CN113122071A - 一种变色油墨配方 - Google Patents
一种变色油墨配方 Download PDFInfo
- Publication number
- CN113122071A CN113122071A CN202010040379.4A CN202010040379A CN113122071A CN 113122071 A CN113122071 A CN 113122071A CN 202010040379 A CN202010040379 A CN 202010040379A CN 113122071 A CN113122071 A CN 113122071A
- Authority
- CN
- China
- Prior art keywords
- parts
- color
- changing ink
- formulation according
- ink formulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种变色油墨配方，按重量计份包括以下组分，水性聚氨酯31.3‑32.2份；苯乙烯‑甲基丙烯酸甲酯乳液2.5‑3.5份；脂肪醇聚氧乙烯醚0.3‑1.3份；水性聚乙烯蜡4.0‑5.0份；水性分散剂760W 1.5‑2.5份；聚醚改性有机硅消泡剂0.2‑0.7份；聚醚改性有机硅流平剂0.1‑0.6份；2.6‑二叔丁基对甲酚0.2‑0.7份；γ―丙基三甲氧基硅烷0.4‑0.9份；所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7‑13.7份；聚四氢呋喃二醇1000 15.9‑16.9份；2.2‑二羟甲基丙酸DMPA 0.7‑1.7份；1.4‑丁二醇0.5‑1.0份；N.N‑二甲基乙酰胺0.3‑0.8份；三乙胺0.2‑0.7份。本发明在常温下，不显颜色，温度升高后颜色变蓝，且该反应属于可逆反应，印刷成品色彩鲜艳，不易褪色，且油墨配方无毒无害，亦可食用。
Description
技术领域
本发明涉及油墨技术领域，具体为一种变色油墨配方。
背景技术
温变油墨又称热变色油墨、热敏油墨或示温油墨。温变油墨分为三大类：常温下显示某种特定颜色，经加温后颜色消失变为无色，冷却后立即恢复到原有颜色，因其变化过程可逆，称为“可逆温变消色油墨”；在常温下显示无色，经加温后变为另外一种颜色，冷却后又恢复为原来的无色，因其变化过程可逆，称为“可逆温变发色油墨”；油墨在常温下显示颜色，加温后变为另外一种颜色，因其变化过程可逆称为“可逆温变转色油墨。以为的油墨在使用的过程中容易褪色。
发明内容
本发明的目的在于提供一种变色油墨配方，解决了上述背景技术提出的问题。
为实现上述目的，本发明提供如下技术方案：一种变色油墨配方，按重量计份包括以下组分，水性聚氨酯31.3-32.2份；苯乙烯-甲基丙烯酸甲酯乳液2.5-3.5份；脂肪醇聚氧乙烯醚0.3-1.3份；水性聚乙烯蜡4.0-5.0份；水性分散剂760W 1.5-2.5份；聚醚改性有机硅消泡剂0.2-0.7份；聚醚改性有机硅流平剂0.1-0.6份；2.6-二叔丁基对甲酚0.2-0.7份；γ―丙基三甲氧基硅烷0.4-0.9份。
优选的，所述脂肪醇聚氧乙烯醚为AE0-9乳化剂。
优选的，所述2.6-二叔丁基对甲酚为抗氧剂264。
优选的，所述γ―丙基三甲氧基硅烷为硅烷偶联剂kh560。
优选的，所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7-13.7份；聚四氢呋喃二醇100015.9-16.9份；2.2-二羟甲基丙酸DMPA 0.7-1.7份；1.4-丁二醇0.5-1.0份；N.N-二甲基乙酰胺0.3-0.8份；三乙胺0.2-0.7份。
优选的，所述2.2-二羟甲基丙酸DMPA为水性单体。
优选的，所述1.4-丁二醇为扩链剂。
优选的，所述N.N-二甲基乙酰胺为催化剂。
优选的，所述三乙胺为中和成盐剂。
与现有技术相比，本发明的有益效果如下：本发明在常温下，不显颜色，温度升高后颜色变蓝，且该反应属于可逆反应，印刷成品色彩鲜艳，不易褪色，且油墨配方无毒无害，亦可食用。
具体实施方式
对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明提供一种变色油墨配方技术方案：一种变色油墨配方，按重量计份包括以下组分，水性聚氨酯31.3-32.2份；苯乙烯-甲基丙烯酸甲酯乳液2.5-3.5份；AE0-9乳化剂0.3-1.3份；水性聚乙烯蜡4.0-5.0份；水性分散剂760W 1.5-2.5份；聚醚改性有机硅消泡剂0.2-0.7份；聚醚改性有机硅流平剂0.1-0.6份；2.6-二叔丁基对甲酚0.2-0.7份；γ―丙基三甲氧基硅烷0.4-0.9份。
进一步的，所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7-13.7份；聚四氢呋喃二醇100015.9-16.9份；2.2-二羟甲基丙酸DMPA 0.7-1.7份；1.4-丁二醇0.5-1.0份；N.N-二甲基乙酰胺0.3-0.8份；三乙胺0.2-0.7份。
进一步的，所述2.2-二羟甲基丙酸DMPA为水性单体。
进一步的，所述1.4-丁二醇为扩链剂。
进一步的，所述N.N-二甲基乙酰胺为催化剂。
进一步的，所述三乙胺为中和成盐剂。
其中，三聚氰胺-甲醛热致变色微胶囊适量；APM-95(pH调节剂)适量，水适量。
实施例2
本发明提供一种变色油墨配方技术方案：一种变色油墨配方，按重量计份包括以下组分，水性聚氨酯31.3-32.2份；苯乙烯-甲基丙烯酸甲酯乳液2.5-3.5份；脂肪醇聚氧乙烯醚0.3-1.3份；水性聚乙烯蜡4.0-5.0份；水性分散剂760W 1.5-2.5份；聚醚改性有机硅消泡剂0.2-0.7份；聚醚改性有机硅流平剂0.1-0.6份；2.6-二叔丁基对甲酚0.2-0.7份；硅烷偶联剂kh5600.4-0.9份。
进一步的，所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7-13.7份；聚四氢呋喃二醇100015.9-16.9份；2.2-二羟甲基丙酸DMPA 0.7-1.7份；1.4-丁二醇0.5-1.0份；N.N-二甲基乙酰胺0.3-0.8份；三乙胺0.2-0.7份。
进一步的，所述2.2-二羟甲基丙酸DMPA为水性单体。
进一步的，所述1.4-丁二醇为扩链剂。
进一步的，所述N.N-二甲基乙酰胺为催化剂。
进一步的，所述三乙胺为中和成盐剂。
其中，三聚氰胺-甲醛热致变色微胶囊适量；APM-95(pH调节剂)适量，水适量。
实施例3
本发明提供一种变色油墨配方技术方案：一种变色油墨配方，按重量计份包括以下组分，水性聚氨酯31.3-32.2份；苯乙烯-甲基丙烯酸甲酯乳液2.5-3.5份；脂肪醇聚氧乙烯醚0.3-1.3份；水性聚乙烯蜡4.0-5.0份；水性分散剂760W 1.5-2.5份；聚醚改性有机硅消泡剂0.2-0.7份；聚醚改性有机硅流平剂0.1-0.6份；抗氧剂2640.2-0.7份；γ―丙基三甲氧基硅烷0.4-0.9份。
进一步的，所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7-13.7份；聚四氢呋喃二醇100015.9-16.9份；2.2-二羟甲基丙酸DMPA 0.7-1.7份；1.4-丁二醇0.5-1.0份；N.N-二甲基乙酰胺0.3-0.8份；三乙胺0.2-0.7份。
进一步的，所述2.2-二羟甲基丙酸DMPA为水性单体。
进一步的，所述1.4-丁二醇为扩链剂。
进一步的，所述N.N-二甲基乙酰胺为催化剂。
进一步的，所述三乙胺为中和成盐剂。
其中，三聚氰胺-甲醛热致变色微胶囊适量；APM-95(pH调节剂)适量，水适量。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (9)
1.一种变色油墨配方，其特征在于：按重量计份包括以下组分，水性聚氨酯31.3-32.2份；苯乙烯-甲基丙烯酸甲酯乳液2.5-3.5份；脂肪醇聚氧乙烯醚0.3-1.3份；水性聚乙烯蜡4.0-5.0份；水性分散剂760W 1.5-2.5份；聚醚改性有机硅消泡剂0.2-0.7份；聚醚改性有机硅流平剂0.1-0.6份；2.6-二叔丁基对甲酚0.2-0.7份；γ―丙基三甲氧基硅烷0.4-0.9份。
2.根据权利要求1所述的一种变色油墨配方，其特征在于：所述脂肪醇聚氧乙烯醚为AE0-9乳化剂。
3.根据权利要求1所述的一种变色油墨配方，其特征在于：所述2.6-二叔丁基对甲酚为抗氧剂264。
4.根据权利要求1所述的一种变色油墨配方，其特征在于：所述γ―丙基三甲氧基硅烷为硅烷偶联剂kh560。
5.根据权利要求1所述的一种变色油墨配方，其特征在于：所述水性聚氨酯按重量计份包括以下组分：甲乙酮肟封闭异佛尔酮二异氰酸酯12.7-13.7份；聚四氢呋喃二醇100015.9-16.9份；2.2-二羟甲基丙酸DMPA 0.7-1.7份；1.4-丁二醇0.5-1.0份；N.N-二甲基乙酰胺0.3-0.8份；三乙胺0.2-0.7份。
6.根据权利要求5所述的一种变色油墨配方，其特征在于：所述2.2-二羟甲基丙酸DMPA为水性单体。
7.根据权利要求5所述的一种变色油墨配方，其特征在于：所述1.4-丁二醇为扩链剂。
8.根据权利要求5所述的一种变色油墨配方，其特征在于：所述N.N-二甲基乙酰胺为催化剂。
9.根据权利要求5所述的一种变色油墨配方，其特征在于：所述三乙胺为中和成盐剂。