CN112830470A - Preparation and application method of pine charcoal - Google Patents
Preparation and application method of pine charcoal Download PDFInfo
- Publication number
- CN112830470A CN112830470A CN202110033645.5A CN202110033645A CN112830470A CN 112830470 A CN112830470 A CN 112830470A CN 202110033645 A CN202110033645 A CN 202110033645A CN 112830470 A CN112830470 A CN 112830470A
- Authority
- CN
- China
- Prior art keywords
- pine
- charcoal
- pine charcoal
- preparation
- phenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method and an application method of pine charcoal. The preparation method of the pine charcoal comprises the following steps: cleaning pine, and grinding into powder; calcining pine wood powder at high temperature in N2Calcining at 600 ℃ for 2h under the environment protection to obtain the pine charcoal. Placing pine charcoal adsorbent into phenol solution with different concentrations, wherein the amount of pine charcoal is 2.5g/L, and the concentration of phenol solution is 50mgL‑1‑200mgL‑1The rotating speed of the shaking table is 150 rpm; adsorption reaction for 24 hoursAnd stopping, and filtering and separating the pine charcoal residue to obtain the phenol solution after adsorption and decrement. The process for preparing the pine charcoal is simple and convenient, and the efficiency of the pine charcoal for adsorbing phenol is higher.
Description
Technical Field
The invention belongs to the technical field of biomass recycling, and particularly relates to a preparation method and an application method of pine charcoal.
Background
Phenolic compounds are an important chemical raw material. However, due to improper emission, the organic fertilizer is widely distributed in various environmental media such as water environment, soil environment and the like, and the large exposure of the organic fertilizer can harm human health. At present, common methods for removing the phenol pollutants comprise an adsorption method, a membrane filtration method, advanced oxidative degradation and the like. In the adsorption process, the choice of adsorbent is particularly important. The biochar has wide raw materials, simple and convenient preparation method and good adsorption performance, and is widely concerned in various fields. This patent technique adopts the pine raw materials to calcine the preparation pine charcoal to the phenol that exists in the environment to adsorb with this adsorbing material and handle phenol, in order to reach the effect that the decrement was eliminated.
The invention content is as follows:
the invention aims to solve the problem of phenolic compound treatment, provides a high-efficiency and low-cost charcoal adsorbing material, and provides a preparation method and an application method of pine charcoal.
In order to achieve the purpose, the invention adopts the following scheme:
wherein the preparation of the pine charcoal comprises the following steps:
(1) cleaning pine, and grinding into powder;
(2) calcining pine wood powder at high temperature in N2Calcining at 600 ℃ for 2h under the environment protection to obtain the pine charcoal.
The method is specifically applied as follows:
(1) putting the pine wood charcoal into the phenol water solution to be treated, wherein the using amount of the biochar is 2.5g/L, and the phenol concentration is 50mg L-1-200mg L-1Adjusting the rotation speed to 150rpm for adsorption;
(2) and stopping the adsorption reaction for 24 hours, and filtering and separating the biochar residue to obtain the adsorption reduction post-treatment liquid.
The invention has the advantages that: the process for preparing the biochar is simple and convenient, the efficiency of adsorbing phenol by the biochar is high, and the treatment period only needs 24 hours. The biochar can be widely applied to soil and water pollution remediation, and is wide in application range.
Detailed Description
The present invention is further described in the following examples, but the technical content described in the examples is illustrative and not restrictive, and the scope of the present invention should not be limited thereby.
Example 1
(1) Cleaning pine, and grinding into powder;
(2) calcining pine wood powder at high temperature in N2Calcining at 600 ℃ for 2h under the environment protection to obtain pine charcoal;
(3) putting pine charcoal into the phenol water solution to be treated, wherein the pine charcoal dosage is 2.5g/L, and the phenol concentration is 100mg L-1Adjusting the rotation speed to 150rpm for adsorption;
(4) the adsorption reaction is stopped after 24 hours, and the phenol solution after adsorption reduction is obtained after the biochar residue is filtered and separated, wherein the phenol environment residue is 24.66mg/L, and the removal rate is 75.34%.
Example 2
(1) Cleaning pine, and grinding into powder;
(2) calcining pine wood powder at high temperature in N2Calcining at 600 ℃ for 2h under the environment protection to obtain pine charcoal;
(3) putting the pine charcoal into the phenol water solution to be treated, wherein the pine charcoal dosage is 2.5g/L, and the phenol concentration is 80mg L-1Adjusting the rotation speed to 150rpm for adsorption;
(4) the adsorption reaction is stopped after 24 hours, and the phenol solution after adsorption reduction is obtained after the biochar residue is filtered and separated, wherein the phenol environment residue is 13.41mg/L, and the removal rate is 83.24%.
The above description is only a preferred embodiment of the present invention, and the description of the embodiment is only for the purpose of helping understanding the central idea of the present invention. For a person skilled in the art, several modifications can be made to the invention, which also fall within the scope of the claims.
Claims (2)
1. A preparation and application method of pine charcoal is characterized in that the prepared pine charcoal is used for adsorbing phenol;
the preparation method of the pine charcoal comprises the following steps: cleaning pine, and grinding into powder; calcining pine wood powder at high temperature in N2Calcining at 600 ℃ for 2h under the environment protection to obtain the pine charcoal.
2. The method of claim 1, wherein pine charcoal is added to a phenol solution of varying concentration, wherein the amount of pine charcoal is 2.5g/L and the concentration of the phenol solution is 50mg L-1-200mg L-1The rotation speed of the shaking table is set to be 150rpm, and the adsorption reaction is carried out for 24 hours.