CN113234393A - 一种绿色环保多功能水性防水涂料及其制备方法 - Google Patents
一种绿色环保多功能水性防水涂料及其制备方法 Download PDFInfo
- Publication number
- CN113234393A CN113234393A CN202110627713.0A CN202110627713A CN113234393A CN 113234393 A CN113234393 A CN 113234393A CN 202110627713 A CN202110627713 A CN 202110627713A CN 113234393 A CN113234393 A CN 113234393A
- Authority
- CN
- China
- Prior art keywords
- waterproof coating
- multifunctional water
- based waterproof
- latex
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种绿色环保多功能水性防水涂料,各组分质量百分数为:复配乳化沥青20‑50%,阳离子氯丁胶乳10‑30%,复配胶乳10‑30%,沸石5‑10%,蒙脱土5‑10%,云母粉2‑4%,铝粉2‑4%,增粘树脂1‑6%。其制备方法是:向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30‑40分钟;边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2‑3小时,直至充分混合均匀,就制成产品。本发明施工简便,生产安全,环境清洁,产品含固量高,成膜性好,防水效果好,抗拉强度高,延伸率大,涂膜粘结强度大,耐热性,低温柔软性好,耐老化,使用寿命长,保温,隔热。可广泛应用于建筑防水涂料领域中。
Description
技术领域
本发明涉及一种绿色环保多功能水性防水涂料及其制备方法,可广泛应用于建筑防水涂料领域中,尤其适用于屋面防水、水池防渗、地下室防潮、防空洞及隧道建筑领域中。
背景技术
现有防水涂料,一般为溶剂型涂料。溶剂型防水涂料中含有一定量的有机挥发物,在生产和施工过程中排向大气,浪费资源,并造成大气环境污染。同时施工人员在施工过程中不可避免地会吸入部分VOC挥发性有机化合物,对人体皮肤具有侵蚀作用,而且对人体中枢神经系统、造血器官、呼吸系统有刺激和破坏作用,因此,对人身健康危害很大。
目前的水性防水涂料产品,为水乳型聚合物的改性沥青,其力学性能、防水性能、耐候性及耐久性性能差,质量不稳定。而且,防水涂料功能单一,不能满足行业需求。
发明内容
本发明的目的在于提供一种施工简便、生产安全、环境清洁、产品含固量高、成膜性好、防水效果好、抗拉强度高、延伸率大、涂膜粘结强度大、耐热性、低温柔软性好、耐老化、使用寿命长、保温、隔热的绿色环保多功能水性防水涂料及其制备方法。
为了达到上述目的,本发明一种绿色环保多功能水性防水涂料,包括复配乳化沥青、阳离子氯丁胶乳、复配胶乳、沸石、蒙脱土、云母粉、铝粉、增粘树脂;各组分质量百分数为:复配乳化沥青20-50%,阳离子氯丁胶乳10-30%,复配胶乳10-30%,沸石5-10%,蒙脱土5-10 %,云母粉2-4 %,铝粉2-4 %,增粘树脂1-6%。
本发明一种绿色环保多功能水性防水涂料,所述的复配乳化沥青,由质量百分数为40-70%的100号沥青,其余质量百分数为10号沥青制成。
本发明一种绿色环保多功能水性防水涂料,所述的阳离子氯丁胶乳,其固含量的质量百分数为55%。
本发明一种绿色环保多功能水性防水涂料,所述的复配胶乳,选择苯乙烯—丁二烯—苯乙烯嵌段共聚物SBS、丁苯橡胶SBR、丁腈橡胶NBR、三元乙丙橡胶EPDM或异戊二烯橡胶IR中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述增粘树脂,选择古隆马树脂、萜烯树脂或聚异丁烯树脂中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述的云母粉,其细度为325-500目。
本发明一种制造所述绿色环保多功能水性防水涂料的方法,按绿色环保多功能水性防水涂料所述的各组分质量百分数配制,首先,向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30-40分钟;然后,边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2-3小时,直至充分混合均匀,就制成一种绿色环保多功能水性防水涂料产品。
本发明一种绿色环保多功能水性防水涂料及其制备方法,与传统的采用单一的高分子乳液改性的乳化沥青相比,本发明所述的复配乳化沥青,采用100号沥青、10号沥青两种不同标号的沥青复配,以让它们相互弥补不足,相得益彰。本发明复合高分子乳液改性的乳化沥青制得的防水涂料综合性能优良,抗拉强度高,延伸率大,粘结强度高,并且耐热性,低温柔性好。
本发明一种绿色环保多功能水性防水涂料及其制备方法,所述的复配乳化沥青,选用针入度小、延伸度大、脆点低、含蜡量少的石油沥青。
本发明一种绿色环保多功能水性防水涂料及其制备方法,沥青是原油蒸馏后的残渣,由于它在生产过程中曾经蒸馏至400℃以上,因而所含挥发成分甚少,但仍可能有高分子的碳氢化合物未经挥发出来,这些物质或多或少对人体健康是有害的,需要清洁处理。本发明采用沸石与蒙脱土作吸附剂,所述沸石,是一种含水的碱或碱土金属铝硅酸盐矿物,具有吸附性。所述蒙脱土,是一种硅酸盐的天然矿物,也具有很强的吸附能力。二者联合协同,增强吸附能力,最大限度吸附石油沥青中残存的未经挥发出来的少量碳氢化合物。因此,无污染,环境清洁。
本发明一种绿色环保多功能水性防水涂料及其制备方法,所述云母粉,是一种层状结构的硅酸盐,也是一种新型功能性绿色环保填料。云母具有弹性、韧性、耐高温、耐酸碱、耐腐蚀及附着力强的特点,独特的二维片状阻隔、屏蔽紫外光,有效地提高涂膜的抗渗透性、耐候性、隔热、防辐射、反光。
本发明一种绿色环保多功能水性防水涂料及其制备方法,所述铝粉,为银灰色的金属,由色浅、金属光泽高的铝制成。分散在载体内的铝粉发生漂浮运动,其运动的结果总是使自身与被载体涂装的底材平行,形成连续的铝粉层,而且这种铝粉层在载体膜内多层平行排列。各层铝粉之间的孔隙互相错开,切断了载体膜的毛细微孔,外界的水分、气体无法透过毛细孔到达底材,这种特点就是铝粉良好的物理屏蔽性。铝粉遮盖力强,能反射可见光、紫外光和红外光的60%-90%。
本发明一种绿色环保多功能水性防水涂料及其制备方法,所述铝粉,含铝粉的屋面乳液防水涂料,本身既具有防水功能,又对原有防水层起到保护作用,并能反射紫外线和太阳光,不但可降低房屋顶层的室内温度,节省空调费用,而且可以延长防水层的使用年限,目前已成为房屋建筑业选用的功能型防水涂料之一。
本发明一种绿色环保多功能水性防水涂料及其制备方法,经试验验证,开发与应用水性涂料,用水代替挥发性有机溶剂是当务之急。本发明常温施工,施工简便,生产安全,不污染环境,环境清洁,产品含固量高;对基材表面无苛刻要求,成膜性好,防水效果好,涂膜粘结强度大,抗拉强度高,延伸率大,耐热性与低温柔软性好,耐老化,使用寿命长,保温,隔热。
综上所述,本发明一种绿色环保多功能水性防水涂料及其制备方法,施工简便,生产安全,环境清洁,产品含固量高,成膜性好,防水效果好,抗拉强度高,延伸率大,涂膜粘结强度大,耐热性,低温柔软性好,耐老化,使用寿命长,保温,隔热。
具体实施方式
实施例1:
本发明一种绿色环保多功能水性防水涂料,包括复配乳化沥青、阳离子氯丁胶乳、复配胶乳、沸石、蒙脱土、云母粉、铝粉、增粘树脂;各组分质量百分数为:复配乳化沥青20%,阳离子氯丁胶乳25%,复配胶乳25%,沸石8%,蒙脱土8 %,云母粉4 %,铝粉4 %,增粘树脂6%。
本发明一种绿色环保多功能水性防水涂料,所述的复配乳化沥青,由质量百分数为40%的100号沥青,其余质量百分数为10号沥青制成。
本发明一种绿色环保多功能水性防水涂料,所述的阳离子氯丁胶乳,其固含量的质量百分数为55%。
本发明一种绿色环保多功能水性防水涂料,所述的复配胶乳,选择苯乙烯—丁二烯—苯乙烯嵌段共聚物SBS、丁苯橡胶SBR、丁腈橡胶NBR、三元乙丙橡胶EPDM或异戊二烯橡胶IR中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述增粘树脂,选择古隆马树脂、萜烯树脂或聚异丁烯树脂中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述的云母粉,其细度为325-500目。
本发明一种制造所述绿色环保多功能水性防水涂料的方法,按绿色环保多功能水性防水涂料所述的各组分质量百分数配制,首先,向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30-40分钟;然后,边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2-3小时,直至充分混合均匀,就制成一种绿色环保多功能水性防水涂料产品。
实施例2:
本发明一种绿色环保多功能水性防水涂料,包括复配乳化沥青、阳离子氯丁胶乳、复配胶乳、沸石、蒙脱土、云母粉、铝粉、增粘树脂;各组分质量百分数为:复配乳化沥青50%,阳离子氯丁胶乳10%,复配胶乳10%,沸石10%,蒙脱土10 %,云母粉4 %,铝粉4 %,增粘树脂2%。
本发明一种绿色环保多功能水性防水涂料,所述的复配乳化沥青,由质量百分数为70%的100号沥青,其余质量百分数为10号沥青制成。
本发明一种绿色环保多功能水性防水涂料,所述的阳离子氯丁胶乳,其固含量的质量百分数为55%。
本发明一种绿色环保多功能水性防水涂料,所述的复配胶乳,选择苯乙烯—丁二烯—苯乙烯嵌段共聚物SBS、丁苯橡胶SBR、丁腈橡胶NBR、三元乙丙橡胶EPDM或异戊二烯橡胶IR中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述增粘树脂,选择古隆马树脂、萜烯树脂或聚异丁烯树脂中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述的云母粉,其细度为325-500目。
本发明一种制造所述绿色环保多功能水性防水涂料的方法,按绿色环保多功能水性防水涂料所述的各组分质量百分数配制,首先,向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30-40分钟;然后,边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2-3小时,直至充分混合均匀,就制成一种绿色环保多功能水性防水涂料产品。
实施例3:
本发明一种绿色环保多功能水性防水涂料,包括复配乳化沥青、阳离子氯丁胶乳、复配胶乳、沸石、蒙脱土、云母粉、铝粉、增粘树脂;各组分质量百分数为:复配乳化沥青35%,阳离子氯丁胶乳21%,复配胶乳21%,沸石7%,蒙脱土7 %,云母粉3 %,铝粉3 %,增粘树脂3%。
本发明一种绿色环保多功能水性防水涂料,所述的复配乳化沥青,由质量百分数为55%的100号沥青,其余质量百分数为10号沥青制成。
本发明一种绿色环保多功能水性防水涂料,所述的阳离子氯丁胶乳,其固含量的质量百分数为55%。
本发明一种绿色环保多功能水性防水涂料,所述的复配胶乳,选择苯乙烯—丁二烯—苯乙烯嵌段共聚物SBS、丁苯橡胶SBR、丁腈橡胶NBR、三元乙丙橡胶EPDM或异戊二烯橡胶IR中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述增粘树脂,选择古隆马树脂、萜烯树脂或聚异丁烯树脂中的一种或多种组分制成。
本发明一种绿色环保多功能水性防水涂料,所述的云母粉,其细度为325-500目。
本发明一种制造所述绿色环保多功能水性防水涂料的方法,按绿色环保多功能水性防水涂料所述的各组分质量百分数配制,首先,向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30-40分钟;然后,边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2-3小时,直至充分混合均匀,就制成一种绿色环保多功能水性防水涂料产品。
本发明一种绿色环保多功能水性防水涂料及其制备方法,以上所述仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例揭露如上,然而并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案内容,依据本发明的技术实质,在本发明的精神和原则之内,对以上实施例所作的任何简单的修改、等同替换与改进等,均仍属于本发明技术方案的保护范围之内。
Claims (7)
1.一种绿色环保多功能水性防水涂料,其特征在于,包括复配乳化沥青、阳离子氯丁胶乳、复配胶乳、沸石、蒙脱土、云母粉、铝粉、增粘树脂;各组分质量百分数为:复配乳化沥青20-50%,阳离子氯丁胶乳10-30%,复配胶乳10-30%,沸石5-10%,蒙脱土5-10 %,云母粉2-4%,铝粉2-4 %,增粘树脂1-6%。
2.根据权利要求1所述的绿色环保多功能水性防水涂料,其特征在于,所述的复配乳化沥青,由质量百分数为40-70%的100号沥青,其余质量百分数为10号沥青制成。
3.根据权利要求1所述的绿色环保多功能水性防水涂料,其特征在于,所述的阳离子氯丁胶乳,其固含量的质量百分数为55%。
4.根据权利要求1所述的绿色环保多功能水性防水涂料,其特征在于,所述的复配胶乳,选择苯乙烯—丁二烯—苯乙烯嵌段共聚物SBS、丁苯橡胶SBR、丁腈橡胶NBR、三元乙丙橡胶EPDM或异戊二烯橡胶IR中的一种或多种组分制成。
5.根据权利要求1所述的绿色环保多功能水性防水涂料,其特征在于,所述增粘树脂,选择古隆马树脂、萜烯树脂或聚异丁烯树脂中的一种或多种组分制成。
6.根据权利要求1所述的绿色环保多功能水性防水涂料,其特征在于,所述的云母粉,其细度为325-500目。
7.一种制造权利要求1所述绿色环保多功能水性防水涂料的制备方法,其特征在于,按绿色环保多功能水性防水涂料所述的各组分质量百分数配制,首先,向所述组分质量百分数的复配乳化沥青中,加入所述组分质量百分数的阳离子氯丁胶乳、复配胶乳、增粘树脂,搅拌30-40分钟;然后,边搅拌、边加入所述组分质量百分数的沸石、蒙脱土、云母粉、铝粉,匀速搅拌2-3小时,直至充分混合均匀,就制成一种绿色环保多功能水性防水涂料产品。