CN113149457A - Glass antibacterial coating liquid, preparation method thereof and preparation method of antibacterial coated glass - Google Patents
Glass antibacterial coating liquid, preparation method thereof and preparation method of antibacterial coated glass Download PDFInfo
- Publication number
- CN113149457A CN113149457A CN202110430792.6A CN202110430792A CN113149457A CN 113149457 A CN113149457 A CN 113149457A CN 202110430792 A CN202110430792 A CN 202110430792A CN 113149457 A CN113149457 A CN 113149457A
- Authority
- CN
- China
- Prior art keywords
- glass
- antibacterial
- coating liquid
- preparation
- antibacterial coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass antibacterial coating liquid, a preparation method thereof and a preparation method of antibacterial coated glass. According to the invention, the organic silicon resin is cured under the action of the catalyst, the cation additive is introduced and uniformly sprayed on the glass, the cation additive can form intercalation modification on the silicon resin after heating and baking at the temperature of 100-150 ℃, so that the glass coating layer structure has the characteristic that positive charges face outwards, the effect of killing bacteria is achieved by adsorbing bacteria with negative charges and invading cell walls of the bacteria, and the glass coating layer structure has smooth hand feeling and low friction coefficient due to the attachment of the organic silicon. The invention forms the antibacterial coated glass by coating the antibacterial coated liquid on the glass by a roller, and the production process of the antibacterial glass is easy to control and is more suitable for industrial production.
Description
[ technical field ] A method for producing a semiconductor device
The invention relates to the technical field of glass coating treatment liquid, in particular to glass antibacterial coating liquid and a preparation method thereof, and a preparation method of antibacterial coated glass.
[ background of the invention ]
The antibacterial coated glass, namely the antibacterial glass, is glass treated by a special antibacterial process, is widely applied to the aspects of medical appliance glass, touch screens and the like, and can reduce the adhesion of bacteria on the surface of the glass by killing or killing most of bacteria. The method for forming the antibacterial coated glass at present mainly uses a nano silver system coating on the surface of the glass, thereby achieving the purpose of killing bacteria. And coating titanium oxide on the surface of the glass so as to achieve the aim of sterilization. The application of the nano silver antibacterial material on glass can cause the following problems: 1. the metal ions are easily oxidized and discolored by air, and the display effect is influenced. 2. The principle is that the silver ions slowly dissolve out to achieve the aims of antibiosis and sterilization, but the silver ions can lose the effect with the lapse of time. 3. The countries of the European Union, etc. forbid the use of nano silver as antibacterial products, and can inquire the relevant information of the European countries, including the United states environmental protection agency. Because silver ions are released continuously, the nano-silver antibacterial agent can be accumulated to cause pathological changes if being absorbed by internal organs of a human body, and can never be discharged out of the body, thereby greatly harming the health of the human body. The titanium oxide antibacterial material applied to glass has the following problems: 1. titanium oxide antibacterial is to decompose organic matters such as bacteria by exciting strong oxidizing power by ultraviolet irradiation, and the antibacterial effect of titanium oxide cannot be achieved in a room or an environment without direct sunlight. 2. Titanium oxide has a high refractive index, and when it is used for glass having a refractive index of about 1.5, the display effect is impaired
[ summary of the invention ]
The invention aims to overcome the problems in the prior art, and provides a glass antibacterial coating solution, a preparation method thereof and a preparation method of antibacterial coated glass so as to solve the problems in the background art.
In order to achieve the aim, the glass antibacterial coating liquid comprises the following components in percentage by weight:
in one or more embodiments, the cationic additive is one or more of cetyltrimethylammonium bromide, cetyltrimethylammonium chloride, dioctadecyldimethylammonium chloride.
In one or more embodiments, the catalyst is a karstedt platinum catalyst or a Willing platinum catalyst.
In one or more embodiments, the hydrogen-containing silicone resin is a terminal hydrogen-containing silicone oil or a side chain moiety hydrogen-containing silicone oil.
In one or more embodiments, the vinyl silicone resin is a vinyl terminated polydimethylsiloxane or a vinyl terminated polymethylvinylsiloxane.
The invention also provides a preparation method of the glass antibacterial coating liquid, which comprises the following steps:
A. uniformly stirring vinyl silicone resin and hydrogen-containing silicone resin to prepare organic silicon mixed resin;
B. adding a catalyst into the organic silicon mixed resin and uniformly stirring;
C. slowly adding the cationic additive, and continuously and uniformly stirring for one hour to obtain the glass antibacterial coating liquid.
The invention also provides a preparation method of the antibacterial coated glass, which comprises the following steps:
a. cleaning glass;
b. uniformly spraying the prepared glass antibacterial coating liquid on the surface of glass;
c. and (3) baking the glass in a baking furnace to obtain the antibacterial coated glass.
In one or more embodiments, in the step c, the baking temperature of the baking furnace is 100-150 ℃, and the baking time is 20-40 minutes.
Compared with the background technology, the invention has the following technical effects: the glass coating layer structure has the characteristic that positive charges face outwards by curing the organic silicon resin under the action of the catalyst and introducing the cationic additive to be uniformly sprayed on the glass, the cationic additive can form intercalation modification on the silicon resin after being heated and baked at the temperature of 100-150 ℃, the effect of killing bacteria is achieved by adsorbing the bacteria with negative charges and invading the cell wall of the bacteria, and the glass coating layer structure has smooth hand feeling and low friction coefficient due to the attachment of the organic silicon. The invention forms the antibacterial coated glass by spraying the antibacterial coated liquid on the glass, and the production process of the antibacterial glass is easy to control and is more suitable for industrial production.
[ description of the drawings ]
FIG. 1 is a table showing the antibacterial properties of the antibacterial coated glass prepared according to the present invention.
[ detailed description ] embodiments
For the purpose of enhancing the understanding of the present invention, the present invention will be further described in detail with reference to the following examples and the accompanying drawings, which are only used for explaining the present invention and are not to be construed as limiting the scope of the present invention.
Example one
Referring to fig. 1, the present application provides an antibacterial glass coating solution, which comprises the following components by weight:
the cationic additive is hexadecyl trimethyl ammonium bromide, the catalyst is karstedt platinum catalyst, the hydrogen-containing silicone resin is end group hydrogen-containing silicone oil, and the vinyl silicone resin is vinyl-terminated polydimethylsiloxane.
The application also provides a preparation method of the glass antibacterial coating liquid, which comprises the following specific preparation steps:
A. uniformly stirring vinyl silicone resin and hydrogen-containing silicone resin to prepare organic silicon mixed resin;
B. adding a catalyst into the organic silicon mixed resin and uniformly stirring;
C. slowly adding the cationic additive, and continuously and uniformly stirring for one hour to obtain the glass antibacterial coating liquid.
The application also provides a preparation method of the antibacterial coated glass, which comprises the following steps:
a. cleaning glass, and conveying the cleaned glass to a spraying machine;
b. uniformly spraying the prepared glass antibacterial coating liquid on the surface of glass;
c. and (3) baking the glass in a baking furnace to obtain the antibacterial coated glass, wherein the baking temperature of the baking furnace is 150 ℃, the baking time is 20 minutes, and the baking furnace is a tunnel furnace.
Example two
The glass antibacterial coating liquid comprises the following components in percentage by weight:
the cationic additive is dioctadecyl dimethyl ammonium chloride, the catalyst is a Willing platinum catalyst, the hydrogen-containing silicone resin is side-chain part hydrogen-containing silicone oil, and the vinyl silicone resin is vinyl-terminated polymethylvinylsiloxane.
The application also provides a preparation method of the glass antibacterial coating liquid, which comprises the following specific preparation steps:
A. uniformly stirring vinyl silicone resin and hydrogen-containing silicone resin to prepare organic silicon mixed resin;
B. adding a catalyst into the organic silicon mixed resin and uniformly stirring;
C. slowly adding the cationic additive, and continuously and uniformly stirring for one hour to obtain the glass antibacterial coating liquid.
The application also provides a preparation method of the antibacterial coated glass, which comprises the following steps:
a. cleaning glass, and conveying the cleaned glass to a spraying machine;
b. uniformly spraying the prepared glass antibacterial coating liquid on the surface of glass;
c. and (3) baking the glass in a baking furnace to obtain the antibacterial coated glass, wherein the baking temperature of the baking furnace is 120 ℃, the baking time is 30 minutes, and the baking furnace is a tunnel furnace.
The above description is only a preferred embodiment of the present invention, and the scope of the present invention is not limited to the above embodiment, but equivalent modifications or changes made by those skilled in the art according to the present disclosure should be included in the scope of the present invention as set forth in the appended claims.
Claims (8)
2. the glass antibacterial coating liquid of claim 1, characterized in that: the cation additive is one or a mixture of cetyl trimethyl ammonium bromide, cetyl trimethyl ammonium chloride and dioctadecyl dimethyl ammonium chloride.
3. The glass antibacterial coating liquid of claim 1, characterized in that: the catalyst is Karstedt platinum catalyst or Willing platinum catalyst.
4. The glass antibacterial coating liquid of claim 1, characterized in that: the hydrogen-containing silicone resin is terminal group hydrogen-containing silicone oil or side chain part hydrogen-containing silicone oil.
5. The glass antibacterial coating liquid of claim 1, characterized in that: the vinyl silicone resin is vinyl-terminated polydimethylsiloxane or vinyl-terminated polymethylvinylsiloxane.
6. The method for preparing glass antibacterial coating liquid according to any one of claims 1 to 5, characterized in that: the method comprises the following steps:
A. uniformly stirring vinyl silicone resin and hydrogen-containing silicone resin to prepare organic silicon mixed resin;
B. adding a catalyst into the organic silicon mixed resin and uniformly stirring;
C. slowly adding the cationic additive, and continuously and uniformly stirring for one hour to obtain the glass antibacterial coating liquid.
7. The preparation method of the antibacterial coated glass is characterized by comprising the following steps:
a. cleaning glass;
b. uniformly spraying the glass antibacterial coating solution prepared by the method of claim 6 on the surface of glass;
c. and (3) baking the glass in a baking furnace to obtain the antibacterial coated glass.
8. The method for preparing antibacterial coated glass according to claim 7, characterized in that: in the step c, the baking temperature of the baking furnace is 100-150 ℃, and the baking time is 20-40 minutes.