CN112961455A - 一种阻燃抗菌abs材料及其制备方法 - Google Patents
一种阻燃抗菌abs材料及其制备方法 Download PDFInfo
- Publication number
- CN112961455A CN112961455A CN202110233830.9A CN202110233830A CN112961455A CN 112961455 A CN112961455 A CN 112961455A CN 202110233830 A CN202110233830 A CN 202110233830A CN 112961455 A CN112961455 A CN 112961455A
- Authority
- CN
- China
- Prior art keywords
- flame
- retardant
- abs
- abs material
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃抗菌ABS材料，所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂，所述阻燃抗拒ABS材料的配比为ABS树脂50%、阻燃剂10%、银离子粉末2%、环氧树脂粘合剂4%、润滑剂6%、偶联剂8%、增塑剂8%、竹纤维10%以及抗氧化剂2%，所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂均独立进行干燥存放，同时竹纤维粉末本身自带的抗菌、抑菌以及耐磨特性，可进一步提高阻燃ABS的抗菌以及耐使用特点，该类特点可在保持阻燃ABS的原有阻燃特性下，获得多样化的使用特性。
Description
技术领域
本发明属于阻燃材料相关技术领域，具体涉及一种阻燃抗菌ABS材料及其制备方法。
背景技术
阻燃材料是能够抑制或者延滞燃烧，而自己并不容易燃烧的材料，其主要分为有机阻燃材料和无机阻燃材料， 其主要应用于服装、石油、化工、冶金、造船、消防、国防等领域。
现有阻燃抗菌ABS材料技术存在以下问题：阻燃ABS在ABS的基础上加入阻燃剂来成为具有阻燃效果的ABS塑料，该阻燃ABS材料的综合性能较好，具有较高的抗冲击强度、高耐热以及阻燃特性，常应用工业生产以及居家用品中，目前阻燃ABS仅仅只能应用于需阻燃环境，即阻燃ABS无法根据使用环境，来进行常规的抗菌操作，使用范围较窄，难以满足使用者的多样化使用需求问题。
发明内容
本发明的目的在于提供一种阻燃抗菌ABS材料及其制备方法，以解决上述背景技术中提出阻燃ABS在ABS的基础上加入阻燃剂来成为具有阻燃效果的ABS塑料，该阻燃ABS材料的综合性能较好，具有较高的抗冲击强度、高耐热以及阻燃特性，常应用工业生产以及居家用品中，目前阻燃ABS仅仅只能应用于需阻燃环境，即阻燃ABS无法根据使用环境，来进行常规的抗菌操作，使用范围较窄，难以满足使用者的多样化使用需求问题。
为实现上述目的，本发明提供如下技术方案：
一种阻燃抗菌ABS材料，所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂，所述阻燃抗拒ABS材料的配比为ABS树脂50%、阻燃剂10%、银离子粉末2%、环氧树脂粘合剂4%、润滑剂6%、偶联剂8%、增塑剂8%、竹纤维10%以及抗氧化剂2%，所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂均独立进行干燥存放。
优选的，所述阻燃剂为十溴联苯醚和三氧化二锑，所述十溴联苯醚和三氧化二锑比例为2:1时为最佳阻燃效果。
优选的，所述润滑剂为硬脂酸钙、氧化聚乙烯粉末、硬脂酸颗粒、硬脂酸甘油酯粉末、石蜡以及聚乙烯白色粉末中的一种或两种的混合物。
优选的，所述偶联剂为氨基硅烷、甲氧基硅烷和乙烯基硅烷中的一种或两种的混合物。
优选的，所述增塑剂为己二酸二辛酯、癸二酸二丁酯、已二酸二正丁酯和邻苯二甲酸二丁酯中一种或两种的混合物。
优选的，所述竹纤维为粉末状，优选干燥良好的竹纤维粉末。
一种阻燃抗菌ABS材料的制备方法，所述阻燃抗菌ABS材料的制备流程为原料准备、原料预处理、原料混合以及物料冷却成型。
优选的，所述阻燃抗菌ABS材料的制备流程如下：
步骤一：准备ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等材料；
步骤二：将ABS树脂放入至八十摄氏度环境中进行两小时的烘干处理，其次将竹纤维粉末放入至七十度摄氏度环境中进行一小时的烘干处理，且在烘干完毕后进行自然冷却操作；
步骤三：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂放入至搅拌釜内，进行混合搅拌，并控制搅拌时间为一至两小时；
步骤四：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等混合后的物料，置于双螺杆挤出机内进行挤出操作；
步骤五：挤出后通过冷却设备对挤出物进行快速定型，且在定型后得阻燃抗菌ABS材料；
与现有技术相比，本发明提供了一种阻燃抗菌ABS材料及其制备方法，具备以下有益效果：
本发明为了提高阻燃ABS的抗菌效果，采用了银离子粉末以及竹纤维粉末这两种物质，该两种物质在组合过程中，可对阻燃ABS内部进行混合处理，处理后银离子对阻燃ABS表面细菌具有强有力的灭活效果，同时竹纤维粉末本身自带的抗菌、抑菌以及耐磨特性，可进一步提高阻燃ABS的抗菌以及耐使用特点，该类特点可在保持阻燃ABS的原有阻燃特性下，获得多样化的使用特性。
具体实施方式
基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种阻燃抗菌ABS材料及其制备方法技术方案：
一种阻燃抗菌ABS材料，包括阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂，阻燃抗拒ABS材料的配比为ABS树脂50%、阻燃剂10%、银离子粉末2%、环氧树脂粘合剂4%、润滑剂6%、偶联剂8%、增塑剂8%、竹纤维10%以及抗氧化剂2%，阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂均独立进行干燥存放。
一种阻燃抗菌ABS材料，包括阻燃剂为十溴联苯醚和三氧化二锑，十溴联苯醚和三氧化二锑比例为2:1时为最佳阻燃效果。
一种阻燃抗菌ABS材料，包括润滑剂为硬脂酸钙、氧化聚乙烯粉末、硬脂酸颗粒、硬脂酸甘油酯粉末、石蜡以及聚乙烯白色粉末中的一种或两种的混合物。
一种阻燃抗菌ABS材料，包括偶联剂为氨基硅烷、甲氧基硅烷和乙烯基硅烷中的一种或两种的混合物。
一种阻燃抗菌ABS材料，包括增塑剂为己二酸二辛酯、癸二酸二丁酯、已二酸二正丁酯和邻苯二甲酸二丁酯中一种或两种的混合物。
一种阻燃抗菌ABS材料，包括竹纤维为粉末状，优选干燥良好的竹纤维粉末。
一种阻燃抗菌ABS材料制备方法，包括阻燃抗菌ABS材料的制备流程为原料准备、原料预处理、原料混合以及物料冷却成型。
一种阻燃抗菌ABS材料制备方法，包括阻燃抗菌ABS材料的制备流程如下：
步骤一：准备ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等材料；
步骤二：将ABS树脂放入至八十摄氏度环境中进行两小时的烘干处理，其次将竹纤维粉末放入至七十度摄氏度环境中进行一小时的烘干处理，且在烘干完毕后进行自然冷却操作；
步骤三：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂放入至搅拌釜内，进行混合搅拌，并控制搅拌时间为一至两小时；
步骤四：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等混合后的物料，置于双螺杆挤出机内进行挤出操作；
步骤五：挤出后通过冷却设备对挤出物进行快速定型，且在定型后得阻燃抗菌ABS材料；
本发明的工作原理及使用流程：准备ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等材料，其后将ABS树脂放入至八十摄氏度环境中进行两小时的烘干处理，其次将竹纤维粉末放入至七十度摄氏度环境中进行一小时的烘干处理，且在烘干完毕后进行自然冷却操作，其后将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂放入至搅拌釜内，进行混合搅拌，并控制搅拌时间为一至两小时，其后将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等混合后的物料，置于双螺杆挤出机内进行挤出操作，且在挤出后通过冷却设备对挤出物进行快速定型，定型后得阻燃抗菌ABS材料。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种阻燃抗菌ABS材料，其特征在于：所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂，所述阻燃抗拒ABS材料的配比为ABS树脂50%、阻燃剂10%、银离子粉末2%、环氧树脂粘合剂4%、润滑剂6%、偶联剂8%、增塑剂8%、竹纤维10%以及抗氧化剂2%，所述阻燃抗拒ABS材料制备原料为ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂均独立进行干燥存放。
2.根据权利要求1所述的一种阻燃抗菌ABS材料，其特征在于：所述阻燃剂为十溴联苯醚和三氧化二锑，所述十溴联苯醚和三氧化二锑比例为2:1时为最佳阻燃效果。
3.根据权利要求1所述的一种阻燃抗菌ABS材料，其特征在于：所述润滑剂为硬脂酸钙、氧化聚乙烯粉末、硬脂酸颗粒、硬脂酸甘油酯粉末、石蜡以及聚乙烯白色粉末中的一种或两种的混合物。
4.根据权利要求1所述的一种阻燃抗菌ABS材料，其特征在于：所述偶联剂为氨基硅烷、甲氧基硅烷和乙烯基硅烷中的一种或两种的混合物。
5.根据权利要求1所述的一种阻燃抗菌ABS材料，其特征在于：所述增塑剂为己二酸二辛酯、癸二酸二丁酯、已二酸二正丁酯和邻苯二甲酸二丁酯中一种或两种的混合物。
6.根据权利要求1所述的一种阻燃抗菌ABS材料，其特征在于：所述竹纤维为粉末状，优选干燥良好的竹纤维粉末。
7.一种阻燃抗菌ABS材料的制备方法，其特征在于：所述阻燃抗菌ABS材料的制备流程为原料准备、原料预处理、原料混合以及物料冷却成型。
8.根据权利要求7所述的一种阻燃抗菌ABS材料制备方法，其特征在于：所述阻燃抗菌ABS材料的制备流程如下：
步骤一：准备ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等材料；
步骤二：将ABS树脂放入至八十摄氏度环境中进行两小时的烘干处理，其次将竹纤维粉末放入至七十度摄氏度环境中进行一小时的烘干处理，且在烘干完毕后进行自然冷却操作；
步骤三：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂放入至搅拌釜内，进行混合搅拌，并控制搅拌时间为一至两小时；
步骤四：将ABS树脂、阻燃剂、银离子粉末、环氧树脂粘合剂、润滑剂、偶联剂、增塑剂、竹纤维以及抗氧化剂等混合后的物料，置于双螺杆挤出机内进行挤出操作；
步骤五：挤出后通过冷却设备对挤出物进行快速定型，且在定型后得阻燃抗菌ABS材料。