CN112961010A - 一种剑麻专用土壤调理剂及其制备方法 - Google Patents
一种剑麻专用土壤调理剂及其制备方法 Download PDFInfo
- Publication number
- CN112961010A CN112961010A CN202110219920.2A CN202110219920A CN112961010A CN 112961010 A CN112961010 A CN 112961010A CN 202110219920 A CN202110219920 A CN 202110219920A CN 112961010 A CN112961010 A CN 112961010A
- Authority
- CN
- China
- Prior art keywords
- sisal
- soil conditioner
- organic fertilizer
- parts
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种剑麻专用土壤调理剂，由下述重量份的原料制成：白云石粉13.6‑33.2份，有机肥63.6‑85.8份，椰糠0‑4.8份。制备方法为：按照上述剑麻专用土壤调理剂称取各原料；将各原料混合均匀，即得剑麻专用土壤调理剂，本发明土壤调理剂富含剑麻大量需要钙、镁营养元素及有机肥，且其钙、镁处于活性状态，剑麻容易吸收利用，可满足剑麻对钙、镁元素需要，促剑麻健壮生长，减少因缺钙、镁造成剑麻病害发生，有机肥含养分齐全，富含活性物质，可显著促进剑麻生长。本发明土壤调理剂安全性高，剑麻根系可在其上直接生长，不产生肥害，制备方法简便，价格便宜，利于大规模推广应用。
Description
技术领域
本发明属于土壤调理剂技术领域，更具体的说是涉及一种剑麻专用土壤调理剂及其制备方法。
背景技术
剑麻是龙舌兰科多年生热带麻类植物，其纤维质地坚韧、富有弹性、拉力强，且耐酸碱、耐腐蚀，用于制作绳缆、帆布、绳芯、传送带、地毯等，广泛用于国防、渔捞航海、石油、工矿、治金、日常生活等行业，是重要工农业原料。全世界龙舌兰麻主要种植在巴西、坦桑尼亚、肯尼亚、马达加斯加、墨西哥和中国。中国剑麻主要种植在广东湛江，广西玉林、南宁，海南昌江和东方。这些地区土壤大多为玄武岩、花岗岩，第四世纪红土发育而成，酸化严重，有机质、大量元素氮、磷、钾，中微量元素钙、镁、硼等元素缺乏。剑麻需要钙营养元素最多，其次是钾、氮、镁、磷，每年剑麻叶收获都带走大量钙、钾、氮、镁、磷等营养元素。与其他作物相比，剑麻的一个主要特点是需要钙、镁很高，而我国栽植剑麻园土壤普遍缺钙、缺镁，同补氮、磷、钾一样，补钙、补镁成为剑麻生产中重要一环。
目前市场改良土壤酸性土壤调理剂有天然矿物质和有机物类：如生石灰、沸石、白云石粉、膨润土、牡蛎壳、贝壳粉、泥炭等；农业废弃物类：如作物秸秆、畜禽粪便、豆科绿肥、菇渣、鱼产品下脚料；工业废弃物类：如污水污泥、粉煤灰、生物质发电灰、高炉渣、碱渣、磷石膏、造纸废弃物等；人工生产与合成类：如硅钙钾镁肥、由畜禽粪便、农业废弃物类生产有机肥、生物质炭、有机-无机复合土壤调理剂等。
天然矿物类和人工生产矿质型土壤调理剂如生石灰、碳酸钙、白云石粉、牡蛎壳粉、硅钙钾镁肥能很好满足剑麻生长对钙或钙镁需要，生石灰含钙量较高，也含有一定镁，价格便宜，在剑麻产区易于购买，目前在剑麻上普遍被应用，但生石灰属强碱性，在施用中撒起粉尘易造成人眼睛等身体上伤害，长期单独施用还易引起土壤板结，不利剑麻生长，劳动者普遍不愿意施用，但没有更好替代物。白云石粉主要成份为碳酸钙、碳酸镁，腐蚀性不强，实验也证明对种植在酸性较强土壤上施用白云石粉可促进剑麻生长，但白云石粉肥效较为缓慢，在强酸性土壤上表现较好，长期单独施用也易引起土壤板结。牡蛎壳粉含有机物，含钙量较高，改土效果较好，但其含镁较少，且价格较贵。生物质发电灰是生物质燃烧发电残留灰分，和草木灰一样，改良酸性土壤效果较好，但其含钙较少，质轻，价格相对较贵。污泥、粉煤灰、高炉渣、碱渣、磷石膏具有一定酸性改土效果，但其重金属含量较高，长期大量施用会引起土壤污染。造纸废弃物含有较多化学物质，施用过多对土壤造成污染。人工生产有机肥、生物质炭不但可提高土壤pH值，还可提高土壤有机质含量，但其含钙量较少，不能满足剑麻对钙需要，且单独施用有机肥成本较高。
有机－无机复合土壤调理剂是以腐殖酸或其他有机物、含钙天然矿物类为主要原料经过一定工艺制造的一种土壤调理剂，有机-无机复合土壤调理剂可以调节土壤pH值，促进根系生长、促进土壤有益微生物活动，活化土壤中中微量元素，促进作物对养分吸收利用。但剑麻需要钙量极大，普通有机-无机复合土壤调理剂难以满足剑麻对钙需求，而且以腐殖酸为主要原料土壤调理剂成本较高，往往需要2000-3500元/吨。剑麻栽培效益不高，每吨剑麻叶仅为350-420元，以亩产8吨计算(较高产，普遍只有5吨/亩)，亩产值仅有3040-3360元，因而应用市售有机－无机复合土壤调理剂除了不能满足剑麻对钙需要，而且较高价格也限制了其在剑麻上应用。广东农垦丰收肥厂采用在发酵完有机肥上添加20％生石灰方法制造成有机-无机复合土壤调理剂，专门用于剑麻上，但添加20％生石灰易引起有机质中氮挥发损失，且易引起有机肥板结，不利剑麻根系生长和对钙、镁元素吸收。所以适合剑麻专用土壤调理剂一方面价格要低，另一方面含钙、镁较高，并可长期施用不引起土壤板结。
因此，研发一种钙、镁含量高、成本低廉、腐蚀性弱、碱性弱、重金属含量低、施用方便，可以长期施用不引起土壤板结，促根生长，且不易引起有机肥中氮挥发损失的一种剑麻专用土壤调理剂及其制备方法是本领域技术人员亟需解决的问题。
发明内容
有鉴于此，本发明提供了一种剑麻专用土壤调理剂及其制备方法。
为了实现上述目的，本发明采用如下技术方案：
一种剑麻专用土壤调理剂，由下述重量份的原料制成：白云石粉13.6-33.2份，有机肥63.6-85.8份，椰糠0-4.8份。
本发明的有益效果：白云石粉在剑麻种植华南区域分布较多，取材方便，价格便宜，含钙、镁较高，而且腐蚀性弱，碱性弱，不易与有机肥中氮化合物反应造成有机物中氮挥发损失。
有机肥养分齐全，富含活性物质，可显著促进剑麻生长。
本发明土壤调理剂添加了疏松剂椰糠，很多土壤调理剂或有机肥放置时间久后就比较板结，一方面造成施用困难，另外一方面效果不好，特别是有机肥+生石灰制造土壤调理剂，板结土壤调理剂和有机肥不利于作物根系生长，本发明添加疏松剂椰糠后，其制成土壤调理剂疏松、透气，非常有利于作物根系生长，从而促进作物生长和产量提高。
本发明将重金属含量低、价格便宜天然矿物-白云石粉(含CaO33％，MgO22％)来代替生石灰，并配以有机肥，让有机肥中有机酸、腐植酸酸解、螯合白云石粉中钙、镁，同时添加一定量疏松剂-椰糠来解决有机-无机肥混合造成板结问题。这种土壤调理剂没有粉尘、腐蚀性弱，施用方便，且不易引起有机肥中氮挥发损失，调理剂中有机肥增加了白云粉中钙、镁有效性，添加椰糠可使土壤调理剂疏松透气，本发明土壤调理剂富含剑麻大量需要钙、镁营养元素和有机肥，且其钙、镁处于活性状态，剑麻容易吸收利用，可满足剑麻对钙、镁元素需要，促剑麻健壮生长，减少因缺钙、镁造成剑麻病害发生，有机肥中大中微量元素和活性物质也促进剑麻生长，且安全性高，剑麻根系可在土壤调理剂上直接生长，不产生肥害。
与现有技术有机肥+20％生石灰相比，本发明土壤调理剂盆栽处理幼苗剑麻生物量增加26.4％-118.7％，效果非常显著。
进一步，上述白云石粉的粒径≤100目。
采用上述进一步的有益效果：白云石粉为白云石粉碎后过100目筛，粒径≤100目，较细白云石粉有利于其钙、镁与土壤调理剂中有机肥里含有机酸、腐植酸、黄腐酸螯合，提高其作物有效性。
进一步，上述所述有机肥为腐熟羊粪有机肥、腐熟鸡粪有机肥、腐熟猪粪有机肥、蚯蚓粪有机肥中的一种或几种的混合。
采用上述进一步的有益效果：上述有机肥养分齐全，富含活性物质，可显著促进剑麻生长。
进一步，上述剑麻专用土壤调理剂由下述重量份的原料制成：白云石粉13.6-31.7份，腐熟羊粪有机肥、腐熟鸡粪有机肥或腐熟猪粪有机肥63.6-81.7份，椰糠4.8份；
优选为白云石粉13.6份，腐熟羊粪有机肥81.7份，椰糠4.8份；
优选为白云石粉23.7份，腐熟鸡粪有机肥或腐熟猪粪有机肥71.5份，椰糠4.8份。
进一步，上述剑麻专用土壤调理剂由下述重量份的原料制成：白云石粉14.2-33.2份，蚯蚓粪有机肥66.8-85.8份，优选为白云石粉14.2份，蚯蚓粪有机肥85.8份。
采用上述进一步的有益效果：不同有机物与白云石粉配比存在差异，主要是不同有机物特性不同，腐熟羊粪有机肥碱性较强，需要配备白云石粉比例较少，鸡粪或腐熟猪粪有机肥酸性含量较高，需要配备白云石粉比例较高，蚯蚓粪有机肥为微酸性，但其有机物含量较少，需要配备白云石粉比例也较少。本发明试验了不同有机物料与白云石粉比例不同配比，筛选了最适合剑麻生长不同有机物料与白云石粉配比，可发挥出剑麻对钙、镁需要和有机物料需要，较好促进剑麻生长。
本发明还提供一种剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)按照上述剑麻专用土壤调理剂称取各原料；
(2)将各原料混合均匀，即得上述剑麻专用土壤调理剂。
本发明的有益效果：本发明剑麻专用土壤调理剂的制备方法简便，价格便宜，利于大规模推广应用。
进一步，上述混合转速为20-30r/min，混合时间为30-40min。
采用上述进一步的有益效果：使原料混合均匀，产品质量均一稳定。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉13.6kg，腐熟羊粪有机肥81.7kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为20r/min，混合时间为30min，即得剑麻专用土壤调理剂。
对比例1：
称取生石粉20kg，腐熟羊粪有机肥100kg，混合均匀，即得土壤调理剂。
实施例1施用效果：与对比例1土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例1盆栽幼苗剑麻生物量增长62.3％。
实施例2
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉23.7kg，腐熟羊粪有机肥71.5kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为20r/min，混合时间为30min，即得剑麻专用土壤调理剂。
实施例2施用效果：与对比例1土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例2盆栽幼苗剑麻生物量增长41.8％。
实施例3
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉31.7kg，腐熟羊粪有机肥63.6kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为20r/min，混合时间为30min，即得剑麻专用土壤调理剂。
实施例3施用效果：与对比例1土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例3盆栽幼苗剑麻生物量增长19.9％。
实施例4
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉13.6kg，腐熟鸡粪有机肥81.7kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为25r/min，混合时间为35min，即得剑麻专用土壤调理剂。
对比例2：
称取生石粉20kg，腐熟鸡粪有机肥100kg，混合均匀，即得土壤调理剂。
实施例4施用效果：与对比例2土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例4盆栽幼苗剑麻生物量增长9.1％。
实施例5
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉23.7kg，腐熟鸡粪有机肥71.5kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为25r/min，混合时间为35min，即得剑麻专用土壤调理剂。
实施例5施用效果：与对比例2土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例5盆栽幼苗剑麻生物量增长32.4％。
实施例6
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉31.7kg，腐熟鸡粪有机肥63.6kg，椰糠4.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为25r/min，混合时间为35min，即得剑麻专用土壤调理剂。
实施例6施用效果：与对比例2土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例6盆栽幼苗剑麻生物量增长26.4％。
实施例7
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉14.2kg，蚯蚓粪有机肥85.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为30r/min，混合时间为40min，即得剑麻专用土壤调理剂。
对比例3：
称取生石粉20kg，蚯蚓粪有机肥100kg，混合均匀，即得土壤调理剂。
实施例7施用效果：与对比例3土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例7盆栽幼苗剑麻生物量增长118.7％。
实施例8
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉24.9kg，腐熟蚯蚓粪有机肥75.1kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为30r/min，混合时间为40min，即得剑麻专用土壤调理剂。
实施例8施用效果：与对比例3土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例8盆栽幼苗剑麻生物量增长66.9％。
实施例9
剑麻专用土壤调理剂的制备方法，包括以下步骤：
(1)称取白云石粉33.2kg，腐熟蚯蚓粪有机肥66.8kg，白云石粉的粒径≤100目；
(2)将各原料混合均匀，混合转速为30r/min，混合时间为40min，即得剑麻专用土壤调理剂。
实施例9施用效果：与对比例3土壤调理剂相比，在用量相同盆栽幼苗试验中，实施例9盆栽幼苗剑麻生物量增长51.1％。
对比实验
土壤调理剂1：称取白云石粉24.9kg，腐熟鸡粪有机肥75.1kg，白云石粉的粒径≤100目，将各原料混合均匀，混合转速为25r/min，混合时间为35min，即得剑麻专用土壤调理剂。
土壤调理剂2：称取白云石粉23.7kg，腐熟鸡粪有机肥71.5kg，椰糠4.8kg，白云石粉的粒径≤100目，将各原料混合均匀，混合转速为25r/min，混合时间为35min，即得剑麻专用土壤调理剂。
施用效果对比：添加了椰糠土壤调理剂2效果最好，其盆栽幼苗剑麻生物量比不添椰糠的土壤调理剂1高11.5％，说明本发明添加疏松剂椰糠后，其制成土壤调理剂疏松、透气，非常有利于作物根系生长，从而促进作物生长和产量提高。
对所公开的实施例的说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (7)
1.一种剑麻专用土壤调理剂，其特征在于，由下述重量份的原料制成：白云石粉13.6-33.2份，有机肥63.6-85.8份，椰糠0-4.8份。
2.根据权利要求1所述一种剑麻专用土壤调理剂，其特征在于，所述白云石粉的粒径≤100目。
3.根据权利要求1所述一种剑麻专用土壤调理剂，其特征在于，所述有机肥为腐熟羊粪有机肥、腐熟鸡粪有机肥、腐熟猪粪有机肥、蚯蚓粪有机肥中的一种或几种的混合。
4.根据权利要求3所述一种剑麻专用土壤调理剂，其特征在于，由下述重量份的原料制成：白云石粉13.6-31.7份，腐熟羊粪有机肥、腐熟鸡粪有机肥或腐熟猪粪有机肥63.6-81.7份，椰糠4.8份。
5.根据权利要求3所述一种剑麻专用土壤调理剂，其特征在于，由下述重量份的原料制成：白云石粉14.2-33.2份，蚯蚓粪有机肥66.8-85.8份。
6.一种剑麻专用土壤调理剂的制备方法，其特征在于，包括以下步骤：
(1)按照权利要求1-5任一项所述剑麻专用土壤调理剂称取各原料；
(2)将各原料混合均匀，即得所述剑麻专用土壤调理剂。
7.根据权利要求6所述一种剑麻专用土壤调理剂的制备方法，其特征在于，所述混合转速为20-30r/min，混合时间为30-40min。