CN113214789A - Novel sealing material for threaded pipe connection - Google Patents
Novel sealing material for threaded pipe connection Download PDFInfo
- Publication number
- CN113214789A CN113214789A CN202110600648.2A CN202110600648A CN113214789A CN 113214789 A CN113214789 A CN 113214789A CN 202110600648 A CN202110600648 A CN 202110600648A CN 113214789 A CN113214789 A CN 113214789A
- Authority
- CN
- China
- Prior art keywords
- parts
- threaded pipe
- sealing material
- pipe connection
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel threaded pipe connection sealing material which comprises a coating material and a coated material which are compounded with each other; the coating material comprises the following components in parts by weight: 10-50 parts of clay, 1-10 parts of cellulose, 10-50 parts of humectant, 10-40 parts of non-woven fabric, 5-30 parts of natural rubber, 0.1-1 part of bactericide and 0.1-1 part of performance regulator. The novel threaded pipe connection sealing material has the advantages that natural gum and clay are arranged as coating layer materials of main ingredients, so that the coating layer materials have the characteristic of being capable of swelling when meeting water, secondary sealing can be achieved, the sealing effect is better, cellulose and humectant which serve as ingredients are added into the coating layer materials, the coating layer materials are better in elasticity and stronger in viscosity, and the products are stronger in tearing and corrosion resistance due to the fact that the bactericide and the performance regulator are used.
Description
Technical Field
The invention belongs to the technical field of sealing materials at threaded joints of pipe materials, and particularly relates to a novel sealing material for threaded pipe connection.
Background
The pipes are common fluid transmission tools in buildings, the connection between the pipes generally adopts a threaded connection mode, and is a connection method used in water supply, heating, oil passages, compressed air and other pipelines.
The sealing materials in the market at present comprise: hemp thread, white and thick lacquer, raw material belt, anaerobic adhesive and the like. The hemp thread is the plant rhizome, has the longest application time and is the oldest sealing material. The technical defects are that the operation is complicated and the use technical requirement is high. The auxiliary product which consumes artificial white and thick paint as a sealing material is extremely high in material cost, time and labor are consumed, a sealing effect cannot be achieved when the auxiliary product is used alone, certain toxic and harmful substances exist, a raw material belt which is not easy to clean is a common sealing material in the current market, the pressure bearing performance of the raw material belt is general, the time consumed for winding one screw thread is extremely long, and the number of the 15-20 turns is 15-20. The anaerobic adhesive is a novel sealing material in the market in the year, has good sealing performance, can be pressed after waiting for more than 24 hours after being used, is convenient to install, is very difficult to disassemble and modify, and is easy to assemble and disassemble. Meanwhile, the threaded connection pipe cannot be stained with oil, the pipe needs to be wiped clean before use, otherwise, the glue does not react with the oil, and the sealing effect cannot be achieved. And the anaerobic adhesive only reacts on the metal piece and does not react with the plastic pipe fitting.
Disclosure of Invention
In view of the problems mentioned in the background, it is an object of the present invention to provide a novel sealing material for threaded pipe connections, which solves the problems mentioned in the background.
The technical purpose of the invention is realized by the following technical scheme:
a novel threaded pipe connection sealing material comprises a coating material and a coated material which are compounded with each other;
the coating material comprises the following components in parts by weight: 10-50 parts of clay, 1-10 parts of cellulose, 10-50 parts of humectant, 10-40 parts of non-woven fabric, 5-30 parts of natural rubber, 0.1-1 part of bactericide and 0.1-1 part of performance regulator.
Preferably, the clay includes one or more of montmorillonite, illite, kaolin, and water-aluminum-quartz-earth.
Preferably, the cellulose includes one or more of hydroxypropyl methylcellulose, hydroxyethyl cellulose, carboxymethyl cellulose, hydroxymethyl cellulose, and the like.
Preferably, the humectant comprises one or more of ethanol, ethylene glycol, propylene glycol, isopropanol, glycerol, butanediol and sorbitol.
Preferably, the natural gum includes one or more of acacia, guar gum, xanthan gum, gelatin and carrageenan.
Preferably, the non-woven fabric type comprises one or more of spunlace non-woven fabric, heat seal non-woven fabric, melt blown non-woven fabric and wet non-woven fabric.
Preferably, the bactericide comprises one or more of lime, copper sulfate, lime bordeaux mixture and copper hydroxide.
Preferably, the performance regulator comprises one or more of tea polyphenol, vitamin E and butyl hydroxy anisole.
The invention also provides a preparation method of the novel threaded pipe connection sealing material, which comprises the following steps:
step 1: taking the components of the coating material according to the formula, mixing and heating the clay, the cellulose, the humectant, the bactericide, the natural gum and the performance regulator to the normal temperature of 80 ℃, and then uniformly stirring to obtain the coating material;
step 2: uniformly coating the coating material on two sides of the coated material by using a coating machine, and then placing and airing or drying to obtain a composite material;
and step 3: and cutting the obtained composite material to a proper size, and then winding and bagging to obtain the novel threaded pipe connection sealing material.
Preferably, the temperature for natural airing or drying in the step 2 is 10 to 40 ℃.
In summary, the invention mainly has the following beneficial effects:
according to the novel threaded pipe connection sealing material, the coating layer material has the characteristic of swelling in water by setting the natural gum and the clay as the coating layer material of the main ingredients, so that secondary sealing can be performed, the sealing effect is better, the coating layer material is better in elasticity and stronger in viscosity by adding the cellulose and the humectant as the ingredients into the coating layer material, and the product is stronger in tearing corrosion resistance due to the use of the bactericide and the performance regulator. Still set up the material of being coated that is used for supplying coating material coating, and the material of being coated adopts the non-woven fabrics to make the holistic structural strength of sealing material more stable, the ability is stronger in the resistance to tearing, and life is longer.
Drawings
FIG. 1 is a block flow diagram of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
Referring to fig. 1, a novel sealing material for threaded pipe connection comprises a coating material and a coated material which are compounded with each other.
The coating material comprises the following components in parts by weight: 25 parts of montmorillonite, 10 parts of hydroxyethyl cellulose, 25 parts of ethylene glycol, 30 parts of spunlace nonwoven fabric, 9 parts of Arabic gum, 0.5 part of copper sulfate and 0.5 part of tea polyphenol. The coated material is spunlace nonwoven fabric, and the coating material is uniformly coated on the surface of the coated material and forms a double-layer composite structure with the coated material.
The non-woven fabric is formed by oriented or random fibers, has the characteristics of light weight, softness, water repellency and air permeability, and also has the characteristics of porosity, good air permeability, high temperature resistance and strong tensile resistance, and the coating layer material can be tightly bonded with the non-woven fabric and is firmly connected.
Then preparing the novel threaded pipe connecting sealing material according to the following steps:
step 1: according to the formula, 25 parts of montmorillonite, 10 parts of hydroxyethyl cellulose, 25 parts of ethylene glycol, 30 parts of spunlace non-woven fabric, 9 parts of Arabic gum, 0.5 part of copper sulfate and 0.5 part of tea polyphenol are added into a container, heated to 80 ℃, and stirred uniformly to obtain the coating material.
Step 2: and uniformly coating the coating layer material on the coated material by adopting a coating machine, and then heating and baking at the temperature of 40-80 ℃ to obtain the composite material.
And step 3: cutting the obtained composite material into required size, and then winding to obtain the novel threaded pipe connection sealing material.
The novel threaded pipe connecting sealing material can achieve an all-dimensional sealing effect, the coating layer has the characteristic of water swelling, the effect of sealing twice can be achieved, the product using method is simple, the national standard 4-6 tapping needs 2-3 circles to bear the pressure of more than 20KG, the novel threaded pipe connecting sealing material can be applied to fire fighting, acid-base solution, oil ways, compressed air and natural gas pipeline transmission, and the material is non-toxic, environment-friendly, degradable and edible. The sealing tape made of the novel threaded pipe connecting sealing material is 8-12 times as efficient as a common raw material tape in the market, solves the problem that the anaerobic adhesive does not react with an oil medium, is suitable for the wire connection of various materials, can be immediately pressed and delivered after being used, and solves the problem that the anaerobic adhesive can be pressed after 24-48 hours. Solves the problems of difficult use, unattractive appearance, difficult use technique and the like of the hemp thread.
Example 2
The embodiment provides a technical scheme: a novel sealing material for threaded pipe connection comprises a coating layer material and a coating material which are compounded with each other.
The coating material comprises the following components in parts by weight: 25 parts of illite, 10 parts of hydroxypropyl methyl cellulose, 15 parts of ethanol, 10 parts of propylene glycol, 30 parts of hydrothermal non-woven fabric, 9 parts of guar gum, 0.5 part of calbodol solution and 0.5 part of butyl hydroxy anisol. The coated material is a hydrothermal non-woven fabric, and the coating material is uniformly coated on the surface of the coated material and forms a double-layer composite structure with the coated material.
The non-woven fabric is formed by oriented or random fibers, has the characteristics of light weight, softness, water repellency and air permeability, and also has the characteristics of porosity, good air permeability, high temperature resistance and strong tensile resistance, and the coating layer material can be tightly bonded with the non-woven fabric and is firmly connected.
Then preparing the novel threaded pipe connecting sealing material according to the following steps:
step 1: according to the formula, 25 parts of illite, 10 parts of hydroxypropyl methyl cellulose, 15 parts of ethanol, 10 parts of propylene glycol, 30 parts of hydrothermal bonded nonwoven fabric, 9 parts of guar gum, 0.5 part of calbodol liquid and 0.5 part of butyl hydroxy anisol are measured. Then adding the mixture into a container, heating to 50 ℃, and uniformly stirring to obtain the coating material.
Step 2: and uniformly coating the coating layer material on the coated material by using a coating machine, and then placing the coated material at room temperature for 2-3 days to obtain the composite material.
And step 3: cutting the obtained composite material into required size, and then winding to obtain the novel threaded pipe connection sealing material.
Example 3
The embodiment provides a technical scheme: a novel sealing material for threaded pipe connection comprises a coating layer material and a coating material which are compounded with each other.
The coating material comprises the following components in parts by weight: 25 parts of kaolin, 10 parts of carboxymethyl cellulose, 25 parts of isopropanol, 30 parts of hydrothermal bonded nonwoven fabric, 9 parts of xanthan gum, 0.5 part of lime boldo liquid and 0.5 part of butyl hydroxy anisol.
The non-woven fabric is formed by oriented or random fibers, has the characteristics of light weight, softness, water repellency and air permeability, and also has the characteristics of porosity, good air permeability, high temperature resistance and strong tensile resistance, and the coating layer material can be tightly bonded with the non-woven fabric and is firmly connected.
Then preparing the novel threaded pipe connecting sealing material according to the following steps:
step 1: weighing 25 parts of kaolin, 10 parts of carboxymethyl cellulose, 25 parts of isopropanol, 9 parts of xanthan gum, 0.5 part of lime boldo liquid and 0.5 part of butyl hydroxy anisol according to a formula, adding into a container, heating to 80 ℃, and uniformly stirring to obtain the coating material.
Step 2: and uniformly coating the coating layer material on the coated material by adopting a coating machine, and then heating and baking at the temperature of 40-80 ℃ to obtain the composite material.
And step 3: cutting the obtained composite material into required size, and then winding to obtain the novel threaded pipe connection sealing material.
Example 4
The embodiment provides a technical scheme: a novel sealing material for threaded pipe connection comprises a coating layer material and a coating material which are compounded with each other.
The coating material comprises the following components in parts by weight: 25 parts of water-alumina-kaolin, 10 parts of hydroxymethyl cellulose, 15 parts of isopropanol, 10 parts of propylene glycol, 30 parts of melt-blown non-woven fabric, 9 parts of gelatin, 0.5 part of lime bordeaux liquid and 0.5 part of butyl hydroxy anisol.
The melt-blown non-woven fabric is formed by oriented or random fibers, has the characteristics of light weight, softness, water repellency and air permeability, and also has the characteristics of porosity, good air permeability, high temperature resistance and strong tensile resistance, and the coating layer material can be tightly bonded with the non-woven fabric and is firmly connected.
Then preparing the novel threaded pipe connecting sealing material according to the following steps:
step 1: according to the formula, 25 parts of water-alumina-bentonite, 10 parts of hydroxymethyl cellulose, 15 parts of isopropanol, 10 parts of propylene glycol, 9 parts of gelatin, 0.5 part of lime bordeaux liquid and 0.5 part of butyl hydroxy anisol are added into a container, heated to 55 ℃, and stirred uniformly to obtain the coating material.
Step 2: and uniformly coating the coating layer material on the coated material by adopting a coating machine, and then heating and baking at the temperature of between normal temperature and 80 ℃ to obtain the composite material.
And step 3: cutting the obtained composite material into required size, and then winding to obtain the novel threaded pipe connection sealing material.
Example 5
The embodiment provides a technical scheme: a novel sealing material for threaded pipe connection comprises a coating layer material and a coating material which are compounded with each other.
The coating material comprises the following components in parts by weight: 10 parts of montmorillonite, 15 parts of water-alumina-bentonite, 10 parts of hydroxymethyl cellulose, 15 parts of isopropanol, 10 parts of ethanol, 30 parts of melt-blown non-woven fabric, 9 parts of carrageenan, 0.5 part of lime polo liquid and 0.5 part of butyl hydroxy anisole.
The melt-blown non-woven fabric is formed by oriented or random fibers, has the characteristics of light weight, softness, water repellency and air permeability, and also has the characteristics of porosity, good air permeability, high temperature resistance and strong tensile resistance, and the coating layer material can be tightly bonded with the non-woven fabric and is firmly connected.
Then preparing the novel threaded pipe connecting sealing material according to the following steps:
step 1: according to the formula, 10 parts of montmorillonite, 15 parts of water-aluminum-kaolin, 10 parts of hydroxymethyl cellulose, 15 parts of isopropanol, 10 parts of ethanol, 9 parts of carrageenan, 0.5 part of lime Bordeaux mixture and 0.5 part of butyl hydroxy anisole are measured, then the mixture is added into a container, heated to 55 ℃, and stirred uniformly to obtain the coating material.
Step 2: and uniformly coating the coating layer material on the coated material by adopting a coating machine, and then heating and baking at the temperature of between normal temperature and 80 ℃ to obtain the composite material.
And step 3: cutting the obtained composite material into required size, and then winding to obtain the novel threaded pipe connection sealing material.
In order to perform performance tests on the novel threaded pipe connection sealing material, the following experiments are performed, and the experiment contents are as follows:
selecting a novel threaded pipe connecting sealing material generated in the market as a comparison group, and selecting the novel threaded pipe connecting sealing materials in the embodiments 1, 2, 3, 4 and 4 as an experimental group for experiment;
experiment 1:
testing the water-swelling degree, namely placing a comparison group, example 1, example 2, example 3, example 4 and example 5 in water for 10min to test the water-swelling degree, wherein the ratio of the water-swelling degrees of the comparison group, example 1, example 2, example 3, example 4 and example 5 is 1: 1.3: 1.4: 1.6: 1.1: 1.2.
experiment 2:
elasticity test, the elasticity of the control group, example 1, example 2, example 3, example 4, example 5 was tested using an elasticity tester, wherein the elasticity ratio of the control group, example 1, example 2, example 3, example 4, example 5 was 1: 1.6: 1.7: 1.9: 1.3: 1.2.
experiment 3:
tear resistance test a control, example 1, example 2, example 3, example 4, example 5 was tested with a tear tester, wherein the ratio of the breaking strength of the control, example 1, example 2, example 3, example 4, example 5 was 1: 2: 2.1: 2.3: 1.9: 1.7.
experiment 4:
and (3) testing the corrosion resistance by putting a control group, an example 1, an example 2, an example 3, an example 4 and an example 5 into a 5% sulfuric acid solution, wherein the ratio of the corrosion resistance of the control group, the example 1, the example 2, the example 3, the example 4 and the example 5 is 1: 2: 2.3: 2.5: 1.8: 1.7, wherein the corrosion resistance is measured predominantly as volume after corrosion consumption.
In conclusion, the novel threaded pipe connection sealing material provided by the invention has the advantages that the natural rubber and the clay are used as coating layer materials of main ingredients, so that the coating layer materials have the characteristic of swelling in water, secondary sealing can be realized, the sealing effect is better, the cellulose and the humectant are added into the coating layer materials as ingredients, so that the coating layer materials are better in elasticity and stronger in viscosity, and the tearing and corrosion resistance of products is stronger due to the use of the bactericide and the performance regulator. Still set up the material of being coated that is used for supplying coating material coating, and the material of being coated adopts the non-woven fabrics to make the holistic structural strength of sealing material more stable, the ability is stronger in the resistance to tearing, and life is longer.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (10)
1. The utility model provides a novel screwed pipe connects sealing material which characterized in that: comprises a coating material and a coated material which are mutually compounded;
the coating material comprises the following components in parts by weight: 10-50 parts of clay, 1-10 parts of cellulose, 10-50 parts of humectant, 10-40 parts of non-woven fabric, 5-30 parts of natural rubber, 0.1-1 part of bactericide and 0.1-1 part of performance regulator.
2. The novel threaded pipe connection sealing material of claim 1, wherein: the clay comprises one or more of montmorillonite, illite, kaolin and water-aluminum-quartz soil.
3. The novel threaded pipe connection sealing material of claim 1, wherein: the cellulose comprises one or more of hydroxypropyl methyl cellulose, hydroxyethyl cellulose, carboxymethyl cellulose, hydroxymethyl cellulose and the like.
4. The novel threaded pipe connection sealing material of claim 1, wherein: the humectant comprises one or more of ethanol, ethylene glycol, propylene glycol, isopropanol, glycerol, butanediol and sorbitol.
5. The novel threaded pipe connection sealing material of claim 1, wherein: the natural gum comprises one or more of acacia, guar gum, xanthan gum, gelatin and carrageenan.
6. The novel threaded pipe connection sealing material of claim 1, wherein: the non-woven fabric types comprise one or more of spunlace non-woven fabrics, heat seal non-woven fabrics, melt-blown non-woven fabrics and wet non-woven fabrics.
7. The novel threaded pipe connection sealing material of claim 1, wherein: the bactericide comprises one or more of lime bordeaux mixture, copper sulfate, lime bordeaux mixture and copper hydroxide.
8. The novel threaded pipe connection sealing material of claim 1, wherein: the performance regulator comprises one or more of tea polyphenol, vitamin E and butyl hydroxy anisole.
9. A preparation method of a novel threaded pipe connection sealing material is characterized by comprising the following steps: the method specifically comprises the following steps:
step 1: taking the components of the coating material according to the formula, mixing and heating the clay, the cellulose, the humectant, the bactericide, the natural gum and the performance regulator to the normal temperature of 80 ℃, and then uniformly stirring to obtain the coating material;
step 2: uniformly coating the coating material on two sides of the coated material by using a coating machine, and then placing and airing or drying to obtain a composite material;
and step 3: and cutting the obtained composite material to a proper size, and then winding and bagging to obtain the novel threaded pipe connection sealing material.
10. The method for preparing the novel threaded pipe connection sealing material as claimed in claim 9, wherein: and (3) naturally airing or drying at the temperature of 10-40 ℃ in the step (2).