CN1131602A - Cutter for cast iron cut-off - Google Patents
Cutter for cast iron cut-off Download PDFInfo
- Publication number
- CN1131602A CN1131602A CN 95100441 CN95100441A CN1131602A CN 1131602 A CN1131602 A CN 1131602A CN 95100441 CN95100441 CN 95100441 CN 95100441 A CN95100441 A CN 95100441A CN 1131602 A CN1131602 A CN 1131602A
- Authority
- CN
- China
- Prior art keywords
- abrasive particle
- abrasive
- base plate
- mentioned
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A cutting tool using for cutting iron casting. Abrasives consisting of diamond particles or particles of cubic boron nitride are electrodeposited on a cutting edge formed at the end face of the outer periphery of a disc-shaped base, and a main abrasive portion that works in cutting and an auxiliary abrasive portion having grain sizes no greater than the average grain size of the main abrasives are alternately placed at approximately equal intervals along the circumferential direction of the base. On both sides of the disc-shaped base, abrasive regions are geometrically arranged and dispersed throughout the exposed portion of each base side face between the cutting edge and a tightening portion, and the abrasives in the regions are electrodeposited by mixing diamonds of diameters or not greater than the cutting-edge abrasive grain size with Al2 O3 , SiO2 , ZnO2 , all of with are hard oxides. Further, the disc-shaped base is made of an Fe-Ni or Fe-Ni-Co alloy.
Description
The present invention relates to the cutter that a kind of foundry goods cuts off usefulness, especially a kind ofly can be used for the cutter that the foundry goods that includes iron casting ductility, malleable cast iron, ductile iron pipe etc. that the cutting machine structure uses cuts off usefulness preferably.
The castings production factory of blank is being provided, in the subsequent handling after casting with unwanted rising head on the blank, the interior manufacturing procedure of cutting off and removing around mouth etc., be the emery wheel that cuts off usefulness to be installed on hand held, electric machine or the empty dynamic formula instrument carry out operation.Especially recent years, in order to improve abominable operating environment and to cut down the machining period expense, all numerous and confused the use cut off special machine automatically.
No matter be method mechanical means by hand, in this cut-out processing, generally all use so-called resin-bonded emery wheel.Generally, this emery wheel is with bonding agents such as phenolic resins the aluminium oxide of fusion and carborundum hard abrasive to be consolidated, and strengthen with fibrous matter.This resin-bonded emery wheel has bigger plasticity and can bear higher peripheral speed, but wearing and tearing along with hard abrasive, can be because of the heating burning of resin used in the bonding agent, make it produce dust and stench, thereby for operating environment and safety and sanitation, must not be called good emery wheel to it.
And, at the management aspect that cuts off manufacturing procedure, also can be along with the wearing and tearing of emery wheel, its diameter diminishes and peripheral speed is descended, thereby makes the working (machining) efficiency variation, therefore just has to change continually emery wheel.Especially when cutting off automatically,, also do not develop this more suitable emery wheel so far although people urgently wish to have a kind of emery wheel that can need not change in a long time, can cut off always.
Under the technical background situation of this reality, often the blade of the abrasive particle sintering of metal dust is attached to the so-called combined type diamond cutter on the base plate, perhaps electroformed abrasive grain is deposited on and cuts off processing and common foundry goods in the general road construction of partly migrating such as diamond cutter of the continuous wheel rim shape on the discoideus base plate and cut off and process.
But rising head etc. is removed processing on the foundry goods, owing to exist problems such as the oxidation of the loss of the casting sand factory in and section or blank get rusty, thereby, not under the environment of wet type, to carry out generally, but carry out the dry type cut-out.Like this, above-mentioned cutter migrated simply just can not make the effect of diamond self be brought into play effectively, and, even the cutter of electro-deposition also need not be used adamantine sandwich construction.Therefore, the diamond abrasive grain on the blade is played a role effectively, should be that what kind of structure could work long hours effectively actually, a problem that has just become the present invention to solve.
Though it is more that electro-deposition type diamond cutter has the exposed portions serve of diamond abrasive grain, thermal diffusivity is better, characteristics such as wear and tear and the life-span is long less, but because abrasive particle shape and particle diameter are not necessarily, the effective knife edge part that works when high speed rotary is less, thereby often begin its sharpness when using and just reduce gradually, generation along with frictional heat when dry type is cut off and simple wearing and tearing, the abrasive particle cutting edge is polished, generally, in the limit of the output horizontal bar in the front of a carriage used as an armrest rate of hand held, electric machine commonly used and people's thrust, though also be less than the life span of use, do not had effective abrasive particle.
Again because complicated as the foundry goods shape of cutting off object, no matter be artificial or mechanical method, the side of discoideus base plate always contacts with foundry goods and high speed rotary, thereby cause local pyrexia with contacting of foundry goods by base plate, can suddenly sharply cause bottom deformation and metal fatigue, form breakneck operating environment easily.
The purpose of this invention is to provide the cutter that a kind of foundry goods cuts off usefulness, it can solve the problem that prior art that foundry goods cuts off the emery wheel of usefulness exists, and can satisfy following requirement again.
(1) because the blade part of former electro-deposition cutter, be that the abrasive particle with practical mesh particle size range is fixed on the whole plectane outer peripheral edges, thereby when continuing to use, under the also remaining state of blade part abrasive particle, instrument has reached its end of life.No matter the present invention is in machinery or artificial cutting-off method if then requiring, can both make sharpness than better in the past, and cutter life is prolonged.
(2) can solve when foundry goods cuts off irregular cut-out campaign such as base plate deflection that forms along with the inclination on workpiece in the process and chassis or by thrust and make workpiece and base plate contacts side surfaces and problem on the safety that causes can be carried out safety work.
(3) produce in the time of preventing to cut off foundry goods, cut off the deflection of accumulating the discoideus base plate that causes that thermal expansion causes of heat and contacts side surfaces wearing and tearing heat by the dry type of the blade part of plectane outer peripheral edges, can make the emery wheel of safer cut-out usefulness.
As follows in order to solve the main points of the present invention that above-mentioned problem done.
(1) the present invention is a kind of like this foundry goods cut-out cutter; promptly the electroformed abrasive grain of diamond particles or cubic crystal boron nitride (CBN) particle formation is deposited on the outer circumference surface of discoideus base plate; form blade part and cut off at foundry goods on the cutter of usefulness with this blade part, the main abrasive particle portion of a cutting action and than the little secondary abrasive particle portion of main abrasive particle average grain diameter along the circumferential direction, alternately roughly the electro-deposition of five equilibrium ground on the blade of cutter.
(2) cutter of the present invention is the abrasive particle particle diameter of size ratio blade part little diamond and Al
2O
3, SiO
2Or ZrO
2The abrasive particle zone of mixing the back electro-deposition Deng the hardening oxidation thing is configured on the blade part and the whole base plate side exposed portions serve between the fastening part on the discoideus base plate two sides dispersedly.
(3) the discoideus base plate of cutter of the present invention is made of Fe-Ni alloy or FE-Ni-Co alloy.
Foundry goods of the present invention with said structure cuts off with cutter and can play following effect.
(1) since make main abrasive particle portion and secondary abrasive particle portion along the circumferential direction, roughly five equilibrium ground alternately alignment arrangements on the blade part of base plate outer circumference surface, make that to produce section between the size particles of main abrasive particle portion and secondary abrasive particle portion poor, thereby when cutting, can in the stress of accepting big cutting and little cutting stress, whole blade part one after the other be worked.
Promptly, the inventor finds, when beginning to cut, owing to the effect that multiplies each other that the shear action and the impact cutting harm of object to be processed are used, big cutting stress by main abrasive particle portion forms sharpness preferably, along with the wearing and tearing and the damage of blade cutting edge, the applied stress of secondary abrasive particle portion just improves constantly, and therefore whole blade part is all worked effectively.
As a result, the blade cutting edge demonstrates effective function, compares with former simple electro-deposition cutter, can finish a lot of workload.In addition, though all be called foundry goods simply, can be according to the material of foundry goods, arrange for how much that change main abrasive particle portion and secondary abrasive particle portion, for example when the diamond electro-deposition ratio of main abrasive particle portion improves, just can make the durability raising of cutter, demonstrate the distinctive significance of material.
(2) when joining, just work in the minor diameter abrasive particle zone that is configured in the electro-deposition on the base plate side dispersedly when the base plate side of high speed rotary and workpiece (as the foundry goods that cuts off object).At this moment, prevent unthinkable base plate damage that the contact wear heat because of base plate and workpiece causes and the metal fatigue that brings out thus by the electro-deposition abrasive particle zone of base plate side.
Found that because the hard particles of electro-deposition and blade part different, its purpose has not been positive shear action, thereby usefulness diamond at high price only, cheap hardening oxidation thing Al
2O
3, SiO
2, ZrO
2Mix use Deng particle and also do not have any influence.
(3) when processed to as if during iron casting, because accumulating of heat in metal cutting, the heating-up temperature skewness of discoideus base plate and thermal expansion different, can cause vertical deflection of base plate, it becomes the difficulty except meeting makes continuous operation, also can produce bigger reaction force, just can not guarantee safe handling machined object.But, FE-Ni alloy or Fe-Ni-Co alloy are used as baseboard material, owing to linear expansion coefficient any in the above-mentioned alloy is all minimum, therefore just above-mentioned skewness can not take place, can continue to carry out high speed rotation cut-out for a long time.
Below, will be explained in detail the present invention in conjunction with the accompanying drawings, in the accompanying drawing:
Fig. 1 is that expression foundry goods of the present invention cuts off the embodiment side view with cutter;
Fig. 2 is the schematic diagram of the roughly dynamic relationship of the state of the expression abrasive particle of electro-deposition on the outer circumference surface of Fig. 1 and its applied stress;
Fig. 3 is the I-I sectional drawing of Fig. 1;
Fig. 4 is the graph of relation between the accumulation workload of the change of that expression is made by the comparative experiments of present embodiment and former example, explanation load current and cut-out.
Below, with reference to accompanying drawing embodiments of the invention are described.
As shown in drawings, electro-deposition one deck abrasive grain layer on foundry goods cuts off with cutter 1, on the periphery of discoideus base plate 2 and the blade part 3 that forms, be the secondary abrasive particle B of portion that constitutes the main abrasive particle A of portion that constitutes by the major diameter abrasive particle with by the minor diameter abrasive particle along the circumferencial direction of base plate 2, alternately arrange ground and be provided with.The abrasive particle of blade part 3, use be the boron nitride particle (CBN) of diamond particles or cubic crystal, the abrasive particle particle diameter of the wherein secondary abrasive particle B of portion is less than the average grain diameter of the main abrasive particle A of portion.
In addition, on two sides of present embodiment cutter 1, on the whole side between the fastening part 4 of blade part 3 and plectane central authorities, all be geometric figure ground decentralized configuration and electro-deposition abrasive particle district 5.The abrasive particle in these electro-deposition districts 5 adopts the little hard particles of abrasive particle of size ratio blade part 3, and diamond particles and Al
2O
3Or SiO
2Or ZrO
2Roughly is mixed that the back fixes in each half ground Deng the hardening oxidation thing.
Found the not directly effect of cut-out of the 5 pairs of blade parts 3 in electro-deposition abrasive particle district of base plate side, be used for suppressing base plate damage and frictional resistance, therefore need not be specially with diamond particles at high price, when reality is used, consideration reduces cost, and can suitably dispose electro-deposition abrasive particle district 5.Especially add man-hour in the cut-out of tilting with automatic cutting off table etc., can be according to practical situation with electro-deposition abrasive particle district 5 decentralized configuration.
In order to prevent the deflection of discoideus base plate 2 when the high speed rotary, the discoideus base plate 2 of present embodiment is that it is made of Fe-Ni alloy or Fe-Ni-Co alloy with the low material of thermal coefficient of expansion.For example, use the invar of Ni36.5%, Fe63.5% or with the superinvar of Ni32%, Co50%, Fe63%.
Below, the effect of present embodiment is described.
Explanation earlier the different main abrasive particle A of portion of particle diameter and the secondary abrasive particle B of portion roughly five equilibrium, alternately be configured in effect on the base plate outer circumference surface.
When the small diameter particles of the major diameter particle of the main abrasive particle A of portion and the secondary abrasive particle B of portion is carried out stock removal action, owing to bear the shear action and the effect that multiplies each other of impacting the breakage effect that causes of big cutting stress and little cutting stress, make the initial stage sharpness of cutter better, make such shear action continue to keep then, whole blade part is all worked effectively.
Proof as cutting-off method artificial or machinery, all is to pass under the state that can fully cut off in actual use thus.As shown in Figure 2, the particle that the secondary abrasive particle B of portion does not present the such degree of the main abrasive particle A of portion damages by pressure, and the result compared with former the sort of simple electro-deposition cutter, had but finished a lot of workload.In addition, also recognize, although all be called foundry goods simply, can be according to the difference of castings material, to arrange for how much that change main abrasive particle A of portion and the secondary abrasive particle B of portion, the diamond electro-deposition ratio that for example the changes abrasive particle portion then durability of cutter also can change.
Existing general deposited Au diamond cutter be the abrasive particle of roughly the same particle diameter as the blade cutting edge, circumferentially fixing along whole base plate outer circumference surface.Although this cutter has the effect of certain cut-out foundry goods, but carrying out portable or mechanical type when cutting off, just the initial stage sharpness is better, As time goes on just wearing and tearing gradually of the cutting edge of blade hard particles, it is plane that grain shape is, make all abrasive particles all be same modality, thereby cause that sharpness descends.In addition, the cutting action power of emery wheel is also limited, is being called the terminal stage in life-span, and the particle that has effective cutting edge during electro-deposition all becomes more blunt plane and stay surplus.
Usually, during the cut-out of the non-metal kind beyond carrying out foundry goods, because of the fixedly wearing and tearing of the bond of hard particles (nickel coating etc.), the obscission of the diamond particles of appropriateness can take place, but then almost can't see the wearing and tearing of bond when cutting off foundry goods.These experimental samples being carried out the result of experiment in service life of adamantine cumulative attrition state finds, especially recently, when cutting off automatically, because subject impetus is to adopt high power output prime mover in design, therefore can provide sufficient cut-out power, thereby be under the situation of same practical particle size range at the blade part abrasive particle, under a certain rated load electric current, just can bring out heating and sharpness decline phenomenon tempestuously, the life-span is influenced.
To all adding roughly the same a certain stable stress between the particle of whole electro-deposition, carrying out result of experiment after respectively the main abrasive particle A of portion that designated size is arranged and the secondary abrasive particle B of portion equally spaced being arranged shows, when certain cutting edge wearing and tearing are arranged, because the impact breakage that when foundry goods cuts off, forms, though better every arranging sharpness with the simple empty standard width of a room in an old-style house, durability has problem.
The present invention makes through these experiments and based on experimental result, its objective is almost whole particles of main abrasive particle A of portion and the secondary abrasive particle B of portion are all worked effectively, and its durability is improved.Shown in the A of Fig. 2, the roughly dynamic relationship figure of applied stress on the B groups of grains, owing to be added in the A groups of grains A of main abrasive particle portion
1～A
nB groups of grains B with secondary abrasive particle portion
1～B
nOn applied stress variant, thereby can make the initial stage sharpness of cutter better, and by with the effect that multiplies each other of impacting damaged effect, can make all effects effectively of cutting edge of all abrasive particles, thereby cutter life is prolonged.
Thus, descending gradually along with the passing of service time though found the initial stage sharpness, as artificial or mechanical cutting method, all is to pass under the state that can fully cut off during actual the use; Although and the particle that the B groups of grains that has proved secondary abrasive particle portion does not present the such degree of the main abrasive particle A of portion damages phenomenon by pressure, its result compared with former simple electro-deposition cutter, but can improve workload greatly; And recognize, although all be called foundry goods simply, can change how much arrangements of A, B groups of grains according to the difference of castings material, can make the characteristic of cutter that significant variation is arranged like this.
(2) the following describes, the electro-deposition zone 5 decentralized configuration role on whole base plate side that constitutes by the diameter abrasive particle littler than the particle of blade part 3.
When supplying blank, under the occasions such as the casting pressing port that cuts off and form when removing casting with the method for artificial or machinery, cast gate, ingate, the base plate side of high speed rotary is under the state that contacts with foundry goods, at this moment, substrate damage and compulsory metal fatigue can have been brought out unawares owing to base plate and as the contact wear heat between the workpiece of cutting object.
Present embodiment on the two sides of base plate, makes base plate and workpiece form the abrasive particle zone 5 of how much distribution shapes non-contiguously in order further to improve the security of cutter when cutter turns round.And find since electro-deposition to remain on purpose and the blade part of hard particles in 5 li in zone different, be not main cutting action, thereby only use diamond at high price can be cheap hardening oxidation thing Al for example as abrasive particle
2O
3, SiO
2, ZrO
2Mix with diamond abrasive grain, roughly to wait part by weight Deng abrasive particle, electro-deposition zone 5 is disperseed and be fixed on the base plate side, can not produce any influence to cutting off like this.
(3) below, baseboard material Ni-Fe alloy or Fe-Ni-Co alloy role are described.
Foundry goods cuts off the cutter of usefulness, even the electroformed abrasive grain of diamond or CBN is deposited on the blade part of cutter outer peripheral edges, still can make the heating of base plate outer peripheral edges portion owing to the dry type cut-out of high speed rotary.
Different in nonmetallic materials such as processed object and general stone, construction material, concrete, and the baseboard material that often uses is when being tool steel or steel alloy again, because heat in metal cutting is put aside, cause discoideus base plate thermal expansion, and bring out vertical skewness of base plate, so that make the violent vibrations of generation such as hand held, electric machine, thereby be difficult to proceed operation.In addition, also quite big to the reaction force of machined object, can form the state that can not use safely.
But, the material of available low thermal coefficient of expansion is made baseboard material, for example adopts Fe-Ni alloy or Fe-Ni-Co alloy material, because their thermal coefficient of expansion is minimum, deflection just can not take place in above-mentioned cutting off tool, just can continue to carry out high speed rotary for a long time and cut off processing.
Below, experimental example of the present invention is described.
Cutter of the present invention shown in Figure 1 is used as sample (A), blade part fifty-fifty only the example of the prior art of fixing identical practical granularity as a comparison the cutter of usefulness be sample (B), and make to cut off the cutter that the large-scale camshaft ingate of automobile uses and be installed in and carry out comparative test on the automatic cutting off table body.
Specification is
Tool dimension: φ 455 (external diameter) * 2.5t (base plate is thick) mm
Baseboard material: 63.5%Fe-36.5%Ni alloy
The driving power of prime mover output: 9KW
Revolution: 2200rpm
Cut workpiece: camshaft (Fc300)
Cut off the basal area shape of (ingate): φ 30mm
Feed velocity: 2.0mm/sec when cutting off automatically
The time of a circulation: 40sec
The diamond of sample (A) blade part:
The main abrasive particle A:35/45 of portion
#(500～350 μ)
The secondary abrasive particle B:40/45 of portion
#(420～297 μ)
The electro-deposition abrasive particle zone of side:
Al2O3 (60/80
#) and diamond (60/80
#) (weight ratio: 1/1)
The diamond of the blade part of sample (B): 40/45
#
The electro-deposition abrasive particle zone of side:
Al
2O
3(60/80
#) and diamond (60/80
#) (weight ratio: 1/1)
# wherein represents the U.S mesh.
Fig. 4 represents this result of experiment.This figure is the change of expression load current and cuts off the curve map that concerns between the accumulation workload, the electric current of no load condition (during idle running) is 13 amperes, 10 of every cut-outs, load current value (minimum～maximum), 35 amperes of rated current as maximum, and with it as the terminal point in service life.As follows with the radical that sample (A) and sample (B) are handled:
Sample (A): 14800 of the radicals of processing
Sample (B): 9020 of the radicals of processing
As mentioned above, the life-span of cutter of the present invention (A) is 1.7 times so big of cutter (B) of usefulness.This is because in cutter of the present invention, the different results that make it bring into play effective shear action of granularity of main abrasive particle portion and secondary abrasive particle portion.
Like this, present embodiment has solved foundry goods and has cut off the existing in prior technology problem of the emery wheel of usefulness, the foundry goods of present embodiment cuts off uses cutter, with existing whole plectane outer peripheral edges all fifty-fifty the cutter of fastening abrasive particle compare, when continuing to use, no matter machinery or in artificial cutting-off method, all better sharpness is arranged than existing cutter, the life-span is prolonged.
In addition, present embodiment can prevent when cutting off foundry goods, workpiece contacted and the fault that produces with the base plate side along with the inclination on workpiece in the processing or chassis or by the irregular cut-out campaigns such as base plate deflection that thrust forms, and processing can be carried out safely.The dry type of the blade part of the plectane outer peripheral edges that can also prevent from when being breaking at foundry goods to be produced is cut off the deflection of the hot discoideus base plate of accumulating, being caused by thermal expansion of heat and contacts side surfaces wearing and tearing, can make the emery wheel of the higher cut-out usefulness of security.
As mentioned above, the present invention can provide a kind of foundry goods to cut off and use cutter, when it provides blanks such as iron casting that frame for movement uses, ductile cast iron pipe, relevant with the manufacturing procedure of rising head, cast gate, ingate etc. after cut off removing casting, can be installed in and cut off easily on the hand held, electric machine, also can be installed on the automatic cut-out special machine, carry out preferably that continuous dry type cuts off.
Claims (9)
1, the helicoid foundry goods of a kind of plectane cuts off and uses cutter, it is characterized in that on the outer circumference surface of discoideus base plate electro-deposition one deck abrasive grain layer and form blade part; Above-mentioned abrasive grain layer is that the secondary abrasive particle portion that main abrasive particle portion that the major diameter abrasive particle is constituted and minor diameter abrasive particle constitute alternately arranges along the circumferencial direction of base plate.
2, foundry goods as claimed in claim 1 cuts off and uses cutter, it is characterized in that above-mentioned blade part has the abrasive particle of 30～50 meshes, and the abrasive particle particle diameter of above-mentioned secondary abrasive particle portion is below the average grain diameter of above-mentioned main abrasive particle portion abrasive particle.
3, foundry goods as claimed in claim 1 cuts off and uses cutter, it is characterized in that the abrasive particle of above-mentioned blade part is made of diamond particles or cubic crystal boron nitride particle.
4, foundry goods as claimed in claim 1 cuts off and uses cutter, it is characterized in that above-mentioned discoideus base plate is that Fe-Ni alloy or Fe-Ni-Co alloy by the low thermal coefficient of expansion material constitutes.
5, foundry goods as claimed in claim 1 cuts off and uses cutter, it is characterized in that above-mentioned discoideus base plate is disposing electro-deposition abrasive particle zone dispersedly between the fastening part of above-mentioned blade part and plectane central authorities.
6, foundry goods as claimed in claim 5 cuts off and uses cutter, it is characterized in that the abrasive particle particle diameter in the electro-deposition abrasive particle zone that disposing dispersedly on the side of above-mentioned discoideus base plate is below the abrasive particle particle diameter of blade part.
7, foundry goods as claimed in claim 5 cuts off and uses cutter, it is characterized in that the above-mentioned abrasive particle that is configured in the electro-deposition abrasive particle zone on the discoideus base plate side dispersedly is by diamond and Al
2O
3, SiO
2Or ZrO
2Constitute Deng the mixing of hardening oxidation thing.
8, the helicoid foundry goods of a kind of plectane cuts off and uses cutter, it is characterized in that on the outer circumference surface of discoideus base plate electro-deposition one deck abrasive grain layer and form blade part; Above-mentioned abrasive grain layer is that the secondary abrasive particle portion that constitutes of main abrasive particle portion that large diameter abrasive particle is constituted and minor diameter abrasive particle is along the circumferencial direction of above-mentioned base plate, alternately the arrangement of five equilibrium ground forms basically; On the side between the fastening part of above-mentioned blade part and plectane central authorities, the zone that is disposing the electro-deposition abrasive particle dispersedly.
9, the helicoid foundry goods of a kind of plectane cuts off and uses cutter, it is characterized in that on the periphery of the discoideus base plate that constitutes by low thermal coefficient of expansion materials such as Fe-Ni alloy or Fe-Ni-Co alloys the abrasive grain layer that electro-deposition one deck is made of the abrasive particle of 30～50 meshes of diamond or cubic crystal boron nitride particle and form blade part; Above-mentioned abrasive grain layer be the main abrasive particle portion that constitutes by the major diameter abrasive particle and by grain through the secondary abrasive particle portion that the minor diameter abrasive particle below the average grain diameter of major diameter abrasive particle constitutes, form along the circumferencial direction alternately basic five equilibrium ground arrangement of above-mentioned base plate; On the side between the fastening part of above-mentioned blade part and plectane central authorities, disposing electro-deposition abrasive particle zone dispersedly, these electro-deposition abrasive particle zones are diamond and the Al of particle diameter below the abrasive particle particle diameter of above-mentioned blade part
2O
3, SiO
2Or ZrO
2Constitute Deng the mixing of hardening oxidation thing.