502388 A CN 202110502388A CN 113265214 B CN113265214 B CN 113265214B
Authority
CN
China
Prior art keywords
parts
magnetic
false
false eyelashes
eyelash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110502388.5A
Other languages
Chinese (zh)
Other versions
CN113265214A (en
Inventor
于超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Jiahe Yongrun Beauty Technology Co ltd
Original Assignee
Qingdao Jiahe Yongrun Cosmetics Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Jiahe Yongrun Cosmetics Co ltd filed Critical Qingdao Jiahe Yongrun Cosmetics Co ltd
Priority to CN202110502388.5A priority Critical patent/CN113265214B/en
Publication of CN113265214A publication Critical patent/CN113265214A/en
Application granted granted Critical
Publication of CN113265214B publication Critical patent/CN113265214B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses magnetic glue for manufacturing false eyelashes, a manufacturing method of the false eyelashes and a product, wherein the magnetic glue comprises the following components in parts by weight: 0.2-1.2 parts of chloroprene rubber, 0.2-1.2 parts of p-tert-butyl phenolic resin, 0.2-1.2 parts of coumarone resin, 0.2-1.2 parts of terephthalic acid ester, 0.2-1 part of hindered phenol antioxidant, 0.2-1 part of magnesium oxide, 0.2-1 part of colorant, 0.2-1.2 parts of n-hexane, 10-16 parts of cyclohexane, 10-16 parts of 2-methylpentane, 10-16 parts of methylcyclopentane, 10-16 parts of dimethanol formal, 10-16 parts of dichloromethane, 10-16 parts of n-heptane, 10-16 parts of methanol, 10-16 parts of toluene, 10-16 parts of water and 10-16 parts of ferroferric oxide. The false eyelash disclosed by the invention is high in wearing comfort, free of magnetic repulsion and capable of being repeatedly worn for a long time.

Description

Magnetic glue for manufacturing false eyelashes, method for manufacturing false eyelashes and product
Technical Field
The invention belongs to the technical field of cosmetics, and particularly relates to magnetic glue for manufacturing false eyelashes, a manufacturing method of the false eyelashes and a product.
Background
The traditional false eyelashes used at present are composed of a connecting stem and false eyelashes adhered to the connecting stem, an adhesive or eyeliner is arranged on one surface of the connecting stem, and the false eyelashes coated with the adhesive are adhered to upper eyelids when the false eyelashes are worn, so that the false eyelashes are worn.
For example, chinese patent document CN110934753A discloses an eyeliner and a method for preparing the same, wherein the eyeliner comprises the following raw materials by weight percent: 35-55% of iron powder; 10-30% of film-forming agent; 5-15% of isododecane; 5-10% of ferric oxide toner; 1.5 to 14 percent of thickening agent; 0.4 to 1.6 percent of preservative. The iron powder and the ferric oxide toner in the eyeliner can be adsorbed together with false eyelashes with magnetic strips under the action of magnetic force, so that the effect of sticking the false eyelashes can be achieved, and the eyeliner can be used for drawing eyeliners and sticking the false eyelashes.
Chinese patent document CN112120967A discloses a magnetic eyeliner composition for adsorbing magnetic false eyelashes, and a preparation method and application thereof. The eyeliner composition comprises a forming agent, a film forming agent, a diluent, a magnetic colorant and a colorant; the eyeliner composition prepared by the invention has magnetism, combines two functions of drawing eyeliners and attaching false eyelashes with magnetism, can reduce stimulation and damage to skin compared with the traditional glue or adhesive plaster used for sticking the false eyelashes, and can save the makeup time and cost.
Chinese patent document CN112040924A discloses a magnetically attachable eyelash prosthesis system and related method, wherein various magnetically attachable eyelash prosthesis systems are disclosed, which include: (a) a carrier magnetic eyeliner adherable to the eyelid surface and incorporating magnetic particles compatible with the carrier structural adhesive; and (b) a magnetic eyelash prosthesis incorporating one or more magnetic elements exhibiting high coercivity and located at least at the base of the eyelash prosthesis, such that the interaction occurring between the ferromagnetic particles (incorporated into the carrier eyeliner) and the ferromagnetic elements (incorporated into the magnetic eyelash prosthesis) stably adheres the eyelash prosthesis to the pre-coated eyelid surface. Various methods for producing and using various magnetically attachable eyelash prostheses and various carrying magnetic eyeliners are also disclosed.
The technical defects of the existing magnet eyelashes are that a plurality of magnets are adhered to the eyelash stalks at equal intervals or unequal intervals:
1. the wearing comfort is low.
2. The object magnet has positive and negative poles, and easily causes magnetism to repel each other in the wearing process.
3. The adhesive magnet is less, the magnetism is less, the long-time wearing is not realized, the adhesive magnet is more, the wearing magnetism is increased, and the load is increased.
4. The magnet is adhered to the false eyelashes, the wearing foreign body feeling is strong, and the false eyelashes are obviously weighted.
Disclosure of Invention
In view of the above, the present invention is directed to a magnetic glue for manufacturing false eyelashes, a method for manufacturing false eyelashes, and a product thereof, such that the manufactured false eyelashes have high wearing comfort, no magnetic repulsion, can be repeatedly worn for a long time, and have no odor when worn, and the false eyelashes are light in weight.
The adopted technical scheme is as follows:
the invention relates to magnetic glue for manufacturing false eyelashes, which consists of the following components in parts by weight:
Figure BDA0003056914020000021
Figure BDA0003056914020000031
further, the magnetic glue for manufacturing the false eyelashes is composed of the following components in parts by weight:
Figure BDA0003056914020000032
Figure BDA0003056914020000041
further, the colorant is CI77266 or CI 77499.
Further, the terephthalic acid ester is dioctyl terephthalate.
The invention relates to a method for manufacturing invisible magnetic false eyelashes, which comprises the following steps:
s1, applying the magnetic glue of any scheme to a false eyelash thread-combining process, bonding false eyelash pieces of different pieces together by using an adhesive tape, carrying out thread-combining on the magnetic glue, airing, and keeping the false eyelash magnetic after the magnetic glue is solidified;
s2, carrying out primary sterilization treatment on the false eyelashes obtained in the step S1, and uniformly coating the magnetic glue on false eyelash stems of the false eyelashes again;
s3, coating the magnetic glue on the eyeliner part of the false eyelashes obtained in the step S2, and airing for the second time;
and S4, carrying out secondary sterilization treatment on the false eyelashes obtained in the step S3.
Further, in steps S1 and S3, the air-drying is natural air-drying at room temperature.
Further, in steps S1 and S3, the airing time is 1 to 3 hours.
Further, in steps S2 and S4, the sterilization is ultraviolet sterilization, and the sterilization time is 10 to 30 minutes.
Further, step S1 is replaced with the following steps:
s1, applying the magnetic glue to finished false eyelashes, and uniformly coating the magnetic glue on the finished false eyelashes.
The invisible magnetic false eyelash is prepared by the manufacturing method of any one of the above aspects.
Further, the false mascara stem is transparent.
The invisible magnetic false eyelash comprises a false eyelash stem, and the magnetic glue of any scheme is smeared on the false eyelash stem.
Further, the false mascara stem is transparent.
In the technical scheme, the chloroprene rubber has high bonding strength, and good bonding force can be generated by using a proper amount of the chloroprene rubber. The para-tert-butyl phenolic resin and the coumarone resin can further play a role in tackifying. The coumarone resin can also provide acid and alkali resistance to the glue. The terephthalate (preferably dioctyl terephthalate) imparts durability and low temperature flexibility to the product. The ferroferric oxide ensures that the product has no magnetic poles to repel each other.
The invention has the beneficial effects that:
1. the false eyelashes can be conveniently worn for a long time, the effect of wearing for many times can be achieved, and the false eyelashes can be repeatedly used.
2. The ferroferric oxide is used, and the product has no magnetic pole and no magnetic pole repulsion.
3. The false eyelash underwear is convenient to wear, free of solid magnets, light in false eyelash load, comfortable to wear and attractive in appearance.
Detailed Description
The present invention is described in detail below with reference to specific examples, but the use and purpose of these exemplary embodiments are merely to exemplify the present invention, and do not set forth any limitation on the actual scope of the present invention in any form, and the scope of the present invention is not limited thereto.
Example 1
The magnetic glue for manufacturing the false eyelashes consists of the following components in parts by weight:
Figure BDA0003056914020000051
Figure BDA0003056914020000061
wherein the colorant is CI 77499. The terephthalate is dioctyl terephthalate.
The method for manufacturing the invisible magnetic false eyelashes comprises the following steps:
s1, applying the magnetic glue to a false eyelash combining process, bonding false eyelash sheets of different sheets together by using an adhesive tape, combining the magnetic glue on the lines, airing, and keeping the false eyelash magnetic after the magnetic glue is solidified; wherein the airing is natural airing at room temperature. The airing time was 3 hours.
S2, carrying out primary sterilization treatment on the false eyelashes obtained in the step S1, and uniformly coating the magnetic glue on false eyelash stems of the false eyelashes again; wherein the sterilization is ultraviolet sterilization, and the sterilization time is 30 minutes.
S3, coating the magnetic glue on the eyeliner part of the false eyelashes obtained in the step S2, and airing for the second time;
and S4, carrying out secondary sterilization treatment on the false eyelashes obtained in the step S3 to obtain the invisible magnetic false eyelashes.
Example 2
Referring to example 1, unlike example 1, the magnetic glue for manufacturing false eyelashes of the present example consists of the following components in parts by weight:
Figure BDA0003056914020000062
Figure BDA0003056914020000071
the method for manufacturing the invisible magnetic false eyelash is as described in example 1.
Example 3
Referring to example 1, unlike example 1, the magnetic glue for manufacturing false eyelashes of the present example consists of the following components in parts by weight:
Figure BDA0003056914020000072
Figure BDA0003056914020000081
the method for manufacturing the invisible magnetic false eyelashes comprises the following steps:
s1, applying the magnetic glue to finished false eyelashes, and uniformly coating the magnetic glue on the finished false eyelashes;
s2, carrying out primary sterilization treatment on the false eyelashes obtained in the step S1, and uniformly coating the magnetic glue on false eyelash stems of the false eyelashes again; wherein the sterilization is ultraviolet sterilization, and the sterilization time is 30 minutes;
s3, coating the magnetic glue on the eye stem part of the false eyelashes obtained in the step S2, and airing for the second time;
and S4, carrying out secondary sterilization treatment on the false eyelashes obtained in the step S3 to obtain the invisible magnetic false eyelashes.
The false eyelash peduncle is transparent.
Example 4
Referring to example 1, unlike example 1, the invisible magnetic false eyelash of this embodiment includes a false eyelash stem, which is transparent, and the false eyelash stem is smeared with the magnetic glue of example 1.
The preparation process of example 1 was not used.
Comparative example 1
Referring to example 3, in contrast to example 3, this comparative example did not use neoprene and the amount of water was 16.457 parts.
Referring to example 3, the method for manufacturing the invisible magnetic false eyelash still includes the following steps of S1: s1, applying the magnetic glue to finished false eyelashes, and uniformly coating the magnetic glue on the finished false eyelashes.
Test and test:
the test method comprises the following steps:
1. is not easy to fall off, and can be worn for a long time for testing: the eyelash extensions produced in examples 1 to 4 and comparative example 1 were worn on a skin simulator, and the eyelash extensions were covered with clear water using a drip cup filled with clear water at a dripping speed of about 1 drop/sec, and whether or not the eyelash extensions fell off and the time taken for them to fall off were recorded.
2. Comfort test: 50 persons were randomly selected to wear the false eyelashes manufactured according to examples 1 to 4, and were recorded through questionnaire whether the false eyelashes were light in weight, comfortable to wear, and felt to repel magnetic poles during wearing.
The test results are shown in Table 1
TABLE 1
Figure BDA0003056914020000091
The above-listed detailed description is only a specific description of a possible embodiment of the present invention, and they are not intended to limit the scope of the present invention, and equivalent embodiments or modifications made without departing from the technical spirit of the present invention should be included in the scope of the present invention.

Claims (13)

1. The magnetic glue for manufacturing the false eyelashes is characterized by comprising the following components in parts by weight:
0.2 to 1.2 portions of chloroprene rubber,
0.2 to 1.2 portions of p-tert-butyl phenolic resin,
0.2 to 1.2 portions of coumarone resin,
0.2 to 1.2 portions of terephthalic acid ester,
0.2 to 1 portion of hindered phenol antioxidant,
0.2 to 1 portion of magnesium oxide,
0.2 to 1 portion of colorant,
0.2 to 1.2 portions of normal hexane,
10-16 parts of cyclohexane, wherein,
10-16 parts of 2-methyl pentane,
10-16 parts of methyl cyclopentane, namely methyl cyclopentane,
10-16 parts of dimethanol formal,
10-16 parts of dichloromethane, and the like,
10-16 parts of n-heptane, wherein,
10-16 parts of methanol, namely 10-16 parts of methanol,
10-16 parts of toluene, wherein the toluene is a mixture of toluene,
10-16 parts of water, namely,
10-16 parts of ferroferric oxide.
2. The magnetic glue for manufacturing false eyelashes according to claim 1, wherein the magnetic glue consists of the following components in parts by weight:
0.6 to 1.2 portions of chloroprene rubber,
0.6 to 1.2 portions of p-tert-butyl phenolic resin,
0.6 to 1.2 portions of coumarone resin,
0.6 to 1.2 portions of terephthalic acid ester,
0.5 to 0.9 portion of hindered phenol antioxidant,
0.5 to 0.9 portion of magnesium oxide,
0.5 to 0.9 portion of colorant,
0.6 to 1.2 portions of normal hexane,
10.250-15.257 parts of cyclohexane,
10.250-15.257 parts of 2-methylpentane,
10.250-15.257 parts of methylcyclopentane,
10.250-15.257 parts of dimethanol formal,
10.250-15.257 parts of dichloromethane, namely,
10.250-15.257 parts of n-heptane,
10.250-15.257 parts of methanol,
10.250-15.257 parts of toluene,
10.250-15.257 parts of water,
10.250-15.257 parts of ferroferric oxide.
3. Magnetic glue for making false eyelashes according to claim 1 or 2, characterized in that the colouring agent is CI77266 or CI 77499.
4. Magnetic glue for making false eyelashes according to claim 1 or 2, characterized in that the terephthalate is dioctyl terephthalate.
5. A method for manufacturing invisible magnetic false eyelashes is characterized by comprising the following steps:
s1, applying the magnetic glue of any one of claims 1 to 4 to a false eyelash thread-combining process, bonding false eyelash pieces of different pieces together by using an adhesive tape, combining the magnetic glue on the thread, airing, and keeping the false eyelash magnetic after the magnetic glue is solidified;
s2, carrying out primary sterilization treatment on the false eyelashes obtained in the step S1, and uniformly coating the magnetic glue on false eyelash stems of the false eyelashes again;
s3, coating the magnetic glue on the eyeliner part of the false eyelashes obtained in the step S2, and airing for the second time;
and S4, carrying out secondary sterilization treatment on the false eyelashes obtained in the step S3.
6. The method for manufacturing invisible magnetic false eyelashes according to claim 5, wherein the airing is natural airing at room temperature in steps S1 and S3.
7. The method for manufacturing invisible magnetic false eyelashes according to claim 6, wherein the airing time is 1-3 hours in steps S1 and S3.
8. The method for manufacturing invisible magnetic false eyelashes according to claim 5, wherein the sterilization is ultraviolet sterilization for 10 to 30 minutes in steps S2 and S4.
9. The method for manufacturing invisible magnetic false eyelashes according to claim 5, wherein the step S1 is replaced with the steps of:
s1, applying the magnetic glue to finished false eyelashes, and uniformly coating the magnetic glue on the finished false eyelashes.
10. A latent magnetic false eyelash characterized by being produced by the production method according to any one of claims 5 to 9.
11. The invisible magnetic eyelash of claim 10, wherein said false eyelash stem is transparent.
12. A hidden magnetic false eyelash, which is characterized by comprising a false eyelash stem, wherein the false eyelash stem is coated with the magnetic glue of any one of claims 1 to 4.
13. The invisible magnetic eyelash of claim 12, wherein said false eyelash stem is transparent.
CN202110502388.5A 2021-05-08 2021-05-08 Magnetic glue for manufacturing false eyelashes, method for manufacturing false eyelashes and product Active CN113265214B (en)