CN113123147A - Dyeing fabric capable of being subjected to high-temperature chlorine bleaching - Google Patents
Dyeing fabric capable of being subjected to high-temperature chlorine bleaching Download PDFInfo
- Publication number
- CN113123147A CN113123147A CN201911389027.3A CN201911389027A CN113123147A CN 113123147 A CN113123147 A CN 113123147A CN 201911389027 A CN201911389027 A CN 201911389027A CN 113123147 A CN113123147 A CN 113123147A
- Authority
- CN
- China
- Prior art keywords
- parts
- dyed fabric
- silver powder
- nano silver
- polyoxyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyed fabric capable of being subjected to high-temperature chlorine bleaching, which comprises the following components in parts by weight: 30-50 parts of coated nano silver powder solution, 10-20 parts of tetraacetylethylenediamine, 10-16 parts of dihydropyridine, 6-14 parts of ethylenediamine sodium iron acetate bis-o-hydroxyphenyl, 6-8 parts of ethylene-vinyl acetate copolymer, 20-30 parts of high temperature resistant stabilizer, 40-60 parts of polyvinylpyrrolidone, 40-80 parts of polyoxyethylene phenyl alkylphenol ether and 40-60 parts of fatty alcohol-polyoxyethylene ether. According to the invention, through selection and structural modification of various raw materials, the coating type nano silver powder solution with a proper proportion is added into the components, so that the adhesive force of the pigment is increased, and the prepared dyed fabric has good high temperature resistance and chlorine bleaching resistance.
Description
Technical Field
The invention relates to a dyed fabric capable of being subjected to high-temperature chlorine bleaching.
Background
The yarn-dyed fabric is woven by warp and weft yarns with different colors, and because the fabric is dyed firstly and then woven, the dye permeability is strong, and the yarn-dyed fabric has the advantages that the yarn is dyed firstly and then woven into the fabric, the color fastness is better than that of the common dyed and dyed fabric, and the color is not easy to fade during washing. The fabric can be divided into cotton fabric, wool fabric, silk fabric, hemp fabric, chemical fiber fabric and mineral fiber fabric according to the types of raw materials, and can be divided into pure woven fabric, blended woven fabric, mixed woven fabric, interwoven fabric, mixed woven fabric, mixed interwoven fabric, core-spun fabric, cladding fabric, fasciated yarn fabric and the like according to the components of the raw materials.
As most of detergents contain chlorine, the high-temperature chlorine bleaching resistance of the existing dyed fabric is poor. Therefore, we provide a dyed fabric capable of high-temperature chlorine bleaching to solve the problems.
Disclosure of Invention
The invention aims to overcome the defects of the existing dyed fabric and provide a dyed fabric capable of being subjected to high-temperature chlorine bleaching.
In order to solve the technical problems, the invention provides the following technical scheme:
a dyed fabric capable of being subjected to high-temperature chlorine bleaching comprises the following components in parts by weight: 30-50 parts of coated nano silver powder solution, 10-20 parts of tetraacetylethylenediamine, 10-16 parts of dihydropyridine, 6-14 parts of ethylenediamine sodium iron acetate bis-o-hydroxyphenyl, 6-8 parts of ethylene-vinyl acetate copolymer, 20-30 parts of high temperature resistant stabilizer, 40-60 parts of polyvinylpyrrolidone, 40-80 parts of polyoxyethylene phenyl alkylphenol ether and 40-60 parts of fatty alcohol-polyoxyethylene ether.
Preferably, the composition comprises the following components in parts by weight: 30 parts of coated nano silver powder solution, 10 parts of tetraacetylethylenediamine, 10 parts of dihydropyridine, 6 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 6 parts of ethylene-vinyl acetate copolymer, 20 parts of high temperature resistant stabilizer, 40 parts of polyvinylpyrrolidone, 40 parts of polyoxyethylene phenyl alkylphenol ether and 40 parts of fatty alcohol-polyoxyethylene ether.
Preferably, the composition comprises the following components in parts by weight: 50 parts of coated nano silver powder solution, 20 parts of tetraacetylethylenediamine, 16 parts of dihydropyridine, 14 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 8 parts of ethylene-vinyl acetate copolymer, 30 parts of high temperature resistant stabilizer, 60 parts of polyvinylpyrrolidone, 80 parts of polyoxyethylene phenyl alkylphenol ether and 60 parts of fatty alcohol-polyoxyethylene ether.
Preferably, the composition comprises the following components in parts by weight: 40 parts of coated nano silver powder solution, 15 parts of tetraacetylethylenediamine, 13 parts of dihydropyridine, 10 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 7 parts of ethylene-vinyl acetate copolymer, 25 parts of high temperature resistant stabilizer, 50 parts of polyvinylpyrrolidone, 65 parts of polyoxyethylene phenyl alkylphenol ether and 50 parts of fatty alcohol-polyoxyethylene ether.
Preferably, the high temperature resistant stabilizer comprises: 70-85 parts of tris (2, 3-dichloropropyl) phosphate, 10-20 parts of 5-ethylidene-2-norbornene and 2-3.5 parts of polyvinyl acetate emulsion.
According to the invention, through selection and structural modification of various raw materials, the coating type nano silver powder solution with a proper proportion is added into the components, so that the adhesive force of the pigment is increased, and the prepared dyed fabric has good high temperature resistance and chlorine bleaching resistance.
Detailed Description
The following description of the preferred embodiments of the present invention is provided for the purpose of illustration and description, and is in no way intended to limit the invention.
Example 1
A dyed fabric capable of being subjected to high-temperature chlorine bleaching comprises the following components in parts by weight: 30 parts of coated nano silver powder solution, 10 parts of tetraacetylethylenediamine, 10 parts of dihydropyridine, 6 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 6 parts of ethylene-vinyl acetate copolymer, 20 parts of high temperature resistant stabilizer, 40 parts of polyvinylpyrrolidone, 40 parts of polyoxyethylene phenyl alkylphenol ether and 40 parts of fatty alcohol-polyoxyethylene ether.
The high-temperature resistant stabilizer comprises: 70 parts of tris (2, 3-dichloropropyl) phosphate, 10 parts of 5-ethylidene-2-norbornene and 2 parts of polyvinyl acetate emulsion.
Example 2
A dyed fabric capable of being subjected to high-temperature chlorine bleaching comprises the following components in parts by weight: 50 parts of coated nano silver powder solution, 20 parts of tetraacetylethylenediamine, 16 parts of dihydropyridine, 14 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 8 parts of ethylene-vinyl acetate copolymer, 30 parts of high temperature resistant stabilizer, 60 parts of polyvinylpyrrolidone, 80 parts of polyoxyethylene phenyl alkylphenol ether and 60 parts of fatty alcohol-polyoxyethylene ether.
The high-temperature resistant stabilizer comprises: 85 parts of tris (2, 3-dichloropropyl) phosphate, 20 parts of 5-ethylidene-2-norbornene and 3.5 parts of polyvinyl acetate emulsion.
Example 3
A dyed fabric capable of being subjected to high-temperature chlorine bleaching comprises the following components in parts by weight: 40 parts of coated nano silver powder solution, 15 parts of tetraacetylethylenediamine, 13 parts of dihydropyridine, 10 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 7 parts of ethylene-vinyl acetate copolymer, 25 parts of high temperature resistant stabilizer, 50 parts of polyvinylpyrrolidone, 65 parts of polyoxyethylene phenyl alkylphenol ether and 50 parts of fatty alcohol-polyoxyethylene ether.
The high-temperature resistant stabilizer comprises: 78 parts of tris (2, 3-dichloropropyl) phosphate, 15 parts of 5-ethylidene-2-norbornene and 3 parts of polyvinyl acetate emulsion.
Compared with the common fabrics in the market, the fabrics in the examples 1 to 3 have the following improved high temperature resistance and chlorine bleaching resistance in percentage:
as can be seen from the above table, the high temperature resistance and the chlorine bleaching resistance of the invention are obviously improved.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that changes may be made in the embodiments and/or equivalents thereof without departing from the spirit and scope of the invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (5)
1. The dyed fabric capable of being subjected to high-temperature chlorine bleaching is characterized by being obtained by padding grey fabric with a high-temperature chlorine bleaching agent; the high-temperature resistant chlorine bleaching agent comprises the following components in parts by weight: 30-50 parts of coated nano silver powder solution, 10-20 parts of tetraacetylethylenediamine, 10-16 parts of dihydropyridine, 6-14 parts of ethylenediamine sodium iron acetate bis-o-hydroxyphenyl, 6-8 parts of ethylene-vinyl acetate copolymer, 20-30 parts of high temperature resistant stabilizer, 40-60 parts of polyvinylpyrrolidone, 40-80 parts of polyoxyethylene phenyl alkylphenol ether and 40-60 parts of fatty alcohol-polyoxyethylene ether.
2. The dyed fabric capable of being high-temperature chlorine bleached according to claim 1, which is characterized by comprising the following components in parts by weight: 30 parts of coated nano silver powder solution, 10 parts of tetraacetylethylenediamine, 10 parts of dihydropyridine, 6 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 6 parts of ethylene-vinyl acetate copolymer, 20 parts of high temperature resistant stabilizer, 40 parts of polyvinylpyrrolidone, 40 parts of polyoxyethylene phenyl alkylphenol ether and 40 parts of fatty alcohol-polyoxyethylene ether.
3. The dyed fabric capable of being high-temperature chlorine bleached according to claim 1, which is characterized by comprising the following components in parts by weight: 50 parts of coated nano silver powder solution, 20 parts of tetraacetylethylenediamine, 16 parts of dihydropyridine, 14 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 8 parts of ethylene-vinyl acetate copolymer, 30 parts of high temperature resistant stabilizer, 60 parts of polyvinylpyrrolidone, 80 parts of polyoxyethylene phenyl alkylphenol ether and 60 parts of fatty alcohol-polyoxyethylene ether.
4. The dyed fabric capable of being high-temperature chlorine bleached according to claim 1, which is characterized by comprising the following components in parts by weight: 40 parts of coated nano silver powder solution, 15 parts of tetraacetylethylenediamine, 13 parts of dihydropyridine, 10 parts of ethylenediamine di-o-hydroxyphenyl macroacetic acid sodium iron, 7 parts of ethylene-vinyl acetate copolymer, 25 parts of high temperature resistant stabilizer, 50 parts of polyvinylpyrrolidone, 65 parts of polyoxyethylene phenyl alkylphenol ether and 50 parts of fatty alcohol-polyoxyethylene ether.
5. The dyed fabric capable of being high-temperature chlorine-bleached according to any one of claims 1 to 4, wherein the high-temperature-resistant stabilizer comprises: 70-85 parts of tris (2, 3-dichloropropyl) phosphate, 10-20 parts of 5-ethylidene-2-norbornene and 2-3.5 parts of polyvinyl acetate emulsion.