CN113122977A - Production process of industrial yarn of renewable fiber - Google Patents
Production process of industrial yarn of renewable fiber Download PDFInfo
- Publication number
- CN113122977A CN113122977A CN201911388218.8A CN201911388218A CN113122977A CN 113122977 A CN113122977 A CN 113122977A CN 201911388218 A CN201911388218 A CN 201911388218A CN 113122977 A CN113122977 A CN 113122977A
- Authority
- CN
- China
- Prior art keywords
- parts
- putting
- delinting
- yarn
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of industrial yarn of renewable fiber, which comprises the following raw materials in parts by weight: 60-80 parts of terylene, 10-15 parts of cotton, 15-30 parts of broken filaments, 2-4 parts of modifier, 0.5-2 parts of plasticizer and 1-3 parts of softening agent. The invention has simple production process, greatly saves the cost of raw materials, realizes the change of waste into valuable in the production of the textile industry, and is beneficial to improving the economic benefit of the textile industry.
Description
Technical Field
The invention belongs to the technical field of industrial yarn, and particularly relates to a production process of industrial yarn of renewable fiber.
Background
The yarn is widely applied to the market as the traditional textile industry in China and almost spread in various fields, wherein the effect of industrial yarn is not replaceable, but a large amount of terylene and fiber are needed for weaving the industrial yarn, the requirement on raw materials is high, the cost is relatively high, a large amount of fragmentary terylene, thread balls, cotton and waste silk generally appear in the textile industry, the waste materials are directly treated as garbage, and aiming at the problem, how to change the fragmentary waste materials into valuables can be processed into renewable fiber to be used as textile raw materials for reproduction, so that the cost of the raw materials is greatly reduced, and the problem that the yarn is troublesome in the market at present is solved.
Disclosure of Invention
The invention aims to solve the defects and provides a process for producing industrial yarn of renewable fibers.
In order to overcome the defects in the background art, the technical scheme adopted by the invention for solving the technical problems is as follows: a process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 60-80 parts of terylene, 10-15 parts of cotton, 15-30 parts of broken filaments, 2-4 parts of modifier, 0.5-2 parts of plasticizer and 1-3 parts of softening agent.
2. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene and the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 30-60 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
Preferably, the plasticizer is dioctyl phthalate.
Preferably, the softening agent is a silicone resin.
The invention has the beneficial effects that: the production process is simple, the cost of raw materials is greatly saved, the waste is changed into valuable in the production of the textile industry, and the economic benefit of the textile industry is favorably improved.
Detailed Description
The following detailed description of the preferred embodiments of the present invention is provided to enable those skilled in the art to more readily understand the advantages and features of the present invention, and to clearly and unequivocally define the scope of the present invention.
A process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 60-80 parts of terylene, 10-15 parts of cotton, 15-30 parts of broken filaments, 2-4 parts of modifier, 0.5-2 parts of plasticizer and 1-3 parts of softening agent.
A production process of industrial yarn of renewable fiber is characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene and the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 30-60 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
Example 1
A process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 60 parts of terylene, 10 parts of cotton, 15 parts of hard waste, 2 parts of modifier, 0.5 part of plasticizer and 1 part of softening agent.
A production process of industrial yarn of renewable fiber is characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene, the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 30 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
Example 2
A process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 70 parts of terylene, 12 parts of cotton, 24 parts of hard waste, 3 parts of modifier, 1 part of plasticizer and 1.5 parts of softening agent.
2. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene, the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 45 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
Example 3
A process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 80 parts of terylene, 15 parts of cotton, 30 parts of hard waste, 4 parts of modifier, 2 parts of plasticizer and 3 parts of softening agent.
2. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene, the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 60 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
The above description is only an embodiment of the present invention, and not intended to limit the scope of the present invention, and all modifications of equivalent structures and equivalent processes, which are made by the present specification, or directly or indirectly applied to other related technical fields, are included in the scope of the present invention.
Claims (4)
1. A process for producing industrial yarn of renewable fiber comprises the following raw materials by weight: 60-80 parts of terylene, 10-15 parts of cotton, 15-30 parts of broken filaments, 2-4 parts of modifier, 0.5-2 parts of plasticizer and 1-3 parts of softening agent.
2. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the method comprises the following steps:
s1, putting the cut tobacco into a three-sawtooth roller refined dried ramie opener for opening, then putting the cut tobacco into an FS600 carding machine for carding, and then putting the cut tobacco into a delinting machine for delinting;
s2, placing the terylene and the cotton, the waste silk in the step S1, the modifier, the plasticizer and the softening agent into a stirring box according to the proportion of 5:1:2:0.4:0.1:0.3 for premixing for 30-60 min;
s3, opening the mixed material obtained in the step S2 in a K50 opener;
s4, putting the semi-finished product in the step S3 into a delinting machine for removing impurities and delinting;
s5, putting the semi-finished product obtained in the step S4 into an FS1500 carding machine for carding to obtain roving;
s6, putting the rough yarn obtained in the step S5 into a spinning machine, and twisting to obtain a spun yarn;
s7: and (5) filling the spun yarn obtained in the step (S6) into a grooved drum to obtain the product.
3. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the plasticizer is dioctyl phthalate.
4. The process for the production of industrial yarn of renewable fibers according to claim 1, characterized in that: the softening agent is organic silicon resin.